1、MIL-P-70695 13 9999906 049bA35 3 1 INCH-POUN 15 November 1991 MIL-P-70695 (AR) MILITARY SPECIFICATION PROJECT1 LE, PRACTICE, 155MM, M 804 E 1 CAST METAL PARTS ASSEMBLY This Specification is approved for use by the U.S. Army Armament, Munitions and Chemical Command, and is available for use by all De

2、partments and Agencies of the Department of Defense. - 1. SCOPE Y 3 1.1 Scope. This specification covers the Metal Parts Assembly for the projectile, Practice, 155MM, M804E1, Cast Body (See 6.1). w 2. APPLICABLE DOCUMENTS 2.1 Government documents 2.1.1 Specifications, standards and handbooks. The fo

3、llowing specifications, standards and handbooks form a part of this document to the extent specified herein. Unless otherwise specified, the Department of Defense Index of Specifications and Standards (DODISS) . issues uf these documents are those listed in the issue of the and supplement thereto, c

4、ited in the solicitation (See 6.2). SPEC IF ICATIONS FEDERAL TT-C-490 - Cleaning Method and Pre-treatment of Ferrous Surfaces for Organic coatings MILITARY MIL-A-2550 - Ammunition, General Specification for MIL-A-48078 - Ammunition, Standard Quality Assurance Provisions, General Specification for AM

5、SC NIA FSC 1320 lXSBUWZQAW51EU Approved for public release; distribution is unlimittd. 0 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,- MIL-P-70675 13 W 99979Ob 049b3b 5 E MIL-P-70695 (AR) STANDARDS M I L I TA R Y MIL-STD-410 - Non-destructive Test

6、ing Personnel MIL-STD-453 - Inspection, Radiographic Qualification and Certification (Unless otherwise indicated, copies of federal and military specifications, standards, and handbooks are available from: Standardization Documents Order Desk, Bldg. 4D, 700 Robbins Avenue, Philadelphia, PA 19111-509

7、4.) 2.1.2 Other Government documents, drawings, and publications. The following other Government documents, drawings and publications form a part of this document to the extent specified herein. Unless otherwise specified, the issues are those cited in the solicitation. DRAWINGS (see 6.9) U.S. Army

8、Armament Research, Development and Engineering Center (ARDEC) 7548993 - Blank, Rotating Band 12953254 - Packaging and Marking for Pallet, Wood, Ammunition, for Projectile, 155MM 12913926 - Projectile, 155MM Practice, M804E1 Loading, Assembly and Marking diagram 12913927 - Projectile, 155MM Practice,

9、 M804E1 Metal Parts Assembly 12913928 - Body Assembly 12913929 - Body PUBLICATIONS FRANKFORD ARSENAL Operating Instructions for Use of Detroit Testing Machine for Band Seat Inspection. (Copies of drawings and other Government documents required by contractors in connection with specific acquisition

10、functions should be obtained from the Contracting activity or as directed by the Government Officer .) 2 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-70b95 13 = 977990b O476837 7 MIL-P-70695 (AR) 2.2 Non-Government publications. The followin

11、g document(s) form a part of this document to the extent specified herein. Unless otherwise specified, the issues of the documents which are DOD adopted are those listed in the issue of the DODISS cited in the solicitation. Unless otherwise specified, the issues of documents not listed in the DODISS

12、 are the issues of the documents cited in the solicitation (See 6.2) . AMERICAN NATIONAL STANDARDS INSTITUTE (ANSI) ANSI B46.1 - Surface Texture (Application for copies should be addressed to the American Standards Institute (ANSI), 1430 Broadway, N.Y., N.Y. 10018 AMERICAN SOCIETY FOR TESTING AND MA

13、TERIALS (ASTM) Na ti ona 1 ASTM A-247 - Evaluating the Microstructure of Graphite in ASTM B-117 - Method of Salt Spray (Fog) Testing ASTM E-3 - Metallographic Specimens ASTM E-8 - Tension Testing of Metallic Materials ASTM E-10 - Brinell Hardness of Metallic Materials ASTM E-103 - Rapid Indentation

14、Hardness Testing of Metallic ASTM E-446 - Reference Radiographs Vol. II for Cast Steel Iron Castings Materials (Application for copies should be addressed to the American Society for Testing and Materials,l916 Race Street, Philadelphia, PA. 19103). . 2.3 Order of precedence. In the event of a confli

