ASTM B730-2008(2013) Standard Specification for Welded Nickel (UNS N02200 UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube《焊接镍(N02200 UNS N02201)和镍铜合金管(UNS N04400)的标准规格》.pdf

《ASTM B730-2008(2013) Standard Specification for Welded Nickel (UNS N02200 UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube《焊接镍(N02200 UNS N02201)和镍铜合金管(UNS N04400)的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B730-2008(2013) Standard Specification for Welded Nickel (UNS N02200 UNS N02201) and Nickel Copper Alloy (UNS N04400) Tube《焊接镍(N02200 UNS N02201)和镍铜合金管(UNS N04400)的标准规格》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B730 08 (Reapproved 2013)Standard Specification forWelded Nickel (UNS N02200/UNS N02201) and NickelCopper Alloy (UNS N04400) Tube1This standard is issued under the fixed designation B730; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers nickel (UNS N02200), low-carbon nickel (UNS N02201), and nicke

3、l copper alloy (UNSN04400) in the form of welded and annealed or welded andstress-relieved tube intended for general corrosive service andfor mechanical applications.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions t

4、o SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to become familiarwith all hazards including those identifie

5、d in the appropriateMaterial Safety Data Sheet (MSDS) for this product/materialas provided by the manufacturer, to establish appropriatesafety and health practices, and determine the applicability ofregulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2B751 Specification for

6、 General Requirements for Nickel andNickel Alloy Welded Tube3. Ordering Information3.1 Orders for material under this specification shall includethe following information:3.1.1 Alloy name or UNS number.3.1.2 ASTM designation and year of issue.3.1.3 Condition (Temper) (Table 1).3.1.4 Dimensions:3.1.4

7、.1 Outside diameter and nominal wall thickness.NOTE 1Tube produced to outside diameter and minimum wallthickness may be furnished upon agreement between the manufacturer andthe purchaser.3.1.4.2 Length (specific or random).3.1.5 Quantity (feet or metres, or number of pieces).3.1.6 CertificationState

8、 if certification is required.3.1.7 Samples for Product (Check) AnalysisState whethersamples for product (check) analysis should be furnished.3.1.8 Purchaser InspectionIf the purchaser wishes towitness tests or inspection of material at the place ofmanufacture, the purchase order must so state indic

9、ating whichtests or inspections are to be witnessed.3.1.9 Nondestructive TestsSpecify either Test Category 1or 2. If Test Category 1 is required, specify if either ahydrostatic, eddy-current or ultrasonic test is to apply. If TestCategory 2 is required, specify which two tests are required.3.1.10 Su

10、pplementary Requirements.4. Materials and Manufacture4.1 Tubes shall be made from flat-rolled material by anautomatic welding process with no addition of filler metal.Subsequent to welding, and prior to heat treatment, the tubesshall be cold worked to assure that optimum corrosion resis-tance in the

11、 weld area and base metal will be developed duringheat treatment.4.2 Tubes shall be furnished with a scale-free finish. Whenbright annealing is used, descaling is not necessary.5. Chemical Requirements5.1 The material shall conform to the requirements as tochemical composition prescribed in Table 2.

12、6. Mechanical and Other Requirements6.1 Mechanical PropertiesThe material shall conform tothe requirements for mechanical properties prescribed in Table1.6.2 Flattening TestOne test per lot.6.3 Flange TestOne test per lot.6.4 Nondestructive Tests:6.4.1 Tubes shall be subjected to the nondestructive

13、testsoutlined in the following test categories:1This specification is under the jurisdiction of ASTM Committee B02 onNonferrous Metals and Alloys and is the direct responsibility of SubcommitteeB02.07 on Refined Nickel and Cobalt and Their Alloys.Current edition approved Feb. 1, 2013. Published Febr

14、uary 2013. Originallyapproved in 1984. Last previous edition approved in 2008 as B730 08. DOI:10.1520/B0730-08R13.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to th

15、e standards Document Summary page onthe ASTM website.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States16.4.1.1 Category 1Hydrostatic, eddy-current, or ultra-sonic test as the manufacturers option unless the purchaserspecifies in accorda

16、nce with 3.1.9.6.4.1.2 Category 2Hydrostatic, pneumatic plus eddy-current, or ultrasonic test at the manufacturers option unlessthe purchaser specifies in accordance with 3.1.9.6.4.1.3 The manufacturer shall have the option to use TestCategory 1 or 2 if the purchaser does not specify the testcategor

17、y options in accordance with 3.1.9.7. General Requirements7.1 Material furnished under this specification shall con-form to the applicable requirements of Specification B751unless otherwise provided herein.SUPPLEMENTARY REQUIREMENTSOne or more of the following supplementary requirements shall spply

18、only when specified in thepurchase order.S1. The tube may be furnished without cold working.S2. The tube may be furnished without a final heat treatment.S3. Tubing over 0.125 in. wall thickness may be welded withthe addition of matching filler metal.ASTM International takes no position respecting th

19、e validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard i

20、s subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International He

21、adquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This s

22、tandard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or

23、 serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).TABLE 1 Mechanical Properties of TubeCondition and SizeTensile Strength,min, psi (MPa)Yield Strength (0.2 % offset),mi

24、n, psi (MPa)Elongation in 2 in.or 50 min (or 4D)min, %NickelLow-CarbonNickelUNSN04400NickelLow-CarbonNickelUNSN04400NickelLow-CarbonNickelUNSN04400Annealed:5 in. (127 mm) andunder outside diameter55 000 (380) 50 00 (345) 70 000 (480) 15 000 (105) 12 000 (80) 28 000 (195) 35 35 35Over 5 in. (127 mm)

25、inoutside diameter55 000 (380) 50 000 (345) 70 000 (480) 12 000 (80) 10 000 (70) 25 000 (170) 40 40 35Stress-relievedAll sizes65 000 (450) 60 000 (415) 85 000 (585) 40 000 (275) 30 000 (205) 55 000 (380) 15 15 15TABLE 2 Chemical RequirementsComposition, %ElementNicke(UNS N02200)Low-CarbonNickel(UNS N02201)Nickel-Copper(UNS N04400)Nickel, min 99.0 99.0 63.0Copper 0.25 max 0.25 max 28.034.0Iron, max 0.40 0.40 2.6Manganese, max 0.35 0.35 2.0Carbon, max 0.15 0.02 0.3Silicon, max 0.35 0.35 0.5Sulfur, max 0.01 0.01 0.024B730 08 (2013)2