1、*USACE / NAVFAC / AFCESA /NASA UFGS-08 88 53 (May 2011)-Preparing Activity: NAVFAC SupersedingUFGS-08 88 53 (April 2006)UFGS-11192 (September 1999)UNIFIED FACILITIES GUIDE SPECIFICATIONSReferences are in agreement with UMRL dated April 2011*SECTION TABLE OF CONTENTSDIVISION 08 - OPENINGSSECTION 08 8

2、8 53DETENTION AND SECURITY GLAZING05/11PART 1 GENERAL1.1 REFERENCES1.2 SUBMITTALS1.3 DELIVERY, STORAGE, AND HANDLING1.4 ENVIRONMENTAL CONDITIONS1.5 WARRANTYPART 2 PRODUCTS2.1 DETENTION GLAZING ASSEMBLIES2.1.1 Glass-Clad Polycarbonate2.1.2 Plastic Laminated (Bonded) Construction2.1.3 Glass Laminated

3、(Bonded) Construction2.2 DETENTION GLAZING MATERIALS2.2.1 Glass, Chemically Strengthened2.2.2 Glass, Annealed, Wire2.2.3 Polycarbonate, Transparent, Rigid Sheet Plastic2.3 DETENTION GLAZING TYPES2.4 SETTING MATERIALS2.4.1 Glazing Compound2.4.2 Elastomeric Sealant2.4.3 Preformed Channels2.4.4 Sealing

4、 Tapes2.4.5 Setting Blocks and Edge Blocks2.4.6 AccessoriesPART 3 EXECUTION3.1 GLAZING TYPES3.2 PREPARATION3.3 GLASS SETTING3.3.1 Wire Glass3.3.2 Plastic Sheet3.4 CLEANINGSECTION 08 88 53 Page 1Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-3.5 SCHE

5、DULE- End of Section Table of Contents -SECTION 08 88 53 Page 2Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-*USACE / NAVFAC / AFCESA /NASA UFGS-08 88 53 (May 2011)-Preparing Activity: NAVFAC SupersedingUFGS-08 88 53 (April 2006)UFGS-11192 (Septemb

6、er 1999)UNIFIED FACILITIES GUIDE SPECIFICATIONSReferences are in agreement with UMRL dated April 2011*SECTION 08 88 53DETENTION AND SECURITY GLAZING05/11*NOTE: This guide specification covers the requirements for security glazing.Adhere to UFC 1-300-02 Unified Facilities Guide Specifications (UFGS)

7、Format Standard when editing this guide specification or preparing new project specification sections. Edit this guide specification for project specific requirements by adding, deleting, or revising text. For bracketed items, choose applicable items(s) or insert appropriate information.Remove infor

8、mation and requirements not required in respective project, whether or not brackets are present.Comments, suggestions and recommended changes for this guide specification are welcome and should be submitted as a Criteria Change Request (CCR).*PART 1 GENERAL1.1 REFERENCES*NOTE: This paragraph is used

9、 to list the publications cited in the text of the guide specification. The publications are referred to in the text by basic designation only and listed in this paragraph by organization, designation, date, and title.Use the Reference Wizards Check Reference feature when you add a RID outside of th

10、e Sections Reference Article to automatically place the reference in the Reference Article. Also use the Reference Wizards Check Reference feature to update the issue dates.SECTION 08 88 53 Page 3Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-Refere

11、nces not used in the text will automatically be deleted from this section of the project specification when you choose to reconcile references in the publish print process.*The publications listed below form a part of this specification to the extent referenced. The publications are referred to with

12、in the text by the basic designation only.AMERICAN ARCHITECTURAL MANUFACTURERS ASSOCIATION (AAMA)AAMA MCWM-1 (1989) Metal Curtain Wall ManualASTM INTERNATIONAL (ASTM)ASTM C 1036 (2006) Standard Specification for Flat GlassASTM C 158 (2002; R 2007) Strength of Glass by Flexure (Determination of Modul

13、us of Rupture)ASTM C 864 (2005) Dense Elastomeric Compression Seal Gaskets, Setting Blocks, and SpacersASTM C 920 (2011) Standard Specification for Elastomeric Joint SealantsGLASS ASSOCIATION OF NORTH AMERICA (GANA)GANA Glazing Manual (2004) Glazing ManualGANA Sealant Manual (2008) Sealant ManualNAT

14、IONAL FIRE PROTECTION ASSOCIATION (NFPA)NFPA 80 (2010; TIA 10-2) Standard for Fire Doors and Other Opening ProtectivesU.S. GENERAL SERVICES ADMINISTRATION (GSA)CID A-A-59502 (Basic) Plastic Sheet, Polycarbonate1.2 SUBMITTALS*NOTE: Review submittal description (SD) definitions in Section 01 33 00 SUB