15、ct between the text of this document and the references cited herein, the text of this document takes precedence. Nothing in this document, however, supersedes applicable laws and regulations unless a specific exemption has been obtained. 3. REQUIREMENTS 3.1 Material. Materials, parts and assemblies

16、 shall comply with the requirements specified on the applicable drawings and specifications. 3.2 Projectile assembly. The projectile assembly and components shall comply with all requirements specified on Drawing 12913928 and with all requirements specified in applicable specifications. 3 Provided b

17、y IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-70695 13 W 999990b 0496838 9 MIL-P-70695 (AR) 3.3 Material quality. The contractor shall establish procedures to provide material in accordance with the applicable ASTM specifications (see 2.2). This materi

18、al shall be free of pipe, porosity and heavy segregation, 3.4 Process Control Document (PCD). A process control document covering the melting, casting and mold cooling operations shall be submitted to the technical agency through the contracting officer for review and approval prior to initiation of

19、 production. This document shall include descriptions of procedures, equipment, process parameters, monitoring practices, calibration procedures and frequencies of testing for all listed control parameters. The 1604. Any revisions to the PCD shall be submitted to the technical process control docume

20、nt shall be submitted in accordance with DI-P- P agency through the contracting officer for review and approval. 4 As a minimum, the following process parameters shall be addressed in the PCD: a. b. d. e. f. g* h. i. C. Melt furnace and ladle chemistry. Inoculation practice . Casting pour temperatur

21、e. Time from inoculation to last metal poured. Time from pour to shakeout. Nodularity control. Mold except that when hot banding at not less than 427 degrees Celsius ( C) , no prior annealing is necessary. 3.6.3 Band seating sidewall contact. The rotating band shall be applied by carefully pressing

22、the band blank into the band seat so as to make contact with the sidewalls for a minimum of eight- tenths of the band seat depth. The band shall be applied in such a manner so as not to distort the body wall. In addition, there shall be no surface gap between the rotating band and the sidewalls of t

23、he band seat, after the rotating band has been machined to final dimension. 3.6.4 Band seating tightness. The diametrical clearance between the rotatins band and the band seat shall not exceed 0.15mm (-006 in), when the*destructive method of testing is used or 0.23mm (.009 in) when non-destructive m

24、ethod of testing is used. 3.7 Metal defects. 3.7.1 B.ody. The body, including the cavity, shall be free from cracks, splits, bursts, cold shuts, pipes, porosity, inclusions, folds, seams and other metal defects. 3.7.2 Visual radiographic standards. Visual standards for evaluation of metal defects wi

25、ll be established by the contractor with guidance from the Government Agency for each contract after the first months production. However, establishment of visual standards will not waive the requirements for compliance with 3.7.1, 3.7.3 Non-destructive testing. Non-destructive testing shall be perf

26、ormed in the following order: 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-70695 13 999990b 0496840 7 MIL-P-70695 (AR) a. Hydrostatic test. Projectile bodies shall withstand an internal hydrostatic pressure of 10,000 t 5J0 pounds per squar

27、e inch (psi) for 15 seconds minimum. There shall be no evidence of leakage, cracks, ruptures or permanent distortion when tested in accordance with 4.5.6. b. Radiographic inspection. Each body shall be radiographed in accordance with 4.5.5 and meet the requirements of ASTM E-446 with the following e

28、xceptions: 1. There shall be no indications in the following categories; A, B, D, E, F, Go 2. Level I or better for the following categories; CA, CB, and CD. 3. Level i or better for category CC - shrink in the area illustrated in figure 1. in the remaining areas. No worse than level III, of categor

29、y CC, Only film as listed in 6.4 shall be used for radiography of this project il e . 3.8 Tool control dimensions. Dimensions marked tool control shall be gaged at the beginning of production and whenever tooling is replaced. inspect these dimensions, measurements of the tool may be substituted prov

30、ided the contractor has established correlation between the tool dimensions and the component dimensions prior to start of production. The contractor shall be responsible for maintaining adequate surveillance to assure that drawing requirements are being met throughout the life of the tool. Where de

31、struction of components is necessary to 3.9 Microstructure. The microstructure of the body shall be examined to determine form, distribution and size of graphite particles. 3.10 Workmanship. The requirements for workmanship are as shown on the applicable drawings and specifications and the following

32、 : P d 6 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-70695 13 m 9999906 0496843 9 m, _ MIL-P-70695 (AR) I / LEVEL I ONLY FIGURE 1. HIGH STRESS AREA Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IH

