EN 513-1999 en Unplasticized Polyvinylchoride (PVC-U) Profiles for the Fabrication of Windows and Doors - Determination of the Resistance to Artificial Weathering《门窗建造用未增塑聚氯乙烯(PVC-.pdf

《EN 513-1999 en Unplasticized Polyvinylchoride (PVC-U) Profiles for the Fabrication of Windows and Doors - Determination of the Resistance to Artificial Weathering《门窗建造用未增塑聚氯乙烯(PVC-.pdf》由会员分享，可在线阅读，更多相关《EN 513-1999 en Unplasticized Polyvinylchoride (PVC-U) Profiles for the Fabrication of Windows and Doors - Determination of the Resistance to Artificial Weathering《门窗建造用未增塑聚氯乙烯(PVC-.pdf（14页珍藏版）》请在麦多课文档分享上搜索。

1、Unplasticized polyvinylchloride (PVC4J) profiles for the fabrication of windows and doors - Determination of the resistance to artificial weathering The European Standard EN 513 1999 has the status of a British Standard ICs 83.080.20; 91.060.50 NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITED BY

2、 COPYRIGHT LAW STD-BSI BS EN 513-ENGL 1999 lb24bb9 0817855 927 BS EN 613:1999 been prepared under the direction of the Sector Amd.No. Date Committee for Building and Civil Engineering, was published under the authority of the Standards Committee and comes into effect on 15 December 1999 O BSI 12-199

3、9 ISBN O 580 35305 2 National foreword Comments This British Standard is the English language version of EN 5131999. The UK participation in its preparation was entrusted by Technical Committee W538, Doors, windows, shutters, hardware and curtain walluig, to Subcommittee BW1, Windows, which has the

4、responsibility to: - aid enquirers to understand the ted, - present to the responsible European committee any enquiries on the - monitor related international and European developments and promulgate interpretation, or proposals for change, and keep the UK interests informed them in the UK This Brit

5、ish Standard forms part of a package of standards on window and doors which wiil not become fully effective until all standards on the package have been published The effective date of publication will be agreed within CEN and wiil be notified. A list of organizations represented on this subcommitte

6、e can be obtained on request to its secretary. Cross-references The British Standards which implement international or European publications referred to in this document may be found in the BSI Standards Catalogue under the section entitled “International standards Correspondence Index“, or by usmg

7、the “Find“ facility of the BSI Standards Elecronic Catalogue. A British Standard does not purport to include al the necessary provisions of a contract. Users of British Stanhds are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from l

8、egal obligations. Summary of pages This document comprises a front cover, an inside front cover, the EN titie page, pages 2 to 11 and a back cover. The BSI copyright notice displayed in this document indicates when the document was last issued. EUROPEAN STANDARD NORME EUROPENNE EUROPISCHE NORM EN 51

9、3 July 1999 ICs 83.080.20; 83.140.99 English version Unplasticized polyvinylchloride (PVC-U) profiles for the fabrication of windows and doors - Determination of the resistance to artificial weathering Profils de polychlorure de vinyle non plastifi (PVC-U) pour la fabrication des fentres et des port

10、es - Dtermination de la rsistance au vieillissement artificiel Profile aus weichmacherfreiem Polyvinylchlorid (PVC-U) zur Herstellung von Fenstern und Tren - Bestimmung der Wetterechtheit und Wetterbestnddig keit duch knstliche Bewitterung This European Standard was approved by CEN on 7 June 1999. C

11、EN members are bound to comply with the CENKENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographic references concerning such national standards may be obtained on appli

12、cation to the Central Secretariat or to any CEN member. This European Standard was established by CEN in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own language and notified to CEN Central S

13、ecretariat has the same status as the official versions. CEN members are the national standards organizations of Austria, Belgium, Denmark, Finland, France, Germany, Greece, Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and United Kingdom. EUROPEAN CO

14、MMITTEE FOR STANDARDIZATION COMITE EUROPEEN DE NORMALISATION EUROPISCHES KOMITEE FUR NORMUNG Central Secretariat : rue de Stassart, 36 All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. B-1050 Brussels 1999 CEN Ref. N3. EN 513:1999 E STD-BSI BS EN 51

15、3-ENGL 1979 = LbZLibbS 0837857 7TT Page 2 EN 513:1999 Contents Page Foreword . 3 1 Scope . . 4 2 Normative references . . . 4 3 Principle . 4 4 Apparatus 4 4.1 Artificial weathering apparatus with a Xenon arc light source . 4 4.2 Grey scale . 5 4.3 Colour change measurement apparatus 5 4.4 Charpy im

16、pact apparatus 5 5 Test pieces . - 6 5.1 Number of test pieces . 6 5.2 Dimensions of the test pieces 6 5.3 Preparation of the test pieces 6 6 Conditioning 6 7 Weathering test conditions 7 7.1 General . 7 7.2 Test conditions for method 1 7 7.3 Test conditions for method 2 7 8 Procedure 8 9 Test Rep0

