ASTM A530 A530M-2004a(2010) Standard Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe《专用碳素钢和合金钢管一般要求的标准规范》.pdf

《ASTM A530 A530M-2004a(2010) Standard Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe《专用碳素钢和合金钢管一般要求的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A530 A530M-2004a(2010) Standard Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe《专用碳素钢和合金钢管一般要求的标准规范》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A530/A530M 04a (Reapproved 2010)Standard Specification forGeneral Requirements for Specialized Carbon and AlloySteel Pipe1This standard is issued under the fixed designation A530/A530M; the number immediately following the designation indicates the yearof original adoption or, in the ca

2、se of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This spec

3、ification2covers a group of requirementswhich, with the exceptions of Section 5.3, Section 13, Section20, and Section 21, are mandatory requirements to the ASTMpipe product specifications noted below unless the productspecification specifies different requirements, in which case therequirement of th

4、e product specification shall prevail.1.2 Sections 5.3 or 20 are mandatory if the product speci-fication has a requirement for product analysis or flatteningtests.1.3 Section 21 is mandatory if the product specification hasa hydrostatic test requirement without defining the test param-eters.1.4 Sect

5、ion 13 is for information only.1.5 In case of conflict between a requirement of the productspecification and a requirement of this general requirementspecification, only the requirement of the product specificationneed be satisfied.Title of Specification ASTM DesignationASeamless Carbon Steel Pipe f

6、or High-TemperatureServiceA106Metal-Arc-Welded Steel Pipe for Use With High-Pressure Transmission SystemsA381Centrifugally Cast Ferritic Alloy Steel Pipe for High-Temperature ServiceA426Centrifugally Cast Austenitic Steel Pipe for High-Temperature ServiceA451Seamless Carbon Steel Pipe for Atmospheri

7、c andLower TemperaturesA524Centrifugally Cast Iron-Chromium-Nickel High-AlloyTubing for Pressure Application at HighTemperaturesA608Centrifugally Cast Carbon Steel Pipe for High-Temperature ServiceA660Electric-Fusion-Welded Steel Pipe for Atmosphericand Lower TemperaturesA671Electric-Fusion-Welded S

8、teel Pipe for High-PressureService at Moderate TemperaturesA672Carbon and Alloy Steel Pipe, Electric-Fusion-Weldedfor High-Pressure Service at High TemperaturesA691Centrifugally Cast Ferritic/Austenitic Stainless SteelPipe for Corrosive EnvironmentsA872AThese designations refer to the latest issue o

9、f the respective specifications.1.6 The values stated in either inch-pound units or SI unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem are not exact equivalents; therefore, each system mustbe used independently of th

10、e other. Combining values from thetwo systems may result in nonconformance with the specifi-cation. The inch-pound units shall apply unless the “M”designation (SI) of the product specification is specified in theorder.NOTE 1The dimensionless designator NPS (nominal pipe size) hasbeen substituted in

11、this standard for such traditional terms as “nominaldiameter,” “size,” and “nominal size.”1.7 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practic

12、es and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:3A370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA450/A450M Specification for General Requirements forCarbon and Low Alloy Steel TubesA700 Practices for Packa

13、ging, Marking, and Loading Meth-ods for Steel Products for ShipmentA751 Test Methods, Practices, and Terminology for Chemi-cal Analysis of Steel ProductsA941 Terminology Relating to Steel, Stainless Steel, Re-lated Alloys, and Ferroalloys1This specification is under the jurisdiction of ASTM Committe

14、e A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.09 on Carbon Steel Tubular Products.Current edition approved April 1, 2010. Published August 2010. Originallyapproved in 1965. Last previous edition approved in 2004 as A530/A530M04a.DOI: 10.1520/A0

15、530_A0530M-04AR10.2For ASME Boiler and Pressure Vessel Code applications see related Specifi-cation SA-530 in Section II of that Code.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume info

16、rmation, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.D3951 Practice for Commercial PackagingE29 Practice for Using Significant Digits in Test Data toDetermine Confor

17、mance with Specifications2.2 ANSI Standards:B 36.10 Welded and Seamless Wrought Steel Pipe4B 36.194Stainless Steel Pipe2.3 Military Standards:MIL-STD-163 Steel Mill Products Preparation for Ship-ment and Storage5MIL-STD-271 Nondestructive Testing Requirements forMetals5MIL-STD-792 Identification Mar

18、king Requirements forSpecial Purpose Components52.4 Federal Standards:Fed. Std. No. 183 Continuous Identification Marking of Ironand Steel Products52.5 Steel Structures Painting Council:SSPC-SP 6 Surface Preparation Specification No. 6 Com-mercial Blast Cleaning63. Terminology3.1 Definitions of Term

