ASTM B705-2017 Standard Specification for Nickel-Alloy (UNS N06625 N06219 and N08825) Welded Pipe《镍合金(UNS N06625 N06219和N08825)焊接管的标准规格》.pdf

《ASTM B705-2017 Standard Specification for Nickel-Alloy (UNS N06625 N06219 and N08825) Welded Pipe《镍合金(UNS N06625 N06219和N08825)焊接管的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM B705-2017 Standard Specification for Nickel-Alloy (UNS N06625 N06219 and N08825) Welded Pipe《镍合金(UNS N06625 N06219和N08825)焊接管的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: B705 05 (Reapproved 2014)B705 17Standard Specification forNickel-Alloy (UNS N06625, N06219 and N08825) WeldedPipe1This standard is issued under the fixed designation B705; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision

2、, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope Scope*1.1 This specification covers welded UNS N06625,2 UNS N062192 and UNS N088252 pipe in the annealed co

3、ndition (temper)for general corrosion applications.1.2 This specification covers pipe sizes in schedules shown in the Permissible Variations in Outside Diameter and WallThickness for Welded Pipe table of Specification B775.1.3 The values stated in inch-pound units are to be regarded as standard. The

4、 values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not considered standard.1.4 The following precautionary caveat pertains only to the test methods portion, Section 8, of this specification: This standarddoes not purport to address all

5、 of the safety concerns, if any, associated with its use. It is the responsibility of the user of thisstandard to become familiar with all hazards including those identified in the appropriate Material Safety Data Sheet (MSDS) forthis product/material as provided by the manufacturer, to establish ap

6、propriate safety and health practices,establish appropriatesafety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.1.5 This international standard was developed in accordance with internationally recognized principles on standardizationestab

7、lished in the Decision on Principles for the Development of International Standards, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:3B751 Specification for General Requirements for Nickel and Nick

8、el Alloy Welded TubeB775 Specification for General Requirements for Nickel and Nickel Alloy Welded PipeB880 Specification for General Requirements for Chemical Check Analysis Limits for Nickel, Nickel Alloys and Cobalt Alloys2.2 ASME Boiler and Pressure Vessel Code:4Section IX Welding and Brazing Qu

9、alifications3. General Requirement3.1 Material furnished in accordance with this specification shall conform to the applicable requirements of the current editionof Specification B775 unless otherwise provided herein.4. Definition of Terms4.1 Class 1Welded, cold-worked, annealed, and nondestructivel

10、y tested in accordance with 9.1.4.2 Class 2Welded, cold-worked, annealed, and nondestructively tested in accordance with 9.2.4.3 Grade 1Annealed condition, relevant for UNS N06625.1 This specification is under the jurisdiction ofASTM Committee B02 on Nonferrous Metals andAlloys and is the direct res

11、ponsibility of Subcommittee B02.07 on RefinedNickel and Cobalt and Their Alloys.Current edition approved Oct. 1, 2014Nov. 1, 2017. Published October 2014November 2017. Originally approved in 1982. Last previous edition approved in 20092014as B705 05 (2009).(2014). DOI: 10.1520/B0705-05R14.10.1520/B0

12、705-17.2 New designation established in accordance with Practice E527 and SAE J 1086, Practice for Numbering Metals and Alloys (UNS).3 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume inform

13、ation, refer to the standards Document Summary page on the ASTM website.4 Available from American Society of Mechanical Engineers (ASME), ASME International Headquarters, Three Park Ave., New York, NY 10016-5990, http:/www.asme.org.This document is not an ASTM standard and is intended only to provid

14、e the user of an ASTM standard an indication of what changes have been made to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the st

15、andard as published by ASTM is to be considered the official document.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States14.4 Grade 2Solution annealed condition, relevant fo

16、r UNS N06625.5. Ordering Information5.1 It is the responsibility of the purchaser to specify all requirements that are necessary for the safe and satisfactoryperformance of material ordered under this specification. Examples of such requirements include, but are not limited to, thefollowing:5.1.1 Al

17、loy name or UNS number,5.1.2 ASTM designation,5.1.3 Dimensions:5.1.3.1 Pipe size,5.1.3.2 Length (specific or random),5.1.4 Class (see Section 3),5.1.5 Grade if UNS N06625 is specified. If neither grade of N06625 is specified, grade 1 will be supplied.5.1.6 Quantity (feet or number of pieces),5.1.7 C

18、ertificationState if certification is required,5.1.8 Samples for Product (Check) AnalysisState whether samples for product (check) analysis should be furnished (7.2), and5.1.9 Purchaser InspectionIf purchaser wishes to witness tests or inspection of material at place of manufacture, the purchaseorde

19、r must so state indicating which tests or inspections are to be witnesses.6. Material and Manufacture6.1 Pipe shall be made from flat-rolled alloy by an automatic welding process with no addition of filler metal. Subsequent towelding and prior to final annealing, the material shall be cold-worked in

20、 either the weld metal only or both weld and base metal.6.2 Pipe shall be furnished with oxide removed. When bright annealing is used, descaling is not necessary.7. Chemical Composition7.1 The material shall conform to the composition limits specified in Table 1. One test per lot shall be performed.

