ASTM B489-1985(2008)e1 Standard Practice for Bend Test for Ductility of Electrodeposited and Autocatalytically Deposited Metal Coatings on Metals《金属表面电解沉积和自动催化沉积金属镀层延展性的弯曲试验的标准实施规.pdf
《ASTM B489-1985(2008)e1 Standard Practice for Bend Test for Ductility of Electrodeposited and Autocatalytically Deposited Metal Coatings on Metals《金属表面电解沉积和自动催化沉积金属镀层延展性的弯曲试验的标准实施规.pdf》由会员分享,可在线阅读,更多相关《ASTM B489-1985(2008)e1 Standard Practice for Bend Test for Ductility of Electrodeposited and Autocatalytically Deposited Metal Coatings on Metals《金属表面电解沉积和自动催化沉积金属镀层延展性的弯曲试验的标准实施规.pdf(3页珍藏版)》请在麦多课文档分享上搜索。
1、Designation: B 489 85 (Reapproved 2008)e1Standard Practice forBend Test for Ductility of Electrodeposited andAutocatalytically Deposited Metal Coatings on Metals1This standard is issued under the fixed designation B 489; the number immediately following the designation indicates the year oforiginal
2、adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.e1NOTEThe units statement in subsection 1.3 was corrected editorially in April
3、2008.1. Scope1.1 This practice covers a test procedure for determining theductility of electrodeposited and autocatalytically depositedcoatings on sheet or strip basis metals. The purpose of the testis to determine the resistance of metal coatings to crackingduring distortion.21.2 Test Methods E8can
4、 be used if the coatings are tooductile and require mandrels too small to be practical.1.3 The values stated in SI units are to be regarded asstandard. No other units of measurement are included in thisstandard.1.4 This standard does not purport to address all of thesafety concerns, if any, associat
5、ed with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3B 177 Guide for Engineering Chromium ElectroplatingD 1193 Spe
6、cification for Reagent WaterE8 Test Methods for Tension Testing of Metallic Materials3. Summary of Practice3.1 The practice consists of bending a narrow strip of theelectroplated or coated article over a mandrel. An elongationmeasurement is obtained from the smallest diameter mandrelthat does not ca
7、use the coating to fracture.4. Significance and Use4.1 The routine measurement of the ductility of electrode-posited and autocatalytically deposited metal coatings can beuseful in process control, especially when the electroplatingprocess is used for decorative and engineering purposes.5. Apparatus5
8、.1 Series of Mandrels, with diameters from 6 to 50 mm, in3-mm steps with lengths of 100 to 150 mm so they can be heldin a vise.5.2 Micrometer, to measure the thickness of the test speci-mens.5.3 Guillotine Shears or other device to cut the specimens tosize.5.4 File or Grinder to remove burrs and to
9、round or chamferedges.5.5 Vise, to hold mandrels.5.6 Magnifier, 103.6. Test Specimen6.1 Flat specimens, 10 mm wide, and not less than 150 mmlong, shall be cut from the electroplated or coated article if theshape permits, no closer than 25 mm from the edges. Guillotineshears are preferred, but any co
10、nvenient method may be used.Basis metal thickness and temper shall be suitable to permitbending around the smallest diameter mandrel, if necessary.Low-carbon AISI 1010 to 1025 steel strip or sheet, 0.25 to 1.0mm thick is usually suitable. Basis metals that have lowductility can initiate cracks that
11、can propagate through thecoatings. The procedure indicated in 6.2 shall then be followed.6.2 When the shape is such that a test specimen cannot beobtained from the part, a test panel may be prepared ofappropriate basis metal, such as low-carbon steel (see 6.1),with the same coating system in the sam
12、e baths. The panel shall1This practice is under the jurisdiction of ASTM Committee B08 on Metallicand Inorganic Coatings and is the direct responsibility of Subcommittee B08.10 onTest Methods.Current edition approved April 1, 2008. Published April 2008. Originallyapproved in 1968. Last previous edit
13、ion approved in 2003 as B 489 85 (2003).2For a discussion and theory for this test see Mohrnheim, A. F., “The Bend Testfor Measuring the Strain Limit of Surfaces,” Plating, Vol 50, 1963, pp. 1094 1099.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Servi
14、ce at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.be sufficiently large to obtain several piece
15、s after trimming 25mm from the edges. The specimens shall be prepared inaccordance with 6.1. Brass or copper panels may be usedinstead of copper-electroplated zinc alloy panels.6.3 The long edges of the test pieces shall be rounded orchamfered by filing or grinding.7. Procedure7.1 Place the largest
16、mandrel in the vise. Bend the testspecimen, with the coating outward, over the mandrel so that asthe bend progresses the test specimen will remain in contactwith the top of the mandrel. Continue bending with slow,steadily applied pressure until the two legs are parallel. If thereare no cracks visibl
17、e under a 103 magnifier, repeat the test,using new specimens, on progressively smaller-diameter man-drels, until cracks appear across or through the coating. Takethe preceding mandrel diameter as the value for the ductilitydetermination. If the coating is electrodeposited chromium, thespecimens may
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ASTMB48919852008E1STANDARDPRACTICEFORBENDTESTFORDUCTILITYOFELECTRODEPOSITEDANDAUTOCATALYTICALLYDEPOSITEDMETALCOATINGSONMETALS
链接地址:http://www.mydoc123.com/p-461361.html