《ASTM A506-2005 Standard Specification for Alloy and Structural Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧合金钢和结构合金钢薄板材与带材的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM A506-2005 Standard Specification for Alloy and Structural Alloy Steel Sheet and Strip Hot-Rolled and Cold-Rolled《热轧和冷轧合金钢和结构合金钢薄板材与带材的标准规范》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A 506 05Standard Specification forAlloy and Structural Alloy Steel, Sheet and Strip, Hot-Rolledand Cold-Rolled1This standard is issued under the fixed designation A 506; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision,

2、the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope*1.1 This specification cove

3、rs hot-rolled and cold-rolledalloy and structural alloy-steel sheet and strip. Alloy steel isfurnished to chemical composition requirements and is in-tended primarily for general or miscellaneous use wherebending and moderate forming is a requirement. Structuralalloy steel is furnished to chemical c

4、omposition requirementsand to specific mechanical property requirements which mayinclude tension tests, hardness tests, or other commonlyaccepted mechanical tests.1.2 If material of a higher degree of uniformity of internalsoundness and freedom from surface imperfections is required,reference should

5、 be made to Specification A 507.1.3 Alloy and structural alloy-steel sheet and strip are notproduced to internal cleanliness requirements. Normally sur-face imperfections are not objectionable, and a good finish isnot a prime requirement.1.4 The formability of structural alloy steel decreases within

6、creasing yield strength or hardness. Therefore, product de-sign in relation to the mechanical properties of the grade usedmust be considered.1.5 The material covered by this specification may befurnished in several conditions: heat treatments, surface con-ditions, and edges, as specified herein, in

7、coils or cut lengths.1.6 The values stated in inch-pound units are to be regardedas the standard. SI units are provided for information only.2. Referenced Documents2.1 ASTM Standards:2A 505 Specification for Steel, Sheet and Strip, Alloy, Hot-Rolled and Cold-Rolled, General Requirements forA 507 Spe

8、cification for Drawing Alloy Steel, Sheet andStrip, Hot-Rolled and Cold-Rolled3. Terminology3.1 Definitions of Terms Specific to This Standard:3.1.1 alloy steelalloy-steel sheet and strip furnished tochemical composition requirements and intended for general ormiscellaneous applications where normal

9、 surface imperfec-tions are not objectionable and a good finish is not the primerequirement.3.1.2 SAESociety of Automotive Engineers.3.1.3 standard steelssteel chemical compositions definedas “standard” by SAE, shown in Table 1.3.1.4 steels other than standardsteel chemical composi-tions other than

10、those defined as “standard,” and furnished tothe composition limits shown in Table 2.3.1.5 structural alloy steelalloy-steel sheet and stripmeeting the requirements of regular quality and also producedto specific mechanical property requirements.4. General Requirements and Ordering Information4.1 Ma

11、terial supplied to this specification shall conform toSpecification A 505, which includes the general requirementsand establishes the rules for the ordering information thatshould be complied with when purchasing material to thisspecification.4.2 In addition to the ordering information required bySp

12、ecification A 505, the following shall also be included:4.2.1 Mechanical properties required for structural quality,when applicable,4.2.2 Surface finish, if other than standard (see 8.1), and4.2.3 Surface treatment, if other than standard (see 8.2).5. Materials and Manufacture5.1 RollingThe material

13、 shall be furnished either hot-rolled or cold-rolled, as specified on the order.5.2 Heat Treatment:5.2.1 Hot-RolledHot-rolled material shall be furnished inone of the following conditions, as specified on the order:5.2.1.1 As-rolled,5.2.1.2 Annealed,1This specification is under the jurisdiction of A

14、STM Committee A01 on Steel,Stainless Steel and Related Alloys, and is the direct responsibility of SubcommitteeA01.19 on Steel Sheet and Strip.Current edition approved Dec. 1, 2005. Published December 2005. Originallyapproved in 1964. Last previous edition approved in 2004 as A 506 04.2For reference

15、d ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.1*A Summary of Changes section appears at the end of this standard.Copyrigh

16、t ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5.2.1.3 Normalized, or5.2.1.4 Normalized-and-tempered.5.2.2 Cold-RolledCold-rolled material shall be fully an-nealed after cold-rolling. (Temper, skin, or roller leveling forthe control of flatn

17、ess, which does not significantly affect theproperties, may be performed after annealing.)6. Chemical Requirements Chemical Requirements6.1 The heat analysis shall conform to the requirements forthe grade specified on the order.6.1.1 Alloy SteelThe grade shall be specified in accor-dance with either

18、 6.1.1.1 or 6.1.1.2.6.1.1.1 Standard steels listed in Table 1 are those commonlyproduced for alloy steel sheet and strip.6.1.1.2 Nonstandard steel grades may be specified using theranges and limits shown in Table 2.6.1.2 Structural Alloy SteelThe grade shall be specified asoutlined in 6.1.1. However

19、, since different mechanical proper-ties may be expected for each of the many chemical compo-sitions and conditions (heat treatment) that may be specified,consideration must be given to these factors in selecting thechemical composition to be specified.7. Mechanical Requirements7.1 Alloy SteelMechan

