《FORD WSS-M1H811-A-2003 FABRIC CANVAS PATTERN WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《帆布（CANVAS）图案的机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD WSS-M1H811-A-2003 FABRIC CANVAS PATTERN WOVEN TO BE USED WITH FORD WSS-M99P1111-A 《帆布（CANVAS）图案的机织织物 与标准FORD WSS-M99P1111-A一起使用 》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Material Name Specification Number Date Action Revisions 2003 02 26 Revised Para 3.0 ; Para 3.1, 3.2, 3.3, 3.10, 3.11, 4 deleted 1999 11 29 Revised Revised para 3.4.1 L. Daniv-Zarewych 1999 05 21 Activated L. Daniv-Zarewych Printed copies are uncontrolled Page 1 o

2、f 2 Copyright 2003, Ford Global Technologies, Inc. FABRIC, CANVAS PATTERN, WOVEN WSS-M1H811-A 1. SCOPE The material defined by this specification is a flat woven body cloth of good quality and uniform composition. 2. APPLICATION This specification was released originally for material used as an inte

3、rior trim fabric for Canvas Bags for 1999 Explorer. The fabric is backcoated, but not laminated. 3. REQUIREMENTS In addition, to the requirements listed herein, the fabric shall meet all requirements of WSS-M8P18-A1/A4 as applicable. Exception: The materials meet resistance to fade requirement at 22

4、5.6 kJ/m2at R=4, only. 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.4 FABRIC CONSTRUCTION 3.4.1 Fabric Count, +/- 5 % tolerance (ASTM D 3775) Warp 323.80 ends/1

5、0 cm Fill 133.80 picks/10 cm 3.4.2 Fabric Weight, range 302.6 - 334.5 g/m2(FLTM BN 106-01) 3.5 COMPOSITION (ASTM D 629) Tolerance as specified in WSS-M8P18-A1/A4 Fabric 100 % Polyester Backoating Acrylic ENGINEERING MATERIAL SPECIFICATION WSS-M1H811-A Page 2 of 2 Copyright 2003, Ford Global Technolo

6、gies, Inc. 3.6 YARN CONSTRUCTION (ASTM D 1244) Warp 33.3 tex, 34 f (100 % semi-dul polyester,txture),2 Fill 73.9 tex, (100 % semi- dull polyester, open end, 38.1 mm staple), 1 ply 3.7 METHOD OF DYEING Piece Dye 3.8 FINISHING OPERATIONS Coat, Inspect 3.9 FLAMMABILITY (ISO 3795/SAE J369) Burn Rate, ma

7、x 100 mm/minute Note: Not required on face fabric when used as a fully bonded composite. 5. GENERAL INFORMATION The information given below is provided for clarification and assistance in meeting the requirements of this specification. 5.1 Purchase departments will ensure that both materials defined in this specification and shipped to any one assembly plant will be produced by one supplier only.