FORD WSS-M18P17-A-2007 COATING ALUMINUM WATER SHEDDING HYDROPHILIC TO BE USED WITH FORD WSS-M99P1111-A 《亲水性分水用铝涂料 与标准FORD WSS-M99P1111-A一起使用 》.pdf

《FORD WSS-M18P17-A-2007 COATING ALUMINUM WATER SHEDDING HYDROPHILIC TO BE USED WITH FORD WSS-M99P1111-A 《亲水性分水用铝涂料 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M18P17-A-2007 COATING ALUMINUM WATER SHEDDING HYDROPHILIC TO BE USED WITH FORD WSS-M99P1111-A 《亲水性分水用铝涂料 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions 2007 08 30 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.3, 3.11 & 4 1999 02 12 Activated L. Rumao Printed copies are uncontrolled Copyright 2007, Ford Global Technologies, LLC Page 1 of 2 COATING, ALUMINUM, WATER SHEDDING, WSS-M18P17-A HYDROPHIL

2、IC 1. SCOPE The coating defined by this specification, typically a resin-bonded silicate, imparts a durable, hydrophilic surface on aluminum heat exchangers to facilitate water shedding, with specified level of resistance to bacterial and fungus growth. 2. APPLICATION This specification was original

3、ly released for evaporator core surfaces in automotive air-conditioning systems. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 PREPARATION OF T

4、EST PANELS The coating under test is to be the same composition and concentration as intended to be used in the manufacturing process and be maintained at 28 - 30 C. Use aluminum alloy 3105 test panels available from any commercial test panel supplier. Panel size to be approximately 300 x 100 x 0.6

5、mm. Preclean panels with neutral surfactant type cleaner at room temperature. Clean panels with slightly acidic or alkaline etching cleaner at 50 +/- 2 C. Rinse by dipping in tap water for 5 - 10 seconds. Rinse by dipping in DI water for 5 - 10 seconds. Allow water to drain for 5 - 10 seconds. Coat

6、panels by immersion for 2 - 3 minutes in the coating. Allow panels to drain for 5 - 10 seconds. Dry panels by hanging them vertically, in an air-circulating oven at 380 - 420 C for 4 minutes +/- 15 seconds. ENGINEERING MATERIAL SPECIFICATION WSS-M18P17-A Printed copies are uncontrolled Copyright 200

7、7, Ford Global Technologies, LLC Page 2 of 2 3.5 Contact Angle, max (Goniometer test) 24 h air dry 15 72 h water wash 35 (ASTM D 870 except air dry panel for 2 - 3 h) 3.6 Odor Rating, max 2 (SAE J 1351) 3.7 FOGGING (SAE J1756, 3 h at 100 C heating, 21 C cooling plate, post test conditioning 1 h) Fog

8、 Number, min 70 Formation of clear film, droplets or crystals is cause for rejection. 3.8 BIOCIDE PERFORMANCE Must pass (Latest test method to be provided by the Product Engineering contact) 3.9 CHEMICAL/COMPOSITIONAL DATA Supplier shall furnish chemical/compositional data and process control plan a

9、s mutually agreed and/or as required by para 3.11. 3.10 ADDITIONAL REQUIREMENTS Specific requirements for material and/or manufactured parts shall be specified on the Engineering drawing, Engineering parts specification and/or performance specification. All critical areas with respect to these properties shall be clearly designated on the engineering drawing. Candidate materials shall successfully complete the following testing prior to approval to this specification. 3.10.1 Production Shop Trial 3.10.2 Component/Module Life Cycle Testing (As specified by the responsible design activity)