ASTM F1514-2003 Standard Test Method for Measuring Heat Stability of Resilient Vinyl Flooring by Color Change《用颜色变化测量弹性乙烯基塑料地板耐热性的标准试验方法》.pdf

《ASTM F1514-2003 Standard Test Method for Measuring Heat Stability of Resilient Vinyl Flooring by Color Change《用颜色变化测量弹性乙烯基塑料地板耐热性的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM F1514-2003 Standard Test Method for Measuring Heat Stability of Resilient Vinyl Flooring by Color Change《用颜色变化测量弹性乙烯基塑料地板耐热性的标准试验方法》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F 1514 03Standard Test Method forMeasuring Heat Stability of Resilient Flooring by ColorChange1This standard is issued under the fixed designation F 1514; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of las

2、t revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This test method covers a procedure for determining theresistance of resilient floor covering to color change fromexposu

3、re to elevated temperature over a specified period oftime.1.2 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bil

4、ity of regulatory limitations prior to use.1.3 The values stated in inch-pound units are to be regardedas the standard. The values given in parentheses are forinformation only.2. Referenced Documents2.1 ASTM Standards:D 794 Practice for Determining Permanent Effect of Heaton Plastics2D 2244 Test Met

5、hod for Calculation of Color Differencesfrom Instrumentally Measured Color Coordinates3E 177 Practice for Use of the Terms Precision and Bias inASTM Test Methods4E 691 Practice for Conducting an Interlaboratory Study toDetermine the Precision of a Test Method43. Significance and Use3.1 Resilient flo

6、or covering is made by fusing polymermaterials under heat or pressure, or both, in various manufac-turing and decorating processes. The polymer material may becompounded with plasticizers, stabilizers, fillers, and otheringredients for processibility and product performance charac-teristics. The for

7、mulation of the compound can be variedconsiderably depending on the desired performance character-istics and methods of processing. See Practice D 794 foradditional significance and use information.3.1.1 Heat stability, which is resistance to discolorationfrom heat, is a basic requirement for proces

8、sing and functionaluse.3.1.2 This test method provides a means of measuring theamount of color change in flooring products when subjected toelevated temperatures over a period of time (functional use ofthe flooring product).3.2 This test method is not intended to be a means ofpredicting the amount o

9、f color change that occurs duringprocessing (manufacture).3.3 This test method specifies that a sample is subjected to158F 6 2F (70C 6 1C) for 7 days, and the color differenceis measured by a spectrophotometer and expressed as DE*units.NOTE 1It is the intent that this test method be used for testing

10、 heatstability performance properties to be referenced in resilient flooringspecifications.4. Apparatus4.1 Circulating Air Oven, which can be maintained at 158F6 2F (70C 6 1C).4.2 Suitable Spectrophotometer or Colorimeter with aminimum14 in. (6.35 mm) diameter opening having both acool white fluores

11、cent (CWF) and daylight light (D-65) sourcesthat measure color in CIE L*, a*, b* using CIE 10 StandardObserver and Specular Included. See Test Method D 2244.When an individual color cannot be totally covered within the14 in. spectrophotometer opening, then the largest spectropho-tometer opening shal

12、l be used.4.3 A suitable holder rack that separates samples a mini-mum12 in. (12.70 mm) in a standing or vertical position.5. Hazards5.1 Cautions:5.1.1 Do not stack specimens while being exposed toelevated temperatures.5.1.2 Be sure each specimen is marked in the corner and onthe back for easy ident

13、ification.5.1.3 Monitor temperature during duration of test in oven toensure maintenance of proper temperature.1This test method is under the jurisdiction of ASTM Committee F06 on ResilientFloor Coverings and is the direct responsibility of Subcommittee F06.30 on TestMethods-Performance.Current edit

14、ion approved March 10, 2003. Published May 2003. Originallyapproved in 1995. Last previous edition approved in 1998 as F 1514 98.2Annual Book of ASTM Standards, Vol 08.01.3Annual Book of ASTM Standards, Vol 06.01.4Annual Book of ASTM Standards, Vol 14.02.1Copyright ASTM International, 100 Barr Harbo

15、r Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.1.4 Be sure color measuring equipment is properlywarmed-up and calibrated prior to use.5.1.5 Be sure specimens are held flat when measuring color.6. Procedure6.1 Cut three specimens from each sample, approximately 2in. by 2 in.