17、rt 9 Annex A (informative) Reasons for the choice of exposure conditions 11 A.l Scope 11 A.2 Moderate climates . 11 A.3 Severe (hot and dry) climates 11 O BSI 12-1999 STDaBSI BS EN 513-ENGL 3997 H bb2libb9 0837858 b3b Page 3 EN 513:1999 Foreword This European Standard has been prepared by Technical

18、Committee CEN/TC 33, Doors, windows, shutters and building hardware, the Secretariat of which is held by AFNOR This European Standard shall be given the status of a national standard, either by publication of an identical text or by endorsement, at the latest by January 2000, and conflicting nationa

19、l standards shall be withdrawn at the latest by January 2000. According to the CENICENELEC Internal Regulations, the national standards organizations of the following countries are bound to implement this European Standard: Austria, Belgium, Czech Republic, Denmark, Finland, France, Germany, Greece,

20、 Iceland, Ireland, Italy, Luxembourg, Netherlands, Norway, Portugal, Spain, Sweden, Switzerland and the United Kingdom. The requirements are incorporated in the appropriate Product Standard. This draft European Standard is based on the results of extensive research and inter-laboratory testing compa

21、ring artificial and natural weathering. From the results it was concluded that the requirements for the retention of mechanical properties after long term artificial weathering were best defined using one method, and Charpy impact strength testing was chosen. In addition, the spray cycles for modera

22、te and severe climates have been chosen. Annex A, which is informative, gives the reasons for the choice of exposure conditions. This standard reflects the state of the art at the time of publication. Further research may necessitate amendments to this standard. O BSI 12-1999 STD-BSI BS EN SL3-ENGL

23、L999 IIbZLIbb7 UBI17857 572 Page 4 EN 51 3: 1999 1 Scope This European Standard specifies a method for exposing test pieces from an unplasticized polyvinylchloride (PVC-U) profile for the fabrication of windows and doors to a Xenon arc laboratory light source, in order to assess changes in impact st

24、rength and colour. The method given in8.10 (b) is the reference method of colour measurement. 2 Nonnative references This European Standard incorporates by dated or undated references, provisions from other publications listed hereafter. These normative references are cited in the appropriate places

25、 in the text and the publications are listed hereafter. For dated references, subsequent amendments to or revisions of any of these publications apply to this European Standard only when incorporated in by amendment or revision. For undated references, the latest edition of the publication referred

26、to applies. EN 20105-A03 EN IS0 179 IS0 4892-1 1994 IS0 4892-2 IS0 7724-1 IS0 7724-2 IS0 7724 - 3 CIE Publication 15.2 Textiles - Tests for colour fastness - Part A03: Grey scale for assessing staining (IS0 105-A03:1993). Plastics - Determination of Charpy impact strength (IS0 179:1993). Plastics -

27、Methods of exposure to laboratory light sources - Part 1 : General guidance. Plastics - Methods of exposure to laboratory light sources - Part 2: Xenon-arc sources. Paints and varnishes - Colorimetry - Part 1 : Principles. Paints and varnishes - Colorimetry - Part 2: Colour measurement. Paints and v

28、arnishes - Colorimetry - Part 3: Calculation of colour differences. Colorimetry. 3 Principle Test pieces taken from the sight surface of the profiles are exposed in a Xenon arc artificial weathering apparatus at a specified irradiance, Black and White Standard Temperatures, relative humidity and spr

29、ay cycle. After specified radiation doses, the changes in Charpy impact strength and colour of the test pieces are determined. 4 Apparatus 4.1 Artificial weathering apparatus with a Xenon arc light source The apparatus shall comply with IS0 4892 Part 1 and 2 and with the requirements of this standar

30、d. Accordingly, each apparatus shall include the following. 4.1.1 Xenon arc source in accordance with method A of IS0 4892 Part 2 with a spectral irradiance in the band pass of 280 nm to 800 nm of (550 f 55) W/d and a spectral irradiance in the band pass of 280 nm to 400 nm of (60 i 12) W/d. 4.1.2 T

31、est enclosure which contains a frame carrying test piece holders. 4.1.3 Spray nozzles to provide uniform and continuous wetting of the exposed test pieces for defined periods of time. O BSI 12-1999 STD=BSI BS EN 513-ENGL 1777 1b24bbS OB178b0 2711 W Page 5 EN 51 3:1999 NOTE : The intention of the spr

32、aying is not to scour loosely bound solid material. It is important, therefore, that the combination of droplet size and velocity is chosen to minimize the removal of solid material. 4.1.4 A means of providing controlled humidity at the defined level. 4.1.5 A means of controlling air temperaturewith

33、in the test chamber. 4.1.6 A Black Standard Thermometer in accordance with 4.1 5.1 .i of IS0 4892 Part 1: 1994 with a response time less than 1 min and a means of recording maximum temperatures during one cycle. 4.1.7 A White Standard Thermometer in accordance with 4.1.5.1 .i of IS0 4892 Part 1:1994

