DIN EN 1977-2013 Copper and copper alloys - Copper drawing stock (wire rod) German version EN 1977 2013《铜和铜合金 铜拉制坯料 (绕材) 德文版本EN 1977-2013》.pdf

《DIN EN 1977-2013 Copper and copper alloys - Copper drawing stock (wire rod) German version EN 1977 2013《铜和铜合金 铜拉制坯料 (绕材) 德文版本EN 1977-2013》.pdf》由会员分享，可在线阅读，更多相关《DIN EN 1977-2013 Copper and copper alloys - Copper drawing stock (wire rod) German version EN 1977 2013《铜和铜合金 铜拉制坯料 (绕材) 德文版本EN 1977-2013》.pdf（25页珍藏版）》请在麦多课文档分享上搜索。

1、April 2013 Translation by DIN-Sprachendienst.English price group 12No part of this translation may be reproduced without prior permission ofDIN Deutsches Institut fr Normung e. V., Berlin. Beuth Verlag GmbH, 10772 Berlin, Germany,has the exclusive right of sale for German Standards (DIN-Normen).ICS

2、77.150.30!$Y“1975456www.din.deDDIN EN 1977Copper and copper alloys Copper drawing stock (wire rod);English version EN 1977:2013,English translation of DIN EN 1977:2013-04Kupfer und Kupferlegierungen Vordraht aus Kupfer;Englische Fassung EN 1977:2013,Englische bersetzung von DIN EN 1977:2013-04Cuivre

3、 et alliages de cuivre Fil machine en cuivre;Version anglaise EN 1977:2013,Traduction anglaise de DIN EN 1977:2013-04SupersedesDIN EN 1977:1998-05www.beuth.deIn case of doubt, the German-language original shall be considered authoritative.Document comprises 25 pages 03.13 DIN EN 1977:2013-04 2 A com

4、ma is used as the decimal marker. National foreword This document (EN 1977:2013) has been prepared by Technical Committee CEN/TC 133 “Copper and copper alloys” (Secretariat: DIN, Germany), Working Group WG 1 “Unwrought copper products” (Secretariat: AENOR, Spain). The responsible German body involve

5、d in its preparation was the Normenausschuss Nichteisenmetalle (Nonferrous Metals Standards Committee), Working Committee NA 066-02-01 AA Httenkupfer und Schrotte. The DIN Standard corresponding to the International Standard referred to in this document is as follows: IEC 60468 DIN IEC 60468 Amendme

6、nts This standard differs from DIN EN 1977:1998-05 as follows: a) Table 2, column “Cu-FRHC”, “Other elements” has been modified and a new footnote “d” has been added. b) Subclauses 6.4 and 8.4 “Annealability” have been modified; c) Subclause A.2 “Standard annealed copper (IACS)” has been updated; d)

7、 Annex B (normative) “Rapid Elongation Test method (AR-Test) for diameter 8 mm Cu-ETP1 wire rod” has been added. Previous editions DIN 17652: 1982-06 DIN EN 1977: 1998-05 National Annex NA (informative) Bibliography DIN IEC 60468, Method of measurement of resistivity of metallic materials EUROPEAN S

8、TANDARD NORME EUROPENNE EUROPISCHE NORM EN 1977 January 2013 ICS 77.150.30 Supersedes EN 1977:1998English Version Copper and copper alloys - Copper drawing stock (wire rod) Cuivre et alliages de cuivre - Fil machine en cuivre Kupfer und Kupferlegierungen - Vordraht aus Kupfer This European Standard

9、was approved by CEN on 24 November 2012. CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning suc

10、h national standards may be obtained on application to the CEN-CENELEC Management Centre or to any CEN member. This European Standard exists in three official versions (English, French, German). A version in any other language made by translation under the responsibility of a CEN member into its own

11、 language and notified to the CEN-CENELEC Management Centre has the same status as the official versions. CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, G

12、reece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and United Kingdom. EUROPEAN COMMITTEE FOR STANDARDIZATION COMIT EUROPEN DE NORMALISATION EUROPISCHES KOMITEE FR NORMU

13、NG Management Centre: Avenue Marnix 17, B-1000 Brussels 2013 CEN All rights of exploitation in any form and by any means reserved worldwide for CEN national Members. Ref. No. EN 1977:2013: EEN 1977:2013 (E) 2 Contents Page Foreword . 3 Introduction 4 1 Scope 5 2 Normative references . 5 3 Terms and

14、definitions 5 4 Designations 5 4.1 Material . 5 4.2 Product . 6 5 Ordering information 7 6 Requirements . 7 6.1 Composition . 7 6.2 Elongation 7 6.3 Electrical properties . 7 6.4 Annealability . 12 6.5 Hydrogen embrittlement 12 6.6 Scale adhesion . 13 6.7 Dimensions and tolerances . 13 6.8 Surface c

15、ondition . 13 6.9 Joins . 13 7 Sampling . 13 7.1 General . 13 7.2 Analysis (oxygen only) and measurement of diameter of Cu-ETP1 (CW003A) drawing stock . 14 7.3 Annealability testing of Cu-ETP1 (CW003A) drawing stock . 14 7.4 Analysis (other than oxygen) and measurement of elongation and electrical p

16、roperties of Cu-ETP1 (CW003A) drawing stock 14 7.5 Tests on drawing stock in grades other than Cu-ETP1 (CW003A). 14 8 Test methods 15 8.1 Analysis 15 8.2 Elongation 15 8.3 Electrical resistivity 15 8.4 Annealability . 16 8.5 Hydrogen embrittlement 16 8.6 Scale adhesion . 16 8.7 Rounding of results .

