GMKOREA EDS-M-4310-2008 EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER (VERSION 3).pdf

《GMKOREA EDS-M-4310-2008 EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER (VERSION 3).pdf》由会员分享，可在线阅读，更多相关《GMKOREA EDS-M-4310-2008 EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER (VERSION 3).pdf（5页珍藏版）》请在麦多课文档分享上搜索。

1、GM DAEWOO Auto & Technology EDS Engineering, GM DAEWOO Auto & Technology Standards EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER EDS-M-4310 ISSUED DATE: 1996. 08. 26 REVISED DATE: 2008. 03. 26 VERSION: 3 EDS-M-4310EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER PAGE: 1/4 IS

2、SUED DATE: 1996. 08. 26 REVISED DATE: 2008. 03. 26 VERSION: 3 GM DAEWOO Auto & Technology 1. SCOPE This specification defines general requirements for raw materials of extrusion molding acrylonitrile-butadiene-styrene copolymer applied to interior and exterior parts of a vehicle. 2. MATERIAL INDICAT

3、ION Material indication: ABS Detailed contents shall conform to the indication method of synthetic resin materials for vehicles.(Spec. No: GMW3116) 3. APPLICATION 3.1. Group 1: Medium heat resistance raw materials which have heat deflection temperature of 90 min. 3.2. Group 2: Heat resistance raw ma

4、terials which have heat deflection temperature of 95 min. 3.3. Group 3: High heat resistance raw materials which have heat deflection temperature of 100 min. 3.4. Group 4: Super heat resistance raw materials which have heat deflection temperature of 105 min. Notice to Use Parts which were molded usi

5、ng this specification material can be damaged as contacted by foam, rubber, seal, PVC products with plasticizer such as DOP, DOA, etc., because contacted parts can be chemically cracked by plasticizers migration. So the use of product must be avoided in case of contact. But, if the contact is necess

6、ary, surface treatment methods such as painting with clear coat, coated gold, etc must be used to prevent chemical crack by plasticizers migration. # Phthalic Acid Ester plasticizer: DOP(Di-Octyl Phathalate), DBP(Di -Butyl Phathalate), etc # Aliphatic Acid Ester plasticizer: DOA(Di 2-ethyl- hexyl Ad

7、ipate), etc 4. REQUIREMENTS 4.1. Mechanical properties Group 1 Type 1 Group 2 Type 1 Group 3 Type 1 Group 4 Type 1 Rockwell hardness EDS-T-7517 R Scale 105 105 105 105 Tensile strength (Kg/ ) EDS-T-7511 Test piece (133mm) Test speed (5mm/min) 450 450 450 450 EDS-M-4310EXTRUSION MOLDING ACRYLONITRILE

8、-BUTADIENE-STYRENE COPOLYMER PAGE: 2/4 ISSUED DATE: 1996. 08. 26 REVISED DATE: 2008. 03. 26 VERSION: 3 GM DAEWOO Auto & Technology Group 1 Type 1 Group 2 Type 1 Group 3 Type 1 Group 4 Type 1 Elongation (%) EDS-T-7511 Test piece (133mm) Test speed (5mm/min) 20 20 20 20 Flexural strength (Kg/ )EDS-T-7

9、518 Test piece (12712.76.4mm) Test speed (2.8mm/min) 600 650 650 700 Flexural modulus (Kg/ )EDS-T-7510 Test piece (12712.76.4mm) Test speed (2.8mm/min) 20,000 20,500 21,000 21,500 Impact strength, IZOD (KgY /Y ) EDS-T-7514 Test piece (63.512.73.2mm)Room temperature -30 25 3.5 15 3 13 4 13 4 4.2. The

10、rmal properties Heat deflection temperature() EDS-T-7520 Test piece (12712.76.4mm) 18.6 Kg/ 90 95 100 105 4.3. General properties Density (g/R ) EDS-T-7406 1.05 1.05 1.05 1.05 Melt flow index (g/10min)EDS-T-7516 10 5 5 5 Note) All the mechanical, thermal and general property values above indicate mi

11、nimum values except having specified ranges. 5. TEST PIECE AND TEST 5.1. Test piece Test pieces shall be prepared with injection molding. Unless otherwise specified in the requirements of clause 4, they shall be conditioned at 235K and a relative humidity of 50% for 24 hours or more. 5.2. Test Tests

12、 shall be performed at 235K and a relative humidity of 50%. EDS-M-4310EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER PAGE: 3/4 ISSUED DATE: 1996. 08. 26 REVISED DATE: 2008. 03. 26 VERSION: 3 GM DAEWOO Auto & Technology 6. APPROVAL OF RAW MATERIALS 6.1. Approved raw materials Division Ap

13、proved suppliers Approved raw materials Remark Group 1 Type 1 MIWON petrochemical 730E Group 2 Type 1 MIWON petrochemical H2938E Group 3 Type 1 MIWON petrochemical HU600E Group 4 Type 1 MIWON petrochemical HU650E 6.2. Approval and quality assurance procedure All raw materials shall be approved and r

14、egularly inspected for its quality prior to and during mass production delivery according to approval and quality assurance procedure for chemical raw materials (Spec. No. EDS-M-0102). 7. AUTOMOTIVE RESTRICTED HAZARDOUS SUBSTANCES Materials and components of parts must comply with GMW3059. 8. OTHERS

15、 8.1. Coding system Material specification of raw materials shall be indicated in drawings as follows. EDS-M-4310 - Required property type (clause 4) Material group (clause 3) Material specification number EDS-M-4310EXTRUSION MOLDING ACRYLONITRILE-BUTADIENE-STYRENE COPOLYMER PAGE: 4/4 ISSUED DATE: 1

16、996. 08. 26 REVISED DATE: 2008. 03. 26 VERSION: 3 GM DAEWOO Auto & Technology 9. RELATED STANDARDS EDS-M-0102 Procedures for approval of chemical raw material and quality control EDS-T-7406 Determination of volume and density of elastomers EDS-T-7510 Testing of plastics determination of the modulus

17、of elasticity by tensile, compression and flexural test EDS-T-7511 Test method for the tensile property of plastics EDS-T-7514 Test method for determining the flexural strength of plastics EDS-T-7516 The test method for the melt flow index of thermoplastics EDS-T-7517 The test method for Rockwell hardness of plastics EDS-T-7518 The method for the flexural strength of plastics EDS-T-7520 Test for deflection temperature of plastics under load GMW 3059 Restricted and reportable substance for parts GMW 3116 Recyclability / recoverability guidelines