ASTM D4570-2002(2012) Standard Test Method for Rubber ChemicalsDetermination of Particle Size of Sulfur by Sieving (Dry) 《橡胶助剂的标准试验方法 筛分法(干法)测定硫的粒度分布》.pdf

《ASTM D4570-2002(2012) Standard Test Method for Rubber ChemicalsDetermination of Particle Size of Sulfur by Sieving (Dry) 《橡胶助剂的标准试验方法 筛分法(干法)测定硫的粒度分布》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4570-2002(2012) Standard Test Method for Rubber ChemicalsDetermination of Particle Size of Sulfur by Sieving (Dry) 《橡胶助剂的标准试验方法 筛分法(干法)测定硫的粒度分布》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4570 02 (Reapproved 2012)Standard Test Method forRubber ChemicalsDetermination of Particle Size of Sulfurby Sieving (Dry)1This standard is issued under the fixed designation D4570; the number immediately following the designation indicates the year oforiginal adoption or, in the case o

2、f revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers the particle size measurement ofthe coarse fraction of ground sulfurs.

3、 It is limited to measure-ment of particles greater than 45 m (No. 325 sieve). If thesulfur is very fine and the screens become plugged by thecaking of the sulfur, it may be necessary to use a wet sieveprocedure instead.1.2 The values stated in SI units are to be regarded as thestandard.1.3 This sta

4、ndard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1

5、ASTM Standards:2E11 Specification for Woven Wire Test Sieve Cloth and TestSievesE145 Specification for Gravity-Convection and Forced-Ventilation Ovens3. Significance and Use3.1 This test method is used to evaluate sulfur for suitabilityas a rubber vulcanizing agent. Sulfur particles must be smalleno

6、ugh to dissolve in rubber during cure to produce a uniformnetwork of cross-links. This test method is used as a qualitycontrol method to ensure that large particles are not present(and to determine if the sulfur follows a typical pattern for sizedistribution).4. Apparatus4.1 Standard Sieves, stainle

7、ss steel, 203 mm in diameterconforming to Specification E11. The stainless steel cloth shallrange in mesh size from 45 to 250 m. The sieve set shouldinclude a lid and a bottom pan.4.2 Mechanical Sieve Shakers, such as a Tyler Ro-Tap3orequivalent unit.4.3 Balance, with a minimum capacity of 500 g sen

8、sitive to0.1 g.4.4 Balance, with a minimum capacity of 150 g sensitive to0.001 g.4.5 Oven, circulating air type, controlled to 70 6 2C.5. Reagent5.1 Tri-calcium Phosphate, screened to a fineness of lessthan 45 m.6. Procedure6.1 Weigh each sieve to the nearest 0.1 g and assemble inorder of increasing

9、 mesh size from bottom to top.Add a bottompan. Choice of sieves depends on the information desired.6.2 Into a beaker or suitable container, weigh precisely100.0 g of sulfur to the nearest 0.1 g. When the sulfur is veryfine, add 2.0 g of tri-calcium phosphate (see 5.1) and blendthoroughly using a spa

10、tula.6.3 Transfer all the sulfur to the top sieve and add the lid.Fix the sieve vest firmly in the mechanical sieve shaker. Runthe unit for 10 min, stop, remove the sieves, and weigh eachsieve to the nearest 0.1 g. Return the sieves to the unit and runan additional 3 min. Reweigh each sieve again to

11、 the nearest0.1 g. Repeat until the sieves reach constant mass.7. Calculation7.1 Determine the residue remaining on each sieve by massdifference. For higher precision, transfer the small residue fromthe coarser screen to a weighing dish and weigh to the nearest0.01 g.7.2 The percent residue on each

12、screen is equal to theamount in grams on each screen.7.3 The percent residue passing through each screen isdetermined by accumulating the total percent material col-lected on that screen and the coarser screens used andsubtracting the total from 100.1This test method is under the jurisdiction of AST

13、M Committee D11 on Rubberand is the direct responsibility of Subcommittee D11.20 on Compounding Materialsand Procedures.Current edition approved May 1, 2012. Published June 2012. Originallyapproved in 1986. Last previous edition approved in 2007 as D4570 02 (2007).DOI: 10.1520/D4570-02R12.2For refer

14、enced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3This unit may be purchased from the Fisher Scientific Co., 585 Alpha D

15、r.,Pittsburgh, PA 15238.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.% residue through (for any screen) =100 sumation of % sulfur collected on thatscreen and on any coarser screens8. Report8.1 The report should include the followi

16、ng information:8.1.1 Proper identification of samples,8.1.2 Identification of each screen used,8.1.3 The percent residue on each screen, and8.1.4 The percent residue through for each screen.9. Precision and Bias9.1 Round robin testing will be conducted, and precisionand bias statements will be ballo

17、ted for inclusion upon thecompletion of this work.10. Keywords10.1 dry sieving; particle size; sulfurASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that det

18、ermination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved o

19、r withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel th

20、at your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints

21、 (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).D4570 02 (2012)2