《ASTM A553 A553M-2014 Standard Specification for Pressure Vessel Plates Alloy Steel Quenched and Tempered 7 8 and 9 % Nickel《压力容器用经回火和淬火的7 8和9%镍合金钢板的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A553 A553M-2014 Standard Specification for Pressure Vessel Plates Alloy Steel Quenched and Tempered 7 8 and 9 % Nickel《压力容器用经回火和淬火的7 8和9%镍合金钢板的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A553/A553M 14Standard Specification forPressure Vessel Plates, Alloy Steel, Quenched andTempered 7, 8, and 9 % Nickel1This standard is issued under the fixed designation A553/A553M; the number immediately following the designation indicates the yearof original adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification2covers 7, 8, and 9 % nickel alloysteel plates for use in the water quenche

3、d and temperedcondition intended for the fabrication of welded pressurevessels.1.2 Material under this specification is available in threetypes having different chemical composition as follows:Type Nominal Nickel Content, %I9II 8III 71.3 Plates produced under this specification are subject toimpact

4、testing at 320F 195C for Type I or Type III, and275F 170C for Type II; or at such other temperatures asare agreed upon.1.4 The maximum thickness of plates is limited only by thecapacity of the material to meet the specified mechanicalproperty requirements; however, current mill practice normallylimi

5、ts this material to 2 in. 50 mm max.1.5 This material is susceptible to magnetization. Use ofmagnets in handling after heat treatment should be avoided ifresidual magnetism would be detrimental to subsequent fabri-cation or service.1.6 The values stated in either inch-pound units or SI unitsare to b

6、e regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently of the other. Combining values from thetwo systems may result in nonconformance with the specifi-cation.1

7、.7 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Do

8、cuments2.1 ASTM Standards:3A20/A20M Specification for General Requirements for SteelPlates for Pressure VesselsA435/A435M Specification for Straight-Beam UltrasonicExamination of Steel PlatesA577/A577M Specification for Ultrasonic Angle-Beam Ex-amination of Steel PlatesA578/A578M Specification for S

9、traight-Beam UltrasonicExamination of Rolled Steel Plates for Special Applica-tions3. General Requirements and Ordering Information3.1 Material supplied to this material specification shallconform to Specification A20/A20M. These requirements out-line the testing and retesting methods and procedures

10、, permit-ted variations in dimensions, and mass, quality and repair ofdefects, marking, loading, and ordering information.3.2 In addition to the basic requirements of thisspecification, certain supplementary requirements are availablewhen additional control, testing, or examination is required tomee

11、t end use requirements. The purchaser is referred to thelisted supplementary requirements in this specification and tothe detailed requirements in Specification A20/A20M.3.3 If the requirements of this specification are in conflictwith the requirements of Specification A20/A20M, the require-ments of

12、 this specification shall prevail.4. Manufacture4.1 Steelmaking PracticeThe steel shall be killed andshall conform to the fine austenitic grain size requirement ofSpecification A20/A20M.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys an

13、d is the direct responsibility of SubcommitteeA01.11 on Steel Plates for Boilers and Pressure Vessels.Current edition approved Oct. 1, 2014. Published October 2014. Originallyapproved in 1965. Last previous edition approved in 2010 as A553/A553M 10.DOI: 10.1520/A0553_A0553M-14.2For ASME Boiler and P

14、ressure Vessel Code applications, see related Specifi-cation SA-553/SA-553M in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards

15、 Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Heat Treatment5.1 All plates shall be heat treated in accordance with 5.2.Sh

16、ell plates and other parts, including heads and reinforcingpads, which are heated for forming, shall be heat treated afterforming in accordance with 5.2.5.2 Heat Treatment ProcedureHeat treat all plates byheating to a suitable temperature within the range from 1475 to1700F 800 to 925C, holding for a

17、 sufficient time to obtainuniform temperature throughout the plate thickness and thenquenching in water. Subsequently, temper the plates within therange from 1050 to 1175F 565 to 635C for Type I and TypeII, or from 1000 to 1125F 540 to 615C for Type III, holdingat this temperature for a minimum of 3

18、0 min/in. 1.2 min/mmof thickness but not less than 15 min, and cool in air or waterquench at a rate not less than 300F/h 165C/h.5.2.1 HardeningThe plates shall be heated to a tempera-ture within the range from 1475 to 1700F 800 to 925C, heldat that temperature for a sufficient time to obtain uniform

19、temperature throughout the plate thickness, and then quenchedin a liquid media.5.2.2 TemperingThe plates shall be tempered at a tem-perature within the range from 1050 to 1175F 565 to 635Cfor Type I and Type II, or from 1000 to 1125F 540 to 615Cfor Type III; being held at that temperature for a mini

20、mum of30 min/in. 1.2 min/mm of thickness, but in no case less than15 min, and then cooled in air or liquid-quenched at a rate notless than 300F/h 165C/h.5.2.2.1 Prior to the tempering treatment, the plates may besubjected to an intermediate heat treatment consisting ofheating to a temperature in the

21、 range from 1165 to 1290F 630to 700C for Type I, or 1185 to 1310F 640 to 710C forType II, or 1205 to 1330F 650 to 720C for Type III; holdingat that temperature for a suitable time, but in no case less than15 min, and then water-quenching to below 300F 150C inthe case of plate thicknesses of more tha

22、n58 in. 16 mm orcooling in air or water-quenching to below 300F 150C inthe case of plate thicknesses of58 in. 16 mm and under.NOTE 1The intermediate heat treatment is for the purpose ofenhancing elongation and notch-toughness and for reducing susceptibilityto strain-aging embrittlement and temper em

