ANSI T 465 SP-2006 Static creasing of paper for water vapor transmission tests.pdf

《ANSI T 465 SP-2006 Static creasing of paper for water vapor transmission tests.pdf》由会员分享，可在线阅读，更多相关《ANSI T 465 SP-2006 Static creasing of paper for water vapor transmission tests.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、T 465 sp-10 SUGGESTED METHOD 1944 REVISED 1971 OFFICIAL STANDARD 1977 CLASSICAL METHOD 1985 STANDARD PRACTICE 1995 REVISED 2001 REVISED 2006 REAFFFIRMED 2010 2010 TAPPI The information and data contained in this document were prepared by a technical committee of the Association. The committee and th

2、e Association assume no liability or responsibility in connection with the use of such information or data, including but not limited to any liability under patent, copyright, or trade secret laws. The user is responsible for determining that this document is the most recent edition published. Appro

3、ved by the Standard Specific Interest Group for this Test Method TAPPI CAUTION: This Test Method may include safety precautions which are believed to be appropriate at the time of publication of the method. The intent of these is to alert the user of the method to safety issues related to such use.

4、The user is responsible for determining that the safety precautions are complete and are appropriate to their use of the method, and for ensuring that suitable safety practices have not changed since publication of the method. This method may require the use, disposal, or both, of chemicals which ma

5、y present serious health hazards to humans. Procedures for the handling of such substances are set forth on Material Safety Data Sheets which must be developed by all manufacturers and importers of potentially hazardous chemicals and maintained by all distributors of potentially hazardous chemicals.

6、 Prior to the use of this method, the user must determine whether any of the chemicals to be used or disposed of are potentially hazardous and, if so, must follow strictly the procedures specified by both the manufacturer, as well as local, state, and federal authorities for safe use and disposal of

7、 these chemicals. Static creasing of paper for water vapor transmission tests 1. Scope 1.1 This standard practice is used for the creasing of paper and other thin sheet materials to provide reproducibly creased specimens for testing water vapor transmission. It is not applicable to paperboard. 1.2 T

8、his is a standard practice for static creasing; for kinetic creasing see TAPPI T 512 “Creasing of Flexible Packaging Material Paper Specimens for Testing.” 1.3 This procedure can be used with water vapor transmission tests TAPPI T 448 “Water vapor transmission rate of sheet materials at standard tem

9、perature and humidity”, TAPPI T 464 “Gravimetric determination of water vapor transmission rate of sheet materials at high temperature and humidity,” and TAPPI T 523 “Dynamic measurement of water vapor transfer through sheet materials.” 2. Summary The procedure described is for creasing square speci

10、mens which will yield test areas from 60 to 140 cm2(about 10-20 in.2), although it may be adapted to other areas. When performed as specified, the creasing mass is 100 g/mm of crease (5.6 lb/in.), and the ratio of the effective area of the test specimen in square centimeters to the total length of c

11、reases in centimeters is as 1 is to 1.05-1.10 (in in. as 2.5 is to 2.67-2.75). 3. Significance This procedure does not necessarily reproduce commercial creasing which is imparted kinetically, but it does provide a controlled means to assess the possible effect of creasing on the barrier properties o

12、f the material. T 465 sp-10 Static creasing of paper for water / 2 vapor transmission tests 4. Apparatus 4.1 Creasing surface, consisting of a flat, smooth, rectangular plate, e.g., a piece of machined metal, steel, about 6-13 mm (about 0.25-0.5 in.) thick, whose width is at least 25 mm (1 in.) grea

13、ter than the length of the specimens to be creased. 4.2 Creasing platen, consisting of a flat, smooth, square, or rectangular metal plate (steel) whose length is about 13 mm greater than that of the specimens to be creased. Its mass in kilograms is one-tenth the specimen length in millimeters. For c

14、onvenience, a handle for tilting the platen should be provided, its mass to be included as part of the platen mass. NOTE 1: If a hinge is used to connect the platen and the creasing surface, it must be carefully designed to prevent binding, because binding will reduce the effective weight of the pla