34、 with a response time less than 1 min and a means of recording maximum temperatures during one cycle. 4.1.8 A device to determine the UV radiant exposure in the wavelength region between 280 nm and 400 nm expressed in joules per square metre (J/m2). 4.1.9 A device to determine the radiant exposure i

35、n the UV and visible wavelength region between 280 nm and 800 nm expressed in joules per square metre (J/n?). NOTE : It is recognized that not all the above parameters can be met on all apparatuses at the present moment but these requirements apply to al/ apparatuses from I January 2000. 4.2 Grey sc

36、ale For the assessment of changes in colour in accordance with EN 201 05-A03. NOTE : This grey scale can be obtained from: British Standards institution AA TCC 389 Chiswick High Road London W4 4AL I Davis Drive PO Box 72215 Research Triangle Park North Carolina 27709 USA Beuth - Verlag GmbH Burggraf

37、enstr. 6 D - 10787 Berlin 4.3 Colour change measurement apparatus In accordance with IS0 7724 : Parts 1 and 2 with the following features : I) employing CIE Publication 15.2 illuminant D65; 2) measuring condition 81d or d/8 including specular reflectance (without gloss trap for both). 4.4 Charpy imp

38、act apparatus Generally in accordance with EN IS0 179 but with the distance between supports equal to 40 mm. The pendulum energy shall be 1 J or 2 J. O BSI 12-1999 STDmBSI BS EN 513-ENGL 1997 U Lb2qbb7 Od178bL 120 m Page 6 EN 51 3: 1999 5 5.1 5.2 5.2.1 5.2.2 5.3 5.3.1 5.3.2 , 6 6.1 6.2 Test pieces N

39、umber of test pieces For the assessment of the change in colour, two test pieces, one of which is a reference, of dimensions specified in 5.2.1 shall be used. For the determination of the change in Charpy impact strength, two series each of six pieces, one of which is a reference series, of dimensio

40、ns as specified in 5.2.2 shall be used. NOTE : Due to the possibility of discarding defective test pieces (see 5.321, it may be advisable to increase the initial number of test pieces in the light of particular experience. Dimensions of the test pieces. Test pieces for the assessment of the change i

41、n colour shall be of minimum dimensions 50 mm x 40 mm. Test pieces for the determination of the change in Charpy impact strength. The test pieces are prepared in two stages : Stage 1 - two series each of six test pieces with a length of (50 I 1) mm, a width of (6 f 0,2) mm and a thickness equal to t

42、he wall thickness of the profile are prepared for weathering or storage. EN IS0 179 designation EN IS0 179/lfA but with a residual width between the notches of (3 i 0,l) mm. Stage 2 - afier storage or weathering, all test pieces are notched generally in accordance with Preparation of the test pieces

43、 The test pieces shall be taken from the sight surface of a profile such that the longitudinal direction of the test pieces and the profile are the same. The test pieces shall be of the dimensions specified in 5.2.1 and 5.2.2. All test pieces for the determination of the change of Charpy impact stre

44、ngth shall be inspected for imperfections such as crazes in the machined surface. When imperfections are found, those test pieces are discarded. Conditioning Conditioning is not required before exposure in the artificial weathering apparatus. Before impact testing the test pieces shall be conditione

45、d at (23 f 2)OC and (50 f 5) % R.H. for at least 16 h. O BSI 12-1999 STD-BSI BS EN 513-ENGL 1999 D Lb2LibbS 08178b2 Ob7 Page 7 EN 513:1999 7 Weathering test conditions 7.1 General For the simulation of the different climates in Europe there are two different methods of exposure defined : Method 1 fo

46、r simulation of moderate climate (M); Method 2 for simulation of severe (hot and dry) climate (S). In annex A reasons for the choice of test conditions are given. 7.2 Test conditions for method 1 7.2.1 The Black Standard Temperature (BST) shall be (60 f 3) OC. The air temperature in the test enclosu

47、re shall be controlled to a constant value such that the BST equals the required value at the end of the dry period. 7.2.2 The White Standard Temperature (WST) shall be (40 to 45) OC. NOTE : The WST is predetermined by the procedure in 7.2.7. It should lie within the specified range, otherwise the m

48、anufacturer of the weathering apparatus should be contacted. 7.2.3 The spray cycle used shall be 18/102 in accordance with IS0 4892 Part 1 NOTE : Sample surfaces have to be continuously sprayed during the spray period otherwise the manufacturer of the weathering apparatus should be contacted. 7.2.4

49、The relative humidity during the dry period shall be (65 f 5) % RH. 7.3 Test conditions for method 2. 7.3.1 The Black Standard Temperature (BST) shall be (65 f 3) OC. The air temperature in the test enclosure shall be controlled to a constant value such that the BST equals the required value at the end of the dry period. 7.3.2 The White Standard Temperature (WST) shall be (45 to 50) “C. NOTE : The WST is predetermined by the procedure in 7.3.1. It shou/d lie within the specified range, otherwise the manufacturer of the weathering apparatus should be contacted. 7.3.3 The spra