ASTM D4704-2000(2010) Standard Test Method for Tearing Strength Tongue Tear of Leather《皮革的撕破强度和切口撕破的标准试验方法》.pdf

《ASTM D4704-2000(2010) Standard Test Method for Tearing Strength Tongue Tear of Leather《皮革的撕破强度和切口撕破的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D4704-2000(2010) Standard Test Method for Tearing Strength Tongue Tear of Leather《皮革的撕破强度和切口撕破的标准试验方法》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D4704 00 (Reapproved 2010)Standard Test Method forTearing Strength, Tongue Tear of Leather1This standard is issued under the fixed designation D4704; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last rev

2、ision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This test method is intended for determining

3、the tearingstrength of leather by measuring the force required to tear aspecimen cut perpendicular to the surface. This test methoddoes not apply to wet blue.1.2 The values stated in inch-pound units are to be regardedas standard. The values given in parentheses are mathematicalconversions to SI uni

4、ts that are provided for information onlyand are not considered standard.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine

5、the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D1610 Practice for Conditioning Leather and Leather Prod-ucts for TestingD1813 Test Method for Measuring Thickness of LeatherTest SpecimensD2209 Test Method for Tensile Strength of LeatherD2813 Pract

6、ice for Sampling Leather for Physical andChemical Tests3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 tongue tear strengththe load required to tear theleather between two tongues formed by splitting the leatherperpendicular to its surface.4. Significance and Use4.1 Knowledge

7、of the strength of the sample can be adetermining factor for the end use of the product.5. Apparatus5.1 Testing Machine, as described in Test Method D2209.5.2 Thickness Gage, a dead weight type of thickness gage asdescribed in Test Method D1813.5.3 Steel Die, to cut test specimens.6. Sampling and Te

8、st Specimens6.1 Unless otherwise specified, sample the leather accordingto Practice D2813.6.2 The specimen shall be a rectangular piece of leather,1 3 4 in. (25.4 3 101.6 mm) by the full thickness of the unit.It shall have a316 in. (4.76 mm) hole located on the long axis1 in. (25.4 mm) from one end

9、and shall be split along its axisfrom the hole to the other end to form two tongues. Thedirection of the long axis of the specimen relative to thebackbone shall be noted. See Fig. 1.7. Conditioning7.1 All specimens shall be conditioned for 48 h in anatmosphere maintained at 73.4 6 3.6F (23 6 2C) and

10、 50 64 % relative humidity and tested under the conditions asdescribed in Practice D1610.8. Procedure8.1 Determine the thickness of the specimen to the nearest0.5 oz (0.2 mm) on the long axis between the hole and theunsplit end of the specimen. The gage foot shall be adjacent to,but shall not overla

11、p, the hole.8.2 Clamp one of the tongues on the specimen in each of thetesting grips so that the long axis of the tongue is in thedirection of the motion of the movable grip. The faces of thegrips shall be approximately 2 in. (50.8 mm) from the commonbase of the tongues (from the hole).8.3 Operate t

12、he machine at 10 6 2 in. (254 6 50.8 mm) perminute until the specimen starts to tear. At the instant of theinitial tear, note and record the load registered by the machine.9. Report9.1 The thickness measurement of all specimens tested shallbe averaged to the nearest 0.5 oz (0.2 mm) and reported as t

13、hethickness of the sample.1This test method is under the jurisdiction of ASTM Committee D31 on Leatherand is the direct responsibility of Subcommittee D31.07 Physical PropertiesCurrent edition approved Oct. 1, 2010. Published November 2010. Originallyapproved in 1987. Last previous edition approved

14、in 2005 as D4704 00 (2005).DOI: 10.1520/D4704-00R10.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1Copyrigh

15、t ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.9.2 The load required to tear the specimens shall be aver-aged to the nearest pound and reported as the tongue tearstrength of the sample.9.3 The direction of the long axis of the specimen relat

16、ive tothe backbone shall be reported.10. Precision and Bias (or Reproducibility)10.1 This test method is adopted from the procedures of theAmerican Leather ChemistsAssociation where it has long beenin use and where it was approved for publication before theinclusion of precision and bias statements

17、was mandated. Theoriginal inter-laboratory test data is no longer available. Theuser is cautioned to verify by the use of reference materials, ifavailable, that the precision and bias (or reproducibility) of thistest method is adequate for the contemplated use.11. Keywords11.1 leather; tear strength

18、; tearing strength; tongue tear;tongue tear strength; strengthASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such

19、patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited

20、either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fa

21、ir hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this st

22、andard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the ASTM website (www.astm.org/COPYRIGHT/).FIG. 1 Test SpecimenD4704 00 (2010)2