BS L 117-1975 Specification for tube of aluminium-magnesium-silicon-copper-chromium alloy (solution treated and artificially aged not tested hydraulically) (not exceeding 10 mm thi.pdf

《BS L 117-1975 Specification for tube of aluminium-magnesium-silicon-copper-chromium alloy (solution treated and artificially aged not tested hydraulically) (not exceeding 10 mm thi.pdf》由会员分享，可在线阅读，更多相关《BS L 117-1975 Specification for tube of aluminium-magnesium-silicon-copper-chromium alloy (solution treated and artificially aged not tested hydraulically) (not exceeding 10 mm thi.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS L 117:1975 Incorporating Amendment No. 1 Specification for Tube of aluminium- magnesium-silicon- copper-chromium alloy (Solution treated and artificially aged: not tested hydraulically) (Not exceeding 10 mm thickness) (Mg 1.0, Si 0.6, Cu 0.28, Cr 0.2) UDC 629.7:6

2、69.715721782326 462 153.71 157.84BSL117:1975 This British Standard, having been approved by the AerospaceIndustry Standards Committee, was published underthe authority of the Executive Board on 30May1975 BSI 01-2000 The following BSI references relate to the work on this standard: Committee referenc

3、e ACE/24 Draft for comment 73/35606 DC ISBN 0 580 08932 0 A British Standard does not purport to include all the necessary provisions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from le

4、gal obligations. Summary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 to 3 and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside fro

5、nt cover. Amendments issued since publication Amd. No. Date of issue Comments 3827 March 1982 Indicated by a sideline in the marginBSL117:1975 BSI 01-2000 i Contents Page 1 Inspection and testing procedure 1 2 Quality of material 1 3 Chemical composition 1 4 Condition 1 5 Heat treatment 1 6 Mechanic

6、al properties 2 7 Tolerances 2 Table 1 Tolerances on thickness 2 Table 2 Tolerances on outside or inside diameters of drawn round tube 3ii blankBSL117:1975 BSI 01-2000 1 NOTE 1Tube of similar composition, in the same heat treatment condition and tested hydraulically is covered by BSL118. NOTE 2The c

7、hemical composition of this material complies with that registered as International Designation6061. 1 Inspection and testing procedure This British Standard shall be used in conjunction with sections 1 and 11 of the latest issue of BSL100, except as specified in6.2 and clause7 below. 2 Quality of m

8、aterial The material shall be made from aluminium and alloying constituents, with or without approved scrap at the discretion of the manufacturer. 3 Chemical composition The chemical composition of the material shall be: 4 Condition The material shall be supplied solution treated and artificially ag

9、ed. 5 Heat treatment The material shall be heat treated as follows: a) solution treat by heating uniformly at a temperature between510 C and540 C and quenching in water at a temperature not exceeding40 C; b) artificially age by heating uniformly at a temperature between165 C and195 C for3h to12h. El

10、ement % min. max. Silicon 0.40 0.8 Iron 0.7 Copper 0.15 0.40 Manganese 0.15 Magnesium 0.8 1.2 Chromium 0.04 0.35 Zinc a 0.25 Titanium a 0.15 Others: each a 0.05 Others: total a 0.15 Aluminium Remainder a Subject to the discretion of the Inspecting Authority, determination of these elements need be m

11、ade on a small proportion only of the samples analysed.BSL117:1975 2 BSI 01-2000 6 Mechanical properties 6.1 Tensile test. The mechanical properties obtained from test pieces selected and prepared in accordance with the relevant requirements of BSL100 shall be not less than the following values: NOT

12、EInformation on SI units is given in BS3763 “The International System of units (SI)” and BS350 “Conversion factors and tables”. 6.2 Flattening test. If stated on the order, the specified number of tubes shall be subjected to the flattening test. The distance between the inner sides of the test piece

13、 after flattening shall not exceed the following values: 7 Tolerances 7.1 Thickness. The thickness of the tube shall comply with the requirements ofTable 1. 7.2 Diameter. The diameters of drawn round tube shall comply with the requirements ofTable 2. Table 1 Tolerances on thickness Nominal thickness

14、 0.2% proof stress Tensile strength Elongation on gauge length of50 mm Full tube section Strip test piece mm MPa (= N/mm 2 ) MPa (= N/mm 2 ) % % Over Up to and including 1.0 240 290 10 8 1.0 5.0 240 290 12 10 5.0 10.0 240 290 14 12 Thickness (T) Maximum distance mm mm Up to and including 6.0 6T Over

15、 6.0 4T All dimensions in millimetres Nominal thickness Mean thickness atolerance Eccentricity b Over Up to and including 0.25 0.90 0.05 0.08 or 10% of nominal thickness, whichever is the greater 0.90 1.25 0.08 1.25 2.10 0.10 2.10 3.05 0.13 3.05 5.15 0.15 5.15 7.60 0.20 7.60 9.50 0.38 a Mean thickne

16、ss: the sum of the thicknesses measured at the ends of any two diameters at right angles, divided by four. b Eccentricity: allowable deviation of the thickness, at any point, from the nominal thickness. BSL117:1975 BSI 01-2000 3 Table 2 Tolerances on outside or inside diameters of drawn round tube A

17、ll dimensions in millimetres Nominal outside or inside diameter Deviation of mean diameter afrom nominal Ovality b Over Up to and including 13.0 0.08 0.15 13.0 25.5 0.10 0.20 25.5 51.0 0.13 0.25 51.0 76.5 0.15 0.30 76.5 127.0 0.20 0.40 127.0 155 0.25 0.50 a Mean diameter: half the sum of any two dia

18、meters at right angles. b Ovality: allowable deviation of the diameter, at any point, from the nominal diameter.BS L 117:1975 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK vi

19、ew on standards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the

20、 quality of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400.

21、 BSI offers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:0

22、2089967001. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and internationa

23、l standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to

24、 date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in

25、the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise withou

26、t prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.