GMW GMW16606-2011 Polypropylene - Glass Fiber Reinforced Mineral Filled Chemically Coupled Heat Stabilized Homopolymer Issue 1 English《聚丙烯 玻璃纤维加强 矿物填充 化学耦合且热稳定的均聚物 第1次出版(英文版本)》.pdf
《GMW GMW16606-2011 Polypropylene - Glass Fiber Reinforced Mineral Filled Chemically Coupled Heat Stabilized Homopolymer Issue 1 English《聚丙烯 玻璃纤维加强 矿物填充 化学耦合且热稳定的均聚物 第1次出版(英文版本)》.pdf》由会员分享,可在线阅读,更多相关《GMW GMW16606-2011 Polypropylene - Glass Fiber Reinforced Mineral Filled Chemically Coupled Heat Stabilized Homopolymer Issue 1 English《聚丙烯 玻璃纤维加强 矿物填充 化学耦合且热稳定的均聚物 第1次出版(英文版本)》.pdf(4页珍藏版)》请在麦多课文档分享上搜索。
1、 WORLDWIDE ENGINEERING STANDARDS Material Specification GMW16606 Polypropylene - Glass Fiber Reinforced/Mineral Filled, Chemically Coupled, Heat Stabilized Homopolymer Copyright 2011 General Motors Company All Rights Reserved June 2011 Originating Department: North American Engineering Standards Pag
2、e 1 of 4 1 Scope 1.1 Material Description. This specification covers the properties of injection moldable, glass fiber reinforced and mineral filled, chemically coupled, heat stabilized polypropylene homopolymer. 1.2 Symbols. The material abbreviations according to ISO 11469 are shown in Table 1. 1.
3、3 Typical Applications. Typical applications include the following: IP retainer and brackets. 1.4 Remarks. The classification into groups is according to the different ranges of mineral and glass fiber content. Additional mineral/glass ranges will be added as they become necessary. 2 References Note
4、: Only the latest approved standards are applicable unless otherwise specified. 2.1 External Standards/Specifications. ISO 75-1 ISO 527-1/2 ISO 75-2 ISO 1183 ISO 75-3 ISO 1873-2 ISO 178 ISO 3167 ISO 179/1eA ISO 3451-1 ISO 179/1eU ISO 4577 ISO 188 ISO 11359-1/2 ISO 294 ISO 11469 ISO 294-4 2.2 GM Stan
5、dards/Specifications. GMW3013 GMW3221 GMW3059 GMW3232 GMW3205 GMW3235 2.3 Additional References. TMC003 Material Safety Data Sheet guidance documents (available at ). 3 Requirements Materials approved to this specification shall meet the requirements of GMW3013, General Requirements for Handling of
6、Technical Terms of Delivery for Plastics. 3.1 Requirements on Delivery. Important physical, mechanical, and thermal properties that characterize the material are summarized in Table 1. Note: For each product, the requirements to Table 1 shall be documented by Certification Statement according to GMW
7、3013. The color shall be specified on drawings, in material specifications and otherwise. 3.2 Requirements on Test Specimens. 3.2.1 Unless otherwise specified, injection molding of test specimens shall be accomplished per ISO 294 with the conditions for injection molding from ISO 1873-2. Test method
8、s and specimen dimensions are also to be in accordance with ISO 1873-2 with the following additions: use ISO 3167, Type A, thickness 4 mm, for tensile and flexural properties. 3.2.2 All tests shall be performed on specimens 40 h minimum after molding and immediately following a conditioning period o
9、f 24 h minimum in a controlled atmosphere per GMW3221, Code A unless otherwise specified. All tests shall be performed on unannealed specimens. In addition, test specified at temperatures below or above 23 3 C shall be conducted at the specific temperature using specimens conditioned at specified te
