ARMY A-A-52408-1993 PRESERVATIVE COATING RUBBER FOR RUBBER SURFACES《橡胶表面防腐涂料》.pdf
《ARMY A-A-52408-1993 PRESERVATIVE COATING RUBBER FOR RUBBER SURFACES《橡胶表面防腐涂料》.pdf》由会员分享,可在线阅读,更多相关《ARMY A-A-52408-1993 PRESERVATIVE COATING RUBBER FOR RUBBER SURFACES《橡胶表面防腐涂料》.pdf(5页珍藏版)》请在麦多课文档分享上搜索。
1、A-A-52408 9999974 0355348 644 W INCH-POUND A-A-52 408 Auaust 31. 1993 SUPERSEDING MIL-P-11520F 10 May 1989 COMMERCIAL ITEM DESCRIPTION PRESERVATIVE COATING, RUBBER: FOR RUBBER SURFACES The General Services Administration has authorized the use of this commercial item description (CID) as a replaceme
2、nt for MIL-P-11520FI which is canceled. ABSTRACT. This CID covers preservative coating for the protection of natural or synthetic rubber items such as tires, track pads, bogey wheels, gaskets, hoses, and others. Its purpose is to eliminate deterioration due to oxidation, ultraviolet light and ozone.
3、 The material can be used where solvent vapor is not a hazard. The preservative is suitable where storage temperatures may be below 32OF. It is intended for spray, brush or dip application. The preservative coating is also referred to herein as “preservative“. SALIENT CHARACTERISTICS. O a. Materials
4、. The preservative shall conform to the physical properties and performance requirements specified herein. The use of recovered material made in compliance with regulatory requirements is acceptable providing that all requirements of this CID are met (see note e). Hazardous materials shall be handle
5、d in accordance with 29 CFR Chapter XVII. b. Toxicity. The preservative shall contain no substances of known toxicity, and shall conform to Rule 442 of the South Coast Air Quality Management District (see Salient Characteristics (SC). c. Homogeneity. The preservative shall remain in a completely hom
6、ogenous state. The homogeneity shall be verified by visual examination of container contents upon opening an as received, non-agitated container for separation of ingredients. Beneficial comments, recommendations, additions, deletions clarifications, etc. and any other data which may improve this do
7、cument should be sent by letter to: U.S. Army Tank-Automotive Command, ATTN: AMSTA-GDS, Warren, MI 48397-5000. AMSC NIA FSC 8030 DISTRIBUTION STATEMENT A. Approved for public release; distribution is unlimited. Licensed by Information Handling ServicesProvided by IHSNot for ResaleNo reproduction or
8、networking permitted without license from IHS-,-,-A-A-52408 9999974 0155349 580 Material -_- SBR 1500 HAF Type Carbon Black (N330) Zinc Oxide Stearic Acid A-A-52408 Parts by weight 100.0 50.0 3.0 1.5 -t- d. Viscosity. The viscosity shall be such that the preservative shall pass through a number 4 Fo
9、rd cup in not more than 60 seconds when tested in accordance with American Society for Testing and Materials (ASTM) D1200. e. Dry time. Applied preservative shall be dry to the touch in no more than 60 minutes, when touched with clean white laboratory filter paper for no less than 5 seconds. The pap
10、er shall show no indication of wetting or discoloration. f. Accelerated storage. The preservative shall be free from gelation, hard caking, separation, or other visible signs of deterioration or nonconformance after storage for 28 days in typical storage containers at both 120 + 5OF and 20 - + 5OF.
11、The preservative shall then conform to SC b through e- 9. Discoloration. The discoloration of the natural or synthetic rubber products treated with the preservative shall be kept to a minimum. h. Ozone resistance. Five preserved type A test specimens shall be free of cracks and crazing when examined
12、 under 7-power magnification after 25% elongation and exposure to an air and ozone mixture of 50 + 5 parts ozone per one hundred million (pphm) of air by volume for 200 + 1 hours, or 100 + 10 pphm of ozone for 100 - + 1 hours, at 104 - + 2OF in accordance with ASTM D1149. - i. Penetration and retent
13、ion of preservative. The average minimum increase in weight for five preserved test specimens shall be at least 2% of the weight of the five test Specimens prior to preservation, when weighed 24 + 1 hour after preservation to the nearest .O001 gram. Test specimens shall be 3 x 1 inches. j. Unit cont
14、ainer sizes. The preservative shall be available in the following unit container sizes: pints, gallons, 5 gallon pails, and 55 gallon drums (see note b and c). k. Material safety data sheet (MSDS). A MSDS shall be prepared in accordance with the latest revision of FED-STD-313 (see note b and f). 1.
15、Identification and markings. Each unit container (see SC j) shall be marked in accordance with MIL-STD-129 and shall include as a minimum the manufacturers name, the date of manufacture, and CID PIN (see note c). m. Test specimens. Test specimens shall conform to the composition shown in table I. Ru
16、bber test specimens shall be cured into sheets 0.075 inch in thickness under a minimum pressure of 500 psi at a temperature of 307OF OK 30 minutes. thoroughly until comp nless otherwise specified (see note b), test specimens shall be cleaned of all contaminants and preservative applied by hand brush
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制:
部分文档作品中含有的国旗、国徽等图片,仅作为作品整体效果示例展示,禁止商用。设计者仅对作品中独创性部分享有著作权。
- 关 键 词:
- ARMYAA524081993PRESERVATIVECOATINGRUBBERFORRUBBERSURFACES 橡胶 表面 防腐涂料 PDF

链接地址:http://www.mydoc123.com/p-439941.html