ASTM A507-2006 Standard Specification for Drawing Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧拉丝合金钢片材和带材的标准规范》.pdf

《ASTM A507-2006 Standard Specification for Drawing Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧拉丝合金钢片材和带材的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A507-2006 Standard Specification for Drawing Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧拉丝合金钢片材和带材的标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 507 06Standard Specification forDrawing Alloy Steel, Sheet and Strip, Hot-Rolled and Cold-Rolled1This standard is issued under the fixed designation A 507; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of

2、last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification covers hot-rolle

3、d and cold-rolleddrawing alloy-steel sheet and strip. Material of this quality isproduced principally for applications involving severe coldplastic deformation such as deep drawn or severely formedparts. This steel is produced by a closely controlled steel-making practice designed to assure internal

4、 soundness, relativeuniformity of chemical composition, and freedom from injuri-ous imperfections.1.2 The material covered by this specification may befurnished in several conditions, heat treatments, surface fin-ishes, and edges, as specified herein, in coils or cut lengths.2. Referenced Documents2

5、.1 ASTM Standards:2A 505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA 941 Terminology Relating to Steel, Stainless Steel, Re-lated Alloys, and Ferroalloys3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 capable ofas used

6、 in this specification, means thattests need not be performed. However, if application by thepurchaser establishes that the material does not meet therequirements, the material shall be subject to rejection.3.1.2 drawing alloy steelalloy-steel sheet and strip in-tended for applications involving sev

7、ere cold plastic deforma-tion such as deep drawn or severely formed parts.3.1.3 standard steelssteel chemical compositions definedas “standard” by the Society of Automotive Engineers (SAE).See Table 1.3.1.4 steels other than standardsteel chemical composi-tions other than those defined as “standard,

8、” and furnished tothe composition limits shown in Table 2.4. General Requirements and Ordering Information4.1 Material supplied to this specification shall conform toSpecification A 505, which includes the general requirementsand establishes the rules for the ordering information thatshould be compl

9、ied with when purchasing material to thisspecification.4.2 In addition to the Ordering Information required bySpecification A 505, the following shall also be included:4.2.1 Mechanical properties, if required (show propertiesdesired, which must be consistent with the grade and heattreatment),4.2.2 S

10、urface finish, if other than that normally furnished(see Section 10), and4.2.3 Application, or end use (identification of the part to bemade).5. Manufacture5.1 RollingThe material shall be furnished either hot-rolled or cold-rolled, as specified on the order.5.2 Heat TreatmentUnless otherwise specif

11、ied on theorder, the material shall be furnished spheroidize-annealed.(See Terminology A 941 for heat treatment terms.)5.2.1 If the material is to be heat treated by other than theproducer, the order shall so state. The material may be orderedin the as-rolled condition, in such cases.6. Chemical Req

12、uirements Chemical Requirements6.1 The heat (cast) analysis shall conform to the require-ments for the grade specified on the order.6.1.1 Standard steels listed in Table 1 are those commonlyproduced for drawing alloy-steel sheet and strip.6.1.2 Nonstandard steel grades may be specified, using theran

13、ges and limits shown in Table 2.7. Metallurgical Structure7.1 Microstructure:1This specification is under the jurisdiction of ASTM Committee A01 on Steel,Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved March

14、1, 2006. Published March 2006. Originallyapproved in 1964. Last previous edition approved in 2005 as A 507 05.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the st

15、andards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.7.1.1 RequirementsAt least 75 % of the carbide micro-structure shall b

16、e of the globular type.7.1.2 Number of TestsThe number of tests shall be inaccordance with the producers standard quality control pro-cedures. A specific number of tests is not required, but thematerial shall be produced by manufacturing practices estab-lished to assure compliance with the specified

17、 requirements.The material shall be subjected to mill tests and inspectionprocedures to assure such compliance. For government pro-curement, mill tests and inspection procedures utilized to showconformance to the microstructure requirements shall be madeavailable on request.8. Mechanical Requirement

18、s8.1 Tension and Hardness Tests:8.1.1 RequirementsWhen tension tests or hardness tests,or both are specified on the order, the test results shall conformto the requirements specified on the order. Yield strength,tensile strength, and elongation requirements may be specified.The tensile properties wi

