GMKOREA EDS-T-7111-2011 Method of Grain Flow Test for Steel.pdf

《GMKOREA EDS-T-7111-2011 Method of Grain Flow Test for Steel.pdf》由会员分享，可在线阅读，更多相关《GMKOREA EDS-T-7111-2011 Method of Grain Flow Test for Steel.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING STANDARDS Test Procedure SUPERCEDED EDS-T-7111 Method of Grain Flow Test for Steel This standard may be applied only for current projects. It is Superceded for all future projects and replaced by USCAR8. I88 $*2T 4G - Note: 8 E:48t G8 =97 FF7 957%L+ , FG P-P Program .Bd# USCAR8 ) $4=F7

2、957F$ . Copyright 2011 General Motors Company All Rights Reserved July 2011 Originating Department: GM Korea Engineering Standards Page 1 of 3 Version : 3 1 Scope Note: Nothing in this standard supersedes applicable laws and regulations. Note: In the event of conflict between the Korean and English

3、language, the Korean language shall take precedence. 1.1 Purpose. This standard specifies the methods of grain flow test for forged or rolled steels. 2 References Note: Only the latest approved standards are applicable unless otherwise specified. 2.1 External Standards/Specifications. None 2.2 GM St

4、andards/Specifications. None 2.3 Additional References. None 3 Resources 3.1 Test Piece. Take the test piece from forged or rolled steels by cutting it along the center part of the product in parallel with the working direction and the cut section to be tested shall be milled or grinded, placing its

5、 surface roughness between 12.5 S and 25 S. 3.2 Test Solution. Test solution used in this test shall be the mixed solution of industrial hydrochloride acid and water in the ratio of 1:1. 4 Procedures 4.1 Conditions. 4.1.1 Test Conditions. Deviations from the requirements of this standard shall have

6、been agreed upon. Such requirements shall be specified on component drawings, test certificates, reports, etc. 4.2 Instructions. 1 P7 :0 : ., E:48 6 therefore observation shall be conducted frequently. 6.4 Hydrochloric acid solution begins to turn green about 30 minutes after commencement of heating

7、. In case it is used for a long time, its color concentration deepens, which means solution is aged, so it shall be replaced by new solution. Aged solution has low etching effect and so new solution shall be, in principle, used for every test. 6.5 When disposing hydrochloric acid solution, store it

8、in a specified container without fail and then dispose it in the waste water disposal plant of the company. 7 Notes 7.1 Glossary. Grain Flow: Grain flow means the flow of grain strained under such stress as forging or rolling from outside. 7.2 Acronyms, Abbreviations, and Symbols. Not applicable. 8

9、Coding System This standard shall be referenced in other documents, drawings, etc., as follows: Test to EDS-T-7111 9 Release and Revisions This standard was originated in August 1990. It was first approved by Engineering Standard Committee in August 1990. It was first published in August 1990. 6.3 4

10、7( 4 701 3L768 !6 “L?: 6$) :08 F+ , 4G D8 % 4 6! .Fp4 88t 77# 4G D8 0 .4%L6 +4%T 70)X4 88p,) , 8:0 4=dF7 6 F$ . 6.4 701 3L768t 47( G 30.8 0 F+2P.Bd “1/8x (x %L#$ , 848 17F 77# “1/8 “$4 ; 6:+ , 8# 68 “GG%P 8,) , 1)7 68p) = F7 6 F$ . “G%P 68t .4G04 94F%L6 88p,) , + 4G *$ 1)7 68x 17F8 8?8$ . 6.5 701 3L

11、768 Ed4 -L&4 :9I%P 7d7 948F G , 1! E3L =*88x BF7 Ed =*F$ 7 768 9I8 7.1 98,l 76 . $*2T : I88 9I8 (GRAIN)8 7.).Bd $9 D# 67$ &%8 8 )Y8x -O6x -GI%P 9I88 H*8x +F$ . 7.2 66 -C dGl . F$-1F 68 . 8 Ed - $* ,l2P! $+ &%72P ., E:48 87%T &# $80 M8 EdF$ . Test to EDS-T-7111 9 9P9I -C P9I 8)Y ., E:48t 1990 “x 8 87

12、 E:4 -Gl4 .7 %L6 , d3TE:41,h7 8F 1990“x 887 38%L6$ . ., E:48t 1990“x 887 ) 9P9I / -PF%L6$ . Issue / P9I8)Y Publication Date / 38 88 Description (Organization) / 9PP9I76 (:04.2P ) 3 JUL 2011 Apply new Engineering Standard Template. Superceded (Corrosion / Metallurgical Material Lab Team) / 4 d3TE:4 64 957 . F9I957 =* (28*4G D4 )