1、Designation: A837/A837M 06 (Reapproved 2016)Standard Specification forSteel Forgings, Alloy, for Carburizing Applications1This standard is issued under the fixed designation A837/A837M; the number immediately following the designation indicates the yearof original adoption or, in the case of revisio

2、n, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers alloy steel forgings for carbur-izing applications.1.2 Forgings are consider

3、ed weldable under proper condi-tions. Welding technique is of fundamental importance and it ispresupposed that welding procedure and inspection shall be inaccordance with approved methods for the class of materialused.1.3 This specification is expressed in both inch-pound unitsand in SI units. Howev

4、er, unless the order specifies theapplicable M specification designation (SI units), the materialshall be furnished to inch-pound units.1.4 The values stated in either SI units or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents;

5、 therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.2. Referenced Documents2.1 ASTM Standards:2A275/A275M Practice for Magnetic Particle Examination ofSteel ForgingsA388/A388M Practice for Ultrasonic Exa

6、mination of SteelForgingsA788/A788M Specification for Steel Forgings, General Re-quirementsE527 Practice for Numbering Metals and Alloys in theUnified Numbering System (UNS)3. Ordering Information3.1 Instructions for purchasing forgings to this specificationare to be in accordance with Specification

7、 A788/A788M.3.2 In addition to the basic requirements of thisspecification, certain supplementary requirements are listed atthe end of this specification. These supplementary require-ments may be applicable when additional control, testing, orexamination is required to meet end use requirements.4. H

8、eat Treatment4.1 The forgings shall be given a normalize or normalizeand temper heat treatment.5. Machining5.1 Rough machining before heat treatment may be per-formed at the option of the manufacturer.6. Chemical Composition6.1 The steel shall conform to the requirements for chemicalcomposition pres

9、cribed in Table 1 unless otherwise modified inaccordance with Supplementary Requirement S4.7. Mechanical Properties7.1 Hardness:7.1.1 Maximum hardness of the forgings shall be 229 BHN.7.1.2 Hardness tests shall be taken on prepared surfaces ofthe forging after machining to the purchasers ordering re

10、quire-ments.7.1.3 Number and Location of Tests:7.1.3.1 For forgings not intended for gear applications, thenumber and location of hardness tests shall be by agreementbetween the purchaser and forger.7.1.3.2 For gear applications on each forging 8 in. 200 mmand over in diameter, four Brinell hardness

11、 tests shall be madeon the outside surface of that portion of the forging on whichteeth will be cut two tests being made on each helix 180 apart,and the tests on the two helices shall be 90 apart. On eachforging under 8 in. 200 mm in diameter two Brinell hardnesstests shall be made, one on each heli

12、x 180 apart. On hollow,cylindrical forgings, one hardness test on each end shall betaken 180 apart. Hardness tests shall be performed at thequarter-face width of the tooth-portion diameter.8. Other Requirements8.1 Forgings supplied to this material specification shallconform to the latest issue of S

13、pecification A788/A788M.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.06 on Steel Forgings and Billets.Current edition approved March 1, 2016. Published April 2016. Originallyapprove

14、d in 1985. Last previous edition approved in 2011 as A837/A837M 06(2011). DOI: 10.1520/A0837_A0837M-06R16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standa

15、rds Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States18.2 Specification A788/A788M covers forging terminology,melting processes, c

16、hemical analysis test methods, productanalysis tolerances, mechanical testing methods, repair weld-ing restrictions, marking, and certification requirements.9. Keywords9.1 alloy steel forgings; carburizingSUPPLEMENTARY REQUIREMENTSThe following supplementary requirements shall apply only when specif

17、ied by the purchaser on theorder and agreed to by the manufacturer.S1. Rough Turning and BoringS1.1 The position of rough turning and boring in thesequence of manufacturing operations is specified.S2. Magnetic Particle ExaminationS2.1 Magnetic particle examination shall be specified inaccordance wit

18、h Test Method A275/A275M. Reporting andacceptance standards shall be a matter of agreement.S3. Ultrasonic ExaminationS3.1 Ultrasonic examination shall be specified in accor-dance with Practice A388/A388M. Reporting and acceptancestandards shall be a matter of agreement.S4. Phosphorous and Sulfur Res

19、trictionS4.1 Phosphorus shall not exceed 0.015 %, and the sulfurshall not exceed 0.018 % for all classes when determined inaccordance with the heat analysis requirements of SpecificationA788/A788M.S5. Vacuum DegassingS5.1 Vacuum treatment of the molten steel prior to or duringthe pouring of the ingo

20、t is required.SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue,A837/A837M 03, that may impact the use of this standard. (Approved May 1, 2006.)(1) In Table 1, corrected UNS number for Grade 9310.TABLE 1 Grade Designations and Chemi

21、cal CompositionsUNSDesignationAGradeDesignationBChemical Composition, Ranges and Limits, %CarbonMan-ganesePhos-phorus,maxSulfur,max SiliconCNickelChro-miumMolyb-denumCopper,maxG33106 E3310 0.080.13 0.450.60 0.025 0.025 0.150.35 3.253.75 1.401.75 0.10 max 0.35G43200 4320 0.170.22 0.450.65 0.035 0.040

22、 0.150.35 1.652.00 0.400.60 0.200.30 0.35G46200 4620 0.170.22 0.450.65 0.035 0.040 0.150.35 1.652.00 0.25 max 0.200.30 0.35G48150 4815 0.130.18 0.400.60 0.035 0.040 0.150.35 3.253.75 0.25 max 0.200.30 0.35G86200 8620 0.180.23 0.700.90 0.035 0.040 0.150.35 0.400.70 0.400.60 0.150.25 0.35G93106 9310 0

23、.070.13 0.400.70 0.035 0.040 0.150.35 2.953.55 1.001.45 0.080.15 0.35S41000 410 0.15 max 1.00 max 0.040 0.030 1.00 max 0.50 max 11.5013.50 0.10 max 0.35ANew designation established in accordance with Practice E527.BGrade designations correspond to the respective Practice E527.CWhen vacuum carbon deo

24、xidation is used, silicon maximum shall be 0.10 %.A837/A837M 06 (2016)2ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of

25、any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are

26、 invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not rece

27、ived a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) o

28、f this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 06 (2016)3