ASTM F680-1980(2002) Standard Test Methods for Nails《钉子的试验方法》.pdf

《ASTM F680-1980(2002) Standard Test Methods for Nails《钉子的试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM F680-1980(2002) Standard Test Methods for Nails《钉子的试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F 680 80 (Reapproved 2002)Standard Test Methods forNails1This standard is issued under the fixed designation F 680; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parentheses ind

2、icates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 These test methods cover procedures for the testing ofnails. The test or tests selected, and the requirements forcompliance, will be as specified in the applic

3、able productstandard. Performance tests for nail withdrawal and lateral loadcapability are not included as they are covered by Test MethodsD 1761.1.2 The tests described are as follows:SectionDimensional tests 5Tension test 6Conventional bend test 7Impact bend test 8Rockwell hardness test 9Coating w

4、eight test 10Coating adherence test for zinc-coated nails 111.3 This standard does not purport to address all of thesafety problems, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-b

5、ility of regulatory limitations prior to use.1.4 The values stated in inch-pound units are to be regardedas the standard. The values in parentheses are provided forinformation purposes only.2. Referenced Documents2.1 ASTM Standards:A 90/A 90M Test Method for Weight Mass of Coating onIron or Steel Ar

6、ticles with Zinc or Zinc-Alloy Coatings2A 370 Test Methods and Definitions for Mechanical Testingof Steel Products3A 428/A 428M Test Method for Weight Mass of Coatingon Aluminum-Coated Iron or Steel Articles2D 1761 Test Methods for Mechanical Fasteners in Wood4E 18 Test Methods for Rockwell Hardness

7、 and RockwellSuperficial Hardness of Metallic Materials5F 547 Terminology of Nails for Use with Wood and Wood-Base Materials6F 592 Terminology of Collated and Cohered Fasteners andTheir Application Tools63. Terminology3.1 DefinitionsFor definitions of terms used in this testmethod, refer to Terminol

8、ogy F 547 and F 592.4. Significance and Use4.1 When specified, the tests selected for application shallbe performed to assure conformance with requirements stipu-lated in the product specification.5. Dimensional Tests5.1 Dimensions to be evaluated include, but shall not belimited to length, stock di

9、ameter, diameter or major dimensionsof head, straightness, head concentricity to shank, and length ofpoint. For mechanically deformed nails, angle, depth, andconfiguration of deformations shall be measured as specified.Other dimensional characteristics shall be measured whenrequired. Any suitable me

10、asuring means may be applied.6. Tension Test6.1 Nails are not subject to tension testing. However, wireused to make the nails may be tested as required by prioragreement or to affect mill product control. The testing of wireis covered in the general section of Test Methods A 370 andSupplement IV, Ro

11、und Wire Products.7. Conventional Bend Test7.1 This test is used as a means of testing the ductility ofcertain types of nails or of the wires used in the manufacture ofnails. The angle of bend and the mandrel diameter will bespecified in the product specification. The cold bending shallbe performed

12、by any hand or power device that will deform thesample closely about a mandrel of specified diameter throughthe required angle without causing damage to the nail surface.The sample shall be considered to have failed if fracture occursprior to attainment of the required minimum bend angle.Unless othe

13、rwise specified, the conventional bend test shall not1These test methods are under the jurisdiction of ASTM Committee F16 onFasteners and are the direct responsibilities of Subcommittee F16.05 on Driven andOther Fasteners.Current edition approved Sept. 26, 1980. Published December 1980.2Annual Book

14、of ASTM Standards, Vol 01.06.3Annual Book of ASTM Standards, Vol 01.03.4Annual Book of ASTM Standards, Vol 04.10.5Annual Book of ASTM Standards, Vol 03.01.6Annual Book of ASTM Standards, Vol 01.08.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, Un

15、ited States.be applied to annularly threaded nails or to the region of a nailexhibiting gripper marks.8. Impact Bend Test8.1 The impact test is primarily applicable to the testing ofpallet nails to assess their suitability for that application. Thetesting device is shown in Fig. 1 and its operation

16、is describedin Annex A1. For any given diameter, the data from this testcan be correlated with Rockwell hardness used to specify themechanical properties of the nail. The impact bend test isintended as a convenient test that may be used in manufactur-ing and consumer quality monitoring of mechanical

17、 properties.However, in the case of dispute, the Rockwell hardness test,supplemented by the conventional bend test, will be consideredthe governing test.9. Rockwell Hardness Test9.1 This test is used to measure the hardness of heat-treatednails. Prepare flat surfaces by grinding or filing. Take care

18、 notto alter the tempered hardness of the nail during preparation ofthe flats. The width of the prepared flat shall be sufficient toprevent edge bulge adjacent to each hardness impression. Thethickness at the test section shall be sufficient to avoid a bulgeor other visible markings on the surface o

