ASTM A818-2006 Standard Specification for Coppered Carbon Steel Wire《镀铜碳素钢丝的标准规范》.pdf

《ASTM A818-2006 Standard Specification for Coppered Carbon Steel Wire《镀铜碳素钢丝的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A818-2006 Standard Specification for Coppered Carbon Steel Wire《镀铜碳素钢丝的标准规范》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 818 06Standard Specification forCoppered Carbon Steel Wire1This standard is issued under the fixed designation A 818; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses

2、 indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This specification covers coppered carbon steel wiresupplied in coils for

3、general use. It may be produced harddrawn, annealed in process, or annealed at finish size. Thecoating is very thin and is not designed for protection againstcorrosion.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in brackets are provided forinformation on

4、ly.2. Referenced Documents2.1 ASTM Standards:2A 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA 510 Specification for General Requirements for WireRods and Coarse Round Wire, Carbon SteelA 700 Practices for Packaging, Marking, and LoadingMethods for Steel Products for Shipm

5、entE29 Practice for Using Significant Digits in Test Data toDetermine Conformance with Specifications2.2 U.S. Federal Standard:Fed. Std. No. 123 Marking for Shipments (Civil Agencies)32.3 U.S. Military Standards:MIL-STD-129 Marking for Shipment and Storage33. Terminology3.1 Definitions of Terms Spec

6、ific to This Standard:3.1.1 annealed coppered wirewire that may be either3.1.2 annealed-in-process wireat some stage before ap-plication of the copper, the steel wire is thermally treated andsubsequently coated with copper and redrawn. coated withcopper, drawn, and annealed at finish size, or drawn,

7、 annealedat finish size and then coppered.3.1.3 carbon steelsteel that has no minimum contentspecified or required for aluminum, chromium, cobalt, colum-bium, molybdenum, nickel, titanium, tungsten, vanadium, orzirconium or any other element added to obtain a desiredalloying effect; steel that has t

8、he specified minimum coppercontent that does not exceed 0.40 %; or the maximum contentfor any of the following elements that does not exceed thesepercentages: manganese 1.65, silicon 0.60, or copper 0.60.3.1.4 coppered steel wireproduced by cold drawing rod orwire that has been immersed in a copper

9、sulfate solution.3.1.5 hard drawn wirewire that is coppered and drawnwithout the use of thermal treatment.4. Ordering Information4.1 Orders for material under this specification shouldinclude the following information:4.1.1 Quantity (weight in pounds),4.1.2 Coated wire diameter, in inches, to the th

10、ird decimalpoint,4.1.3 Name of material (coppered carbon steel wire),4.1.4 Grade of steel,4.1.5 Condition (hard drawn, annealed in process, or an-nealed at finished size),4.1.6 Finish (lustrous or matte),4.1.7 Packaging requirements, and4.1.8 ASTM designation and year of issue.NOTE 1A typical orderi

11、ng description is as follows: 40 000 lb,0.148-in. coppered carbon steel wire, Grade 1008, hard drawn, lustrousfinish in 600-lb catch-weight coils on tubular carriers to ASTM A 818 .5. Materials and Manufacture5.1 The steel rod from which the wire is drawn shall bemanufactured by the open-hearth, ele

12、ctric-furnace, or basic-oxygen process.1This specification is under the jurisdiction of ASTM Committee A05 onMetallic-Coated Iron and Steel Products and is the direct responsibility ofSubcommittee A05.12 on Wire Specifications.Current edition approved June 15, 2006. Published July 2006. Originallyap

13、proved in 1983. Last previous edition approved in 2001 as A 818 - 91(2001).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe

14、 ASTM website.3Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2 Coppered wire may be supplied in any

15、 of the followingconditions: hard-drawn, annealed-in-process, or annealed.6. Mechanical Properties6.1 The coppered steel wire shall meet the tensile strengthrequirements shown in Table 1 when tested in accordance withMethods A 370.6.2 Test specimens found to contain a weld or an obviousdefect shall

16、be discarded and another test specimen obtained toverify conformance to the tensile strength requirements.7. Dimensions and Tolerances7.1 The permissible variation in diameter of the copperedwire as represented by the test specimens shall be as indicatedin Specification A 510.8. Coating Requirements

17、 Coating Requirements8.1 Due to the nature of the process, the thickness of thecopper coating is extremely thin. Therefore, there is norequirement for thickness of coating; the requirement is that thecoating be continuous.8.2 The coppered wire as represented by the test specimensshall be capable of

18、being wrapped in a close helix at a rate notexceeding 15 turns/min around a cylindrical steel mandrelhaving a diameter equal to the diameter of the coated wirewithout cracking or flaking the copper coating to such an extentthat any copper can be removed by rubbing with the barefingers. Loosening or

19、detachment during the adhesion test ofsuperficial, small particles of copper formed by mechanicalpolishing of the surface of the coppered wire shall not beconsidered cause for rejection.9. Workmanship9.1 The coppered wire shall be free of slivers, scale, andother imperfections that would be detrimen

20、tal to intended use.The copper coating shall be continuous and reasonably smooth.To ensure large continuous length coils, welds may be presentin the finished wire.10. Number of Tests and Retests10.1 Alot shall consist of all of the coils of wire of the samesize, type and class, and shall be offered