19、s Specific to This Standard:3.1.1 remelted heat, nin secondary melting, all of theingots remelted from a single primary heat.3.1.2 jointer, na length of pipe created by welding two ormore shorter lengths of pipe, end-to-end.3.1.3 thin-wall pipe, na pipe having a wall thickness of3 % or less of the o

20、utside diameter.3.2 Other defined termsThe definitions in Test Methodsand Definitions A370, Test Methods, Practices, and Terminol-ogy A751, and Terminology A941 are applicable to thisspecification and to those listed in 1.5.4. Process4.1 The steel shall be made from any process.4.2 If a specific typ

21、e of melting is required by the purchaser,it shall be stated on the purchase order.4.3 The primary melting may incorporate separate degas-sing or refining and may be followed by secondary melting,using electroslag remelting or vacuum remelting.4.4 Steel may be cast in ingots or may be strand cast. W

22、hensteel of different grades is sequentially strand cast, identifica-tion of the resultant transition material is required. Theproducer shall remove the transition material by an establishedprocedure that positively separates the grades.5. Chemical Composition5.1 Chemical AnalysisSamples for chemica

23、l analysis andmethod of analysis shall be in accordance with Test Methods,Practices, and Terminology A751.5.2 Heat AnalysisIf the heat analysis reported by the steelproducer is not sufficiently complete for conformance with theheat analysis requirements of the applicable product specifica-tion to be

24、 fully assessed, the manufacturer may complete theassessment of conformance with such heat analysis require-ments by using a product analysis for the specified elementsthat were not reported by the steel producer, provided thatproduct analysis tolerances are not applied and the heatanalysis is not a

25、ltered.5.2.1 For stainless steels ordered under product specifica-tions referencing this specification of general requirements, thesteel shall not contain an unspecified element, other thannitrogen, for the ordered grade to the extent that the steelconforms to the requirements of another grade for w

26、hich thatelement is a specified element having a required minimumcontent. For this requirement, a grade is defined as an alloydescribed individually and identified by its own UNS designa-tion in a table of chemical requirements within any specifica-tion listed within the scope as being covered by th

27、is specifi-cation.5.3 Product AnalysisProduct analysis requirements andoptions, if any, are contained in the product specification.6. Mechanical Requirements Mechanical Requirements6.1 Method of Mechanical TestsThe specimens and themechanical tests required shall be in accordance with TestMethods an

28、d Definitions A370, especially Annex A2 thereof.6.2 Specimens shall be tested at room temperature.6.3 Small or subsize specimens as described in Test Meth-ods and Definitions A370 may be used only when there isinsufficient material to prepare one of the standard specimens.When using small or subsize

29、 specimens, the largest onepossible shall be used.7. Tensile Requirements7.1 The material shall conform to the requirements as totensile properties prescribed in the individual specifications.7.2 The yield strength corresponding to a permanent offsetof 0.2 % of the gage length or to a total extensio

30、n of 0.5 % ofthe gage length under load shall be determined.7.3 If the percentage of elongation of any test specimen isless than that specified and any part of the fracture is more than34 in. 19.0 mm from the center of the gage length, asindicated by scribe marks on the specimen before testing, aret

31、est shall be allowed.8. Permissible Variation in Weight8.1 The weight of any length of pipe NPS 12 and under shallnot vary more than 10 % over or 3.5 % under that specified.For sizes over NPS 12, the weight of any length of pipe shallnot vary more than 10 % over or 5 % under that specified.Unless ot

32、herwise specified, pipe of NPS 4 and smaller may beweighed in convenient lots; pipe in sizes larger than NPS 4shall be weighed separately.9. Permissible Variations in Wall Thickness9.1 Seamless and Welded (no filler metal added)Theminimum wall thickness at any point shall be within thetolerances spe

33、cified in Table 1 , except that for welded pipe the4Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036, http:/www.ansi.org.5Available from Standardization Documents Order Desk, DODSSP, Bldg. 4,Section D, 700 Robbins Ave., Philadelphia, PA 19111-

34、5098, http:/dodssp.daps.dla.mil.6Available from Society for Protective Coatings (SSPC), 40 24th St., 6th Floor,Pittsburgh, PA 15222-4656, http:/www.sspc.org.A530/A530M 04a (2010)2weld area shall not be limited by the over tolerance. Theminimum wall thickness on inspection for 12.5 % is shownin Table

35、 X1.1.9.2 Forged and BoredThe wall thickness shall not varyover that specified by more than18 in. 3.2 mm. There shallbe no variation under the specified wall thickness.9.3 CastThe wall thickness shall not vary over thatspecified by more than116 in. 1.6 mm. There shall be novariation under the specif

