GMKOREA EDS-T-7134-2008 DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMANENT SET OF ELASTOMERIC COMPONENTS.pdf

《GMKOREA EDS-T-7134-2008 DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMANENT SET OF ELASTOMERIC COMPONENTS.pdf》由会员分享，可在线阅读，更多相关《GMKOREA EDS-T-7134-2008 DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMANENT SET OF ELASTOMERIC COMPONENTS.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、GM DAEWOO Auto # Total accuracy ; Force measuring equipment : 1.5% of the measured value. Displacement measuring equipment : 0.05 mm 4.2. Environmental chamber for use on the testing machine. The environmental chamber shall be of the air-circulating type, and comply with the following requirements ;

2、 Temperature range : -40 +250 Temperature variation : 2K Temperature change rate : 1.5 K/minute for empty cabinet 4.3. Suitable fixtures for locating and attaching the elastomeric components to the test machine. EDS-T-7134DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMANENT SET OF ELA

3、STOMERIC COMPONENTS PAGE: 3/5 ISSUED DATE: 1988. 07. 15 REVISED DATE: 2008. 10. 15 VERSION: 5 GM DAEWOO Auto & Technology 4.4. Dimensional measuring equipment 4.4.1. Dimensional measuring equipment, e.g. a linear dial gauge to DIN 878 or BS 907, with a range of 10mm an accuracy of 0.01mm, and extend

4、ing a relatively constant force of less than 2N over its range of travel. 4.4.2. Gauge block to DIN 862 or BS 4311. 4.4.3. Precision height vernier accurate to 0.1mm, height max. 500mm. 5. PRECAUTIONANDTESTMETHOD 5.1. Precaution 5.1.1. Requirement for force-deflection test The test shall be carried

5、out at a room temperature and comply with the force and the test direction specified on the drawing. Care shall be taken that the test piece is not deflected during mounting into the fixture. If the test result is inappropriate, the test piece shall be tested again after at least 24 hours. If the fo

6、rce, on the force indicating device on the test machine is influenced by the weight of the test piece and/or its fixtures, compensation shall be made prior to the commencement of the test. 5.1.2. Precaution for permanent set test The temperature of chamber and the test period shall be observed, taki

7、ng care that the test piece is not deflected during mounting into the fixture. 5.2. Test method 5.2.1. Test method for the force-deflection characteristics. (1) The unstressed height ho shall be measured prior to testing. (2) After attaching the test piece to the fixture, the initial force Fvshall b

8、e applied to the test piece and removed at the same velocity. This procedure shall be repeated until the zero range is within 0.01mm (generally repeated 3 times). Test speed for force-deflection characteristics is referred to test condition of force-deflection mapping (see relevant component DWG) (3

9、) Apply Fvto the test sample, and then adjust as zero point. Fkshall be applied to the test piece after the given period(6 , 60 , 600 , 6000 seconds), the deflection shall be measured. For S6measurement, the deflection shall be measured after 6seconds. For S6000, after 6000 seconds. (4) For the cree

10、p characteristics test, the deflection shall be generally measured after 6000 seconds, but may be calculated from the following formula so as to reduce the test period. S6000= 1.5(S600- S6) Both S6and S600shall be measured, and the difference between two shall be multiplied by 1.5 to obtain the valu

11、e. (5) If specially specified as EDS-T-7134 on drawing, the test shall be carried out as follows. The force of 1.25(Fv+ Fk) shall be applied to and removed from the test sample 5 times prior to testing. After removal, the test EDS-T-7134DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMA

12、NENT SET OF ELASTOMERIC COMPONENTS PAGE: 4/5 ISSUED DATE: 1988. 07. 15 REVISED DATE: 2008. 10. 15 VERSION: 5 GM DAEWOO Auto & Technology sample shall be maintained for 16 to 48 hours. S6 and S6000shall be determined according to steps (1) (4). (6) Calculation Creep S6000= 1.5(S600- S6) Force-deflect

13、ion characteristics S6000= S6+ S6000Installed height H = ho- S60005.2.2. Test method for permanent set (1) S6and S6000shall be calculated through the force-deflection characteristics test to clause 5.2.1. The test sample shall be maintained for 241 hours at room temperature and tested as follows. (2

14、) The test sample shall be inserted to the test fixture, and the distance between the upper fixture and the bottom fixture shall be measured. Thereafter, the distance between fixtures shall be adjusted in compliance with the deflection of S6+ S6000using the bolt attached to the fixture. (3) The test

15、 sample shall be placed into chamber, and maintained for given period at the temperature specified on the relevant component drawing. (4) At the end of specified period, the test sample shall be removed from the chamber and maintained for 61 hours at 235k with still stressed. (5) The stress shall be

16、 removed, and the test sample shall be detached from the test fixture. After 603 minutes, hsshall be measured in the same way as hois measured. (6) The test result shall be calculated as follows, and evaluated according to the specification of the appropriate component drawing. (%) ) - () - (= SET P

17、ERMANENT )III 9JPJTJPJ (7) Code of Test Condition Code of Test Condition shall be specified by Code on the following table indicated on the relevant component drawing. Condition Code Letter 0 Duration (H) -2 Temperature ( K ) A 24 -30 3 B 24 -20 3 C 24 -10 3 D 24 +80 2.5 E 24 +100 2.5 F 24 +125 2.5

18、G 24 +150 2.5 H 24 +175 2.5 I 24 +200 2.5 K 24 +225 2.5 L 72 +23 5 M 72 +80 2.5 EDS-T-7134DETERMINATION OF THE FORCE-DEFLECTION CHARACTERISTICS AND PERMANENT SET OF ELASTOMERIC COMPONENTS PAGE: 5/5 ISSUED DATE: 1988. 07. 15 REVISED DATE: 2008. 10. 15 VERSION: 5 GM DAEWOO Auto & Technology Condition

19、Code Letter 0 Duration (H) -2 Temperature ( K ) N 72 +100 2.5 O 72 +125 2.5 P 72 +150 2.5 Q 72 +175 2.5 R 72 +200 2.5 S 72 +225 2.5 T 168 +80 2.5 U 168 +100 2.5 V 168 +125 2.5 W 168 +150 2.5 X 168 +175 2.5 Y 168 +200 2.5 Z 168 +225 2.5 6. CODING SYSTEM The requirements for the Permanent Set of elast

20、omeric components shall be specified on drawings, test specifications and material specifications etc. as follows. e. g PERMANENT SET to EDS-T-7134 - XB1 - MAX 20% Specification Test condition Test method Designation 7. DEVIATIONS Deviations from the requirements of this test method (e.g. test piece

21、 preparation, test fixture, time and temperature of test) shall have been agreed upon. These shall be specified on engineering drawings, material specifications etc. and shall be indicated on test certificates, report etc. 8. REFERENCE GME 60 231 Determination of the force-deflection characteristics and creep properties of elastomeric components