23、brittlement. It may beperformed at the option of the material manufacturer or may be specifiedby the purchaser.6. Chemical Requirements6.1 The steel shall conform to the chemical requirementsshown in Table 1 unless otherwise modified in accordance withSupplementary Requirement S17, Vacuum Carbon-Deo

24、xidizedSteel, in Specification A20/A20M.7. Mechanical Requirements7.1 Tension Test RequirementsThe material as representedby tension-test specimens shall conform to the requirementsspecified in Table 2.7.1.1 Upon agreement between the purchaser and themanufacturer, yield strength may be determined b

25、y the exten-sion under load method, using 0.005 in./in. mm/mm totalextension.7.1.2 For nominal plate thicknesses of34 in. 20 mm andunder, the 112 in. 40 mm wide rectangular specimen may beused for the tension test and the elongation may be determinedin a 2 in. 50 mm gage length that includes the fra

26、cture andshows the greatest elongation.7.2 Impact Test Requirements:7.2.1 Charpy V-notch impact tests shall be made in accor-dance with Specification A20/A20M.7.2.2 The longitudinal axis of the test specimens shall betransverse to the final rolling direction of the plate.7.2.3 Unless otherwise agree

27、d, tests shall be conducted at320F 195C for Type I or Type III, and at 275F170C for Type II.7.2.4 Each test specimen shall have a lateral expansionopposite the notch of not less than 0.015 in. 0.381 mm.8. Finish8.1 Because retained scale may mask surface imperfections,as well as mar the plate surfac

28、e, plates shall be descaled by theproducer after heat treatment. In the case of material to beheat-treated by the purchaser, the plates shall be descaled bythe producer prior to shipment.TABLE 1 Chemical RequirementsElement Composition, %Type I Type II Type IIICarbon, maxA0.13 0.13 0.13Manganese, ma

29、x:Heat analysis 0.90 0.90 0.90Product analysis 0.98 0.98 0.98Phosphorus, maxA0.015 0.015 0.010Sulfur, maxA0.015 0.015 0.010Silicon:Heat analysis 0.150.40B0.150.40B0.050.30AProduct analysis 0.130.45C0.130.45CNickel:Heat analysis 8.509.50 7.508.50 6.507.50AProduct analysis 8.409.60 7.408.60MolybdenumA

30、. . 0.100.30Columbium, maxA. . 0.03AApplies to both heat and product analyses.BSilicon may be less than 0.15 %, provided total aluminum is 0.030 % or over, or provided acid soluble aluminum is 0.025 % or over.CSilicon may be less than 0.13 %, provided total aluminum is 0.030 % or over, or provided a

31、cid soluble aluminum is 0.025 % or over.A553/A553M 1429. Marking9.1 In addition to the marking required in SpecificationA20/A20M, each plate shall be legibly stamped or stenciled,depending upon the ordered thickness, with the letters QT,except as otherwise specified in 9.1.1.9.1.1 When the optional

32、heat treatment in 5.2.2.1 isperformed, the plates shall be marked with the letters QTTinstead of QT.10. Keywords10.1 alloy steel; alloy steel plate; pressure containing parts;pressure vessel steels; steel plates; steel plates for pressurevessel applicationsSUPPLEMENTARY REQUIREMENTSSupplementary req

33、uirements shall not apply unless specified in the order.A list of standard supplementary requirements for use at the option of the purchaser are includedin Specification A20/A20M. Several of those considered suitable for use with this specification arelisted below by title. Other tests may be perfor

34、med by agreement between the supplier and thepurchaser.S1. Vacuum Treatment,S2. Product Analysis,S3. Simulated Post-Weld Heat Treatment of MechanicalTest Coupons,S6. Drop Weight Test (for Material 0.625 in. 16 mm andover in Thickness),S8. Ultrasonic Examination in accordance with Specifica-tion A435

35、/A435M,S9. Magnetic Particle Examination,S11. Ultrasonic Examination in accordance with Specifica-tion A577/A577M,S12. Ultrasonic Examination in accordance with Specifica-tion A578/A578M, andS17. Vacuum Carbon-Deoxidized Steel.ADDITIONAL SUPPLEMENTARY REQUIREMENTSAlso listed below are additional opt

36、ional Supplementary Requirements S55 and S56, which aresuitable for this specification.S55. Longitudinal Charpy Impact Energy Absorption Re-quirementS55.1 The longitudinal Charpy V-notch impact propertiesshall not be less than 25 ftlbf 34 J at the specified tempera-ture.S55.2 Each impact test value

37、shall constitute the averagevalue of three specimens, with not more than one value belowthe specified minimum value of 25 ftlbf 34 J but in no casebelow 20 ftlbf 27 J for full size specimens.S56. Transverse Charpy Impact Energy Absorption Re-quirementS56.1 The transverse Charpy V-notch impact proper

38、tiesshall not be less than 20 ftlbf 27 J at the specified tempera-ture.S56.2 Each impact test value shall constitute the averagevalue of three specimens, with not more than one value belowthe specified minimum value of 20 ftlbf 27 J but in no casebelow 15 ftlbf 20 J for full size specimens.TABLE 2 T

39、ensile RequirementsTensile strength, ksi MPa 100 to 120 690825Yield strength (0.2 % offset), min, ksi MPa 85 585Elongation in 2 in. 50 mm, min, %A20.0ASee Specification A20/A20M for elongation adjustment.A553/A553M 143SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to

40、 this standard since the last issue(A553/A553M 10) that may impact the use of this standard. (Approved Oct. 1, 2014.)(1) Added new Type III. (2) Revised title, Table 1, 1.2, 1.3, 5.2, 5.2.2, 5.2.2.1, and 7.2.3.ASTM International takes no position respecting the validity of any patent rights asserted

41、 in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the

42、 responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive c

43、areful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM Internati

44、onal, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 144