20、ical tests are not applicable toregular quality alloy steel sheet and strip.7.2 Structural Alloy Steel:7.2.1 Tension Tests:TABLE 1 Standard Steels Commonly Produced for Alloy-Steel Sheet and StripUNSDesignationSAENo.Chemical Composition Ranges and Limits, % (Heat Analysis)ACMn PSSiBNi Cr Mo V. . . E

21、3310 0.080.13 0.450.60 0.025 0.025 0.150.30 3.253.75 1.401.75 . . . . . .G40120 4012 0.090.14 0.751.00 0.025 0.025 0.150.30 . . . . . . 0.150.25 . . .G41180 4118 0.180.23 0.700.90 0.025 0.025 0.150.30 . . . 0.400.60 0.080.15 . . .G41300 4130 0.280.33 0.400.60 0.025 0.025 0.150.30 . . . 0.801.10 0.15

22、0.25 . . .G41350 4135 0.330.38 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41370 4137 0.350.40 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41400 4140 0.380.43 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41420 4142 0.400.45 0.751.00 0.025 0.025 0.150.30

23、 . . . 0.801.10 0.150.25 . . .G41450 4145 0.430.48 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41470 4147 0.450.50 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G41500 4150 0.480.53 0.751.00 0.025 0.025 0.150.30 . . . 0.801.10 0.150.25 . . .G43200 4320 0.170.22 0.450.65

24、0.025 0.025 0.150.30 1.652.00 0.400.60 0.200.30 . . .G43400 4340 0.380.43 0.600.80 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .G43406 E4340 0.380.43 0.650.85 0.025 0.025 0.150.30 1.652.00 0.700.90 0.200.30 . . .G45200 4520 0.180.23 0.450.65 0.025 0.025 0.150.30 . . . . . . 0.450.60 . . .G46

25、150 4615 0.130.18 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .G46200 4620 0.170.22 0.450.65 0.025 0.025 0.150.30 1.652.00 . . . 0.200.30 . . .G47180 4718 0.160.21 0.700.90 0.025 0.025 0.150.30 0.901.20 0.300.50 0.300.40 . . .G48150 4815 0.130.18 0.400.60 0.025 0.025 0.150.30 3.253.75

26、. . . 0.200.30 . . .G48200 4820 0.180.23 0.500.70 0.025 0.025 0.150.30 3.253.75 . . . 0.200.30 . . .G50150 5015 0.120.17 0.300.50 0.025 0.025 0.150.30 . . . 0.300.50 . . . . . .G50460 5046 0.430.50 0.751.00 0.025 0.025 0.150.30 . . . 0.200.35 . . . . . .G51150 5115 0.130.18 0.700.90 0.025 0.025 0.15

27、0.30 . . . 0.700.90 . . . . . .G51200 5120 0.170.22 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51300 5130 0.280.33 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . . . .G5132 5132 0.300.35 0.600.90 0.025 0.025 0.150.30 . . . 0.751.00 . . . . . .G51400 5140 0.380.43 0.700.90 0.025 0.0

28、25 0.150.30 . . . 0.700.90 . . . . . .G51500 5150 0.480.53 0.700.90 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G51600 5160 0.550.65 0.751.00 0.025 0.025 0.150.30 . . . 0.700.90 . . . . . .G15116 E51100 0.951.10 0.250.45 0.025 0.025 0.150.30 . . . 0.901.15 . . . . . .G15216 E52100 0.951.10 0.250.

29、45 0.025 0.025 0.150.30 . . . 1.301.60 . . . . . .G61500 6150 0.480.53 0.700.90 0.025 0.025 0.150.30 . . . 0.801.10 . . . 0.15 minG61580 6158 0.550.62 0.701.10 0.025 0.025 0.150.30 . . . 0.901.20 . . . 0.100.20G86150 8615 0.130.18 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86170

30、8617 0.150.20 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86200 8620 0.180.23 0.700.90 0.035 0.035 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86300 8630 0.280.33 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86400 8640 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.7

31、0 0.400.60 0.150.25 . . .G86420 8642 0.400.45 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86450 8645 0.430.48 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86500 8650 0.480.53 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86550 8655 0.500.60 0.751

32、00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G86600 8660 0.550.65 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.150.25 . . .G87200 8720 0.180.23 0.700.90 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G87350 8735 0.330.38 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30

33、. . .G87400 8740 0.380.43 0.751.00 0.025 0.025 0.150.30 0.400.70 0.400.60 0.200.30 . . .G92600 9260 0.550.65 0.701.00 0.025 0.025 1.802.20 . . . . . . . . . . . .G92620 9262 0.550.65 0.751.00 0.025 0.025 1.802.20 . . . 0.250.40 . . . . . . . . E9310 0.080.13 0.450.65 0.025 0.025 0.200.35 3.003.50 1.