17、 16 9 Declaration of conformity and inspection documentation . 16 9.1 Declaration of conformity 16 9.2 Inspection documentation . 17 10 Marking . 17 Annex A (informative) Information on electrical resistivity and conductivity relationships . 18 A.1 Volume resistivity. 18 A.2 Standard annealed copper

18、 (IACS) . 18 A.3 Commercial annealed copper 18 A.4 Nominal mass resistivity 18 A.5 Differences between measured and nominal values 19 Annex B (normative) Rapid Elongation Test method (AR-Test) for diameter 8 mm Cu-ETP1 wire rod . 20 B.1 General . 20 B.2 Procedure . 20 B.3 Test results . 22 Bibliogra

19、phy 23 DIN EN 1977:2013-04 EN 1977:2013 (E) 3 Foreword This document (EN 1977:2013) has been prepared by Technical Committee CEN/TC 133 “Copper and copper alloys”, the secretariat of which is held by DIN. This European Standard shall be given the status of a national standard, either by publication

20、of an identical text or by endorsement, at the latest by July 2013, and conflicting national standards shall be withdrawn at the latest by July 2013. Attention is drawn to the possibility that some of the elements of this document may be the subject of patent rights. CEN and/or CENELEC shall not be

21、held responsible for identifying any or all such patent rights. This document supersedes EN 1977:1998. This document is one of a series of European Standards for products manufactured from refined copper grades. Other products are specified as follows: EN 1976, Copper and copper alloys Cast unwrough

22、t copper products EN 1978, Copper and copper alloys Copper cathodes EN 13602, Copper and copper alloys Drawn, round copper wire for the manufacture of electrical conductors In comparison with EN 1977:1998, the following significant technical changes were made: a) Table 2, Cu-FRHC, Other elements: co

23、ntent has been modified and a new footnote “d” has been added; b) 6.4 and 8.4 “Annealability” have been modified; c) A.2 “Standard annealed copper (IACS)” has been modified; d) Annex B (normative) “Rapid Elongation Test method (AR-Test) for diameter 8 mm Cu-ETP1 wire rod” has been added. According t

24、o the CEN/CENELEC Internal Regulations, the national standards organisations of the following countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia, Finland, Former Yugoslav Republic of Macedonia, France, Germany, Greec

25、e, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland, Turkey and the United Kingdom. DIN EN 1977:2013-04 EN 1977:2013 (E) 4 Introduction Copper drawing stock (wire rod) is normally ma

26、nufactured by one of the following process routes: continuous casting and hot rolling in tandem; continuous or semi-continuous casting and cold rolling; rolling of wire bar or billets; or extrusion. Annex A (informative) gives information on the relationships between electrical resistivity and condu

27、ctivity (of copper). Annex B (normative) describes the rapid elongation test method (AR-Test) for diameter 8 mm Cu-ETP1 wire rod. DIN EN 1977:2013-04 EN 1977:2013 (E) 5 1 Scope This European Standard specifies the composition, mechanical, electrical and physical properties for high conductivity copp

28、er drawing stock (wire rod) suitable for fabrication into wire by cold drawing, principally for the manufacture of electrical conductors. This European Standard covers drawing stock (wire rod), in nine grades of copper and nine silver-bearing copper grades. Normally, the cross-section is approximate

29、ly circular, in a range of diameters from 6 mm. 2 Normative references The following documents, in whole or in part, are normatively referenced in this document and are indispensable for its application. For dated references, only the edition cited applies. For undated references, the latest edition

30、 of the referenced document (including any amendments) applies. EN 1655, Copper and copper alloys Declarations of conformity EN 10204, Metallic products Types of inspection documents EN 12893, Copper and copper alloys Determination of spiral elongation number EN ISO 2626, Copper Hydrogen embrittleme

31、nt test (ISO 2626) EN ISO 6892-1:2009, Metallic materials Tensile testing Part 1: Method of test at room temperature (ISO 6892-1:2009) IEC 60468, Method of measurement of resistivity of metallic materials ISO 4746, Oxygen-free copper Scale adhesion test 3 Terms and definitions For the purposes of th

32、is document, the following terms and definitions apply. 3.1 drawing stock wire rod intermediate solid wrought product, of uniform cross-section along its whole length, supplied in coils 4 Designations 4.1 Material 4.1.1 General The material is designated either by symbol or number (see Tables 1 to 4

