ASTM D4705-2000(2010) Standard Test Method for Stitch Tear Strength of Leather Double Hole《皮革 双孔的缝合撕裂强度标准试验方法》.pdf

《ASTM D4705-2000(2010) Standard Test Method for Stitch Tear Strength of Leather Double Hole《皮革 双孔的缝合撕裂强度标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4705-2000(2010) Standard Test Method for Stitch Tear Strength of Leather Double Hole《皮革 双孔的缝合撕裂强度标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4705 00 (Reapproved 2010)Standard Test Method forStitch Tear Strength of Leather, Double Hole1This standard is issued under the fixed designation D4705; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last

2、 revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method is intended for use in d

3、etermining thestitch tearing resistance of leather using a double hole tear. It isparticularly applicable to lightweight leathers. This test methoddoes not apply to wet blue.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconve

4、rsions to SI units that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practice

5、s and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1610 Practice for Conditioning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength of Le

6、atherD2813 Practice for Sampling Leather for Physical andChemical Tests3. Significance and Use3.1 This test method is designed to measure the loadrequired to tear leather through two holes in the test specimen.Tanners and leather buyers have found that this test gives anindication of the resistance

7、of leather to tearing. It is ofparticular value in estimating the durability of leather towithstand tearing stresses encountered in the manufacture ofshoes, garments, and upholstered products. The thickness ofthe specimen and direction of tear relative to the backbone willaffect the uniformity of th

8、e test results. This test method maynot apply when the conditions of the test employed differwidely from those specified in the test method.4. Apparatus4.1 Testing Machine, as described in Test Method D2209.4.2 Thickness Gage, a dead weight type of thickness gage asdescribed in Method D1813.4.3 Stee

9、l Die, to cut test specimens (as described in 5.1).4.4 Paper Clip, #1/Premium, with wire diameter 0.041 60.001 in. (1.04 6 0.0254 mm).5. Sampling Test Specimen5.1 Unless otherwise specified, sample the leather accordingto Practice D2813.5.2 The specimen shall be a rectangle of leather 2 in. (50.8mm)

10、 in length and 1 in. (25.4 mm) in width with two holes (564in. (1.98 mm) in diameter on one end of the specimen. Thecenters of the holes shall be14 in. (6.35 mm) from the end,14in. (6.35 mm) apart, and located equidistant from the centerline (length wise) of the specimen. See Fig. 1.5.3 The specimen

11、 shall be cut with the long dimensionperpendicular to the backbone.6. Conditioning6.1 All specimen shall be conditioned for 48 h in anatmosphere maintained at 73.4 6 3.6F (23 6 2C) and 50 64 % relative humidity and tested under the conditions asdescribed in Practice D1610.7. Procedure7.1 Determine t

12、he thickness of the specimen to the nearest0.5 oz (0.2 mm) on the long axis near one end.7.2 Bend the wire into a “U” shape, preferably by bendingover a14 in. (6.35 mm) rod, and pass the ends through the holesin the specimen so that both ends project from the flesh side ofthe specimen. Clamp both en

13、ds of the wire in the testing1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31.07 on Physical Properties.Current edition approved Oct. 1, 2010. Published November 2010. Originallyapproved in 1987. Last previous edition ap

14、proved in 2005 as D4705 - 00 (2005).DOI: 10.1520/D4705-00R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.

15、1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.machine grip, the jaws of which have been covered. Clamp thefree end of the specimen in the other grip of the testingmachine.7.3 Operate the machine at 10 6 2 in. (254 6 50.8 mm) permin

16、 until the specimen tears. At the instant that the specimenbegins to tear, note and record the load registered by themachine.8. Report8.1 Report the following:8.1.1 Thickness to the nearest 0.5 oz (0.2 mm) reported foreach specimen or averaged and reported as the thickness of thesample.8.1.2 The tea

17、ring strength of the specimen shall be reportedto the nearest 1 lb (0.45 kg).9. Precision and Bias (or Reproducibility)9.1 This test method is adopted from the procedure of theAmerican Leather ChemistsAssociation where it has long beenin use and where it was approved for publication before theinclus

18、ion of precision and bias statements was mandated. Theoriginal interlaboratory test data is no longer available. Theuser is cautioned to verify by the use of reference materials, ifavailable, that the precision and bias (or reproducibility) of thistest method is adequate for the contemplated use.10.

19、 Keywords10.1 leather; stitch tear; stitch tear strength; strength; tearstrength; tearing strengthASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determ

20、ination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or w

21、ithdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that

22、your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (s

23、ingle or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).FIG. 1 Test SpecimenD4705 00 (2010)2