10、mperature for 4 h minimum. 3.2.3 The values specified in Table 1 shall be met by test specimens in natural or black. For integrally colored grades where other additive systems (e.g., stabilizer) are used, the impact values shall not decrease more than 10% from the specified minimum value. 3.3 Chemic
11、al Requirements. All parts manufactured from molding compounds shall be resistant to the media they contact at their place of use. 3.4 Compound Properties. See Table 1. The following are also required for full specification approval. The minimum number of lots per test required is one in natural: Te
12、nsile Modulus, Poissons Ratio, Stress Strain Curve at +23 C, +85 C, -30 C. Copyright General Motors Company Provided by IHS under license with General Motors CompanyNot for ResaleNo reproduction or networking permitted without license from IHS-,-,-GM WORLDWIDE ENGINEERING STANDARDS GMW16606 Copyrigh
13、t 2011 General Motors Company All Rights Reserved June 2011 Page 2 of 4 3.5 Performance Requirements. Performance requirements shall be specified on part drawings or in component specifications. Table 1: Compound Properties (Black or Natural) Property Test Method Units Nominal Glass Fiber/Mineral Fi
14、ller Percentage ISO Symbol ISO 11469 - PP-(GF10+M10)PP-(GF25+ M10)PP-(GF20+ M15)PP-(M20+ GF15)PP-(GF30+ M10)PP-(GF25+ M15)PP-(GF20+ M20) Ash ISO 3451-1, Method A, at +800 C % by mass 20 2 35 2 35 2 35 2 40 2 40 2 40 2 Density ISO 1183, Method A g/cm Target Range 1.05 0.03 Target Range 1.19 0.03 Targ
15、et Range 1.19 0.03 Target Range 1.19 0.03 Target Range 1.23 0.03 Target Range 1.23 0.03 Target Range 1.23 0.03 Melt Flow Rate MFR230/2.16 Report Results g/10 minutes Report Results Report Results Report Results Report Results Report Results Report Results Report Results Melt Volume Flow Rate MVR230/
16、2.16 Report Results cm/10 minutes Report Results Report Results Report Results Report Results Report Results Report Results Report Results Tensile Modulus ISO 3167, 4 mm thick, Type A bar 1mm/minute MPa 3400 to 4300 5800 to 7000 5600 to 6600 5300 to 6400 6500 to 8100 6300 to 7900 6100 to 7600 Tensil
17、e Strength at Break ISO 527-1/2, specimen 1A, 5 mm/minute MPa 35 to 55 55 to 85 50 to 75 50 to 70 60 to 90 55 to 85 50 to 75 Tensile Strength at Break after Heat Aging Note 1 ISO 527-1/2, specimen 1A, 5 mm/minute % Retention 85Flexural Modulus ISO 178, 2 mm minute MPa 3000 to 4000 5600 to 6600 5300
18、to 6300 5000 to 6000 6200 to 7800 6100 to 7500 6000 to 7400 Charpy Impact Strength Unnotched at +23 C ISO 179/1eU kJ/m Report Results Report Results Report Results Report Results Report Results Report Results Report Results Charpy Impact Strength Unnotched at -30 C ISO 179/1eU kJ/m Report Results Re
19、port Results Report Results Report Results Report Results Report Results Report Results Charpy Impact Strength Unnotched at +23 C after Heat Aging Note 1 ISO 179/1eU % Retention 85 Charpy Impact Strength Notched at +23 C ISO 179/1eA kJ/m 2.5 5 4.5 4 3.5 3 2.5 Copyright General Motors Company Provide
- 1.请仔细阅读文档,确保文档完整性,对于不预览、不比对内容而直接下载带来的问题本站不予受理。
- 2.下载的文档,不会出现我们的网址水印。
- 3、该文档所得收入(下载+内容+预览)归上传者、原创作者;如果您是本文档原作者,请点此认领!既往收益都归您。
下载文档到电脑,查找使用更方便
10000 积分 0人已下载
下载 | 加入VIP,交流精品资源 |
- 配套讲稿:
如PPT文件的首页显示word图标,表示该PPT已包含配套word讲稿。双击word图标可打开word文档。
- 特殊限制: