ASTM D1414-1994(2003) Standard Test Methods for Rubber O-Rings《O型橡胶圈的标准试验方法》.pdf

《ASTM D1414-1994(2003) Standard Test Methods for Rubber O-Rings《O型橡胶圈的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D1414-1994(2003) Standard Test Methods for Rubber O-Rings《O型橡胶圈的标准试验方法》.pdf（11页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 1414 94 (Reapproved 2003)Standard Test Methods forRubber O-Rings1This standard is issued under the fixed designation D 1414; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in pare

2、ntheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 These test methods describe the procedures for deter-mining the phy

3、sical properties of O-rings and changes in theseproperties due to aging.1.2 The values stated in SI units are to be regarded as thestandard. The values given in parentheses are for informationonly.1.3 This standard does not purport to address all of thesafety concerns, if any, associated with its us

4、e. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory limitations prior to use.2. Referenced Documents2.1 ASTM Standards:2D 297 Test Methods for Rubber ProductsChemicalAnalysisD 395 Test Methods fo

5、r Rubber PropertyCompressionSetD 412 Test Methods for Vulcanized Rubber and Thermo-plastic ElastomersTensionD 471 Test Method for Rubber PropertyEffect of LiquidsD 573 Test Method for RubberDeterioration in an AirOvenD 865 Test Method for RubberDeterioration by Heatingin Air (Test Tube Enclosure)D 1

6、329 Test Method for Evaluating Rubber PropertyRetraction at Lower Temperatures (TR Test)D 1415 Test Method for Rubber PropertyInternationalHardnessD 2240 Test Method for Rubber PropertyDurometerHardnessD 4483 Practice for Determining Precision for Test MethodStandards in the Rubber and Carbon Black

7、Industries2.2 Aerospace Standard:AS568A Oring Sizes33. Terminology3.1 Definitions:3.1.1 O-ringa rubber seal of homogeneous compositionmolded in one piece to the configuration of a torus with circularcross section. The O-ring is used as a dynamic or static sealusually installed in a machined groove.4

8、. Significance and Use4.1 These test methods provide acceptable procedures forquality control purposes and for the determination of engineer-ing characteristics.5. General Methods5.1 Except as otherwise specified in these test methods forrubber O-rings, the following ASTM test methods applicable ing

9、eneral to vulcanized rubber, shall be complied with asrequired and are hereby made a part of these test methods:5.1.1 Tension Test Test Methods D 412.5.1.2 Compression Set Test Methods D 395.5.1.3 Low Temperature Test Method D 1329.5.1.4 DensityTest Methods D 297.5.1.5 Fluid Aging Test Method D 471.

10、5.1.6 Heat AgingTest Methods D 865 and D 573.5.1.7 HardnessTest Methods D 2240 and D 1415.5.2 In case of conflict between the provisions of these testmethods and those of detailed procedures herein, the lattershall take precedence.6. Test Conditions6.1 The temperature of the testing room shall be 23

11、 6 2C(73.4 6 3.6F). The specimens to be tested shall be kept in thisroom for a minimum of 30 min previous to the time of testing.For referee tests the minimum time for conditioning shall be 16h. In cases where this temperature cannot be obtained, theactual temperature shall be reported.7. Dimensiona

12、l Measurements7.1 Thickness:1These test methods are under the jurisdiction of ASTM Committee D11 onRubber and are the direct responsibility of Subcommittee D11.36 on Seals.Current edition approved Nov. 1, 2003. Published December 2003. Originallyapproved in 1956. Last previous edition approved in 19

13、99 as D 1414 94 (1999).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.3Standardization Documents Order Desk,

14、 Bldg. 4 Section D, 700 Robbins Ave.,Philadelphia, PA 19111-5094, Attn: NPODS.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7.1.1 The thickness or cross section may be measured byone of the following methods: (a) a hand micrometer

15、equippedwith 6-mm (0.25-in.) diameter hemispherical tips (ballpoint ortubing micrometers), (b) dial indicators that have a maximumcontact force of 0.29 N (29 gf), or (c) an electronic micrometerwith a spring force of 0.1 N (10 gf) maximum. Better accuracycan be obtained with a 0.05-N (5-gf) spring o

16、r with no spring.In case of referee tests, both laboratories shall use the samespring force.7.1.2 The O-ring specimen shall be measured at four pointsequally distributed around the circumference in both the radialand axial direction. An average reading shall be used forcalculation.7.2 DiameterA step

17、ped cone or optical comparator maybe used for measuring the inside diameter of small rings. Thediametric intervals of the stepped cone shall not exceed 2 % ofthe diameter to be measured (see Fig. 1).8. Tension Testing8.1 Testing Machine The testing machine shall conformto the requirements specified

