ASTM D4438-2013 Standard Test Method for Particle Size Distribution of Catalysts and Catalyst Carriers by Electronic Counting《利用电子计数法测定催化剂和催化剂载体粒度分布的标准试验方法》.pdf

《ASTM D4438-2013 Standard Test Method for Particle Size Distribution of Catalysts and Catalyst Carriers by Electronic Counting《利用电子计数法测定催化剂和催化剂载体粒度分布的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4438-2013 Standard Test Method for Particle Size Distribution of Catalysts and Catalyst Carriers by Electronic Counting《利用电子计数法测定催化剂和催化剂载体粒度分布的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4438 13Standard Test Method forParticle Size Distribution of Catalysts and Catalyst Carriersby Electronic Counting1This standard is issued under the fixed designation D4438; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revis

2、ion, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the determination of particlesize distribution of catalyst and catalyst carri

3、er particles usingan electroconductive sensing method and is one of severalvaluable methods for the measurement of particle size.1.2 The range of particle sizes investigated was 20 to 150m (see IEEE/ASTM SI 10) equivalent spherical diameter. Thetechnique is capable of measuring particles above and b

4、elowthis range. The instrument used for this method is an electriccurrent path of small dimensions that is modulated by indi-vidual particle passage through an aperture, and producesindividual pulses of amplitude proportional to the particlevolume.1.3 This standard does not purport to address all of

5、 thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1193 Specification for

6、Reagent WaterE177 Practice for Use of the Terms Precision and Bias inASTM Test MethodsE691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test MethodIEEE/ASTM SI 10 Standard for Use of the InternationalSystem of Units (SI): The Modern Metric System3. Summary of Test

7、Method3.1 Acarefully dispersed, dilute suspension of the sample ina beaker filled with an electrolyte is placed in the countingposition on the instrument sample stand. The suspension isforced through a restricting aperture. Each passing particle isrecorded on an electronic counter, and the data are

8、accumulatedaccording to selected particle size intervals for subsequentprocessing.3.2 The instrument response is proportional to liquid dis-placement by the particle volume. Equivalent spherical diam-eter is commonly used to express the particle size.4. Significance and Use4.1 This test method can b

9、e used to determine particle sizedistributions for material specifications, manufacturing control,and research and development work in the particle size rangeusually encountered in fluidizable cracking catalysts.5. Apparatus35.1 Electronic Particle Counter, with sample stand andstirring motor.5.2 Ap

10、erture Tubes, with varying diameters. The diameterrequired is dependent upon the particle size distribution of thesample. Generally, any given tube will cover a particle sizerange from 2 to 40 % of its aperture diameter.5.3 Ultrasonic Tank, 100 W.5.4 Beaker, 100-mL.5.5 Graduated Glass Pipet, 5-mL.5.

11、6 Wash Bottles.5.7 Membrane Filtering Device with 0.22-m filters.5.8 Round-Bottom Sample Beakers, 250-mL.5.9 Micro-Riffler or Chute Riffler.6. Reagents6.1 Purity of ReagentsReagent grade chemicals shall beused in all tests. Unless otherwise indicated, it is intended thatall reagents shall conform to

12、 the specifications of the Commit-tee on Analytical Reagents of the American Chemical Society,1This test method is under the jurisdiction of ASTM Committee D32 onCatalysts and is the direct responsibility of Subcommittee D32.02 on Physical-Mechanical Properties.Current edition approved Dec. 1, 2013.

13、 Published December 2013. Originallyapproved in 1985. Last previous edition approved in 2007 as D4438 85 (2007).DOI: 10.1520/D4438-13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume info

14、rmation, refer to the standards Document Summary page onthe ASTM website.3Supporting data have been filed at ASTM International Headquarters and maybe obtained by requesting Research Report RR:D32-1011.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959

15、. United States1where such specifications are available.4Other grades may beused, provided it is first ascertained that the reagent is ofsufficiently high purity to permit its use without lessening theaccuracy of the determination.6.2 Purity of WaterUnless otherwise indicated, referencesto water sha

16、ll be understood to mean reagent water conformingto Specification D1193, Type II.6.3 ElectrolyteDissolve 10.0 g of reagent grade sodiumchloride (NaCl) in 1 L of distilled or deionized water and filtertwice through a 0.22-m filter.NOTE 1Commercially available Electrolyte solution of the sameconcentra

17、tion can also be used, but should be filtered for apertures smallerthan 100 m.6.4 Wash WaterDistilled or deionized water, twice filteredthrough a 0.22-m filter. Electrolyte may also be used as washwater.6.5 Calibration Spheres5, Near monosized, having a relativestandard deviation from the mean of le

18、ss than 5 %, orequivalent, as certified by the manufacturer.7. Procedure7.1 Follow instrument manufacturers instruction manualfor instrument settings.7.2 Follow the manufacturers instructions for calibratingeach aperture and electrolyte combination that will be used.7.3 Before each analysis, using t

