《ASTM C140 C140M-2017 Standard Test Methods for Sampling and Testing Concrete Masonry Units and Related Units《混凝土砌块和相关砌块取样和测试的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM C140 C140M-2017 Standard Test Methods for Sampling and Testing Concrete Masonry Units and Related Units《混凝土砌块和相关砌块取样和测试的标准试验方法》.pdf（36页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C140/C140M 16C140/C140M 17Standard Test Methods forSampling and Testing Concrete Masonry Units and RelatedUnits1This standard is issued under the fixed designation C140/C140M; the number immediately following the designation indicates the yearof original adoption or, in the case of revi

2、sion, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 These test me

3、thods provide various testing procedures commonly used for evaluating characteristics of concrete masonryunits and related concrete units. Methods are provided for sampling, measurement of dimensions, compressive strength,absorption, unit weight (density), moisture content, flexural load, and ballas

4、t weight. Not all methods are applicable to all unittypes, however.1.2 Specific testing and reporting procedures are included in annexes to these test methods for the following specific unit types:Annex A1Concrete masonry units (Specifications C90, C129)Annex A2Concrete and calcium silicate brick(Sp

5、ecifications C55, C73, C1634)Annex A3Segmental retaining wall units (Specification C1372)Annex A4Concrete interlocking paving units(Specification C936/C936M)Annex A5Concrete grid paving units (Specification C1319)Annex A6Concrete roof pavers (Specification C1491)Annex A7Dry-cast articulating concret

6、e block(Specification D6684)1.3 The test procedures included in these test methods are also applicable to other types of units not referenced in these testmethods, but specific testing and reporting requirements for those units are not included.1.4 These test methods include the following sections:S

7、ectionScope 1Referenced Documents 2Terminology 3Significance and Use 4Sampling 5Measurement of Dimensions 6Compressive Strength 7Absorption 8Calculations 9Report 10Keywords 11AnnexesTest ProceduresConcrete Masonry Units Annex A1Concrete and Calcium Silicate Brick Annex A2Segmental RetainingWall Unit

8、sAnnex A3Concrete Interlocking Paving Units Annex A4Concrete Grid PavingUnitsAnnex A5Concrete Roof Pavers Annex A6Dry-Cast ArticulatingConcrete BlockAnnex A7Determining Plate ThicknessRequirements forCompression TestingAnnex A81 These test methods are under the jurisdiction of ASTM Committee C15 on

9、Manufactured Masonry Units and are the direct responsibility of Subcommittee C15.03 onConcrete Masonry Units and Related Units.Current edition approved June 1, 2016Feb. 1, 2017. Published July 2016March 2017. Originally approved in 1938. Last previous edition approved in 20152016 asC140 15aC140 16.1

10、. DOI: 10.1520/C0140_C0140M-16.10.1520/C0140_C0140M-17.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes a

11、ccurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Har

12、bor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1SectionWorksheet and Test Report forConcrete Masonry UnitsAppendix X1NOTE 1The testing laboratory performing these test methods should be evaluated in accordance with Practice C1093.1.5 The text of this test method references no

13、tes and footnotes that provide explanatory material. These notes and footnotes(excluding those in tables and figures) shall not be considered as requirements of the standard.1.6 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in e

14、achsystem may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from thetwo systems may result in non-conformance with the standard.1.7 This standard does not purport to address all of the safety concerns, if any, associated with its use. It

15、is the responsibilityof the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatorylimitations prior to use.2. Referenced Documents2.1 ASTM Standards:2C55 Specification for Concrete Building BrickC73 Specification for Calcium Silicate

16、Brick (Sand-Lime Brick)C90 Specification for Loadbearing Concrete Masonry UnitsC129 Specification for Nonloadbearing Concrete Masonry UnitsC143/C143M Test Method for Slump of Hydraulic-Cement ConcreteC936/C936M Specification for Solid Concrete Interlocking Paving UnitsC1093 Practice for Accreditatio

17、n of Testing Agencies for MasonryC1232 Terminology of MasonryC1319 Specification for Concrete Grid Paving UnitsC1372 Specification for Dry-Cast Segmental Retaining Wall UnitsC1491 Specification for Concrete Roof PaversC1552 Practice for Capping Concrete Masonry Units, Related Units and Masonry Prism

18、s for Compression TestingC1634 Specification for Concrete Facing BrickD6684 Specification for Materials and Manufacture of Articulating Concrete Block (ACB) Revetment SystemsE4 Practices for Force Verification of Testing MachinesE6 Terminology Relating to Methods of Mechanical Testing2.2 Other Docum

19、ents:SP 960-12 NIST Recommended Practice Guide Stopwatch and Timer Calibration33. Terminology3.1 Terminology defined in Terminologies C1232 and E6 shall apply for these test methods.3.2 Definitions of Terms Specific to This Standard:3.2.1 lot, nany number of concrete masonry units or related units,

20、designated by the producer, of any configuration ordimension manufactured by the producer using the same materials, concrete mix design, manufacturing process, and curingmethod.4. Significance and Use4.1 These test methods provide general testing requirements for application to a broad range of conc

21、rete products. Those generaltesting requirements are included in the body of this standard.NOTE 2Consult manufacturer, supplier, product specifications, or other resources for more specific measurement or testing guidelines for thoseproducts not addressed with the annex of this standard.4.2 These te

22、st methods provide specific testing requirements in two distinct sections, the requirements applicable to all unitscovered by these test methods and those applicable to the specific unit types. The requirements applicable to all units are includedin the body of these test methods and those applicabl

23、e to the specific unit types are included within the annexes.5. Sampling5.1 Selection of Test Specimens:2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards

24、 Document Summary page on the ASTM website.3 Available at http:/tf.nist.gov/general/pdf/2281.pdfC140/C140M 1725.1.1 For purposes of testing, full-sized units shall be selected by the purchaser or authorized representative. The selectedspecimens shall be of similar configuration and dimensions. Speci

25、mens shall be representative of the whole lot of units from whichthey are selected.5.2 Number of Specimens:5.2.1 Unless specified otherwise in the applicable annex, a set of units shall consist of six full-size units.5.3 Remove loose material from the specimens (including the cores) prior to determi

26、ning the received weight.NOTE 3An abrasive stone or wire brush is typically used to remove loose material.5.4 IdentificationMark each specimen so that it may be identified at any time. Markings shall cover not more than 5 % of thesurface area of the specimen.5.5 Received WeightWeigh each specimen im

27、mediately after sampling and marking, and record as wr (received weight).Record time and place wr was measured.NOTE 4Received weights often have direct relationships with other unit properties and are therefore a useful method of evaluating results or forsorting purposes. The weight of a concrete ma

28、sonry unit and related unit changes with time and exposure conditions, primarily as a result of the moisturewithin the unit. Therefore, to understand the context of a received weight value, it is also important to understand the point in time and the frame ofreference when that weight was determined

29、. “Time and place” should not refer to when and where the unit was sampled but when and where the receivedweights were determined. In addition to date and time references, it is also important to know if those weights were determined after units reachedequilibrium with lab environment, or before uni

30、ts were shipped, or after delivery to the job site, and so forth.6. Measurement of Dimensions6.1 Apparatus:6.1.1 Measurement DevicesDevices used to measure specimen dimensions shall have divisions not greater than 0.1 in.2.5 mm when the dimension is to be reported to the nearest 0.1 in. 2.5 mm and n

31、ot greater than 0.01 in. 0.25 mm when thedimension is to be reported to the nearest 0.01 in. 0.25 mm.6.1.2 Measuring devices shall be readable and accurate to the division required to be reported.Accuracy shall be verified at leastonce annually. Verification record shall include date of verification

32、, person or agency performing verification, identification ofreference standard used, test points used during verification, and readings at test points.6.2 SpecimensThree full-size units shall be selected for measurement of dimensions.6.3 MeasurementsMeasure specimens in accordance with the applicab

33、le annex of this standard. For those products notcovered by the annexes of this standard, measure overall dimensions (width, height, length) in at least two locations on oppositesides of the specimen to the nearest division required to be reported. Document location of each measurement on a sketch o

34、rphotograph of the specimen.NOTE 5Specimens used for measurement of dimensions may be used in other tests.NOTE 6Calipers, micrometers, and steel scales and dividers of the appropriate accuracy and readability have been shown to be adequate for thesemeasurements.7. Compressive Strength7.1 Test Appara

35、tus:7.1.1 The testing machine shall have an accuracy of 61.0 % over the anticipated load range. The upper platen shall be aspherically seated, hardened metal block firmly attached at the center of the upper head of the machine. The center of the sphereshall lie at the center of the surface held in i

36、ts spherical seat but shall be free to turn in any direction, and its perimeter shall haveat least 0.25 in. 6 mm clearance from the head to accommodate specimens whose bearing surfaces are not parallel. The diameterof the upper platen (determined in accordance with Annex A8) shall be at least 6 in.

37、150 mm. A hardened metal bearing platemay be used beneath the specimen to minimize wear of the lower platen of the machine.7.1.2 When the bearing area of the upper platen or lower platen is not sufficient to cover the area of the specimen, a single steelplate with a thickness equal to at least the d

38、istance from the edge of the platen to the most distant corner of the specimen shallbe placed between the platen and the capped specimen. The length and width of the steel plate shall be at least 0.25 in. 6 mmgreater than the length and width of the units. See Annex A8 for information on determining

39、 the required minimum bearing platethickness, tBP. The provided bearing plate (when needed) shall have a thickness at least equal to the value of tBP as determinedin Annex A8.7.1.3 The surfaces of the platen or plate intended for contact with the specimen shall have a hardness not less than HRC 60(B

40、HN 620). The surfaces of the platen and plate shall not depart from plane surfaces by more than 0.001 in. 0.025 mm in any6 in. 150 mm dimension.NOTE 7Research has shown that thickness of bearing plates has a significant effect on the tested compressive strength of masonry units when thebearing area

41、of the platen is not sufficient to cover the area of the specimen. Plate bending results in nonuniform stress distributions that can influencethe failure mechanisms of the tested specimens. The magnitude of this effect is controlled by the stiffness of the plate, the size of the specimen tested,and

42、the strength of the specimen. Tested compressive strengths will typically increase with increased plate thickness and with reduced distance to thefurthest corner of the specimen. Some testing laboratories have limitations that limit the practicality of eliminating plate bending entirely. Therefore t

43、heC140/C140M 173plate thickness requirements in 7.1 are intended to provide an adequate level of accuracy in the compression test results so as to conform to the limitsof practicality of the testing laboratory.7.1.4 The testing machine shall be verified in accordance with Practices E4 at a frequency

44、 defined by Practice C1093.7.2 Test Specimens:7.2.1 Unless specified otherwise in the applicable annex, test three specimens in compression.7.2.2 Unless specified otherwise in the applicable annex, specimens shall be full-sized units except when the units cannot betested full-size due to specimen co

45、nfiguration or testing machine requirements. In these cases, reduce the specimen size inaccordance with Annex A1.7.2.3 After delivery to the laboratory, store compression specimens (unstacked and separated by not less than 0.5 in. 13 mmon all sides) continuously in air at a temperature of 75 6 15F 2

46、4 6 8C and a relative humidity of less than 80 % for not lessthan 48 h.Alternatively, if compression results are required sooner, store units unstacked in the same environment described abovewith a current of air from an electric fan passing over them for a period of not less than 4 h. Continue pass

47、ing air over the specimensuntil two successive weighings at intervals of 2 h show an increment of loss not greater than 0.2 % of the previously determinedweight of the specimen and until no moisture or dampness is visible on any surface of the unit. Specimens shall not be subjectedto oven-drying.NOT

48、E 8In this test method, net area (other than certain solid units, see 9.5) is determined from specimens other than those subjected to compressiontesting. The compressive strength method is based on the assumption that units used for determining net volume (absorption specimens) have the samenet volu

49、me as units used for compression testing. Sampled split face units, which have irregular surfaces, should be divided at the time they are sampledfrom the lot, such that the absorption test specimens have a net volume that is visually representative and a weight that is representative of the compressiontest specimens.7.2.4 Where saw-cutting of test specimens is allowed or required by the standard or applicable annex, sawing shall be performedin an accurate, competent manner, subjecting the specimen to as little saw vibration as