ASTM A521 A521M-2006(2011) Standard Specification for Steel Closed-Impression Die Forgings for General Industrial Use《一般工业用闭式压模钢锻件的标准规范》.pdf

《ASTM A521 A521M-2006(2011) Standard Specification for Steel Closed-Impression Die Forgings for General Industrial Use《一般工业用闭式压模钢锻件的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A521 A521M-2006(2011) Standard Specification for Steel Closed-Impression Die Forgings for General Industrial Use《一般工业用闭式压模钢锻件的标准规范》.pdf（9页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A521/A521M 06 (Reapproved 2011)Standard Specification forSteel, Closed-Impression Die Forgings for General IndustrialUse1This standard is issued under the fixed designation A521/A521M; the number immediately following the designation indicates the yearof original adoption or, in the cas

2、e of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers untreated and heat-treatedsteel, closed-impression die forgings

3、(Note 1) for generalindustrial use.NOTE 1For the definition of a forging, refer General RequirementsSpecification A788/A788M.1.2 The Grades of forgings are as follows, the choicedepending on design and stress or service to be imposed:1.2.1 Grade CAUntreated, carbon steel forgings,1.2.2 Grades CC, CC

4、1, and CEAnnealed, normalized andtempered, carbon steel forgings,1.2.3 Grade CFNormalized and tempered carbon steelforgings,1.2.4 Grade CF1Double normalized and tempered car-bon steel forgings,1.2.5 Grade CGQuenched and tempered, or normalized,quenched and tempered carbon steel forgings,1.2.6 Grade

5、AAAnnealed, normalized, or normalized andtempered alloy steel forgings,1.2.7 Grades AB and ACNormalized and tempered alloysteel forgings, and1.2.8 Grades AD, AE, AF, AG, and AHNormalized,quenched, and tempered alloy steel forgings.1.3 Unless the order specifies the applicable “M” specifica-tion desi

6、gnation, the forgings shall be furnished with theinch-pound units.1.4 The values stated in either inch-pound units or SI(metric) units are to be regarded separately as standard. Withinthe text and tables, the SI units are shown in brackets. Thevalues stated in each system are not exact equivalents;

7、there-fore, each system shall be used independently of the other.Combining values from the two systems may result in noncon-formance with the specification.2. Referenced Documents2.1 ASTM Standards:2A29/A29M Specification for Steel Bars, Carbon and Alloy,Hot-Wrought, General Requirements forA275/A27

8、5M Practice for Magnetic Particle Examinationof Steel ForgingsA322 Specification for Steel Bars, Alloy, Standard GradesA370 Test Methods and Definitions for Mechanical Testingof Steel ProductsA388/A388M Practice for Ultrasonic Examination of SteelForgingsA576 Specification for Steel Bars, Carbon, Ho

9、t-Wrought,Special QualityA788/A788M Specification for Steel Forgings, General Re-quirementsA921/A921M Specification for Steel Bars, Microalloy, Hot-Wrought, Special Quality, for Subsequent Hot ForgingE3 Guide for Preparation of Metallographic SpecimensE45 Test Methods for Determining the Inclusion C

10、ontent ofSteelE94 Guide for Radiographic ExaminationE112 Test Methods for Determining Average Grain SizeE340 Test Method for Macroetching Metals and AlloysE381 Method of Macroetch Testing Steel Bars, Billets,Blooms, and ForgingsE407 Practice for Microetching Metals and Alloys3. Ordering Information

11、and General Requirements3.1 Material supplied to this specification shall conform tothe requirements of Specification A788/A788M, which out-lines additional ordering information, manufacturing require-ments, testing and retesting methods and procedures, productanalysis variations, marking, certifica

12、tion, and additional1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.06 on Steel Forgings and Billets.Current edition approved April 1, 2011. Published June 2011. Originallyapproved in

13、1964. Last previous edition approved in 2006 as A521/A521M 06.DOI: 10.1520/A0521_A0521M-06R11.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document

14、 Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.supplementary requirements. Failure to comply with the re-quirements of Specification

15、A788/A788M constitutes non-conformance with this specification3.2 In addition to the ordering information required bySpecificationA788/A788M, the purchaser may require that thetolerances stated in the appendices to this specification shallapply.3.3 If the requirements of this specification should co

16、nflictwith the requirements of A788/A788M, then the requirementsof this specification shall prevail.4. Forging Manufacture4.1 Sufficient discard shall be taken from the ingot orforging stock to secure freedom from piping and unduesegregation.4.2 Manufacturing practice shall be in accordance withacce

17、pted commercial procedures designed to produce forgingsfree from harmful surface discontinuities, roughness, excessivescale, fins, indications of overheating, burning, or other inju-rious conditions. The manufacturer may be required to certifythat furnaces used for all heating operations for forging

18、 andheat treating are controlled to minimize scaling and decarbur-ization.4.3 Heat treatment, if required, shall be in accordance withthe ordered Grade description.5. Chemical Requirements5.1 Depending on the forging size, type of heat treatment,and the requirements of the purchaser, the chemical co