19、pposite to theimpression. Hardness can be determined using a shank havingprepared parallel surfaces. Determine the hardness in accor-dance with Test Methods E 18. Usually three readings aremade on a nail and these readings are averaged for the finalresult.9.2 An alternate method for determining Rock

20、well hardnessis to cut the nail off about12 in. (13 mm) from the head. Grindthe top of the head to remove scale and obtain a flat surface.Grind the transversely cut end flat, using proper precautionsnot to alter the tempered hardness of the nail. Place the samplehead down on the anvil of the hardnes

21、s testing machine anddetermine the hardness on the transverse section.10. Coating Weight Test10.1 This test deals with zinc, aluminum, and copper-cladcoatings only and does not deal with other metallic coatingssuch as cadmium.10.2 Cut the heads and points from samples of zinc-coatedor aluminum-coate

22、d nails selected for testing. Take a sufficientnumber of such specimens to provide a total length over 12 in.NOTEThis device is available from The National Wooden Pallet and Container Assn., 1625 Massachusetts Ave., Washington, DC 20036FIG. 1 A Typical Impact Bend Tester for the Impact Bend Testing

23、of NailsF 680 80 (2002)2(300 mm), preferably about 24 in. (600 mm). Since the densityof the steel is known (0.2836 lb/in.3(0.1276 kg/m3), it is notnecessary to use a specific total length of specimens.10.3 Determine the weight of zinc coating in accordancewith Test Method A 90.10.4 Determine the wei

24、ght of aluminum coating in accor-dance with Test Method A 428.10.5 Determine the thickness of coating of copper-clad nailsby one of the following three methods:10.5.1 Accurately measuring the diameter of the wire beforeand after removing the cladding by any suitable means.10.5.2 Cutting off the wire

25、, grinding one end smooth,etching the exposed cross section to differentiate between coreand cladding, and measuring under suitable magnification.10.5.3 Using electrical indicating instruments.10.6 Calculate the weight of the copper cladding from thethickness as measured above or determine the weigh

26、t of thecladding by chemically stripping the copper and accuratelyweighing the wire sample before and after stripping.11. Coating Adherence Test for Zinc-Coated Nails11.1 Determine the adherence of the zinc coating to thesurface of the base metal by cutting or prying with the point ofa stout knife,

27、applied with considerable pressure in a mannertending to remove a portion of the coating. The adherence shallbe considered inadequate if the coating flakes off in the form ofa layer or skin so as to expose the base metal in advance of theknife point. Testing carried out at edges or corners (points o

28、flowest coating adherence) shall not be used to determineadherence of coating. Likewise, removal of small particles ofthe coating by paring or whittling shall not be used todetermine failure.12. Precision and Bias12.1 The precision and bias of these tests have not beendetermined at this time.ANNEX(M

29、andatory Information)A1. OPERATION OF THE IMPACT BEND TESTER (FIG. NO. 1)A1.1 ScopeThe test is applicable to nails with shankdiameters of 0.106 in. (2.7 mm) to 0.135 in. (3.4 mm) andlengths of 112 in. (38 mm) to 3 in. (76 mm) and with or withoutdeformations.A1.2 Hold the nail to be tested in a chuck

30、 in such a way thatit cantilevers1532 in. (12 mm) at an angle of 80 to the vertical.Hit its head after the free-fall drop of a 3.50-lb (1.58-kg)weight from a 15716 in. (392 mm) height, thereby applying54.0 in.lbf (6.1-J potential or 4.52-J kinetic) energy to the headof the inclined nail. As a result

31、 of this impacting, soft nails arebent readily without breaking and non-ductile nails failabruptly partially or completely while being bent only a fewdegrees. The test includes recording the bend angle of thetested nail as well as the number and type of failure, if any.A1.3 The impact bend test devi

32、ce, shown in Fig. 1, shallconsist of a 0.750-in. (19.0-mm) diameter shaft, along whichthe 3.50-lb (1.58-kg) drop weight slides to hit the head of thenail. A protractor shall be used to measure the angle of thetested nail.A1.4 Measure the dimensions of the nails prior to testing.Replace chuck inserts

33、 with worn edges with new ones. Positionthe specimen properly between the chuck inserts in such a waythat the specimen protrudes1532 in. (12 mm) from the inserts.Tighten the chuck securely, to prevent the displacement of thenail during application of the impact load, and release the dropweight. Reco

34、rd the type of failure, if any, and the bend anglefor each nail and determine the average bend angle for the nailstested.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expres

35、sly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised,

36、 either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may at

37、tend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).F 680 80 (2002)3