GMKOREA EDS-M-4307-2008 STYRENE-ACRYLONITRILE COPOLYMER (VERSION 3).pdf

《GMKOREA EDS-M-4307-2008 STYRENE-ACRYLONITRILE COPOLYMER (VERSION 3).pdf》由会员分享，可在线阅读，更多相关《GMKOREA EDS-M-4307-2008 STYRENE-ACRYLONITRILE COPOLYMER (VERSION 3).pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、GM DAEWOO Auto & Technology EDS Engineering, GM DAEWOO Auto & Technology Standards STYRENE-ACRYLONITRILE COPOLYMER EDS-M-4307 ISSUED DATE: 1995. 01. 10 REVISED DATE: 2008. 03. 26 VERSION: 3 EDS-M-4307STYRENE-ACRYLONITRILE COPOLYMER PAGE: 1/3 ISSUED DATE: 1995. 01. 10 REVISED DATE: 2008. 03. 26 VERSI

2、ON: 3 GM DAEWOO Auto & Technology 1. SCOPE This specification defines general requirements for raw materials of styrene-acrylonitrile copolymer applied to interior and exterior parts of a vehicle. 2. MATERIAL INDICATION Material indication: SAN Detailed contents shall conform to the indication metho

3、d of synthetic resin materials for vehicles. (Spec. No: GMW3116) 3. APPLICATION 3.1. Group 1: Raw materials of high melt flow injection mold which have excellent dimensional stability and molding ability. 3.2. Group 2: Heat resistance raw materials having excellent dimensional stability and molding

4、ability 3.3. Group 3: Raw materials of high melt flow injection mold which have excellent dimensional stability, molding ability and especially chemical resistance. Notice to Use Parts which were molded using this specification material can be damaged as contacted by foam, rubber, seal, PVC products

5、 with plasticizer such as DOP, DOA, etc., because contacted parts can be chemically cracked by plasticizers migration. So the use of product must be avoided in case of contact. But, if the contact is necessary, surface treatment methods such as painting with clear coat, coated gold, etc must be used

6、 to prevent chemical crack by plasticizers migration. # Phthalic Acid Ester plasticizer: DOP(Di-Octyl Phathalate), DBP(Di -Butyl Phathalate), etc # Aliphatic Acid Ester plasticizer: DOA(Di 2-ethyl- hexyl Adipate), etc 4. REQUIREMENTS 4.1. Mechanical properties Group 1 Type 1 Group 2 Type 1 Group 3 T

7、ype 1 Rockwell hardness EDS-T-7517 R Scale 122 123 123 Tensile strength (kg/cm2) EDS-T-7511 Test piece (133mm) Test speed(50mm/min) 640 650 660 EDS-M-4307STYRENE-ACRYLONITRILE COPOLYMER PAGE: 2/3 ISSUED DATE: 1995. 01. 10 REVISED DATE: 2008. 03. 26 VERSION: 3 GM DAEWOO Auto & Technology Group 1 Type

8、 1 Group 2 Type 1 Group 3 Type 1 Elongation (%) EDS-T-7511 Test piece (133mm) Test speed(50mm/min) 5 5 5 Flexural strength (kg/cm2) EDS-T-7518 Test piece (12712.76.4mm) Test speed(28mm/min) 1,050 1,150 1,150 Flexural modulus (kg/cm2) EDS-T-7510 Test piece (12712.76.4mm) Test speed(28mm/min) 31,000 3

9、2,000 34,000 Impact strength, IZOD (kg cm/cm) EDS-T-7514 Test piece (63.512.73.2mm) Room temperature -30 2 - 2.5 - 2.5 - 4.2. Thermal properties Heat deflection temperature () EDS-T-7520 Test piece (12712.76.4mm) 18.6 kg/cm285 87 87 4.3. General properties Density (g/cm3) EDS-T-7406 1.07 1.07 1.07 M

10、elt flow index (g/10min) EDS-T-7516 20 15 30 Note) All the mechanical, thermal and general property values above indicate minimum values except having the specified ranges. 5. TEST PIECE AND TEST 5.1. Test piece Test pieces shall be prepared with injection molding. Unless otherwise specified in the

11、requirements of clause 4, they shall be conditioned at 235K and a relative humidity of 50% for 24 hours or more. 5.2. Test Tests shall be performed at 235K and a relative humidity of 50%. EDS-M-4307STYRENE-ACRYLONITRILE COPOLYMER PAGE: 3/3 ISSUED DATE: 1995. 01. 10 REVISED DATE: 2008. 03. 26 VERSION

12、: 3 GM DAEWOO Auto & Technology 6. APPROVAL OF RAW MATERIALS 6.1. Approved raw materials Division Approved suppliers Approved raw materials Remarks Group 1 Type 1 LG 80HF Group 2 Type 1 LG 90HR Group 3 Type 1 LG 95HC 6.2. Approval and quality assurance procedure All raw materials shall be approved a

13、nd regularly inspected for its quality prior to and during mass production delivery according to approval and quality assurance procedure for chemical raw materials (Spec. No. EDS-M-0102). 7. AUTOMOTIVE RESTRICTED HAZARDOUS SUBSTANCES Materials and components of parts must comply with GMW3059. 8. OT

14、HERS 8.1. Coding system Material specification of raw materials shall be indicated in drawings as follows. EDS-M- 4307 - Required property type (clause 4) Material group (clause 3)Material specification number 9. RELATED STANDARDS EDS-M-0102 Procedures for approval of chemical raw material and quali

15、ty control EDS-T-7406 Determination of volume and density of elastomers EDS-T-7510 Testing of plastics determination of the modulus of elasticity by tensile, compression and flexural test EDS-T-7511 Test method for the tensile property of plastics EDS-T-7514 Test method for determining the flexural

16、strength of plastics EDS-T-7516 The test method for the melt flow index of thermoplastics EDS-T-7517 The test method for Rockwell hardness of plastics EDS-T-7518 The method for the flexural strength of plastics EDS-T-7520 Test for deflection temperature of plastics under load GMW 3059 Restricted and reportable substance for parts GMW 3116 Recyclability / recoverability guidelines