21、7.2 If a product (check) analysis is performed by the purchaser, the material shall conform to the product (check) analysisvariations per Specification B880.8. Mechanical Properties and Other Requirements8.1 Mechanical PropertiesThe material shall conform to the mechanical properties specified in Ta

22、ble 2. One pipe per lot shallbe examined.8.2 Flattening TestAsection of pipe not less than 4 in. (102 mm) in length shall be capable of withstanding, without cracking,flattening under a load applied gradually at room temperature until the distance between the platens is five times the wall thickness

23、.The weld shall be positioned 90 from the direction of the applied flattening force. One pipe per lot shall be examined.8.2.1 Superficial ruptures resulting from surface imperfections shall not be a cause for rejection.8.3 Transverse Guided Bend Test:TABLE 1 Chemical RequirementsComposition Limits,

24、%UNSN06625UNSN06219UNSN08825Ni 58.0 minA Bal 38.046.0Cr 20.023.0 18.0-22.0 19.523.5Fe 5.0 max 2.0-4.0 22.0 minAMo 8.010.0 7.0-9.0 2.5 3.5Cb + Ta 3.154.15 . .C 0.10 max 0.05 max 0.05 maxMn 0.50 max 0.50 max 1.0 maxSi 0.5 max 0.70-1.10 0.5 maxP 0.015 max 0.020 max .S 0.015 max 0.010 max 0.03 maxAl 0.4

25、 max 0.50 max 0.2 maxTi 0.40 max 0.50 max 0.61.2Co (if determined) 1.0 max 1.0 max .Cu . 0.50 max 1.53.0A Element may be determined arithmetically by difference.B705 1728.3.1 At the option of the pipe manufacturer, the transverse guided bend test may be substituted in lieu of the flattening test.Two

26、 bend specimens shall be taken transversely from pipe or the test specimens may be taken from a test plate of the same materialand heat as pipe, which is attached to the end of the cylinder and welded as a prolongation of the pipe longitudinal seam. Exceptas provided in 8.3.2, one shall be subjected

27、 to a face guided bend and a second to a root guided bend test. One specimen shall bebent with the inside surface of the pipe against the plunger and the other with the outside surface of the pipe against the plunger.Guided bend test specimens shall be prepared and tested in accordance with Section

28、IX, Part QW 160 of the ASME Boiler andPressure Vessel Code and shall be one of the types shown in QW462.2 and QW462.3 of that code. One bend test (two bendspecimens) per lot shall be examined.8.3.2 For specified wall thicknesses 38 in. (9.5 mm) and over, but less than 34 in. (19 mm) side bend tests

29、may be made insteadof the face and root bend tests. For specified wall thicknesses 34 in. (19) and over, both specimens shall be subjected to the sidebend tests. Side bend specimens shall be bent so that one of the side surfaces becomes the convex surface of the bend specimen.8.3.3 The bend test sha

30、ll be acceptable if no cracks or other defects exceeding 18 in. (3 mm) in any direction be present in theweld metal or between the weld and the pipe or plate metal after bending. Cracks which originate along the edges of the specimenduring testing, and are less than 14 in. (6.5 mm) measured in any d

31、irection shall not be considered.9. Nondestructive Testing9.1 Class 1Each piece in each lot shall be subjected to one of the following four tests: hydrostatic, pneumatic (air underwater),eddy current, or ultrasonic.9.2 Class 2Each piece in each lot shall be subjected to a leak test and an electric t

32、est as follows:9.2.1 Leak TestHydrostatic or pneumatic (air underwater).9.2.2 Electric TestEddy current or ultrasonic.9.3 The manufacturer shall have the option to test to Class 1 or 2 and select the nondestructive test methods, if not specifiedby the purchaser.10. Product Marking10.1 In addition to

33、 the requirements of Specification B751B775, UNS N06625 tubespipe shall be marked with gradeinformation.11. Keywords11.1 N06219; N06625; N08825; welded pipeTABLE 2 Mechanical Property RequirementsAlloyAlloy GradeTensileStrengthmin, psi (MPa)YieldStrength0.2 % Offset,min, psi(MPa)Elonga-tion in 2in.

34、or 50mm, min,%UNS N06625 1 (annealed) 120 000 (827) 60 000 (414) 30UNS N06625 2 (solutionannealed)A100 00 (690) 40 000 (276) 30UNS N06219 96 000 (660) 39 000 (270) 30UNS N08825 85 000 (586) 35 000 (240) 30A Solution annealed at 2000F (1093C) minimum, with or without subsequentstabilization anneal at

35、 1800F (982C) minimum to increase resistance tosensitization.B705 173SUMMARY OF CHANGESCommittee B02 has identified the location of selected changes to this standard since the last issue(B705-05(2014) that may impact the use of this standard. (Approved November 1, 2017.)(1) Deleted Specification B75

36、1 from Section 2.(2) Replaced Specification B751 with Specification B775 in Section 10.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of

37、the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn.Yo

38、ur comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comment

39、s have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or mul

40、tiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 174