19、he wash bottle and filteredwash water, wash all surfaces coming in contact with thesample.7.4 Place 150 to 200 mL of electrolyte in a round-bottombeaker on the sample stand with the stirring rod turningmoderately fast. Position the stirring blades near the bottom ofthe beaker and increase the stirre

20、r speed to a rate just below airbubble formation (Note 2). Follow the instruction manual andtake several background counts. If they exceed the limit in themanual for the aperture in use, refilter the electrolyte and flushthe glassware. If the background is due to electricalinterference, the instrume

21、nt manufacturers recommendationsfor sample should not be used when it can disintegrate fragileprimary particles.NOTE 2Proper adjustment of the position and speed of the stirrer willprevent the loss of large particles by settling and formation of air bubblesduring counting.7.4.1 Transfer the sample i

22、nto a 250-mL round-bottombeaker containing about 200 mL of clean electrolyte. Be sureall the sample is transferred.7.4.2 Place the sample and beaker (from 7.4.1)intheinstrument sampling stand. Adjust the stirring blades close tothe bottom of the round-bottom beaker so that they effectivelysweep the

23、bottom of the beaker to maintain all particlesuniformly in suspension.7.4.3 During stirring, using a 5-mL pipet, transfer 2 mL ofthe sample suspension (from 7.4.2) to another 250-mL round-bottom beaker containing 200 mL of clean electrolyte. Be sureall the contents in the pipet are transferred.7.4.4

24、 Remove the beaker (from 7.4.1) from the samplingstand. Flush the outside of the aperture tube, the stirrer, andouter electrode. Place the sample and beaker from 7.4.3 in thesampling stand. Adjust the stirring blades close to the bottomof the round-bottom beaker so that they effectively sweep thebot

25、tom of the beaker again. Increase the stirrer speed moder-ately. Check for particle settling by visually observing thestirring system with a flashlight and viewing the surfaceperpendicular to the bottom. If particles are observed settling,increase stirring rate without generating air bubbles or incr

26、easethe electrolyte viscosity, or both.NOTE 3Electrolyte viscosity can be increased, for example, by addingfiltered glycerol up to 30 % by volume.7.4.5 Initiate a preliminary count and check that the totalcount is in the range suggested in the manufacturers instruc-tions to avoid excessive coinciden

27、ce loss. If the count is toohigh, adjust by diluting with clean electrolyte.7.4.6 Initiate an analysis count, and accumulate and processdata in accordance with the manufacturers instructions. Forincreased precision take a total of three sets of data and averagethem. If the resulting data in differen

28、tial volume form showmore than a few percent in the smallest active channel,additional data may be obtained using a smaller aperture afterlarge particles are scalped from the sample. Data from bothapertures may then be combined, as described in the instrumentmanufacturers instruction manual, althoug

29、h this step is be-yond the scope of this test method.8. Presentation of Data8.1 The instrument measures the volume of each particle.Assuming all the particles in the sample have the same density,relative volume and weight can be considered to be inter-changeable; therefore, cumulative and differenti

30、al volume orweight percent can be printed or graphed directly from theaccumulated data.8.2 Results for samples containing mixed densities shouldbe expressed as volume percent instead of weight percent andcannot be compared to a direct weight analysis method.NOTE 4Comparisons with other techniques ha

31、ve been found to begood for spherical particles within the sensing range covered by theaperture or apertures used. For non-spherical particles, and especially forelongated or plate-like particles, results may vary considerably.8.3 Data are accumulated on a number basis, and may beprocessed in that f

32、orm as well.8.4 The median diameter is taken as the diameter corre-sponding to the 50th percentile of the cumulative volumedistribution. This can be determined manually by drawing aline connecting the incremental segments corresponding toeach data storage channel as shown in the sample curve in Fig.

33、1. A perpendicular is then dropped to the X-axis scale from theintersection of the drawn line and the 50th percentile grid line.4“Reagent Chemicals, American Chemical Society Specifications,” Am. Chemi-cal Soc., Washington, DC. For suggestions on the testing of reagents not listed bythe American Che

34、mical Society, see “Analar Standards for Laboratory U.K.Chemicals,” BDH Ltd., Poole, Dorset, and the “United States Pharmacopeia.”5Calibration spheres or equivalent calibration materials are generally availablefrom respective instrument manufacturers.D4438 1329. Precision and Bias39.1 PrecisionBased

35、 on the results of a multilaboratorystudy and using the procedures and definitions of Practice E177and Practice E691 the single-laboratory, single-day repeatabil-ity is 62.3 % (2S %) of the mean of the measurements of thevolume percent median equivalent spherical diameter. Themultilaboratory, multid

36、ay reproducibility is 64.6 % (2S %) ofthe mean of the measurements of the volume percent medianequivalent spherical diameter, when a common calibrationstandard is used.9.2 BiasReference standards have not yet been certified todetermine the bias of this test method.10. Keywords10.1 catalyst; electroc

37、onductive sensing; particle sizeASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof

38、infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this st

39、andard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your

40、 views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by cont

41、acting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).FIG. 1 Median Diameter-Sample CurveD4438 133