FORD ESB-M3G137-A-2005 TAPE POLYVINYL CHLORIDE FOAM - PRESSURE SENSITIVE TO BE USED WITH WSS-M99P1111-A 《压敏型聚氯乙烯泡沫胶带 与标准WSSS-M99P1111-A一起使用 》.pdf

《FORD ESB-M3G137-A-2005 TAPE POLYVINYL CHLORIDE FOAM - PRESSURE SENSITIVE TO BE USED WITH WSS-M99P1111-A 《压敏型聚氯乙烯泡沫胶带 与标准WSSS-M99P1111-A一起使用 》.pdf》由会员分享，可在线阅读，更多相关《FORD ESB-M3G137-A-2005 TAPE POLYVINYL CHLORIDE FOAM - PRESSURE SENSITIVE TO BE USED WITH WSS-M99P1111-A 《压敏型聚氯乙烯泡沫胶带 与标准WSSS-M99P1111-A一起使用 》.pdf（3页珍藏版）》请在麦多课文档分享上搜索。

1、 ENGINEERING MATERIAL SPECIFICATIONDate Action Revisions 2005 10 19 Revised Inserted 3.0; Deleted 3.1, 3.2, 3.13, 4 1984 03 05 Released C3N1-AF523183 Printed copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 1 of 3 TAPE, POLYVINYL CHLORIDE FOAM PRESSURE SENSITIVE ESB-M3G137-

2、A 1. SCOPE The material defined by this specification is an extruded polyvinyl chloride foam tape displaying a skin on all sides with an adhesive on one side protected by a polyethylene release liner. 2. APPLICATION This specification was released originally for material used as a dam or shim for wi

3、ndshields and backlites. This material provides protection from glass breakage during installation and seals against water leaks and wind noise. 3. REQUIREMENTS 3.0 STANDARD REQUIREMENTS FOR PRODUCTION MATERIALS Material suppliers and part producers must conform to the Companys Standard Requirements

4、 For Production Materials (WSS-M99P1111-A). 3.3 COLOR Black or as specified on the engineering drawing. Dimension 6 mm x 6 mm or as specified on engineering drawing. 3.4 TENSILE STRENGTH 276 - 827 kPa 3.4.1 Elongation 50 - 120% 3.5 LOW TEMPERATURE FLEXIBILITY No Cracking Test Method: Condition three

5、 150 mm length samples of tape at -29 +/- 1 C for 4 h. Bend each sample 180 around a temperature conditioned mandrel 6.4 mm diameter. 3.6 HARDNESS - DUROMETER “00“ 30 +/- 10 (ASTM D 2240 except samples are single ply and instantaneous reading is used. Testing is to be done on the non-adhesive side)

6、3.7 COMPRESSION DEFLECTION 3.7.1 Instantaneous 14 - 41 kPa 3.7.2 After 60 s 3.4 - 14 kPa (ASTM D 1667, except test tape as received. A sample of extrusion 25 mm in length by sample width 6.35 mm and single ply is compressed 25% at a rate of 50 mm/min. Record both instantaneous load and load 60 s aft

7、er compressed height is reached.) ENGINEERING MATERIAL SPECIFICATIONESB-M3G137-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Page 2 of 3 3.8 COMPRESSION SET, max 90% (ASTM D 1667 except at 70 +/- 1 C for 22 h. Sample is tested single ply. Measure recovered height 30

8、min after clamps are recovered.) 3.9 WATER ABSORPTION, max 8% Test Method: A 100 mm sample is weighed and immersed under a 50 mm head of water for 24 h. Sample is then removed, bottled, dried of all surface water and reweighed. Calculate % Absorption New Wt. - Orig. Wt. % by wt. = Original Wt. x 100

9、 3.10 DENSITY 132 - 184 kg/m3(ASTM D 1667, except use strips of tape as received with adhesive using a steel rule to measure length and width and a dead weight load for thickness determination.) 3.11 RELEASE LINER The seal assembly shall have a suitable release liner which shall be readily removed,

10、but shall not fall off in shipping and handling. There shall be no transfer of the release agent to the tape after 6 months storage at temperatures not exceeding 32 C or accelerated storage of 14 days at 49 C. Approval of the release liner shall be predicated on storage stability and production proc

11、essing feasibility. 3.12 ADHESION, min 438 N/M Test Method: A glass panel is cleaned and primed. After 15 minutes dwell time, a sample of the extrusion is bonded to the primed glass rolled down with a 2.04 kg roller once in each direction. The extrusion is reinforced with a non-stretch backing tape

12、and pulled in a tensile tester after the 15 minute dwell time at 23 +/- 2 C. The sample is pulled at a 90 angle with a crosshead speed of 305 mm/min. ADHESION PRIMERS FOR ELASTOMERIC BONDING TAPE Adhesion Primer for Elastomeric Bonding Tape - Fast Drying ESB-M2G157-AD ESB-M2G157-BD Adhesion Primer f

13、or Elastomer for Elastomeric Bonding Tape ESB-M2G171-AB ESB-M2G171-BB SUPPLIERS IDENTIFICATION ESB-M3G95-AB Protective Treatments, Inc. ESB-M3G95-BB Tremco Manufacturing Co. ENGINEERING MATERIAL SPECIFICATIONESB-M3G137-APrinted copies are uncontrolled Copyright 2005, Ford Global Technologies, LLC Pa

14、ge 3 of 3 SUPPLIER IDENTIFICATION ESB-M2G157-D (Glass Primer) Protective Treatments, Inc. ESB-M2G171-D (Metal Primer) ADHESION PRIMERS FOR URETHANE BONDING SUPPLIER IDENTIFICATION Essex Chemical Corp. ESB-M5B280-A (Glass Cleaner) ESB-M5B280-B (Glass Cleaner) ESB-M2G224-A (Glass Adhesion Primer) ESB-

15、M2G224-B (Glass Adhesion Primer) 3.14 FUNCTIONAL APPROVAL Candidate materials being evaluated for initial approval to the specification shall be subjected to a production trial in an area intended for use. This trial will be conducted after all other specification requirements have been met including laboratory evaluation and engineering approval for the trail.