34、001.40 0.080.15 . . .AThe chemical ranges and limits shown are subject to product analysis tolerances. See Specification A 505.BOther silicon ranges are available. Consult the producer.A5060527.2.1.1 RequirementsThe tension test requirements shallconform to the requirements specified on the order. Y

35、ieldstrength, tensile strength, and elongation requirements may bespecified. The tensile properties will vary depending on thechemical composition, condition, and heat treatment. Produc-ers are frequently consulted as to grade, resultant mechanicalproperties, recommended heat treatment, and other in

36、formationneeded to establish the property parameters to meet end userequirements. Rockwell hardness requirements may be speci-fied, providing the requirements are compatible with thetension test requirements.7.2.1.2 Number of TestsTwo tension tests and two hard-ness tests, when specified, shall be m

37、ade from couponsobtained from each heat (cast) and heat treatment lot.7.2.2 Bend Tests:7.2.2.1 RequirementsMaterial in the annealed, normal-ized, or normalized-and-tempered condition shall be capable ofmeeting the longitudinal bend test requirements of Table 3.7.2.2.2 Number of TestsTwo bend tests s

38、hall be made onspecimens representative of each lot. A lot shall consist ofmaterial from the same heat (cast), of the same condition andfinish, the same nominal thickness, and subjected to the sameheat treatment.7.2.2.3 Bend test specimens shall be at least34 in. (19 mm)wide, or the same width of th

39、e material if it is less than34 in.(19 mm) wide. The length shall be sufficient to permit bendingto the angle specified.7.2.2.4 The edges of bend test specimens shall be practicallyfree of burrs. Filing or machining to remove burrs is permis-sible.8. Workmanship, Finish, and Appearance8.1 Surface Fi

40、nish:8.1.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial shall be furnished without removing the hot-rolledoxide or scale. (That is, with the as-rolled or as-heat-treatedscale.) The material may be specified to be descaled.8.1.2 Cold-RolledUnless otherwise specified, cold-rolledmaterial s

41、hall be furnished with a commercial dull matte finish.8.2 Oiling:8.2.1 Hot-RolledUnless otherwise specified, as-rolled oras-heat-treated material shall be furnished without oiling, anddescaled material shall be oiled. Descaled material may bespecified to be furnished dry, without oiling.8.2.2 Cold-R

42、olledUnless otherwise specified, cold-rolledmaterial shall be furnished oiled. Cold-rolled material may bespecified to be furnished dry, without oiling.8.3 Edges:8.3.1 Hot-RolledUnless otherwise specified, hot-rolledmaterial shall be furnished with Mill Edge. The material maybe specified to have oth

43、er types of edges, in accordance withSpecification A 505.8.3.2 Cold-RolledUnless otherwise specified, cold-rolledsheet shall be furnished with Cut Edge and cold-rolled stripshall be furnished with No. 3 Edge. The material may bespecified to have other types of edges, in accordance withSpecification

44、A 505.9. Keywords9.1 alloy steel sheet; alloy steel strip; cold-rolled alloy steel;hot-rolled alloy steel; standard alloy steel; structural alloy steelTABLE 2 Heat (Cast) Analysis Ranges for Other than StandardSteel Alloy Sheet and StripElement When Maximum ofSpecified Element Is, %Range orLimit, %C

45、arbon To 0.55 incl 0.05Over 0.55 to 0.70 incl 0.08Over 0.70 to 0.80 incl 0.10Over 0.80 to 0.95 incl 0.12Over 0.95 to 1.35 incl 0.13Manganese To 0.60 incl 0.20Over 0.60 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.90 incl 0.30Over 1.90 to 2.10 incl 0.40Phosphorus . . . 0.025 maxSulfur .

46、 . . 0.025 maxSilicon To 0.15 incl 0.08Over 0.15 to 0.20 incl 0.10Over 0.20 to 0.40 incl 0.15Over 0.40 to 0.60 incl 0.20Over 0.60 to 1.00 incl 0.30Over 1.00 to 2.20 incl 0.40Copper To 0.60 inclOver 0.60 to 1.50 inclOver 1.50 to 2.00 incl0.200.300.35Nickel To 0.50 incl 0.20Over 0.50 to 1.50 incl 0.30

47、Over 1.50 to 2.00 incl 0.35Over 2.00 to 3.00 incl 0.40Over 3.00 to 5.30 incl 0.50Over 5.30 to 10.00 incl 1.00Chromium To 0.40 incl 0.15Over 0.40 to 0.90 incl 0.20Over 0.90 to 1.05 incl 0.25Over 1.05 to 1.60 incl 0.30Over 1.60 to 1.75 incl 0.35Over 1.75 to 2.10 incl 0.40Over 2.10 to 3.99 incl 0.50Mol

48、ybdenum To 0.10 incl 0.05Over 0.10 to 0.20 incl 0.07Over 0.20 to 0.50 incl 0.10Over 0.50 to 0.80 incl 0.15Over 0.80 to 1.15 incl 0.20Vanadium To 0.25 inclOver 0.25 to 0.50 incl0.050.10A506053SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the la

49、st issue, A 506 04,that may impact the use of this standard. (Approved Dec. 1, 2005.)(1) Added all the grades in Table A1.1 to Table 1.(2) Eliminated Table A1.1 and the Annex section.(3) Added new grade 6158 to Table 1.(4) Revised the phosphorus and sulfur requirements to0.025 % maximum for all grades in Table 1, exc