21、for inspection at onetime. A wire sample of sufficient length, approximately 4 ft.1.2 m, shall be cut from either end of each coil selected fortests described in Sections 6, 8 and 9.10.2 The number of test specimens taken from the ends ofcoils during production to assure compliance with Sections 6an

22、d 7 varies with the quality control procedures and themanufacturing facilities of each manufacturer, but is generallynot less than 10 % of the coils produced. For the purpose offinal product testing, one specimen from every ten coils orfraction thereof in a lot shall be selected at random, or a tota

23、lof seven specimens, whichever is less.10.3 Should one or more of the wire specimens fail anyrequirement, the lot shall be subjected to retest. For retestpurposes the original lot shall be regrouped into 50 coil lots orfractions thereof. Each lot shall be tested for the property inwhich the original

24、 sample failed to comply at a frequency of10 % or more so that the total number of tests is at least doublethe original. Any lot that exhibits a failure shall be rejected. Ifduring retesting an additional quality parameter is observed tobe defective, the lot of 50 is subject to rejection for that ca

25、use.The manufacturer may test each coil in the failed lot for theproperty in which failure occurred and reject only the noncon-forming coils.11. Inspection11.1 The manufacturer shall afford the inspector represent-ing the purchaser all reasonable facilities to satisfy that thematerial is being furni

26、shed in accordance with this specifica-tion. All tests and inspections shall be made at the place ofmanufacture prior to shipment, unless otherwise specified, andshall be so conducted as not to interfere with the operation ofthe works.12. Rejection and Rehearing12.1 Any rejection by the purchaser sh

27、all be reported to themanufacturer within a reasonable time from receipt of material.12.2 The material must be adequately protected and cor-rectly identified in order that the manufacturer may make aproper investigation.TABLE 1 Tensile Strength RequirementsWire Diameter,in. mmAWire ConditionHard Dra

28、wn,min,ksi MPaAnnealed-in-Proc-ess, max,ksi MPaAnnealed,Bmax,ksi MPaGrade 1006Less than 0.035 0.89 . . . 95 655 60 4150.035 to 0.057 0.89 to 1.46 105 725 90 620 60 4150.058 to 0.085 1.47 to 2.17 90 620 90 620 60 4150.086 to 0.127 2.18 to 3.27 80 550 85 585 60 4150.128 to 0.177 3.28 to 4.50 70 485 80

29、 550 60 4150.178 to 0.250 4.51 to 6.35 60 415 70 485 60 415Grades 1008 and 1010Less than 0.035 0.89 . . . 95 655 70 4850.035 to 0.057 0.89 to 1.46 . . . 90 620 65 4500.058 to 0.085 1.47 to 2.17 100 690 90 620 65 4500.086 to 0.127 2.18 to 3.27 85 585 90 620 65 4500.128 to 0.177 3.28 to 4.50 75 517 83

30、 570 65 4500.178 to 0.250 4.51 to 6.35 65 450 75 517 65 450Grade 1015Less than 0.035 0.89 . . . 95 655 75 5170.035 to 0.057 0.89 to 1.46 . . . 95 655 70 4850.058 to 0.085 1.47 to 2.17 105 725 95 655 70 4850.086 to 0.127 2.18 to 3.27 90 620 95 655 70 4850.128 to 0.177 3.28 to 4.50 80 550 85 585 70 48

31、50.178 to 0.250 4.51 to 6.35 70 485 78 540 70 485Grades 1018 and 1020Less than 0.035 0.89 . . . 100 690 75 5170.035 to 0.057 0.89 to 1.46 . . . 100 690 75 5170.058 to 0.085 1.47 to 2.17 . . . 100 690 75 5170.086 to 0.127 2.18 to 3.27 105 725 100 690 75 5170.128 to 0.177 3.28 to 4.50 85 585 90 620 75

32、 5170.178 to 0.250 4.51 to 6.35 75 517 82 570 75 517AFor the purpose of determining conformance with this specification, anobserved value shall be rounded to the nearest 0.001 in. in accordance with therounding method of Practice E29.BAnnealed denotes annealed at finished size.A81806213. Marking, Pa

33、ckaging, and Loading for Shipment13.1 The size, name of product, grade and condition,ASTMspecification number, weight, and name or mark of the manu-facturer shall be indicated on a tag securely attached to eachcoil or package of wire.13.2 The coil weight, dimensions, and methods of packag-ing shall

34、be as specified on the purchase order. Unlessotherwise specified, loading for shipment shall be in accor-dance with Practices A 700.13.3 When specified in the contract or order, and for directprocurement by or direct shipment to the U.S. Government,marking for shipment, in addition to requirements s

35、pecified inthe contract or order, shall be in accordance with MIL-STD-129 for U.S. Military agencies and in accordance with Fed. Std.No. 123 for U.S. Government civil agencies.14. Keywords14.1 copper coated carbon steel wire; coppered wire; steelwire; wireASTM International takes no position respect

36、ing the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This stan

37、dard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM Internatio

38、nal Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.

39、This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).A818063