ISO 1209-1-2007 Rigid cellular plastics - Determination of flexural properties - Part 1 Basic bending test《硬质泡沫塑料 弯曲特性测定 第1部分 基本弯曲试验》.pdf

《ISO 1209-1-2007 Rigid cellular plastics - Determination of flexural properties - Part 1 Basic bending test《硬质泡沫塑料 弯曲特性测定 第1部分 基本弯曲试验》.pdf》由会员分享，可在线阅读，更多相关《ISO 1209-1-2007 Rigid cellular plastics - Determination of flexural properties - Part 1 Basic bending test《硬质泡沫塑料 弯曲特性测定 第1部分 基本弯曲试验》.pdf（10页珍藏版）》请在麦多课文档分享上搜索。

1、INTERNATIONAL STANDARD ISO 1209-1 Third edition 2007-05-01 Reference number ISO 1209-1:2007(E) ISO 2007 Rigid cellular plastics Determination of flexural properties Part 1: Basic bending test Plastiques alvolaires rigides Dtermination des proprits de flexion Partie 1: Essai simple de flexionISO 1209

2、-1:2007(E) ii ISO 2007 All rights reserved PDF disclaimer This PDF file may contain embedded typefaces. In accordance with Adobes licensing policy, this file may be printed or viewed but shall not be edited unless the typefaces which are embedded are licensed to and installed on the computer perform

3、ing the editing. In downloading this file, parties accept therein the responsibility of not infringing Adobes licensing policy. The ISO Central Secretariat accepts no liability in this area. Adobe is a trademark of Adobe Systems Incorporated. Details of the software products used to create this PDF

4、file can be found in the General Info relative to the file; the PDF-creation parameters were optimized for printing. Every care has been taken to ensure that the file is suitable for use by ISO member bodies. In the unlikely event that a problem relating to it is found, please inform the Central Sec

5、retariat at the address given below. COPYRIGHT PROTECTED DOCUMENT ISO 2007 All rights reserved. Unless otherwise specified, no part of this publication may be reproduced or utilized in any form or by any means, electronic or mechanical, including photocopying and microfilm, without permission in wri

6、ting from either ISO at the address below or ISOs member body in the country of the requester. ISO copyright office Case postale 56 CH-1211 Geneva 20 Tel. + 41 22 749 01 11 Fax + 41 22 749 09 47 E-mail copyrightiso.org Web www.iso.org Published in SwitzerlandISO 1209-1:2007(E) ISO 2007 All rights re

7、served iii Contents Page 1 Scope 1 2 Normative references 1 3 Principle 1 4 Apparatus . 2 5 Test specimens 3 6 Procedure . 3 7 Expression of results 4 8 Precision . 4 9 Test report 4ISO 1209-1:2007(E) iv ISO 2007 All rights reserved Foreword ISO (the International Organization for Standardization) i

8、s a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represe

9、nted on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are d

10、rafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards. Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International

11、Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 1209-1 was prepa

12、red by Technical Committee ISO/TC 61, Plastics, Subcommittee SC 10, Cellular plastics. This third edition cancels and replaces the second edition (ISO 1209-1:2004), which has been technically revised. ISO 1209 consists of the following parts, under the general title Rigid cellular plastics Determina

13、tion of flexural properties: Part 1: Basic bending test Part 2: Determination of flexural strength and apparent flexural modulus of elasticityINTERNATIONAL STANDARD ISO 1209-1:2007(E) ISO 2007 All rights reserved 1 Rigid cellular plastics Determination of flexural properties Part 1: Basic bending te

14、st 1S c o p e This part of ISO 1209 specifies a simple method for assessing the behaviour of a bar of rigid cellular plastic under the action of three-point bending. It may be used to determine either the load for a specified deformation; or the load at break. The version of the method specified in

15、this part of ISO 1209 uses small test specimens and does not produce pure bending. Hence it does not permit the calculation of the flexural strength or the apparent flexural modulus (modulus of elasticity). The user is referred to ISO 1209-2 for the determination of these parameters. The method is n

16、ot applicable to cellular plastics in which significant crushing is observed. Numerical values should be compared only when determined on materials of similar physical properties and dimensions. The method is limited to materials of thickness or greater. 2 Normative references The following referenc

17、ed documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies. ISO 1923, Cellular plastics and rubbers Determination of linear dimensi

18、ons 3 Principle A load is applied at a uniform rate by means of a loading edge to a test specimen supported at two positions. The load is applied perpendicularly to the specimen at a position midway between the supporting positions (see Figure 1). The load at a specified deflection or at break is re

19、corded. 20 mmISO 1209-1:2007(E) 2 ISO 2007 All rights reserved 4 Apparatus 4.1 Test machine, consisting of either a universal mechanical-testing machine or a bending-test machine, capable of operating at a constant rate of movement of the moveable head. The range of the test machine shall be such th

20、at the applied load can be measured with an accuracy of . 4.2 Test specimen support, consisting of two parallel cylindrical support edges set in the same horizontal plane, each having an edge radius of . The length of the support edges shall be greater than the width of the test specimens. The span

21、between the support edges shall be . 4.3 Test specimen loading edge, having the same shape and dimensions as the support edges. The loading edge shall be located midway between and parallel to the support edges. 4.4 Dial-gauge micrometer, as described in ISO 1923. Key 1 loading edge with cylindrical

22、 edge having a radius of 2 support edges with cylindrical edge having a radius of 3 test specimen distance between support edges test specimen length test specimen thickness applied force Figure 1 Side view of test specimen and support edges (15 1) mm (15 1) mm L l d F 1% (15 1) mm (100 1) mmISO 120

23、9-1:2007(E) ISO 2007 All rights reserved 3 5 Test specimens 5.1 Shape and dimensions Each test specimen shall be a rectangular parallelepiped having the following dimensions: length: width: thickness: 5.2 Preparation Test specimens shall be cut without deformation of the original cell structure. The

24、 test specimens may have a skin on one or more sides. If so, this fact shall be recorded. 5.3 Number At least five specimens shall be tested for each sample. When testing materials which are suspected of being anisotropic, duplicate sets of test specimens shall be prepared having axes respectively p

25、arallel to and normal to the suspected direction of anisotropy. When testing specimens with only one surface skin, unless otherwise specified, duplicate sets of test specimens shall be tested, one set with the skin in tension and one set with the skin in compression. Report the results separately. 5

26、.4 Conditioning and test conditions Condition the test specimens for a minimum of at the conditions under which testing will be carried out. Normal test conditions areand R.H.;and R.H.;and R.H. Temperatures of , , , and are preferred alternative temperatures, although other conditions may be used, f

27、or example those reflecting end use. 6 Procedure Determine the dimensions of the test specimens in accordance with ISO 1923. Place a test specimen symmetrically upon the support edges so that the direction of loading is perpendicular to the longitudinal axis of the specimen (see Figure 1). Bring the

28、 loading edge into contact with the test specimen, ensuring that only a minimum force is applied. Note this as the zero-deflection point. Apply a force by means of the loading edge moving at a rate of . Record the force, in newtons, corresponding to a deflection of . If the test specimen fractures b

29、efore the deflection of is reached, record the breaking force and deflection at the breaking point. (120 1,20) mm (25 0,25) mm (20 0,20) mm 6h (23 2) C (50 10) % (23 5) C 50 +20 10 % (27 5) C 65 +20 10 % 196 C 70 C 10 C 0 C 40 C (10 2) mm/min (20 0,2) mm 20 mmISO 1209-1:2007(E) 4 ISO 2007 All rights

30、 reserved 7 Expression of results The results shall be reported as either the force, in newtons, at deflection; or the breaking force, in newtons, and the corresponding deflection, in millimetres. 8P r e c i s i o n An interlaboratory test was performed with 10 laboratories in 1993. Four products wi

31、th different flexural characteristics were tested, three of which were used for statistical evaluation of the reproducibility (two test results for each product) while one product was used for statistical evaluation of the repeatability (five test results). The results, analysed in accordance with I

32、SO 5725:1986, Precision of test methods Determination of repeatability and reproducibility for a standard test method by inter-laboratory tests (now withdrawn), are given in Table 1. 9 Test report The test report shall include the following information: a) a reference to this part of ISO 1209; b) a

33、description and identification of the material; c) the presence or absence of skins or facings on the test specimens and, if applicable, on which faces; d) the conditioning procedure used; e) the test conditions (temperature, humidity); f) the direction of application of the force with respect to an

34、y anisotropy; g) the presence of any crushing, if observed; h) the individual test results; i) the arithmetic mean of the test results and the standard deviation; j) details of any deviation from this part of ISO 1209, and of any incident that may have influenced the results; k) the date of the test. Table 1 Results of interlaboratory testing Bending strength Repeatability limit Reproducibility limit ( confidence level) ( confidence level) Approximately Approximately 20 mm 95 % 95 % 5% 15 %. 5 ISO 1209-1:2007(E) ICS 83.100 Price based on 4 pages ISO 2007 All rights reserved