ASTM D6163-2000(2008) 952 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements《玻璃纤维增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层.pdf

《ASTM D6163-2000(2008) 952 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements《玻璃纤维增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层.pdf》由会员分享，可在线阅读，更多相关《ASTM D6163-2000(2008) 952 Standard Specification for Styrene Butadiene Styrene (SBS) Modified Bituminous Sheet Materials Using Glass Fiber Reinforcements《玻璃纤维增强的苯乙烯丁二烯苯乙烯(SBS)改良沥青层.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 6163 00 (Reapproved 2008)Standard Specification forStyrene Butadiene Styrene (SBS) Modified BituminousSheet Materials Using Glass Fiber Reinforcements1This standard is issued under the fixed designation D 6163; the number immediately following the designation indicates the year oforig

2、inal adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification covers prefabricated modified bitumi-nous sh

3、eet materials with glass fiber reinforcement, with orwithout granules, that use styrene butadiene styrene (SBS)thermoplastic elastomer as the primary modifier and areintended for use in the fabrication of multiple ply roofing andwaterproofing membranes.1.2 This specification is intended as a materia

4、l specificationonly. Issues regarding the suitability of the specific roofconstructions or application techniques are beyond this scope.1.3 The specified tests and property limits used to charac-terize the sheet materials are intended to establish minimumproperties. In-place roof system design crite

5、ria, such as fireresistance, field strength, impact/puncture resistance, materialcompatibility, uplift resistance, and others, are factors beyondthe scope of this material specification.1.4 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for infor

6、mationonly.2. Referenced Documents2.1 ASTM Standards:2D 1079 Terminology Relating to Roofing and Waterproof-ingD 5147 Test Methods for Sampling and Testing ModifiedBituminous Sheet Material3. Terminology3.1 DefinitionsFor definitions of terms used in this speci-fication, refer to Terminology D 1079.

7、4. Classifications4.1 Modified bituminous sheet materials reinforced withglass fiber, Type I, Type II, and Type III are covered by thisspecification.4.2 The following grades are used to describe the materialsurfacing:4.2.1 Grade GGranule surfaced.4.2.2 Grade SSmooth surfaced.5. Material and Manufact

8、ure5.1 In the process of manufacture, the reinforcement isimpregnated and coated on both sides with an SBS modifiedbituminous coating. The SBS modified bituminous coatingshall be permitted to be compounded with a mineral stabilizer.5.2 The Grade G sheet is surfaced on the weather side withmineral gr

9、anules, except for any selvage. To prevent sticking inthe roll, the reverse side and any selvage shall be permitted tobe covered with a fine mineral surfacing or any other surfacingthat will not interfere with adhesion or bonding of the lapduring application.5.3 Sheet material intended for applicati

10、on by heat welding(torching) shall meet the minimum bottom coating requirementfound in Table 1.6. Physical Properties6.1 The sheet shall conform to the minimum physicalproperties prescribed in Table 2.6.2 The finished product shall not crack nor be so sticky asto cause tearing or other material dama

11、ge upon being unrolledat any product temperature between 4 and 60C (40 and140F).7. Dimensions, Mass, and Permissible Variations7.1 The finished product shall conform to the followingdimensions and variations:7.1.1 The width of the roll shall be as agreed between thepurchaser and the seller and shall

12、 not vary more than 1 %.7.1.2 The area of the roll shall be no less than as agreedbetween the purchaser and the seller.7.1.3 The selvage width shall be within 6.4 mm (14 in.) ofthe nominal selvage width and shall be not less than 76.2 mm(3 in.) in width without a laying line and 63.5 mm (2.5 in.) in

13、width if the sheet has a laying line. If a laying line is provided,the line must not be less than 76.2 mm (3 in.) from the edge ofthe sheet.7.2 The mass and thickness of the finished product shall beas prescribed in Table 1.1This specification is under the jurisdiction of ASTM Committee D08 onRoofin

14、g and Waterproofing and is the direct responsibility of Subcommittee D08.04on Felts and Fabrics.Current edition approved Dec. 1, 2008. Published December 2008. Originallyapproved in 1997. Last previous edition approved in 2000 as D 6163 002.2For referenced ASTM standards, visit the ASTM website, www

15、.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.8. Wo

16、rkmanship, Finish, and Appearance8.1 The finished product shall be coated completely in acontinuous, unbroken film and shall be free of such defects asholes, tears, cracks, wrinkles, or permanent deformations,blisters, ragged or untrue edges, and areas of uncoated rein-forcement.8.2 The surface of t

