AIR FORCE MIL-C-87261-1992 CLOTH LAMINATED POLYBENZIMIDAZOLE ARARMID SUBSTRATE ACTIVATED CARBON SPHERE FIRE RESISTANT AND CHEMICAL PROTECTIVE《抗火和化学防护活性炭聚苯并咪唑 ARARMID衬底夹层布》.pdf

《AIR FORCE MIL-C-87261-1992 CLOTH LAMINATED POLYBENZIMIDAZOLE ARARMID SUBSTRATE ACTIVATED CARBON SPHERE FIRE RESISTANT AND CHEMICAL PROTECTIVE《抗火和化学防护活性炭聚苯并咪唑 ARARMID衬底夹层布》.pdf》由会员分享，可在线阅读，更多相关《AIR FORCE MIL-C-87261-1992 CLOTH LAMINATED POLYBENZIMIDAZOLE ARARMID SUBSTRATE ACTIVATED CARBON SPHERE FIRE RESISTANT AND CHEMICAL PROTECTIVE《抗火和化学防护活性炭聚苯并咪唑 ARARMID衬底夹层布》.pdf（21页珍藏版）》请在麦多课文档分享上搜索。

1、MIL-C-7261 3 99999Ob 0501802 4 = INCH-POUND MIL-C-87261 (USAI?) 11 February 1992 IvIILIARY SPECIFICATION CLOTH, LAMINATED, POLYBENZIMIDAZOLE/ARAMID SUBSTRATE, ACTIVATED CARBON SPHERE, FIRE RESISTANT AND CHEMICAL PROTECTIVE This specification is approved for use by all Departments and Agencies of the

2、 Department of Defense. *, 1. SCOPE. This specification covers the requirements for chemical protective and flame resistant fabric with activated carbon spheres laminated between polybenzimidazole/aramid blendedwoven outer layer cloth and knit inner layer cloth. 2. APPLICABLE DOCUMENTS 2.1 Governmen

3、t documents 2.1.1 Specifications and standards. Unless otherwise specified (see 6.2), the following specifications and standards of the issue listed in that issue of the Department of Defense Index of Specifications and Standards (DoDISS) specified in the solicitation, form a part of this specificat

4、ion to the extent specified herein. 8 Beneficial comments (recommendations, additions, deletions) and any pertinent data which may be of use in improving this document should be addressed to: ASDENES, Wright-PattersonAFB OH 464334603 by using the self-addressed Standardization Document Improvement P

5、roposal (DD Form 1426) appearing at the end of this document or by letter. AMSC N/A FSC 8306 DISTUBU“ION STATEMENT A. Approved for public release; distribution is unlimited, Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-72bL 3 W 9999906 05030

6、3 b MIL-C-87261 SPECIFICATIONS FEDERAL PPP-P-1136 MILITARY MIL-C-87262 MIM-87263 MIL-T-441 O0 STANDARDS FEDERAL FEDSTD-4 FED-STD-191 FED-STD-596 MlLITARY MIGSTD-105 Packaging of Coated (Plastic; Rubber) and Laminated Fabrics Cloth, Plain Weave, PolybenzimidazoldAramid Blend Cloth, Knit, Jersey, Poly

7、benzimidazole/Aramid Blend Thread, Para-Aramid, Spun, Intermediate Modulus Glossary of Fabric Imperfections Textile Test Methods Colors Used in Government Procurement Sampling Procedures and Tables for Inspection by Attributes (Copies of specifications, standards, drawings and publications required

8、by suppliers in connection with specific procurement functions should be obtained form the procuring activity or as directed by the contracting officer.) 2.1.2 Other Government documents, drawings, and publications. The following other Government documents form a part of this specification to the ex

9、tent specified herein. Rules and Regulations Under the Textile Fiber Products Identification Act (Copies may be obtained without charge from the Federal Trade Commission, Washington, D.C. 20580) CRDCSP-84010 - Laboratory Methods for Evaluating Protective Clothing Systems Against Chemical Agents (App

10、lication for copies should be addressed to the Commander, Chemical Research and Development Center, ATTN: DRSMC-CLJ-IR (A), Aberdeen Proving Ground, Maryland 21010.) 2.13 Other publications. The following documents, of the issue in effect on date of invitation for bids or request for proposal, forms

11、 a part of this specification to the extent specified herein. Technical Manual of the American Association of Textile Chemists and Colorists Method Number 135-1987 - Dimensional Changes in Automatic Durable Press Woven or Knit Fabric Home Laundering of 2 I Provided by IHSNot for ResaleNo reproductio

12、n or networking permitted without license from IHS-,-,-I/ - MIL-C-87261 3 9999906 0503804 MILC-87261 (Applications for copies of the AATCC Manual should be addressed to the AATCC National Headquarters, P.O. Box 12215, Research Triangle Park, North Carolina 27709). Annual Book of ASTM Standards: Volu