16、(50 mm by 50 mm). All specimens shall be of thesame color, pattern, and texture.NOTE 2White, monochromatic, flat material is preferred for testing.6.2 Obtain and record initial L*, a*, and b* readings on eachof the three specimens with the color measuring equipmentbefore placing in the circulating a

17、ir oven set at 158F 6 2F(70C 6 1C). Mark the exact initial area of the measurementfor future location in the color measurement equipment.6.3 Place test specimens, positioned on edge, in the racks(4.3) into the circulating air oven at 158F 6 2F (70C 61C) for 7 days 6 1 h. The samples are placed in th

18、e ovenparallel to the direction of air flow.6.4 Remove specimens from circulating air oven and recon-dition at 73.4F 6 2F (23C 6 1C) for 1 h.6.5 Within 24 h after reconditioning, obtain final L*, a*, b*and calculate DE* readings on each specimen at the markedposition using the color measuring equipm

19、ent. Use either thecool white fluorescent (CWF) or daylight (D-65) light source.7. Report7.1 Record the light source used for measurement.7.2 Record initial and final L*, a*, b*, and DE* values foreach specimen and report the individual and average DE*values.8. Precision and Bias8.1 Interlaboratory

20、Test Program5An interlaboratorystudy evaluating the color stability of resilient vinyl flooring tothe effects of exposure to heat was run in 1991 through 1993.Six laboratories tested three categories of an experimentalunprinted resilient sheet flooring structure having a 0.010 in.(0.254 mm) transpar

21、ent top layer containing varying levels ofstabilizers. Exposure to 158F 6 2F (70C 6 1C) heat for 7days was used to provide an accelerated heat aging environ-ment. Color measurements were made under daylight (D-65)and cool white fluorescent (CWF) illumination. Each categorylevel contained four test s

22、pecimens randomly drawn from themaster batch of material prepared by a single manufacturingsite. Practice E 691 was followed for the design and analysis ofthe data; the details of the test program are being compiled intoa research report.8.2 Test ResultsThe terms repeatability limit and repro-ducibi

23、lity limit are used as specified in Practice E 177. Theprecision information has been summarized in Table 1. There isa mixture of constancy and proportionality when the 2.8sindices are compared throughout the test range. It should benoted that in this study measurement of color change correlatedwith

24、 the varying levels of stabilization. As a result, this testmethod shows that color stability performance varies as thelevel of stabilization is varied.8.3 PrecisionSee Table 1.8.4 BiasSince there is no accepted reference material,method, or laboratory suitable for determining the bias for theproced

25、ure in this test method for measuring the heat induceddiscoloration in vinyl resilient flooring, no statement on bias isbeing made.9. Keywords9.1 accelerated test; heat resistance; heat stability; resilientflooring; spectrophotometer5Supporting data have been filed at ASTM Headquarters and may be ob

26、tained byrequesting Research Report RR: F06-1003.F1514032ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such paten

27、t rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited eithe

28、r for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair he

29、aring you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standar

30、d may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).TABLE 1 Statistical Analysis of Interlaboratory Test ProgramMaterial Stabilization Level DE* AverageRepeatabilityStandard De

31、viationARepeatabilityLimitReproducibilityStandard DeviationAReproducibilityLimitDaylight (D-65)B High 1.093 0.150 0.420 0.282 0.790A Medium 1.804 0.153 0.428 0.385 1.078C Low 5.885 0.313 0.876 1.467 4.108Cool White Fluorescent (CWF)B High 1.220 0.208 0.582 0.324 0.970A Medium 2.039 0.168 0.470 0.431 1.207C Low 6.636 0.353 0.988 1.671 4.679AA comparison of standard deviations shows the reproducibility value to be approximately 2 to 5 times greater than the corresponding repeatability value. Repeatabilitywithin a laboratory is better than reproducibility between laboratories.F1514033