18、in Section 3 of Test MethodsD 412, with the exception of the grips. Grips for testing ringsshall consist of ball-bearing spools at least 9 mm (0.35 in.) indiameter, and be capable of being brought within 19 mm (0.75in.) center-to-center distance at closest approach. Stresseswithin the specimen shall

19、 be minimized by (1) rotating onespool one full revolution for each 150 mm (6.0 in.) of travel ofthe power-driven grips or (2) lubricating the contact surface ofthe spools with castor oil. Grips for testing straight specimensmay be of any type provided breaks do not occur in a portionof the specimen

20、 that has been at any time in contact with thegrips. For specimens smaller than 25 mm (1 in.) in insidediameter, spools of smaller diameter and closer approach maybe employed.8.2 Test Specimen:8.2.1 The test specimen shall consist of an entire O-ringexcept in the following cases: (1) when the diamet

21、er is toolarge to permit a break within the limits of travel of the testingmachine, (2) when the specimen has been previously cut opento permit an aging test, and (3) when the specimen is unagedbut is to be compared with an aged specimen as described in(2). For these cases a specimen cut from a ring

22、 shall beemployed.8.2.2 Specimens that exhibit obvious flaws at any point onthe surface, such as might result from imperfect molding orflash removal, shall not be tested.8.3 Procedure for Determination of Tensile Strength, Ulti-mate Elongation, and Tensile Stress:8.3.1 Bring the grips close enough t

23、ogether so the specimencan be installed without stretching. Set the machine for a speedof 500 6 50 mm (20 6 2 in.)/min, set the chart recorder, andengage the clutch. (If a recorder is not used, note the spoolcenter-to-center distance continually by means of a suitablescale). The stressed inside circ

24、umference, L, is equal to twicethe distance between spools plus the circumference of onespool. Record the breaking force value, F, at the elongationspecified for tensile stress and at the time of rupture. Measurethe center-to-center distance between the spools at rupture tothe nearest 2.5 mm (0.1 in

25、.) and record as the value for D.8.3.2 For the application of bench marks to segmentedspecimens as described in 8.2, hold the piece as straight aspossible being careful not to apply excessive stress. Follow theprocedure described in 8.3.1. Discard results for any specimenthat breaks at a point that

26、has at any time contacted the grip,and test an additional specimen. A suitable extensiometer maybe employed for elongation determination.8.4 Calculations:8.4.1 Tensile Strength Calculate the tensile strength asfollows:8.4.1.1 For O-rings on spool grips:T 5 F/A (1)where:T = tensile strength,F = break

27、ing force, andA = twice the cross-sectional area calculated from axialthickness, W, as follows:A 5pW2/2 5 1.57 W2(2)therefore:T 5 F/1.57 W2(3)8.4.1.2 For straight or single-strand specimens:A 5 0.785 W2(4)FIG. 1 Stepped Cone GageD 1414 94 (2003)2T 5 F/0.785 W2(5)8.4.2 Ultimate ElongationCalculate th

28、e ultimate elonga-tion as follows:8.4.2.1 For rings:Ultimate elongation, % 5 2D 1 G 2 C!/C 3 100 (6)where:D = distance between centers of the spool grips at the timeof rupture of specimen,G = circumference of one spool (spool diameter 3 3.14),andC = inside circumference of the specimen (or inside di

29、am-eter 3 3.14).8.4.2.2 For straight or single-strand specimen cut from anO-ring:Ultimate elongation, % 5 L 2 Lo!/Lo# 3 100 (7)where:L = observed distance between bench marks of stressedspecimen, andLo= original distance between bench marks.8.4.3 Tensile Stress Calculate the tensile stress as in the

30、case of tensile strength except the stress is reported at apredetermined elongation below the ultimate elongation. Cal-culate the center-to-center distance of the spool grips, D, wherethe prescribed elongation, E, occurs, as follows:D 5 1/2EC/100! 1 C 2 G (8)NOTE 1This value of tensile stress at a p

31、redetermined elongation isbased upon inside circumference and differs from that determined by TestMethods D 412, which is based on the mean circumference.8.5 Characteristics of Sample TestedThe median of thevalues for three specimens shall be taken as the characteristicsof the sample tested, except

32、that under the following conditionsthe median of the values for five specimens (two additional)shall be used:8.5.1 If one or more values do not meet the specifiedrequirements when testing for compliance with specifications.8.5.2 If referee tests are being made.8.6 Report:8.6.1 The report shall inclu

33、de the following:8.6.1.1 Results calculated as in 8.4,8.6.1.2 Date of test,8.6.1.3 Temperature of test room if other than provided forin Section 6,8.6.1.4 Type of testing machine used, including diameter ofspool grip if other than standard, and speed, if other than 8.360.8 mm (20.0 6 2 in.)/min, and