13、me 15.01 - Refractories: Carbon and Graphite Products: Activated Carbon Designation C 819-77 Designation D 2854-83 - Apparent Density of Activated Carbon Designation D 4607-86 - Special Surface Area of Carbon or Graphite (BET Method) . Designation D 2862-82 - Particle Size Distribution of Granular A

14、ctivated Carbon - Determination of Iodine Number of Activated Carbon (Applications for copies of the ASTM Annual Book of ASTM Standards: Volume 15.01 should be addressed to: ASTM, 1916 Race Street, Philadelphia, PA 19103-1187) 2.2 Order of precedence. In the event of a conflict between the text of t

15、his specification and the references cited herein, the text of this specification shall take precedence. I 3. REQUIREMENTS 3.1 Standard sample. The laminated fabric shall match the standard sample for shade and shall be equal to or better than the standard sample with respect to all characteristics

16、for which the standard sample is referenced (see 6.3). (As referenced in FEDSTD-595.) 3.2 First article. This specification contains provisions for first article inspection and approval (see 0 4.2 and 6.2). 3.3 Material 3.3.1 Outer layer cloth. The flame resistant, woven outer layer cloth of the lam

17、inated fabric shall conform to the requirements of MIL-C-87262. 3.3.2 Inner layer cloth. The flame resistant, circular knit jersey inner layer cloth of the laminated fabric shall conform to the requirements of MILrc-87263. 3.3.3 Activated carbon. The activated carbon spherical sorbent shall be treat

18、ed to render the activated carbon water insensitive. The activated carbon spheres shall meet the physical and chemical requirements as specified in table I when tested as specified in 4.7. 3.3.4 Laminated fabric. The activated carbon spheres shall be applied with continuous, uniform distribution to

19、one side of the outer layer cloth with a suitable adhesive. The inner layer cloth shall then be bonded to the exposed activated carbon spheres with a suitable adhesive. 3 L Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-872bL 3 = 9999906 050L8

20、05 T = MILC-87261 TABLE I. Activated carbon reauirements. Characteristic Requirements Type Spherical Size Diameter range (mm) Average diameter (minimum) Surface area, single point Brunaver-Emmett-Teller (BET) (minimum) before detergent exposure aft er de tergent exposure Active surface, iodine numbe

21、r (minimum) before detergent exposure after detergent exposure Carbon tetrachloride sorption before detergent exposure after detergent exposure 0.1 - 0.46 0.36 mm 900 m2/gm SOO m2/gm 900 mdgm 800 mglgm 160 mglgm 100 mdgm 3.4 Physical requirements. The physical requirements of the finished fabric sha

22、ll be as specified in table II when tested as specified in 4.7. 3.5 Width. Unless otherwise specxed (see 6.2), the width shall be 66 inches inclusive of selvages. i c 3.6 Carbon tetrachloride sorption. The laminated fabric shall absorb 2.6 mg/cm2 (minimum) of carbon tetrachloride both before and aft

23、er ten (10) launderings when tested as specified in 4.7.1.1. 4 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-872bL 83 99999Ob 050LBOb 1 D MIL-C-87261 TABLE II. Physical requirements. Characteristics Requirements Weight (ounces/square yard) (m

24、aximum) 13.5 Thickness (inches) (maximum) 0.050 Flex Stiffness (mg - cm) (maximum) warp 8,000 Filling 2,500 warp 160 Breaking Strength (pounds) (minimum) Filling 1 O0 Seam efficiency (percent) (minimum) warp 70 Filling 70 Tearing strength (pounds) (minimum) warp 6 Filling 4 Adhesion Strength (ounces

25、/inch) (minimum) . Before laundering warp 30 Filling 20 After laundering warp 24 Filling 16 Air permeability (feet3/minute/feet2 at 1A-inch water pressure) Flame resistance (minimum) 42 (FSTM-191-5903) Flaming time (seconds)(maximum) 8 Glow time (seconds)(maximum) 10 Char length (inches)(maximum)(av

26、erage) 2 First burn flaming time (seconds)(maximum) Second burn flaming time (seconds)(maximum) Percent consumed (maximumxaverage) 20 (FSTM-191-5905) 10 10 5 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-72bL 3 m 99999Ob 0501807 3 m MILC-8726

27、1 3.7 Chemical agent protection. The laminated fabric shall provide chemical agent protection against the agent concentration levels and exposure times given in table III after ten (10) launderings when tested as specified in 4.7.2.2, TABLE III. Chemical agent protection requirements. Test Agent Age

28、nt Exposure Breakthrough Concentration Time Criteria (minimum) (minimum) Vapor Agent Contamination/ HD 20 UgA 24 hours 4 ug/cm2 Vapor Penetration Liquid Agent Contamination/ HD 2 g/m2 6 hours 4 ug/cm2 Vapor Permeation 3.8 Dimensional stability. The laminated fabric shall not shrink more than 4.6 per

29、cent in the direction of the warp nor more than 2.6 percent in the direction of the filling, after five launderings when tested as specified in 4.7. 3.9 Laundering durability. The laminated fabric shall not separate nor shall the outer layer fabric pucker after ten (10) launderings when tested as sp