19、mposi-tion shall be as specified by the purchaser. To assist in thischoice attention is drawn to the chemical requirements ofSpecification A576 for carbon steels, Specification A322 foralloy steels, and Specification A29/A29M for both carbon andalloy steels; however, the purchaser may wish to specif

20、y morerestrictive sulfur and phosphorous limits than are provided inthese specifications.5.2 For microalloyed forgings, forging stock to Specifica-tion A921/A921M may be used.5.3 Attention is drawn to the supplementary requirementsincluded in Specification A788/A788M regarding specialchemical requir

21、ements.5.4 The heat and product analyses requirements of Specifi-cation A788/A788M shall apply.6. Metallurgical Requirements6.1 Provision has been made, through the use of supplemen-tary requirements in Specification A788/A788M and thisspecification, for the purchaser to specify preferred grain flow

22、and limits for grain size as well as any microscopic examina-tion requirements.7. Dimensional Tolerances7.1 The purchaser may specify tolerances for impression dieforgings according to Appendix X1 or Appendix X2 asappropriate.8. Tensile Properties8.1 The material shall conform to the requirements fo

23、rtensile properties prescribed in Table 1 when tested in accor-dance with the latest issue of Test Methods and DefinitionsA370.8.2 The yield strength shall be determined by the offsetmethod, using an offset value of 0.2 % of the gauge length, orby the total extension under load method, using an exte

24、nsionvalue of 0.005 in./in. 0.005 mm/mm (0.5 %) for Grades ADand AE, 0.006 in./in. 0.006 mm/mm (0.6 %) for Grades AFand AG, and 0.007 in./in. 0.007 mm/mm (0.7 %) for GradeAH.8.3 Tests for acceptance shall be made after final heattreatment of the forgings.9. Number of Tests and Orientation9.1 Unless

25、otherwise specified, one tension test shall bemade for each heat of steel for each heat treat charge. Foruntreated forgings (Grade CA) no tension tests need be madeunless when specified in the purchase order, when one tensiontest shall represent each heat.9.2 For the purpose of tests of heat-treated

26、 forgings, thenecessary extra forgings shall be provided. When it is imprac-ticable to provide extra forgings for test purposes, test bars maybe made from the same billet or bar material, provided theyrepresent the maximum cross section of the forging, do notexceed the production forging reduction,

27、and are heat treatedwith the forgings they represent.9.3 Unless otherwise specified, the axis of the specimenshall be located at any point midway between the center andthe surface of solid forgings or at any point midway betweenthe inner and outer surfaces of the wall of hollow forgings, andshall be

28、 parallel to the direction of maximum metal flow.10. Test Specimen10.1 Location, size, and number of test specimens shall bespecified by the purchaser. Unless otherwise stated in thecontract or purchase order, test bars may be separately forgedor swaged from the same bars, billets, or blooms used in

29、manufacture of the forgings. The percentage reduction giventhe forged tests bars shall not be greater than the minimumamount of reduction given the forging itself. The test bars shallbe heat treated with the forgings they represent. The manufac-turer may elect to submit an extra forging in lieu of f

30、orged testbars.10.2 Unless otherwise specified, the axis of the specimenshall be located at any point midway between the center andthe surface of solid forgings or at any point midway betweenthe inner and outer surfaces of the wall of hollow forgings, andshall be parallel to the direction of maximum

31、 metal flow.10.3 The specimens shall be machined to the form anddimensions shown in Test Methods and Definitions A370 forthe standard or subsize round tension test specimens.11. Cleaning11.1 The forgings shall be furnished in a scale-free condi-tion. Unless otherwise specified, the manufacturer may

32、cleanby acid pickling, grit blasting, sand blasting, or other abrasivemethod.A521/A521M 06 (2011)212. Keywords12.1 alloy steel; carbon steel; closed die; forging tolerances;heat treated; impression die; Steel ForgingsSUPPLEMENTARY REQUIREMENTSOne or more of the following supplementary requirements s

33、hall apply only when specified by thepurchaser in the inquiry, contract, and order. Details of these supplementary requirements shall bespecified by purchaser.S1. Magnetic Particle TestS1.1 When magnetic particle inspection of forgings isrequired, the areas to be inspected, and the acceptance stan-d

34、ards shall be specified by purchaser.S1.2 Unless otherwise required by the purchaser, TestMethod A275/A275M shall be used.S2. Grain FlowS2.1 When a specific pattern of grain flow is required by thepurchaser, a sample forging shall be sectioned as specified. Thesection shall be ground and subjected t

35、o acid etching, using thetype of acid, temperature, and time of etching agreed upon toreveal flow lines. The section may be preserved using a coatingof mineral oil or clear lacquer.S2.2 Unless otherwise specified by the purchaser, MethodE381 or Test Method E340 shall be used.S3. Microscopic Examinat