33、). 4.1.2 Symbol The material symbol designation is based on the designation system given in ISO 1190-1. NOTE Although material symbol designations used in this standard might be the same as those in other standards using the designation system given in ISO 1190-1, the detailed composition requiremen

34、ts are not necessarily the same. 4.1.3 Number The material number designation is in accordance with the system given in EN 1412. DIN EN 1977:2013-04 EN 1977:2013 (E) 6 4.2 Product The product designation provides a standardized pattern of designation from which a rapid and unequivocal description of

35、 a product is conveyed in communication. It provides mutual comprehension at the international level with regard to products which meet the requirements of the relevant European Standard. The product designation is no substitute for the full content of the standard. The product designation for produ

36、cts to this European Standard shall consist of: denomination (copper drawing stock); number of this European Standard (EN 1977); material designation, either symbol or number (see Tables 1 to 4); nominal diameter; nominal coil mass; surface condition (the following designations shall be used, as app

37、ropriate: M for as manufactured, CL for cleaned). The derivation of a product designation is shown in the following example. EXAMPLE Drawing stock (wire rod) conforming to this standard, in material designated either Cu-ETP or CW004A, nominal diameter 8 mm, in 1 000 kg coils, cleaned surface conditi

38、on, shall be designated as follows: Copper drawing stock EN 1977 Cu-ETP 8 1 000 CL or Copper drawing stock EN 1977 CW004A 8 1 000 CL Denomination Number of this European Standard Material designation Nominal diameter in millimetres Nominal coil mass in kilograms Surface condition DIN EN 1977:2013-04

39、 EN 1977:2013 (E) 7 5 Ordering information In order to facilitate the enquiry, order and information of order procedures between the purchaser and the supplier, the purchaser shall state on his enquiry and order the following information: a) quantity of product required (mass or number of coils); b)

40、 denomination (copper drawing stock); c) number of this European Standard (EN 1977); d) material designation (see Tables 1 to 4); e) nominal diameter; f) nominal coil mass; g) surface condition (see 6.8). It is recommended that the product designation as described in 4.2 is used for items b) to g).

41、In addition, the purchaser shall also state on the enquiry and order any of the following, if required: h) whether joins are permitted in the coils (see 6.9); i) additional tests, if any, which the purchaser requires to be carried out by the manufacturer on the material, selected from the tests appr

42、opriate to each copper grade given in Table 5; j) whether a declaration of conformity is required (see 9.1); k) whether an inspection document is required, and if so which type (see 9.2). EXAMPLE Ordering details for 5 000 kg of drawing stock conforming to EN 1977, in material designated either Cu-E

43、TP or CW004A, nominal diameter 8 mm, in 1 000 kg coils, cleaned surface condition: 5 000 kg Copper drawing stock EN 1977 Cu-ETP 8 1 000 CL or 5 000 kg Copper drawing stock EN 1977 CW004A 8 1 000 CL 6 Requirements 6.1 Composition The composition shall conform to the requirements for the appropriate g

44、rade given in Tables 1 to 4. 6.2 Elongation Hot-finished drawing stock shall have a minimum elongation of 30 %. The test shall be carried out in accordance with 8.2. No elongation requirements are specified for cold-finished drawing stock. If such requirements are necessary, they should be agreed be

45、tween the purchaser and the supplier. 6.3 Electrical properties The maximum volume resistivity at 20 C of hot-finished drawing stock shall conform to the appropriate requirements given in Table 6. The test shall be carried out in accordance with 8.3. DIN EN 1977:2013-04 EN 1977:2013 (E) 8 Table 1 Co

46、mposition of copper grades made from Cu-CATH-1 (CR001A) Material designation Composition % (mass fraction) ElementCu Ag As Bi Cd Co Cr Fe Mn Ni O P Pb S Sb Se Si Sn Te Zn Elements listed in this table other than copper Symbol Number totalexcludingCu-ETP1 CW003A min. max. 0,002 5 0,000 5a 0,000 20b a

47、 c a 0,001 0c a c 0,040 a 0,000 5 0,001 5 0,000 4a 0,000 20b c c 0,000 20b c 0,006 5 O Cu-OF1 CW007A min. max. 0,002 5 0,000 5a 0,000 20b a c a 0,001 0c a c d a 0,000 5 0,001 5 0,000 4a 0,000 20b c c 0,000 20b c 0,006 5 O Cu-OFE CW009A min. max. 99,99 0,002 5 0,000 5 0,000 20 0,000 1 0,001 0 0,0005 0,0010 d 0,000 3 0,000 5 0,001 5 0,000 4 0,000 20 0,000 2 0,000 20 0,000 1 Cu-PHCE CW022A min. max. 99,99 0,002 5 0,000 5 0,000 20 0,000 1 0,001 0 0,0005 0,0010 d0,001 0,006 0,000 5 0,001 5 0,000 4 0,000 20 0,000 2 0,000 20 0,000 1 a(As + Cd + Cr + Mn + P + Sb) max. 0,001 5 %. b(Bi + Se +