ASTM C1396C1396M-17 Standard Specification for Gypsum Board.pdf

《ASTM C1396C1396M-17 Standard Specification for Gypsum Board.pdf》由会员分享，可在线阅读，更多相关《ASTM C1396C1396M-17 Standard Specification for Gypsum Board.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: C1396/C1396M 17Standard Specification forGypsum Board1This standard is issued under the fixed designation C1396/C1396M; the number immediately following the designation indicates theyear of original adoption or, in the case of revision, the year of last revision. A number in parentheses

2、 indicates the year of lastreapproval. A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers the gypsum boards describedin 1.1.1 1.1.9.NOTE 1Specifications C840, C841, C844 and C1280 contain appli-cation procedures for gyp

3、sum board.1.1.1 Gypsum wallboard, designed for use on walls,ceilings, or partitions and that affords a surface suitable toreceive decoration.1.1.2 Predecorated gypsum board, designed for use as thefinished surfacing for walls, ceilings, or partitions.1.1.3 Gypsum backing board, coreboard, and shaftl

4、inerboard, designed for use as a base in multilayer systems or as agypsum stud or core in semisolid or solid gypsum boardpartitions, or in shaft wall assemblies.NOTE 2The terms backing board, coreboard, and shaftliner boardrefer to different end uses. The term gypsum backing board, as used in thissp

5、ecification, shall include gypsum coreboard and gypsum shaftlinerboard unless otherwise stated.1.1.4 Water-resistant gypsum backing board, designed pri-marily to be used as a base for the application of ceramic orplastic tile on walls or ceilings. This product is also suitable fordecoration.1.1.5 Ex

6、terior gypsum sofft board, designed for use onexterior soffits and carport ceilings that are completely pro-tected from contact with liquid water.1.1.6 Gypsum sheathing board, designed for use as sheath-ing on buildings.1.1.7 Gypsum base for veneer plaster, designed for use as abase for the applicat

7、ion of gypsum veneer plaster.1.1.8 Gypsum lath, designed for use as a base for theapplication of gypsum plaster.1.1.9 Gypsum ceiling board, designed for use on interiorceilings with framing spaced not more than 24 in. 610 mm oncenter and that affords a surface suitable to receive water-basedtexture

8、and other decoration. This product is also suitable foruse on interior walls.1.2 Specifications applicable to all gypsum boards arelocated in Section 14and 1315. Specifications applicableto specific gypsum boards are located in the following sections:SectionGypsum Wallboard, Predecorated Gypsum Boar

9、d,and Laminated Gypsum Board5Gypsum backing board, gypsum coreboard,gypsum shaftliner board6Water-resistant gypsum backing board 7Exterior gypsum soffit board 8Gypsum sheathing board 9Gypsum base for veneer plaster 10Gypsum lath 11Gypsum Ceiling Board 121.3 The values stated in either SI units or in

10、ch-pound unitsare to be regarded separately as standard. Within the text, theSI units are shown in brackets. The values stated in eachsystem may not be exact equivalents; therefore, each systemshall be used independently of the other. Combining valuesfrom the two systems may result in non-conformanc

11、e with thestandard1.4 This international standard was developed in accor-dance with internationally recognized principles on standard-ization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recom-mendations issued by the World Trade Organization Te

12、chnicalBarriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2C11 Terminology Relating to Gypsum and Related BuildingMaterials and SystemsC22/C22M Specification for GypsumC471M Test Methods for ChemicalAnalysis of Gypsum andGypsum Products (Metric)C473 Test Methods for Physical

13、 Testing of Gypsum PanelProductsC645 Specification for Nonstructural Steel Framing Mem-bersC840 Specification forApplication and Finishing of GypsumBoard1This specification is under the jurisdiction of ASTM Committee C11 onGypsum and Related Building Materials and Systems and is the direct responsib

14、ilityof Subcommittee C11.01 on Specifications and Test Methods for Gypsum Products.Current edition approved July 1, 2017. Published July 2017. Originally approvedin 1998. Last previous edition approved in 2014 as C1396/C1396M 14a. DOI:10.1520/C1396_C1396M-17.2For referenced ASTM standards, visit the

15、 ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the end of this standardCopyright ASTM International, 100 Bar

16、r Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United StatesThis international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for theDevelopment of International Standards, Guides and Recomm

17、endations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.1C841 Specification for Installation of Interior Lathing andFurringC844 Specification for Application of Gypsum Base toReceive Gypsum Veneer PlasterC1264 Specification for Sampling, Inspection, Rejection,Cer

18、tification, Packaging, Marking, Shipping, Handling,and Storage of Gypsum Panel ProductsC1280 Specification for Application of Exterior GypsumPanel Products for Use as SheathingD3273 Test Method for Resistance to Growth of Mold on theSurface of Interior Coatings in an Environmental Cham-berE84 Test M

19、ethod for Surface Burning Characteristics ofBuilding MaterialsE96/E96M Test Methods for Water Vapor Transmission ofMaterialsE119 Test Methods for Fire Tests of Building Constructionand Materials3. Terminology3.1 Definitions used in this specification shall be in accor-dance with Terminology C11.3.2