36、ionS3.1 When microscopical examination is specified, the steelshall be inspected by utilizing samples cut from the undistortedTABLE 1 Tensile RequirementsGrade Solid Diameter or Thickness,in. mmBored Wall Thickness in. mm TensileStrength,min, ksiMPaYield Strength,min, ksiMPaElongationin 2 in. or50 m

37、m,min, %Reductionof Area,min, %Over Not Over Over Not OverAA (Annealed, normalized, or . 12 300 . . 80 550 50 345 24 40normalized, and tempered) 12 300 20 500 . . 80 550 50 345 22 38AB (Normalized and tempered) . 7 175 . 4 100 80 550 55 380 26 527 175 20 500 4 100 712 190 80 550 55 380 24 50AC (Norm

38、alized and tempered) . 7 175 . 4 100 90 620 60 415 22 447 175 20 500 4 100 712 190 90 620 58 400 21 42AD (Normalized, quenched, and . 7 175 . 312 85 96 655 70 485 20 50tempered) 7 175 10 250 312 85 5 125 90 620 65 450 20 50AE (Normalized, quenched, and . 7 175 312 85 105 725 80 550 20 50tempered) 7

39、175 10 250 312 85 5 125 100 690 75 520 19 5010 250 20 500 5 125 8 200 95 655 70 485 19 50AF (Normalized, quenched, and . 4 100 . 2 50 125 860 105 725 16 50tempered) 4 100 7 175 2 50 312 85 115 795 96 655 16 457 175 10 250 312 85 5 125 110 760 85 585 16 45AG (Normalized, quenched, and . 4 100 . 2 50

40、145 1000 120 830 15 45tempered) 4 100 7 175 2 50 312 85 140 965 115 795 14 407 175 10 250 312 85 5 125 135 930 110 760 13 40AH (Normalized, quenched, and . 4 100 . 2 50 170 1175 140 965 13 40tempered) 4 100 7 175 2 50 312 85 165 1140 135 930 12 357 175 10 250 312 85 5 125 160 1105 130 895 11 35CA (U

41、ntreated) No tensile requirement except as covered by 8.1CC (Annealed, normalized, or . 12 300 . . 60 415 30 205 25 36normalized, and tempered) 12 300 . . . 60 415 30 205 24 36CC1 (Annealed, normalized, or . 12 300 . . 66 455 33 230 23 36normalized and tempered) 12 300 20 500 . . 66 455 33 230 22 34

42、CE (Annealed, normalized, or . 8 200 . . 75 520 37 290 24 40normalized and tempered) 8 200 12 300 . . 75 520 37 290 22 3512 300 20 500 . . 75 520 37 290 20 3220 500 . . . 75 520 37 290 19 30CF (Normalized and tempered) . 8 200 . . 80 550 40 275 22 368 200 12 300 . . 80 550 40 275 21 3312 300 20 500

43、. . 80 550 40 275 20 31CF1 (Double normalized and tempered) . 8 200 . . 85 585 44 300 25 408 200 12 300 . . 83 570 43 295 23 3712 300 20 500 . . 83 570 43 295 22 35CG (Quenched, and tempered or . 4 100 . 2 50 90 620 55 380 20 39normalized, quenched and tempered) 8 200 7 175 2 50 312 85 85 585 50 345

44、 20 397 175 10 250 312 85 5 125 85 585 50 345 19 37. . 5 125 10 250 82 565 48 330 19 36A521/A521M 06 (2011)3portion of tension test specimens. Requirements for number ofmicroscopical tests, grain size, cleanliness, or microstructureshall be specified by purchaser.S3.2 For grain size determination Te

45、st Methods E112 or thegrain size provisions of SpecificationA29/A29M shall be used,and the grain size requirement shall be as specified by thepurchaser.S3.3 For non-metallic inclusion rating Test Methods E45shall be used, and the acceptance limits shall be specified bythe purchaser.S3.4 Guide E3 and

46、 Practice E407 shall be used for thedetermination of the microstructure. Acceptance criteria shallbe specified by the purchaser.S4. Impact TestS4.1 Impact testing in accordance with Test Methods A370shall be done on specimens taken adjacent to the tension test.The test temperature and acceptance cri

47、teria shall be asspecified by the purchaser.S5. Ultrasonic ExaminationS5.1 Ultrasonic examination shall be conducted in accor-dance with Practice A388/A388M unless otherwise specifiedby the purchaser who will also specify the acceptance criteria.S6. Radiographic TestsS6.1 When radiographic tests are

48、 required, the number oftests, location, and ASTM standards of acceptance shall bespecified by the purchaser. Reference shall be made to GuideE94.S7. Brinell HardnessS7.1 When hardness is required, Brinell hardness tests takenin accordance with Test Methods A370 shall be made ofsample forgings from each furnace charge of heat-treatedforgings, or from an 8 h shift for continuous furnaces. Thenumber of samples per charge and location of the hardnessimpressions shall be specified by the purchaser.S7.2 The ac