FORD ESN-M1P50-A-2008 PLATING ZINC - NICKEL TO BE USED WITH FORD WSS-M99P1111-A 《电镀锌 镍(和FORD WSS-M99P1111-A一起使用)(使用 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA.pdf

《FORD ESN-M1P50-A-2008 PLATING ZINC - NICKEL TO BE USED WITH FORD WSS-M99P1111-A 《电镀锌 镍(和FORD WSS-M99P1111-A一起使用)(使用 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA.pdf》由会员分享，可在线阅读，更多相关《FORD ESN-M1P50-A-2008 PLATING ZINC - NICKEL TO BE USED WITH FORD WSS-M99P1111-A 《电镀锌 镍(和FORD WSS-M99P1111-A一起使用)(使用 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA-M1P87-A1 FORD WSA.pdf（1页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATION Date Action Revisions Ver. 4 2008 07 18 N-STATUS Replaced by WSA-M1P87-A1 G. Weber, FNA 2006 05 09 Revised Updated format 1967 10 16 Released NT-14551 Printed copies are uncontrolled Copyright 2008, Ford Global Technologies, LLC Page 1 of 1 PLATING, ZINC NICKEL ES

2、N-M1P50-A NOT TO BE MADE FOR NEW DESIGN 1. SCOPE This specification defines an electrolytic coating of zinc that contains evidence of nickel additions. Part supplied to this specification must have a minimum coating thickness of 5 micrometers and be capable of passing a 48 h salt spray test. 2 APPLI

3、CATION This finish is applied to steel strip used in the manufacture of spring guards that protect hydraulic houses used on industrial backhoes and loaders. 3. REQUIREMENTS Material specification requirements are to be used for initial qualification of materials. 3.0 STANDARD REQUIREMENTS FOR PRODUC

4、TION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements For Production Materials (WSS-M99P1111-A). 3.2 SALT SPRAY RESISTANCE, min 48 h (ASTM B 117) Parts shall pass salt spray requirements if the tested coatings have six red spots or less for any 930 c

5、m2 area that is visible to the unaided eye. A part is allowed one red rust spot on the significant surface for any size area, however, the total area of the number of parts tested if over 155 cm2 in area, shall not have more than one red rust spot per 155 cm2 of area. Also, a part showing a red spot

6、 larger than 1.6 mm in diameter on a significant surface shall be evaluated as a failure. 3.3 THICKNESS The thickness of plating shall be determined by a suitable acid dropping test, by magnetic methods such as “Magnegage“, by electronic deplating (Kocour Test) or by metallographic methods. In case

7、of dispute between a supplier and the Ford Motor Company, the umpire method shall be the met. 3.4 VISUAL EXAMINATION Plated parts are subject to surface inspection for such imperfections as excessively rough plate, incompletely covered areas, etc. The testing of the quality of plate by salt spray and/or determination of coating thickness will be done on pieces passing this inspection.