20、Definitions of Terms Specific to This Standard:3.2.1 decorative coating, na paint or other liquid materialwith or without aggregate.3.2.2 decorative sheet or film, na plastic film, eitherbacked or unbacked; plastic sheet; or combination of these.3.2.3 edge, nthe bound edge as manufactured.3.2.4 gyps

21、um backing board, na14 to58-in. 6.4 to 15.9-mm gypsum board used as a backing for gypsum wallboard,acoustical tile, or other dry cladding.3.2.5 gypsum coreboard, na34 to 1-in. 19.0 to 25.4-mmgypsum board used as a gypsum stud or core in semisolid orsolid gypsum board partitions.3.2.6 nominal thickne

22、ss, nthe manufacturer-stated frac-tional value of thickness of the gypsum panel product ex-pressed in decimal value to the nearest one-thousandth (11000)of an inch.4. Materials and Manufacture4.1 Gypsum board shall consist of a noncombustible core ofgypsum complying with Specification C22/C22M, surf

23、acedwith paper bonded to the core.4.1.1 Gypsum sheathing board shall consist of a noncom-bustible water-resistant core of gypsum complying with Speci-fication C22/C22M, surfaced on both the face and back withwater-repellant paper bonded to the core.4.1.2 Gypsum coreboard shall be either a single boa

24、rd orcomposed of two factory-laminated gypsum boards to provideup to 1 in. 25.4 mm total nominal thickness.4.1.3 Water-resistant gypsum backing board shall consist ofa noncombustible water-resistant core of gypsum complyingwith Specification C22/C22M, surfaced on both the back andface with water-rep

25、ellant paper bonded to the core.4.1.4 Predecorated gypsum board shall consist of a noncom-bustible core of gypsum complying with Specification C22/C22M, surfaced with paper bonded to the core with the facecovered with a decorative sheet, film, or coating.4.1.4.1 Class I predecorated gypsum board sha

26、ll have adecorative sheet or film laminated to the face.4.1.4.2 Class II predecorated gypsum board shall have adecorative coating applied to the face.4.1.5 Laminated gypsum board shall consist of two or morefactory laminated gypsum boards that conform to this specifi-cation.4.2 The back surface of f

27、oil-backed gypsum board shall inaddition be covered with aluminum foil.4.3 Gypsum board, mold resistant, designates gypsum boardhaving not more than 20 % mold growth, based on surface areacoverage, when tested in accordance with Test Method D3273.4.4 Gypsum Board, type X (Special Fire-Resistant):4.4

28、.1 Gypsum Board, type X, designates gypsum board,except gypsum lath, gypsum coreboard, and gypsum shaftlinerboard, complying with this specification that provides not lessthan 1 h fire-resistance rating for boards58 in. 15.9 mm thickor34 h fire-resistance rating for boards12 in. 12.7 mm thick,applie

29、d parallel with and on each side of load bearing 2 by 4wood studs spaced 16 in. 406 mm on centers with 6d coatednails, 178 in. 48 mm long, 0.0915-in. 2.3-mm diametershank,14-in. 6.4-mm diameter heads, spaced 7 in. 178 mmon centers with gypsum board joints staggered 16 in. 406 mmon each side of the p

30、artition and tested in accordance with TestMethods E119.4.4.2 Gypsum Lath, type X designates gypsum lath comply-ing with this specification that provides not less than a 1-hfire-resistance rating for gypsum lath38 in. 9.5 mm thick,when applied at right angles to and on each side of loadbearing2 4 wo

31、od studs spaced 16 in. 406 mm on centers with bluelath nails spaced 5 in. 127 mm on centers over which isapplied12 in. 12.7 mm 1:2 gypsum sand plaster and tested inaccordance with the requirements of Test Method E119.NOTE 3Consult producers for independent test data on assemblydetails and fire-resis

32、tance ratings for other types of construction. See firetest reports or listings from recognized fire testing laboratories forassembly particulars, materials, and ratings.4.4.3 Gypsum shaftliner board, type X, designates gypsumshaftliner board complying with this specification that meetsthe acceptanc

33、e criteria for temperature rise for not less than1-12 h for boards34-in. 19.0 mm thick or 2 h for boards 1-in.25.4 mm thick, when applied in a double layer solid nonloadbearing partition as described in 4.4.3.1 and tested in accor-dance with Test Methods E119 with thermocouple locations asspecified

34、in 4.4.3.2.4.4.3.1 Two layers of gypsum shaftliner board appliedvertically and friction fit into vertical 25-gauge steel “H”members, 1-12-in. 38.1 mm deep for boards34-in. 19.0 mmthick or 2-in. 50.8 mm deep for boards 1-in. 25.4 mm thick,spaced 24-in. 610 mm on centers and 25-gauge steel track atthe