36、ied wall thickness.10. Permissible Variations in Inside Diameter10.1 Forged and Bored, and CastThe inside diametershall not vary under that specified by more than116 in. 1.6mm. There shall be no variation over the specified insidediameter.11. Permissible Variations in Outside Diameter11.1 Variations

37、 in outside diameter, unless otherwise speci-fied, shall not exceed the limits prescribed in Table 2. Thetolerances on outside diameter include ovality except asprovided for in 11.211.2 Thin-wall pipe usually develops significant ovality(out-of-roundness) during final annealing, straightening, orbot

38、h. The diameter tolerances of Table 2 are not sufficient toprovide for additional ovality expected in thin-wall pipe andare applicable only to the mean of the extreme (maximum andminimum) outside diameter readings in any one cross-section.However, for thin-wall pipe the difference in extreme outside

39、diameter readings (ovality) in any one cross-section shall notexceed 1.5 % of the specified outside diameter.12. Permissible Variations in Length12.1 Seamless and Welded (no filler metal added)If defi-nite cut lengths are ordered, no length of pipe shall be under thelength specified and not more tha

40、n14 in. 6 mm over thatspecified.12.2 Forged and Bored, Cast, and Cast Cold-WroughtIfdefinite cut lengths are ordered, no length of pipe shall beunder the length specified and not more than18 in. 3 mm overthat specified.12.3 For pipe ordered to random lengths, the lengths andvariations shall be agree

41、d upon between the manufacturer andpurchaser.12.4 No jointers are permitted unless otherwise agreedupon.13. Standard Weight13.1 A system of standard pipe sizes has been approved bythe American National Standards Institute as ANSI B 36.10and B 36.19. These standard sizes do not prohibit the produc-ti

42、on and use of other sizes of pipe produced to the variousspecifications referenced to this Specification.13.2 For nonstandard sizes of pipe, the calculated weightper foot, shall be determined from the following equation:W 5 CD 2 t!t (1)where:C = 10.69 0.0246615,W = weight, lb/ft kg/m,D = specified o

43、r calculated (from specified inside diameterand wall thickness) outside diameter, in. mm, andt = specified wall thickness, in. (to 3 decimal places) mmto 2 decimal places.NOTE 2The weights given in the American National Standards andthe calculated weights given by Eq 1 are based on the weights for c

44、arbonsteel pipe. The weight of pipe made of ferritic stainless steels may beabout 5 % less, and that made of austenitic stainless steel about 2 %greater than the values given.14. Ends14.1 Unless otherwise specified, the pipe shall be furnishedwith plain ends. All burrs at the ends of the pipe shall

45、beremoved.15. Straightness15.1 The finished pipe shall be reasonably straight.15.2 For metal-arc welded pipe, the maximum deviationfrom a 10-ft 3.0-m straightedge placed so that both ends arein contact with the pipe shall be18 in. 3.2 mm. For metal-arcwelded pipe with lengths shorter than 10 ft 3.0

46、m, thismaximum deviation shall be pro-rated with respect to the ratioof the actual length to 10 ft 3.0 m.16. Repair by Welding16.1 Repair by welding of defects in seamless pipe (includ-ing centrifugally cast and forged and bored) and of platedefects in welded pipe and, when specifically stated by th

47、eproduct specification weld seam defects in welded pipe, shallbe permitted subject to the approval of the purchaser and withthe further understanding that the composition of the depositedTABLE 1 Permissible Variations in Wall ThicknessNPS Designator Tolerance, % fromNominalOver Under18 to 212 , incl

48、., all t /DA,Bratios 20.0 12.53to18incl.,t /D up to 5 % incl. 22.5 12.53to18incl.,t /D 5 % 15.0 12.520 and larger, welded, all t /D ratios 17.5 12.520 and larger, seamless, t /D up to5 % incl.22.5 12.520 and larger, seamless, t /D 5 % 15.0 12.5At = Nominal wall thickness.BD = Ordered outside diamete

49、r.TABLE 2 Permissible Variations in Outside DiameterNPS Designator Permissible Variations In Outside DiameterOver Underin. mm in. mm18 to 112 , incl164 (0.015) 0.4132 (0.031) 0.8Over 112 to 4, incl132 (0.031) 0.8132 (0.031) 0.8Over 4 to 8, incl116 (0.062) 1.6132 (0.031) 0.8Over 8 to 18, incl332 (0.093) 2.4132 (0.031) 0.8Over 18 to 26, incl18 (0.125) 3.2132 (0.031) 0.8Over 26 to 34, incl532 (0.156) 4.0132 (0.031) 0.8Over 34316 (0.187) 4.8132 (0.031) 0.8A530/A530M 04a (2010)3filler metal shall be suitable for