1、Designation: C1311 14Standard Specification forSolvent Release Sealants1This standard is issued under the fixed designation C1311; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses i

2、ndicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification describes the properties of a one-component solvent release sealant for use in building construc-tion. These sealants are generally formula

3、ted to withstand amaximum joint movement of 7.5 % in extension and 7.5 % incompression of the nominal joint width.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 The committee with jurisdiction of this specification isn

4、ot aware of any similar specification within ISO or any otherorganization.2. Referenced Documents2.1 ASTM Standards:2C661 Test Method for Indentation Hardness of Elastomeric-Type Sealants by Means of a DurometerC712 Test Method for Bubbling of One-Part, Elastomeric,Solvent-Release Type SealantsC717

5、Terminology of Building Seals and SealantsC1193 Guide for Use of Joint SealantsC1216 Test Method for Adhesion and Cohesion of One-PartElastomeric Solvent Release SealantsC1257 Test Method for Accelerated Weathering of Solvent-Release-Type SealantsC1442 Practice for Conducting Tests on Sealants Using

6、Artificial Weathering ApparatusD2202 Test Method for Slump of SealantsD2203 Test Method for Staining from SealantsD2377 Test Method for Tack-Free Time of Caulking Com-pounds and SealantsD2452 Test Method for Extrudability of Oil- and Resin-BaseCaulking Compounds3. Terminology3.1 DefinitionsDefinitio

7、ns of the following terms used inthis specification are found in Terminology C717: adhesivefailure (adhesion loss), caulk (v), compound, durometer,hardness, joint, primer, seal, sealant, sealing material, solventrelease sealant, and standard conditions.4. Materials and Manufacture4.1 The sealing com

8、pound shall be a solvent release mate-rial compounded to conform to the requirements prescribed inthis specification.4.2 All material and workmanship shall be in accordancewith good commercial practice. The producer is permitted awide latitude in choice of raw materials for making theseproducts. Con

9、sequently, there is no implication that the com-pounds are equivalent in all physical properties.4.3 The manufacturing process shall be such as will ensurea homogeneous mix, free of defects that would affectserviceability, and of a consistency suitable for immediateapplication.5. General Requirement

10、s5.1 Standard ConditionsPerform all of the tests in acontrolled environment at standard conditions. Condition seal-ant samples for at least5hatthese conditions before any testsare performed.5.2 The sealant in the original container shall be suitable foruse for at least 12 months from the date of man

11、ufacture whenstored at a temperature neither below 5C (41.0F) norexceeding 27C (80.6F).5.3 The color of the sealant shall be as agreed upon betweenthe purchaser and the manufacturer.5.4 The sealant shall be intended for use only on clean, drysurfaces. When a primer is recommended by a manufacturerfo

12、r a specific substrate, all tests on that substrate shall includethe primer. The proper use of primers (or surface conditioners)with the application of sealants is described in detail in GuideC1193. This guide also describes proper methods for jointdesign, backup materials, surface preparation, tool

13、ing ofsealant, and other important procedures in sealant applicationin buildings.1This specification is under the jurisdiction of ASTM Committee C24 onBuilding Seals and Sealants and is the direct responsibility of Subcommittee C24.10on Specifications, Guides and Practices.Current edition approved J

14、une 1, 2014. Published July 2014. Originally approvedin 1995. Last previous edition approved in 2010 as C131110. DOI: 10.1520/C1311-14.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume inf

15、ormation, refer to the standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16. Significance and Use6.1 This specification describes solvent release sealants forgeneral caulking and sealing

16、 operations in building construc-tion. However, it should be recognized by the user that not allsealants meeting this specification are suitable for all applica-tions and all substrates and that there is no implication that thesealants are equivalent in all physical properties.6.2 Refer to Guide C11

17、93 for information on the proper useof sealants meeting this specification.7. Physical Requirements7.1 Indentation HardnessThe sealant shall have durom-eter hardness with a mean value of not more than 50 units whentested in accordance with Test Method C661.7.2 BubblingThe sealant shall exhibit no mo

18、re than 650mm2(1.0 in.2) in bubbling when tested in accordance with TestMethod C712.7.3 Adhesion and Cohesion After Cyclic MovementThesealant shall have no more than 9.0 cm2(1.5 in.2) total failureper substrate when tested in accordance to Test Method C1216.7.4 Accelerated WeatheringThe sealant shal

19、l be rated nohigher than a 3 for Edge Cracking, 3 for Center Cracking, and3 for Adhesion Loss when tested in accordance with 7.4.1.Color change is to no more than that as agreed upon betweenuser and manufacturer.7.4.1 The sealant is exposed to 1 cycle (1000 h) using aFluorescent UV/Condensation Mach

20、ine as described in TestMethod C1257 Section 6.1.1, or a xenon-arc apparatus de-scribed in Test Method C1257 Section 6.1.2. As mentioned inthat standard, when using irradiance values other thanspecified, consult Annex A1 of Test Method C1442.7.5 SlumpThe sealant shall have a slump of not more than0.

21、40 cm (0.15 in.) when tested in accordance with Test MethodD2202.7.6 StainingThe sealant shall have a stain index of nomore than 3 when tested in accordance with Test MethodD2203.7.7 Tack-Free TimeThe sealant shall have a tack-free timeof not more than 72.0 h when tested in accordance with TestMetho

22、d D2377.7.8 Extrudability After AgingThe sealant shall have a flowrate of not more than 9.0 s/mL when tested in accordance withTest Method D2452.7.9 A summary of the physical requirements is contained inTable 1.8. Test Methods8.1 Indentation HardnessRefer to Test Method C661.8.2 BubblingRefer to Tes

23、t Method C712.8.3 Adhesion and Cohesion After Cyclic MovementReferto Test Method C1216.8.4 Accelerated WeatheringRefer to Test Method C1257.8.5 SlumpRefer to Test Method D2202.8.6 StainingRefer to Test Method D2203.8.7 Tack-Free TimeRefer to Test Method D2377.8.8 Extrudability After AgingRefer to Te

24、st MethodD2452.9. Packaging and Package Marking9.1 Unless otherwise specified in the contract or order, thesealant shall be packaged in standard commercial containersconstructed so as to ensure acceptance by common or othercarrier for safe transportation to the point of delivery.9.2 Shipping contain

25、ers shall be marked with the name,grade, and quantity of the sealant contained therein, as definedby the contract or order under which shipments are made. Thename of the supplier and the lot or batch shall also be shown.10. Keywords10.1 accelerated weathering; application life; bubbling; ex-trusion

26、rate; sealant; sealing compound (sealing material);slump; solvent-release sealant; staining; tack freeASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that de

27、termination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved

28、or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel t

29、hat your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprint

30、s (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyr

31、ight Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 1 Physical RequirementsProperty Requirement Test MethodExtrudability 9/s/mL, max D2452Indentation hardness 50, max C661Bubbling 25 %, max C712Adhesive and cohesive loss 9 cm2(1.5 in.2), max persubstrateC1216Slump 0.38 cm (0.15 in.), max D2202Stain index 3, max D2203Tack-free time 72 h, max D2377Accelerated weathering 10000 h exposure C1257Edge cracking 3, maxCenter cracking 3, maxAdhesion loss 3, maxColor Change as agreedC1311 142