19、ll vary depending on the chemicalcomposition, condition, and heat treatment. Producers arefrequently consulted as to grade, resultant mechanical proper-ties, recommended heat treatment, and other informationneeded to establish the property parameters to meet end userequirements. Rockwell hardness re

20、quirements may be speci-fied, providing the requirements are compatible with thetension test requirements.8.1.2 Number of TestsTwo tension tests and two hardnesstests, when specified, shall be taken at random from each heat(cast) and heat treatment lot.TABLE 1 Standard Steels Commonly Produced for D

21、rawing Alloy-Steel Sheet and StripUNSDesignationSAE No.Chemical Composition Ranges and Limits, % (Heat Analysis)ACMnPSSiANi Cr Mo V. . . E3310 0.080.13 0.450.60 0.025 0.025 0.150.30 3.253.75 1.401.75 . . . . . .G40120 4012 0.090.14 0.751.00 0.025 0.025 0.150.30 . . . . . . 0.150.25 . . .G41180 4118

22、0.180.23 0.700.90 0.025 0.025 0.150.30 . . . 0.400.60 0.080.15 . . .G41300 4130 0.280.33 0.400.60 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41350 4135 0.330.38 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41370 4137 0.350.40 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.

23、25 . . .G41400 4140 0.380.43 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41420 4142 0.400.45 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41450 4145 0.430.48 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41470 4147 0.450.50 0.751.00 0.025 0.025 0.150.30 .

24、 . . 0.801.10 0.150.25 . . .G41500 4150 0.480.53 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G43200 4320 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 0.400.60 0.200.30 . . .G43400 4340 0.380.43 0.600.80 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .G43406 E4340 0.380.43 0.65

25、0.85 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .G45200 4520 0.180.23 0.450.65 0.025 0.025 0.150.30 . . . . . . 0.450.60 . . .G46150 4615 0.130.18 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .G46200 4620 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .G4718

26、0 4718 0.160.21 0.700.90 0.025 0.025 0.150.30 0.901.20 0.350.55 0.300.40 . . .G48150 4815 0.130.18 0.400.60 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .G48200 4820 0.180.23 0.500.70 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .G50150 5015 0.120.17 0.300.50 0.025 0.025 0.150.30 . . . 0.300

27、.50 . . . . . .G50460 5046 0.430.50 0.751.00 0.025 0.025 0.150.30 . . . 0.200.35 . . . . . .G51150 5115 0.130.18 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51200 5120 0.170.22 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51300 5130 0.280.33 0.700.90 0.025 0.025 0.150.30 . .

28、 . 0.801.10 . . . . . .G5132 5132 0.300.35 0.600.90 0.025 0.025 0.150.30 . . . 0.751.00 . . . . . .G51400 5140 0.380.43 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51500 5150 0.480.53 0.790.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51600 5160 0.550.65 0.751.00 0.025 0.025 0.150

29、.30 . . . 0.700.90 . . . . . .G15116 E51100 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 0.901.15 . . . . . .G15216 E52100 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 1.301.60 . . . . . .G61500 6150 0.480.53 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . 0.15 minG61580 6158 0.550.62 0.701.10 0.

30、025 0.015 0.150.30 . . . 0.901.20 . . . 0.100.20G86150 8615 0.130.18 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86170 8617 0.150.20 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86200 8620 0.180.23 0.700.90 0.035 0.035 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86

31、300 8630 0.280.33 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86400 8640 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86420 8642 0.400.45 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86450 8645 0.430.48 0.751.00 0.025 0.025 0.150.30 0.4

32、00.70 0.400.60 0.150.25 . . .G86500 8650 0.480.53 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86550 8655 0.500.60 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86600 8660 0.550.65 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G87200 8720 0.180.23 0

33、.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G87350 8735 0.330.38 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G87400 8740 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G92600 9260 0.550.65 0.701.00 0.025 0.025 1.802.20 . . . . . . . . . . .