30、ecified in 4.7. 3.10 Length and put-up. Unless otherwise specified (see 6.2), the laminated fabric shall be furnished in continuous lengths each not less than 26 yards. Each length shall be put-up in full width rolls as specified in PPP-P-1136. 3.ll Labeling. An information label shall be securely a

31、ttached to each roll from each lot of finished fabric. The label shall idente day, month and year of manufacture and manufacturers name. 3.12 Workmanship. The finished cloth shall conform to the quality and grade of product established by this specification. The occurrence of defects shall not excee

32、d the point level specified. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for inspection. Unless otherwise Specified in the contract or purchase order, the contractor is responsible for the performance of all inspection requirements (examinations and tests) as specified herein. Except as other

33、wise specified in the contract or purchase order, the contractor may use his own or any other facilities suitable for the performance of the inspection requirements specified herein, unless disapproved by the Government. The Government reserves the right to perform any of the inspections set forth i

34、n the specification where such inspections are deemed necessary to assure supplies and services conform to prescribed requirements. 6 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-872b1 83 99999Ob 0501808 5 MIL-(3-87261 4.1.1 Responsibility f

35、or compliance. All items shall meet all requirements of sections 3 and 6. The inspection set forth in this specification shall become a part of the contractors overall inspection system or quality program. The absence of any inspection requirements in the specification shall not relieve the contract

36、or of the responsibility of insuring that all products or supplies submitted to the Government for acceptance comply with all requirements of the contract. Sampling inspection, as part of manufacturing operations is an acceptable practice to ascertain compliance to requirements, however, this does n

37、ot authorize submission of known defective material, either indicated or actual, nor does it commit the Government to accept defective material. 4.1.2 Certificate of compliance. Where certificates of compliance are submitted, the Government reserves the right to check test such items to determine th

38、e validity of the certification. 4.2 Classification of inspections. The inspection requirements specified herein are classified as b follows: a. First article inspection (see 4.4). b. Quality conformance inspection (see 4.6) 4 4.3 Inspection conditions. Unless otherwise specified, all inspections sh

39、all be performed in accordance with the test conditions specified in sections 4.4,4.6 and 4.6 of this specification. 4.4 First article inspection. The first article inspection shall consist of specified examinations and tests performed on samples of chemical protective laminated cloth and activated

40、carbon spheres to determine that the production item conforms to the requirements of this specification. 4.4.1 First article samples. Unless otherwise specified, as soon as practical after the award of the contract or order, the manufacturer shall submit five linear yards of the chemical protective

41、laminated cloth and 1.0 kilogram of the activated carbon spheres for subjection to the examinations and tests specified in 4.4.2. The samples shall be representative of the construction, workmanship, components and materials to be used during production. 4.4.2 First article tests. The first article

42、samples shall be subjected to tests specified in section 3 in accordance with methods specified in 4.7 of this specification. 4.5 Quality Conformance Inspection. Sampling for inspection shall be performed in accordance with MIGSTD-106, except where otherwise indicated hereinafter. 4.6.1 Component an

43、d material inspection. In accordance with 4.1 above, components and materials shall be tested in accordance with all the requirements or referenced specifications, drawings, and standards, unless otherwise excluded, amended, modified or qualified in this specification or applicable purchase document

44、s. 4.5.2 Examination of the end item. Examination of the end item shall be in accordance with the provisions of 4.6.2.1 through 4.6.2.2.2. . 7 Provided by IHSNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-MIL-C-87261 83 999990b 0501809 7 MIL-C-87261 4.5.2.1 Yard-b

45、y-yard examination. Each roll in the sample shall be examined on the outer layer (woven) and inner layer (knit) sides and visual defects as defined herein shall be classified as listed in table N. All defects found shall be counted regardless of their proximity one to another except where two or mor

46、e defects represent a single local condition of the cloth, in which case only the more serious defect shall be counted, Acontinuous defect shall be counted as one sample unit for each lengthwise yard or fraction thereof in which it occurs. The sample unit for this examination shall be one linear yar

47、d. The sample size shall be in accordance with Inspection Level II of MIGSTD-106. The Acceptable Quality Level (AQL) shall be 4.0 major defects and 10.0 minor defects per100 units (yards). The total size shall be expressed in units of one linear yard. An approximate equal number of yards shall be ex

48、amined from each roll selected for yard by yard examination. TABLE Il? End item inspection. - 1/ Classification Defect Major Minor Part A - Outer layer (woven cloth) side 1. Any cut, tear, hole, mend or burn through laminated cloth over 1/4 inch long . X 2. Any misweave, slub, smash, float, broken o

49、r missing yarn or thin place 3. Color not as specified, shade bar or dye streak 4. Area of delamination over 1-inch in diameter . X 6. Spot or stain (grease, oil or ink) . X X X Part B - Inner layer (knit cloth) side 1. Any cut, tear, or hole through liner - overl-inchlong . X - less than 1-inch long X 2, Mends in liner over 2-inches long X 3. Folds or creases in liner X 4. Color not as specified. X 6. Foreign matter under liner