15、MITTAL PROCEDURES and edit the following list to reflect only the submittals required for the project. Submittals should be kept to the minimum required for adequate quality control.A “G” following a submittal item indicates that the submittal requires Government approval. Some submittals are alread

16、y marked with a “G”. Only delete an existing “G” if the submittal item is not complex and can be reviewed through the Contractors Quality Control system. Only add a “G” if the SECTION 08 88 53 Page 4Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-sub

17、mittal is sufficiently important or complex in context of the project.For submittals requiring Government approval on Army projects, a code of up to three characters within the submittal tags may be used following the “G“ designation to indicate the approving authority. Codes for Army projects using

18、 the Resident Management System (RMS) are: “AE“ for Architect-Engineer; “DO“ for District Office (Engineering Division or other organization in the District Office); “AO“ for Area Office; “RO“ for Resident Office; and “PO“ for Project Office. Codes following the “G“ typically are not used for Navy,

19、Air Force, and NASA projects.Choose the first bracketed item for Navy, Air Force and NASA projects, or choose the second bracketed item for Army projects.*Government approval is required for submittals with a “G“ designation; submittals not having a “G“ designation are for Contractor Quality Control

20、 approval.for information only. When used, a designation following the “G“ designation identifies the office that will review the submittal for the Government. The following shall be submitted in accordance with Section 01 33 00 SUBMITTAL PROCEDURES:SD-03 Product DataGlazing materialsInclude glass m

21、anufacturers printed literature for setting and sealing materials and for cleaning of each type of glazing material specified.SD-04 SamplesGlazing materialsSubmit samples, 250 mm 10 inches square, factory labeled, for each type of glazing specified.SD-08 Manufacturers InstructionsGlass setting1.3 DE

22、LIVERY, STORAGE, AND HANDLINGDeliver products to the site in their original unopened containers, plainly labeled with manufacturers names and brands. Store all glass and setting materials in safe, dry locations and do not unpack until needed for installation. Handle and install materials in a manner

23、 that protects them from damage.1.4 ENVIRONMENTAL CONDITIONSDo not start glazing work until the outdoor temperature is above 4 degrees C40 degrees F and rising unless approved provisions are made to warm the SECTION 08 88 53 Page 5Provided by IHSNot for ResaleNo reproduction or networking permitted

24、without license from IHS-,-,-glass and rabbet surfaces. Provide sufficient ventilation to prevent condensation of moisture on glazing work during installation. Do not perform glazing work during wet weather.1.5 WARRANTY*NOTE: The warranty clause in this guide specification has been approved by NAVFA

25、CENGCOMHQ in accordance with the requirements of Naval Facilities Acquisition Supplement (NFAS). NFAS can be found at the following link:https:/portal.navfac.navy.mil/portal/page/portal/navfac/navfac_forbusinesses_The paragraph in this specification may be used without any HQ approval or request for

26、 waiver.*Warranty glass units against development of material obstruction to vision as a result of delamination, other than through glass breakage for at least a 5 year period from the date of acceptance of the work. Provide new units for units failing to comply with terms of this warranty no later

27、than 45 working days following receipt of notice from the Government.PART 2 PRODUCTS2.1 DETENTION GLAZING ASSEMBLIES2.1.1 Glass-Clad PolycarbonateTwo glass outer layers (plies), bonded to a core of one or more plastic layers (plies).2.1.2 Plastic Laminated (Bonded) ConstructionTwo or more layers (pl

28、ies) of plastic sheet bonded together with polyurethane.2.1.3 Glass Laminated (Bonded) ConstructionTwo or more layers (plies) of chemically-strengthened float glass bonded together with polyvinyl butyral (PVB).2.2 DETENTION GLAZING MATERIALS2.2.1 Glass, Chemically StrengthenedASTM C 158, transparent

29、 prestressed.2.2.2 Glass, Annealed, WireASTM C 1036, Type II, Class 1, form 1, Quality q8, 6 mm 1/4 inch thick, with diamond or square mesh.2.2.3 Polycarbonate, Transparent, Rigid Sheet Plastic*NOTE: The type, class, and thickness of polycarbonate glazing material to be used in detention glazing ass

30、emblies is specified in SECTION 08 88 53 Page 6Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-paragraph entitled “Detention Glazing Types“ by Type. Note that mar-resistant coating is to be provided in Glazing Types 3, 5, and 5W only.*CID A-A-59502,

31、Type I Grade A Type III Grade A clear transparent, thickness as specified.2.3 DETENTION GLAZING TYPES*NOTE: Glazing types should be indicated on project drawings.*a. Type 1: Tempered Glass; Conform to Section 08 81 00 GLAZING.b. Type 2: 11 mm 7/16 inch nominal glass-clad polycarbonate: 3 mm 1/8 inch

32、 clear chemically-strengthened glass, 1.3 mm 0.050 inch polyurethane interlayer, 3 mm 1/8 inch polycarbonate sheet, 1.3 mm 0.050 inch polyurethane interlayer, 3 mm 1/8 inch clear chemically-strengthened glass.c. Type 3: 10 mm 3/8 inch nominal laminated plastic: 4.8 mm 3/16 inch mar-resistant (hard c

33、oat) polycarbonate (threat side), 0.9 mm 0.034 inchpolyurethane interlayer, 4.8 mm 3/16 inch polycarbonate sheet.d. Type 4: 11 mm 7/16 inch nominal laminated glass: 3 mm 1/8 inch clear chemically-strengthened glass, 2.3 mm 0.090 inch polyvinyl butyral interlayer, 3 mm 1/8 inchclear chemically-streng

34、thened glass, 2.3 mm 0.090 inchpolyvinyl butyral interlayer, 3 mm 1/8 inch clear chemically-strengthened glass.e. Type 4W: Add a separate (not laminated) 6 mm 1/4 inchannealed wire glass on staff side to Type 4.f. Type 5: 14.3 mm 9/16 inch nominal glass-clad polycarbonate: 3 mm 1/8 inch clear chemic

35、ally-strengthened glass (threat side), 1.3 mm 0.050 inch polyurethane interlayer, 6 mm 1/4 inch polycarbonate sheet, 1.3 mm 0.050 inch polyurethane interlayer, 3 mm 1/8 inch clear chemically-strengthened glass.g. Type 5W: Add a separate (not laminated) 6 mm 1/4 inchannealed wire glass on staff side

36、to Type 5.h. Type 6: 8 mm 5/16 inch nominal laminated glass: 3 mm 1/8 inch clear chemically-strengthened glass, 2.3 mm 0.090 inch polyvinyl butyral interlayer, 3 mm 1/8 inchclear chemically-strengthened glass.2.4 SETTING MATERIALSProvide types required for the applicable setting method specified in

37、GANA Glazing Manual and GANA Sealant Manual, except as modified in this section. Do not use metal sash putty, nonskinning compounds, nonresilient preformed sealers, or impregnated preformed gaskets. Materials exposed to view shall be gray or neutral color.SECTION 08 88 53 Page 7Provided by IHSNot fo

38、r ResaleNo reproduction or networking permitted without license from IHS-,-,-2.4.1 Glazing CompoundUse for face glazing metal sash. Verify compatibility with materials in glazing assembly.2.4.2 Elastomeric SealantASTM C 920, Type S, Grade NS, Class 12.5, use NT. Use for channel or stop glazing metal

39、 sash. Sealant shall be chemically compatible with setting blocks, edge blocks, and sealing tapes , and with plastic sheet. Color of sealant shall be white.2.4.3 Preformed ChannelsNeoprene, AAMA MCWM-1, as recommended by the glass manufacturer for the particular condition. Channels shall be chemical

40、ly compatible with plastic sheet.2.4.4 Sealing TapesPreformed, semisolid, polymeric-based material of proper size and compressibility for the particular condition. Use only where glazing rabbet is designed for tape and tape is recommended by the glass or sealant manufacturer. Provide spacer shims fo

41、r use with compressible tapes. Tapes shall be chemically compatible with plastic sheet.2.4.5 Setting Blocks and Edge BlocksASTM C 864 neoprene of 70 to 90 Shore “A“ durometer hardness, chemically compatible with sealants used, and of sizes recommended by the glass manufacturer.2.4.6 AccessoriesAs re

42、quired to provide a complete installation, including glazing points, clips, shims, angles, beads, and spacer strips. Provide noncorroding metal accessories. Provide primer-sealers and cleaners as recommended by the glass and sealant manufacturers.PART 3 EXECUTION3.1 GLAZING TYPES*NOTE: Glazing types

43、 should be indicated on project drawings.*Locations and types of glass for use in glazed openings as indicated.3.2 PREPARATIONDetermine the sizes to provide the required edge clearances by measuring the actual opening to receive the glass. Leave labels in place until the installation is approved. Se

44、curely attach movable items or keep in a closed and locked position until glazing compound has thoroughly set.SECTION 08 88 53 Page 8Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-3.3 GLASS SETTINGItems to be glazed shall be either shop or field glazed using glass of the quality and thickness specified. Preparation and glazing shal