35、 perimeter of the partition. “H” members shall be formedwith a single web or shall be two pieces of perimeter trackfastened together along the web with screws spaced 24-in.610 mm on centers.C1396/C1396M 1724.4.3.2 Temperature rise on the unexposed surface shall bemeasured using not less than five th

36、ermocouples; one shall belocated at the center of the assembly and one shall be locatedat the center of each quadrant. Thermocouples shall be locatednot less than 3-in. 76 mm from an “H” member.4.5 Gypsum wallboard, gypsum backing board, exteriorgypsum soffit board, and gypsum ceiling board shall ha

37、ve aflame spread index of not more than 25 when tested inaccordance with Test Method E84.4.6 Physical Properties, Dimensions, and Tolerances ofGypsum Board:4.6.1 Specimens shall be taken from the samples obtained inaccordance with Specification C1264.4.6.1.1 Specimens shall be tested in accordance w

38、ith TestMethods C473.4.6.2 Core, End, and Edge HardnessThe specimens shallhave an average hardness of not less than 15 lbf 67 N whentested by Method A and 11 lbf 49 N when tested by MethodB.4.6.2.1 When testing laminated gypsum board, if the lami-nated components are the same product and thickness,

39、the testshall be conducted on either component of the laminatedproduct. If the laminated gypsum board is comprised ofdifferent products or thicknesses, each component shall betested.4.6.3 Edges and EndsThe edges and ends shall bestraight.4.6.4 LengthThe tolerance in length shall be 614 in.66 mm.4.6.

40、5 Tapered Edge DepthThe average thickness of theedge of recessed or tapered edge gypsum board shall be notless than 0.020 in. 0.51 mm but not more than 0.090 in.2.29 mm less than the average thickness of the gypsumboard.4.6.6 The method for determining properties for a nominalthickness not listed in

41、 the tables of Sections 5 through 12 shallbe calculated as detailed in 4.6.6.1 and 4.6.6.2.4.6.6.1 For a board whose nominal thickness is not specifiedin the tables in Sections 5 through 12 interpolate between thetwo adjacent thicknesses in the tables.4.6.6.2 Properties shall not be extrapolated to

42、nominalthicknesses outside the range of values specified in the tables.4.7 Volatile Sulfur Compounds:4.7.1 Gypsum board shall contain not greater than 10 ppmof orthorhombic cyclooctasulfur (S8), when tested in accor-dance with Test Methods C471M.NOTE 4When exposed to heat, humidity, or both, gypsum

43、board con-taining S8 in quantities above 10 ppm may emit volatile sulfur compoundsin quantities that cause abnormal corrosion on electrical wiring, plumbingpipes, fuel gas lines, HVAC equipment, or any components of theforegoing.5. Gypsum Wallboard, Predecorated Gypsum Board, andLaminated Gypsum Boa

44、rd5.1 Physical Properties of Gypsum Wallboard, Predeco-rated Gypsum Board, and Laminated Gypsum Board:5.1.1 Flexural StrengthThe specimens shall be tested faceup and face down. The average breaking load shall be not lessthan the following:Thickness,in. mmMethod ABearing EdgesPerpendicularto Panel Le

45、ngth,lbf NMethod ABearing EdgesParallel to PanelLength, lbf NMethod BBearing EdgesPerpendicularto Panel Length,lbf NMethod BBearing EdgesParallel to PanelLength, lbf N14 6.4 50 222 20 89 46 205 16 71516 7.9 65 289 25 111 62 276 21 9338 9.5 80 356 30 133 77 343 26 11612 12.7 110 489 40 178 107 476 36

46、 16058 15.9 150 667 50 222 147 654 46 20534 19.0 170 756 60 267 167 743 56 2495.1.2 Humidified DeflectionThe specimens shall have anaverage deflection of not more than the following:Thickness, Deflection,in. mm eighths of an inch mm14 6.4 not required516 7.9 not required38 9.5 15 4812 12.7 10 3258 1

47、5.9 5 1634 19.0 5 165.1.3 Nail Pull ResistanceThe specimens shall have anaverage nail-pull resistance of not less than the following:Thickness, Method A, Method B,in. mm lbf N lbf N14 6.4 40 178 36 160516 7.9 50 222 46 20538 9.5 60 267 56 24912 12.7 80 356 77 34358 15.9 90 400 87 38734 19.0 100 445

48、97 4325.1.4 Foil-Backed Gypsum Wallboard and Foil-Backed Pre-decorated Gypsum Board:5.1.4.1 Foil-backed gypsum wallboard and foil-backed pre-decorated gypsum board shall meet all of the requirements forgypsum wallboard and predecorated gypsum board.5.1.4.2 When tested in accordance with Test Methods

49、 E96/E96M, the permeance of foil-backed gypsum wallboard andfoil-backed predecorated gypsum board shall be not more than0.30 perm 17 ng/Pasm2 (Desiccant Method) for the condi-tion of 50 % relative humidity on the face of the board, and0 % relative humidity on the back (foil-covered) side of theboard.5.2 Dimensions and Tolerances