33、S-,-,-I l , MIL-P-70b95 13 m 9999906 0496842 O m MIL-P-70695 (AR) 3.10.1 Surface preparation. Preeparation of metal surfaces shall be as specified on the applicable drawings and specifications. Cleaning and preparation are required by component details, the finish specified shall apply to indicated

34、surfaces regardless of contour configuration. 3.10.2 Painting. Painting shall comply with the requirements of the applicable drawings and specifications. All paint shall be dry to the touch before packing for shipment. Drying time prior to testing shall be in accordance with the applicable specifica

35、tion. as detailed on the applicable drawing. The roughness comparison specimens prescribed in ANSI-B46.1 shall be used as a basis for surface roughness determinations. 3.10.3 Surface finish. The requirements for surface finish are i il 3.10.4 Threads. Threads shall be full and undamaged for the enti

36、re minimum length or depth as spcified on the applicable drawing . 3.10.5 Burr. No part shall have a burr which might interfere with the assembly or function of the projectile or which might be injurious to personnel handling the item. 3.10.6 Foreign matter. No part or assembly shall contain dirt, g

37、rease, rust, corrosion or other foreign mater . 3.10.7 Protection of rotating band. The machined rotating band 0 shall be protected from being nicked, burred or otherwise damaged in subsequent handling pr ior to shipment. 3.11 Proving ground. There shall be no break-up or separation of metal parts i

38、n the gun bore or in flight, when tested. 3.12 First article inspection. This specification makes provisions for first article inspection. Requirements for the submission of first article sample by the contractor shall be specified in the contract. 8 Provided by IHSNot for ResaleNo reproduction or n

39、etworking permitted without license from IHS-,-,-MIL-P-70695 13 999990b 049b43 2 MIL-P-70695 (AR) 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise specified in the contract or purchase order, the contractor is responsible for the performance of all inspection requi

40、rements (examinations and tests) as specified herein. Except as otherwise specified in the contract or purchase order, the contractor may use his own ar any other facilities suitable for the performance of the inspection requirements specified herein, unless disapproved by the Government. The Govern

41、ment reserves the right to perform any of the inspections set forth in the specification where such inspections are deemed necessary to assure supplies and services conform to prescribed r equ i r em en t s . 4.1.1 Responsibility for compliance. All items must meet all requirements of Section 3 and

42、5. The inspection set forth in this specification shall become a part of the contractors overall inspection system or quality program. The absence of any inspection requirements in the specification shall not relieve the contractor of the responsibility of ensuring that all products or supplies subm

43、itted to the Government for acceptance comply with all requirements of the contract. Sampling inspection, as part of manufacturing operations, is an acceptable practice to ascertain conformance to requirements, however, this does not authorize 2 . submission of known defective material, either indic

44、ated or actual, nor does it commit the Government to accept defective material. 4.2 Classification of inspections. The following types of inspection shall be conducted on this item: O a. Fir st ar ticle inspection b. Quality conformance inspection 4.3 First article inspection. 4.3.1 Inspection and t

45、ests (non ballistic). 4.3.1.1 Submission. The contractor shall submit a first article sample as designated by the Contracting Officer for evaluation in accordance with the provisions of 4.3.2. The first article sample shall consist of the following items in sample quantities as indicated. 9 Provided

46、 by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-P-70695 13 H 9979906 0496844 4 H MI L-P- 70 6 9 5 (AR) Part Description Drawing - Quantity Blank, Rotating Band 7548993 Body (unpainted) 12913929 Body Assembly 12913928 Projectile Metal Parts 12913927 5 5 5

47、 45 All assemblies and components shall have been produced by the con- tractor or furnished by a supplier and shall have been manufactured using the same production processes, procedures and equipment which will be used in fulfilling the contract. All parts and materials, including packaging and pac

48、king, shall be obtained from the same source of supply as will be used in regular production. Prior to submission, the contractor shall inspect the sample to the degree necessary to assure that it conforms to the requirements of the contract and submit a record of this inspection with the sample in-

49、 cluding statements of findings for materials, processes and tests. A sample containing known defects will not be submitted unless specifically authorized, by the Contracting Officer. ticle sample, or portion thereof, as directed by the Contracting Officer, shall also be submitted whenever there is a lapse in production for a period in excess of 90 days or whenever a change occurs in manufacturing