15、ten. It is simpler to fix a low back-stop to the creasing surface to aid in positioning the platen. 4.3 Ruler or scale marked in 1 mm increments. 4.4 Flat strip of wood, such as a ruler, to give the specimen a very light preliminary crease. 5. Test specimen 5.1 Obtain a sample of the paper in accord

16、ance with TAPPI T 400 “Sampling and Accepting a Single Lot of Paper, Paperboard, Containerboard, or Related Product.” 5.2 For each test, cut a square specimen with the edges parallel to the principal directions of the paper and large enough that one specimen for the water vapor transmission test can

17、 be obtained from it. 6. Procedure 6.1 Crease the specimen, after conditioning it in an atmosphere in accordance with TAPPI T 402 “Standard Conditioning and Testing Atmospheres for Paper, Board, Pulp Handsheets, and Related Products,” as follows: 6.2 With a pencil lightly mark a series of lines para

18、llel to one edge of a specimen and spaced 19 mm 1 mm (0.75 in.) apart, arranging the lines so one goes through the center of the effective test area. NOTE 2: If a large number of specimens are to be prepared, a jig or template will greatly facilitate this marking. 6.3 Starting with the first mark ne

19、xt to one edge, fold the specimen on this mark parallel to this edge and lightly crease the fold by gently pressing the ruler upon it. 6.4 Tilt the creasing platen and slip the lightly creased specimen under it and parallel to its edge so that the crease lies under the center of gravity of the plate

20、n. Lower the platen very gently to rest on the crease, leave for 12 2 s, then raise the platen and remove the specimen. 6.5 Unfold the specimen so that the valley of the crease is up, flatten the crease by pressing it gently with the ruler, and make another lightly creased fold at the next adjacent

21、mark along the edge and parallel to the first crease, but make this fold about the opposite side of the sheet. 6.6 Repeat 6.4 and 6.5 until creases have been made through all the marks on one edge of the specimen. The specimen now has zig-zag folds and looks like accordian pleating. 6.7 Repeat 6.2,

22、6.3, 6.4, 6.5, and 6.6 along an adjacent edge to produce a similar set of creases intersecting the first set at right angles. NOTE 3: While a spacing of about 19 mm will give substantially the required ratio of length of crease to area for the range of specimen sizes mentioned, the exact spacing may

23、 be found by geometrical construction using the “trial and error” method. 6.8 Obtain a specimen of the desired size for the water vapor apparatus from the creased specimen so that the center of the effective test area coincides with the center of the crossed crease lines. 6.9 The specimens are now r

24、eady to be tested. 3 / Static creasing of paper for water T 465 sp-10 vapor transmission tests 7. Report No report is required for this standard practice. 8. Precision A precision statement is not applicable for this standard practice. 9. Keywords Paper, Static tests, Creasing, Water vapor permeabil

25、ity, Mass transfer. 10. Additional information 10.1 Effective date of issue: October 6, 2010. 10.2 This method was issued in 1944 as a Suggested Method and became an Official Standard in 1977. It became a Classical Method in 1985. In 1995, it was revised under the new test method guidelines as a Sta

26、ndard Practice. 10.3 A precision statement is not applicable. The result of creasing is measured by the final results as obtained under other methods (TAPPI T 464 “Gravimetric Determination of Water Vapor Transmission Rate of Sheet Materials at High Temperature and Humidity” and TAPPI T 523 “Dynamic

27、 Measurement of Water Vapor Transfer Through Sheet Materials”) for water vapor transmission. 10.4 Steel is the required material for the plates, because the hardness of alternative surfaces making the crease would have a marked effect on the severity of the crease. 10.5 Related methods: ISO Standard 2528; PAPTAC D.15; and SCAN P22. Your comments and suggestions on this procedure are earnestly requested and should be sent to the TAPPI Standards Department. g