34、.G92620 9262 0.550.65 0.751.00 0.025 0.025 1.802.20 . . . 0.250.40 . . . . . . . . E9310 0.080.13 0.450.65 0.025 0.025 0.200.35 3.003.50 1.001.40 0.080.15 . . .AThe chemical ranges and limits shown are subject to product analysis tolerances. See Specification A 505.A5070629. Other Tests and Requirem

35、ents9.1 End Use Suitability:9.1.1 When steel is to be furnished in the spheroidize-annealed condition, the user and producer shall review anypart(s) to be produced to reach adequate agreement on capa-bility to produce said parts.9.1.2 Material in the spheroidize-annealed condition gener-ally work ha

36、rdens and may require stress-relief-annealingbetween drawing operations.10. Workmanship, Finish, and Appearance10.1 Surface Finish:10.1.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial shall be furnished descaled and oiled. When required,the material may be specified to be furnished not oi

37、led.10.1.2 Cold-RolledUnless otherwise specified, cold-rolled material shall be furnished with a commercial dull mattefinish and shall be oiled. When required, the material may bespecified to be furnished not oiled.10.2 Edges:10.2.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial shall be f

38、urnished with Mill Edge. The material maybe specified to have other types of edges, in accordance withSpecification A 505.10.2.2 Cold-RolledUnless otherwise specified, cold-rolled sheet shall be furnished with Cut Edge and cold-rolledstrip shall be furnished with No. 3 Edge. The material may bespeci

39、fied to have other types of edges, in accordance withSpecification A 505.11. Keywords11.1 alloy steel with improved formability; cold-rolled alloysteel; deep drawn alloy steel; drawing alloy steel sheet;drawing alloy steel strip; forming alloy steel; hot-rolled alloysteel; special soundness alloy st

40、eelSUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue, A 507 05,that may impact the use of this standard. (Approved March 1, 2006.)(1) Revised 9.1.1 and corrected a typographical error in 9.1.2.TABLE 2 Heat (Cast) Analysis Ranges for

41、 Other Than StandardSteel Alloy Sheet and StripElementWhen Maximum ofSpecified Element Is, %Range orLimit, %Carbon To 0.55 incl 0.05Over 0.55 to 0.70 incl 0.08Over 0.70 to 0.80 incl 0.10Over 0.80 to 0.95 incl 0.12Over 0.95 to 1.35 incl 0.13Manganese To 0.60 incl 0.20Over 0.60 to 0.90 incl 0.20Over 0

42、.90 to 1.05 incl 0.25Over 1.05 to 1.90 incl 0.30Over 1.90 to 2.10 incl 0.40Phosphorus . . . 0.025 maxSulfur . . . 0.025 maxSilicon To 0.15 incl 0.08Over 0.15 to 0.20 incl 0.10Over 0.20 to 0.40 incl 0.15Over 0.40 to 0.60 incl 0.20Over 0.60 to 1.00 incl 0.30Over 1.00 to 2.20 incl 0.40Copper To 0.60 in

43、clOver 0.60 to 1.50 inclOver 1.50 to 2.00 incl0.200.300.35Nickel To 0.50 incl 0.20Over 0.50 to 1.50 incl 0.30Over 1.50 to 2.00 incl 0.35Over 2.00 to 3.00 incl 0.40Over 3.00 to 5.30 incl 0.50Over 5.30 to 10.00 incl 1.00Chromium To 0.40 incl 0.15Over 0.40 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Ov

44、er 1.05 to 1.60 incl 0.30Over 1.60 to 1.75 incl 0.35Over 1.75 to 2.10 incl 0.40Over 2.10 to 3.99 incl 0.50Molybdenum To 0.10 incl 0.05Over 0.10 to 0.20 incl 0.07Over 0.20 to 0.50 incl 0.10Over 0.50 to 0.80 incl 0.15Over 0.80 to 1.15 incl 0.20Vanadium To 0.25 inclOver 0.25 to 0.50 incl0.050.10A507063

45、Committee A01 has identified the location of selected changes to this standard since the last issue, A 507 04, that mayimpact the use of this standard. (Approved Dec. 1, 2005.)(1) Added all the grades in Table A1.1 to Table 1.(2) Eliminated Table A1.1 and the Annex section.(3) Added new grade 6158 t

46、o Table 1.(4) Revised the phosphorus and sulfur requirements to0.025 % maximum for all grades in Table 1 except grade 6158.(5) Revised the phosphorus and sulfur requirements to0.025 % maximum in Table 2.(6) In Section 3.1.3, deleted reference to Table A1.1.(7) Revised the wording in Section 6.1.1.(8

47、) Deleted Section 6.1.2 and renumbered Section 6.1.3 to6.1.2.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such p

48、atent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited e

49、ither for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake