《FORD WSS-M1H897-A-2008 FABRIC DIAMOND PATTERN WOVEN JACQUARD UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A 《钻石图案的不分层提花机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H897-A-2008 FABRIC DIAMOND PATTERN WOVEN JACQUARD UNLAMINATED TO BE USED WITH FORD WSS-M99P1111-A 《钻石图案的不分层提花机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2008 12 05 N-STATUS No Replacement L. Schmalz, FNA / M. Montgomery, FOE 2004 05 26 Activated N. J. Komatsu Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 2 FABRIC, DIAMOND PATTERN, WOVEN JACQUARD, WSS-M

2、1H897-A UNLAMINATED NOT TO BE USED FOR NEW DESIGN 1. SCOPE The material defined by this specification is a woven jacquard polyester face fabric. 2. APPLICATION This specification was released originally for material used as an interior trim fabric for C195 China Model Year 2002. 3. REQUIREMENTS In a

3、ddition to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A2/A3/A4 as applicable. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111

4、-A). 3.2 FABRIC CONSTRUCTION 3.2.1 Fabric Count, +/- 10% tolerance (ASTM D 3775) Warp 290 ends/10 cm Weft 163 picks/10 cm 3.2.2 Fabric Weight, range. (FLTM BN 106-01) 360 g/m23.3 COMPOSITION (ASTM D 629) Fabric 100% polyester 3.4 YARN CONSTRUCTION (ASTM D 1244) Warp 500 dtex f144 (air texturized, se

5、mi-dull, round) Weft 722 dtex f192 (air texturized, semi-dull round) ENGINEERING MATERIAL SPECIFICATIONWSS-M1H897-A Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 2 of 2 3.5 METHOD OF DYEING Yarn dyed or as approved by Materials Engineering 3.6 FINISHED OPERATIONS

6、 As approved by Materials Engineering 3.7 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, max 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 4. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 4.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.