17、he weather side shall be uniform infinish and texture.8.3 For Grade G material, the mineral granules shall bedistributed uniformly over the entire surface in an even layerexcluding any selvage, shall be embedded firmly in the SBSmodified bituminous coating, and the line of demarcationbetween the gra

18、nule-surfaced portion of the weather side andany selvage shall be straight and parallel to the edges of thesheet.8.4 When unrolled on a smooth plane, the sheet shall bestraight and true so that the lap will mate with the adjacentsheet within the tolerance for the lap without wrinkles, buckles,or fis

19、hmouths.9. Sampling and Test Methods9.1 Sample the material and determine the properties de-scribed in this specification in accordance with Test MethodsD 5147, unless otherwise indicated.9.2 Ultimate ElongationSee Test Methods D 5147, Sec-tion 6.10. Inspection10.1 InspectionInspection shall be in a

20、ccordance with therequirements of this specification.TABLE 1 Dimensions and Masses of SBS Modified Bituminous Sheet Materials Using Glass Fiber ReinforcementsDescription Type I Type II Type IIIThickness, min, mm (mils),Grade S 2.0 (80) 2.0 (80) 2.0 (80)Grade G 2.4 (95) 2.7 (105) 3.0 (120)Net mass/un

21、it area, min, g/m2(lbs/100 ft2)Grade S 2197 (45) 2197 (45) 2197 (45)Grade G 3173 (65) 3661 (75) 3661 (75)Bottom coating thickness, heat welding applicationproducts, min, mm (mils)Grade S 1.0 (40) 1.0 (40) 1.0 (40)Grade G 1.0 (40) 1.0 (40) 1.0 (40)TABLE 2 Physical Properties of SBS Modified Bituminou

22、s Sheet Materials Using Glass Fiber ReinforcementsAPropertyType IGrade: G and SType IIGrade: G and SType IIIGrade: G and SPeak load at 18 6 2C (0 6 3.6F),MD and XMD, min, before and afterheat conditioning, kN/m (lbf/in.) 12.3 (70) 26.25 (150) 32 (180)Elongation at 18 6 2C (0 6 3.6F),MD and XMD, min,

23、 at peak load, beforeand after heat conditioning, (%) 1 2 2Peak load at 23 6 2C (73.4 6 3.6F),MD and XMD, min, before and afterheat conditioning, kN/m (lbf/in.) 5.3 (30) 14 (80) 26 (150)Elongation at 23 6 2C (73.4 6 3.6F),MD and XMD, min, at peak load, beforeand after heat conditioning, (%) 2 4 3Ult

24、imate elongation 23 6 2C (73.4 63.6F), MD and XMD, min, (%)as manufactured: 3 40 2after heat conditioning: 3 20 2Tear strength at 23 6 2C (73.4 63.6F), min, N (lbf) 156 (35) 489 (110) 934 (210)Low temperature flexibility, max, beforeand after heat conditioning, C (F) 18 (0) 18 (0) 15 (5)Dimensional

25、stability, max, (%) 0.5 0.5 0.5Compound stability at 102C (215F) no failures no failures . . .Compound stability at 91C (195F) . . . . . . no failuresGranule embedment, g, (max) (GradeG only) 2 2 2AThe properties in this table are “as manufactured” unless otherwise noted.D 6163 00 (2008)210.2 Inspec

26、tion AlternativesAlternative inspection re-quirements shall be determined by and as agreed upon betweenthe purchaser and supplier.11. Rejection and Resubmittal11.1 Failure to ConformFailure to conform to any of therequirements as stated in this specification constitutes groundsfor rejection.11.2 Rej

27、ection RedressThe supplier shall have the right toinspect the rejected materials. The supplier and the purchasershall agree to the quantity of rolls deemed unacceptable. Thesupplier shall then have the right to submit the same number ofnew rolls as replacement.12. Packaging and Package Marking12.1 T

28、he finished material shall be furnished as rolls. Therolls shall be wrapped securely to prevent shifting of materialand to permit normal handling. If a roll contains a manufac-turing splice, the splice shall be marked clearly; no roll shallcontain more than one splice or two pieces.12.2 Unless other

29、wise agreed upon by the supplier andpurchaser, each product package shall be marked plainly withthe suppliers name, the product name, the ASTM designationincluding type and grade, the net coverage, and the type ofbitumen if not evident in the label name of the product.13. Keywords13.1 glass fiber re

30、inforcement; modified bituminous sheet;styrene butadiene styrene (SBS); thermoplastic elastomerASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determina

31、tion of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or with

32、drawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that you

33、r comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).D 6163 00 (2008)3