34、8.6.1.5 Type of specimen (ring or straight).9. Tension Set Test9.1 Procedure:9.1.1 Stretch the O-ring specimens to 100 % elongation andhold at this strain for 10 min. At the end of this period releasethe specimen and allow it to recover for 10 min. At the end ofthis recovery period, measure the insi

35、de diameter with a stepgage reference in 7.2 and shown in Fig. 1.9.1.2 Apply the strain by (1) stretching the specimen over atapered cone which has a step at the required 100 % elongation,or (2) by means of a tension test machine stopping the machineat 100 % elongation, or ( 3) by the use of any spe

36、cial fixturecapable of holding the O-ring over two spools at constantdistance between spool centers.9.2 Calculation Calculate tension set as follows:Tension set, % 5 L12 Lo!/Lo# 3 100 (9)where:L1= diameter after testing, andLo= original diameter.9.3 Straight specimens cut from large O-rings may be t

37、estedand calculated in accordance with Test Methods D 412.10. Compression Set Test10.1 Nature of Test The compression set of O-ring speci-mens shall follow the general procedures of Method B of TestMethods D 395, with the following exceptions:10.2 Apparatus:10.2.1 SpacersThe spacers shall be adjuste

38、d to within0.025 mm (0.01 in.). This can be done by employing shimstock of various thickness.10.2.2 Measurement The cross section before and aftertest shall be measured in the same marked location with aball-point (tubing) micrometer or other method as described in7.1.10.3 Test Specimen The specimen

39、 shall be a suitablesection cut from the sample O-ring. A52-mm (2-in.) section hasbeen found to be satisfactory on sample O-rings of 17-mm(0.67-in.) or larger inside diameter. On smaller O-rings, asection of approximately 3 mm (18 in.) shall be cut from thesample and discarded.NOTE 2Testing a whole

40、O-ring for compression set is always avoidedbecause air trapped inside the O-ring results in a different set of conditionson the inside and outside surface of the specimen.10.4 ProcedureMeasure the actual specimen to within0.025 mm (0.001 in.) and calculate the spacer to be 75 % ofthis thickness, to

41、 within 0.025 mm (0.001 in.). Close the plates,employing a sufficient number of bolts to prevent deflectionupon heating. At the end of the heating period, release theplates as soon as possible and allow the specimens to cool toroom temperature under the conditions described in TestMethods D 395.11.

42、Compression Set in Liquids11.1 Compression set may be conducted immersed in anyliquid provided a suitable container is available. The containerneeds to be large enough to hold the plates and withstand thevapor pressure of the liquid at test temperature.11.2 The specimen is prepared in accordance wit

43、h 10.3, andat the termination of the heating period the plates are releasedimmediately and the specimens are allowed to cool to roomtemperature for 30 min in a fresh cool portion of the test liquid.Measurement and reporting are the same except the type ofliquid is listed in the report.D 1414 94 (200

44、3)312. Low-Temperature Test12.1 Nature of Test The TR-10 or Temperature RetractionTest shall be in accordance with Test Method D 1329 with theexceptions given in 12.2 to 12.4.12.2 Test Specimen The test specimen shall be an O-ringof 1.5 to 3.8-mm (0.06 to 0.15-in.) cross-sectional diameter andof suf

45、ficient length to reach from clamp to clamp when the ringis cut and held in straight position.12.3 ProcedureStretch the mounted specimen 50 % asstandard. If a greater or lesser stretch is used, report the actualstretch.12.4 ReportThe report shall include the following:12.4.1 Testing elongation, in p

46、ercent, and12.4.2 Temperature at which the specimen retracts 10 %,designated as TR-10 and at other points, such as 30, 50, or70 %, or all, if required.13. Relative Density Test13.1 Test Specimen Any O-ring, O-rings, or segment of anO-ring may be considered as the specimen. The minimum massof the spe

47、cimen shall be 0.005 N (0.5 gf). In the case of verysmall O-rings, two or more pieces may be used as the specimento accomplish this total minimum mass.13.2 ProcedureEmploy the procedure outlined in TestMethods D 297, density hydrostatic method.NOTE 3Extreme accuracy is required in making relative de

48、nsitydeterminations on small O-rings 0.001 N (1 g or less). The surface tensionon the suspending wire is critical; this wire should be of the smallestdiameter corrosion-resistant wire that will support the specimen weight.This surface tension on the wire and the elimination of small air bubbleson th

49、e surface of the specimen can be reduced by the addition of a fewdrops of wetting agent to the water in the weighing beaker.14. Immersion Test14.1 Nature of Test For determination of the changes inphysical properties after liquid immersion, the definitions,standard test liquid descriptions, and general technique shall bein accordance with Test Method D 471. The detailed procedurefor O-rings, outlined in this section however, shall takeprecedence in case of conflict.14.2 Apparatus:14.2.1 The apparatus specified in Test Method D 47