ASTM C1330-2018 Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants.pdf

《ASTM C1330-2018 Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants.pdf》由会员分享，可在线阅读，更多相关《ASTM C1330-2018 Standard Specification for Cylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1330 02 (Reapproved 2013)C1330 18Standard Specification forCylindrical Sealant Backing for Use with Cold Liquid-Applied Sealants1This standard is issued under the fixed designation C1330; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers the basic requirements for cylindrical sealant backing to be

3、used with cold liquid applied sealantsfor use in building seals.1.2 Cylindrical sealant backing serves one or more of the following functions:1.2.1 Limits the amount and depth of sealant applied into a joint,1.2.2 Acts as a bond breaker to allow joint movement without undue stress to the sealant,1.2

4、.3 Provides a form to assist the sealant in developing the proper shape factor, and1.2.4 Acts as a barrier to the flow of sealant through the joint.1.3 The committee with jurisdiction over this standard is not aware of any comparable standards published by other ASTMcommittees or other organizations

5、.1.4 This specification may involve hazardous materials, operations, and equipment. This standard does not purport to addressall of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriatesafety safety, health, and healthenv

6、ironmental practices and determine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the Decision on Principles for the Development of International Standard

7、s, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2C717 Terminology of Building Seals and SealantsC1016 Test Method for Determination of Water Absorption of Sealant Backing (Joint Filler) Material

8、C1087 Test Method for Determining Compatibility of Liquid-Applied Sealants with Accessories Used in Structural GlazingSystemsC1253 Test Method for Determining the Outgassing Potential of Sealant BackingD1622 Test Method for Apparent Density of Rigid Cellular PlasticsD1623 Test Method for Tensile and

9、 Tensile Adhesion Properties of Rigid Cellular PlasticsD5249 Specification for Backer Material for Use with Cold- and Hot-Applied Joint Sealants in Portland-Cement Concrete andAsphalt Joints3. Terminology3.1 DefinitionsThe definitions for the following terms used in this standard are found in Termin

10、ology C717:3.1.1 bi-cellular sealant backing, bond breaker, closed cell, joint, open cell, outgassing, seal, sealant, sealant backing, skin.4. Classification4.1 Cylindrical sealant backings are divided into three types.1 This specification is under the jurisdiction of ASTM Committee C24 on Building

11、Seals and Sealants and is the direct responsibility of Subcommittee C24.10 onSpecifications, Guides and Practices.Current edition approved May 1, 2013Sept. 15, 2018. Published May 2013October 2018. Originally approved in 1996. Last previous edition approved in 20072013 asC133002(2007).C133002(2013).

12、 DOI: 10.1520/C1330-02R13.10.1520/C1330-18.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is n

13、ot an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropria

14、te. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14.1.1 Type Ccylindrical flexible sealant backings composed predomi

15、nately of closed cell material as defined in TerminologyC717.4.1.2 Type Ocylindrical flexible sealant backings composed of predominantly open cell material as defined in TerminologyC717.4.1.3 Type Bcylindrical flexible sealant backings composed of bi-cellular material as defined in Terminology C717.

16、5. Significance and Use5.1 This specification is designed to give some indication as to the differences in performance for various cylindrical sealantbackings.5.2 Although this specification qualifies a cylindrical sealant backing for use, it does not address the compatibility of the backingwith the

17、 sealants with which it will make contact. Sealant compatibility should be confirmed by the sealant manufacturer.Compatibility characteristics of sealants in contact with cylindrical sealant backings can be determined by Test Method C1087.6. Test Methods6.1 Water AbsorptionTesting for water absorpti

18、on shall be made in accordance with Test Method C1016, Procedure B.6.2 DensityTesting for density shall be made in accordance with Test Method D1622.6.3 OutgassingTesting for outgassing shall be made in accordance with Test Method C1253.6.4 Compression Deflection and RecoveryTesting to be made in ac

19、cordance with Specification D5249.6.5 Tensile StrengthTesting for tensile strength to be made in accordance with Test Method D1623. In all cases use a samplelength sufficient to fit the tensile testing equipment.6.6 Use of a 58 in. diameter sample shall be standard.7. Sampling7.1 Samples used for te

20、sting shall be taken directly from the package as commercially supplied by the manufacturer.8. Physical Properties8.1 Physical properties of the cylindrical sealant backing material shall conform to the requirements of Table 1.9. Workmanship, Finish, and Appearance9.1 The product shall be clean, fre

21、e of scale, foreign matter, oil, or water which could wipe off on a joint sidewall and interferewith the proper cure or adhesion of the sealant.10. Packaging and Package Marking10.1 Packaging shall be marked with the following information:10.1.1 Name, brand, or trademark of the manufacturer,10.1.2 Q

22、uantity and size,10.1.3 ASTM designation (Type C, O, or B), and10.1.4 Any other information that the manufacturer requires.TABLE 1 Sealant Backer PropertiesNOTE 1This table applies to cylindrical sealant backing for use withcold liquid applied sealants.Property Test Method Type C Type B Type OWater

23、absorption (g/cc) C1016Procedure B0.10Density (kg/m3) D1622 2448 2448 2448Outgassing (No. of bubbles) C1253 1 90 90 90Compression deflection (kPa) D5249 20.5 20.5 20.5 200 200 100C1330 18211. Keywords11.1 backer rod; cylindrical sealant backing; joint backing; sealant backingASTM International takes

24、 no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own resp

25、onsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Your comments are invited either for revision of this standard or for additional standardsand should be addressed

26、 to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the a

27、ddress shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 183