BS ISO 5269-3-2008 Pulps - Preparation of laboratory sheets for physical testing - Conventional and Rapid-K then sheet formers using a closed water system《纸浆 物理测试用实验室纸板的制备 使用封闭水系统的.pdf

《BS ISO 5269-3-2008 Pulps - Preparation of laboratory sheets for physical testing - Conventional and Rapid-K then sheet formers using a closed water system《纸浆 物理测试用实验室纸板的制备 使用封闭水系统的.pdf》由会员分享，可在线阅读，更多相关《BS ISO 5269-3-2008 Pulps - Preparation of laboratory sheets for physical testing - Conventional and Rapid-K then sheet formers using a closed water system《纸浆 物理测试用实验室纸板的制备 使用封闭水系统的.pdf（16页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARDBS ISO 5269-3:2008Pulps Preparation of laboratory sheets for physical testing Part 3: Conventional and Rapid-Kthen sheet formers using a closed water systemICS 85.040g49g50g3g38g50g51g60g44g49g42g3g58g44g55g43g50g56g55g3g37g54g44g3g51g40g53g48g44g54g54g44g50g49g3g40g59g38g40g51g55g3g

2、36g54g3g51g40g53g48g44g55g55g40g39g3g37g60g3g38g50g51g60g53g44g42g43g55g3g47g36g58BS ISO 5269-3:2008This British Standard was published under the authority of the Standards Policy and Strategy Committee on 31 October 2008 BSI 2008ISBN 978 0 580 58442 8National forewordThis British Standard is the UK

3、 implementation of ISO 5269-3:2008.The UK participation in its preparation was entrusted to Technical Committee PAI/11, Methods of test for paper, board and pulps.A list of organizations represented on this committee can be obtained on request to its secretary.This publication does not purport to in

4、clude all the necessary provisions of a contract. Users are responsible for its correct application.Compliance with a British Standard cannot confer immunity from legal obligations.Amendments/corrigenda issued since publicationDate CommentsReference numberISO 5269-3:2008(E)INTERNATIONAL STANDARD ISO

5、5269-3First edition2008-05-15Pulps Preparation of laboratory sheets for physical testing Part 3: Conventional and Rapid-Kthen sheet formers using a closed water system Ptes Prparation des feuilles de laboratoire pour essais physiques Partie 3: Formettes conventionnelle et Rapid-Kthen, circuit deau f

6、erm BS ISO 5269-3:2008ii iiiContents Page Foreword iv Introduction v 1 Scope . 1 2 Normative references . 1 3 Principle. 2 4 Apparatus 2 5 Preparation of sample 2 5.1 Disintegration 2 5.2 Dilution. 2 6 Procedure for the conventional sheet former 3 6.1 Preparation of white water in retention equilibr

7、ium 3 6.2 Preparation of laboratory sheets for physical testing 3 7 Procedure for the Rapid-Kthen sheet former 3 7.1 Preparation of white water in retention equilibrium 3 7.2 Preparation of laboratory sheets for physical testing 4 8 Test report . 4 Annex A (informative) Differences between conventio

8、nal and Rapid-Kthen sheet preparation . 5 Bibliography . 6 BS ISO 5269-3:2008iv Foreword ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies (ISO member bodies). The work of preparing International Standards is normally carried out through

9、ISO technical committees. Each member body interested in a subject for which a technical committee has been established has the right to be represented on that committee. International organizations, governmental and non-governmental, in liaison with ISO, also take part in the work. ISO collaborates

10、 closely with the International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization. International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2. The main task of technical committees is to prepare International Standards.

11、 Draft International Standards adopted by the technical committees are circulated to the member bodies for voting. Publication as an International Standard requires approval by at least 75 % of the member bodies casting a vote. Attention is drawn to the possibility that some of the elements of this

12、document may be the subject of patent rights. ISO shall not be held responsible for identifying any or all such patent rights. ISO 5269-3 was prepared by Technical Committee ISO/TC 6, Paper, board and pulps, Subcommittee SC 5, Test methods and quality specifications for pulps. ISO 5269 consists of t

13、he following parts, under the general title Pulps Preparation of laboratory sheets for physical testing: Part 1: Conventional sheet-former method Part 2: Rapid-Kthen method Part 3: Conventional and Rapid-Kthen sheet formers using a closed water system BS ISO 5269-3:2008vIntroduction This part of ISO

14、 5269 specifies two procedures for the preparation of laboratory sheets using a closed water system; one based on the conventional sheet former and the other on the Rapid-Kthen sheet former. Since the two procedures are based on different principles for forming and drying of the sheets, the results

15、from testing of laboratory sheets prepared using the conventional sheet former and the Rapid-Kthen sheet former will not give the same results, see Annex A. For this reason, the sheet former used shall be reported. The purpose of the preparation of laboratory sheets is to carry out subsequent physic

16、al tests on these, in order to assess the relevant properties of the pulp itself. This part of ISO 5269 is intended for use when preparing laboratory sheets from pulps with a high fines content, such as mechanical and chemimechanical pulps, as well as for pulps prepared from recycled fibres, for whi

17、ch ISO 5269-1 and ISO 5269-2, using an open water system, in general cannot be used to prepare representative sheets (see 5in the Bibliography). BS ISO 5269-3:2008blank1Pulps Preparation of laboratory sheets for physical testing Part 3: Conventional and Rapid-Kthen sheet formers using a closed water

18、 system 1 Scope This part of ISO 5269 specifies two procedures for preparing a closed water system which is in retention equilibrium, to be used for the preparation of laboratory sheets from pulps with a high fines content. One procedure is applicable to the preparation of laboratory sheets using th

19、e conventional sheet former and the other using the Rapid-Kthen sheet former. The sheets prepared prior to attaining retention equilibrium are discarded. This part of ISO 5269 is especially applicable to mechanical and chemimechanical pulps, as well as to pulps prepared from recycled fibres, i.e. pu

20、lps with a high fines content for which retention of fines is poor when using the open water system as described in ISO 5269-1 or ISO 5269-2. This part of ISO 5269 is not applicable to some very long-fibred pulps, such as those from unshortened cotton, flax and similar materials. After retention equ

21、ilibrium is attained, the preparation of laboratory sheets for testing the physical properties follows the procedures described in ISO 5269-1 (conventional sheet former) or ISO 5269-2 (Rapid-Kthen sheet former), whichever is relevant. This part of ISO 5269 is generally not applicable for the prepara

22、tion of laboratory sheets from chemical pulps for which ISO 5269-1 or ISO 5269-2 are used. This part of ISO 5269 is not applicable for the preparation of laboratory sheets for measuring ISO brightness. These sheets can be prepared in accordance with ISO 36883. NOTE The procedures for forming, pressi

23、ng and drying are different when using the conventional sheet former and Rapid-Kthen sheet former, see Annex A. 2 Normative references The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated referenc

24、es, the latest edition of the referenced document (including any amendments) applies. ISO 5263-1, Pulps Laboratory wet disintegration Part 1: Disintegration of chemical pulps ISO 5263-2, Pulps Laboratory wet disintegration Part 2: Disintegration of mechanical pulps at 20 C ISO 5263-3, Pulps Laborato

25、ry wet disintegration Part 3: Disintegration of mechanical pulps at W 85 C ISO 5269-1:2005, Pulps Preparation of laboratory sheets for physical testing Part 1: Conventional sheet-former method ISO 5269-2:2004, Pulps Preparation of laboratory sheets for physical testing Part 2: Rapid-Kthen method BS

26、ISO 5269-3:20082 3 Principle White water at retention equilibrium is produced by preparing laboratory sheets of defined grammage using a closed water system. This white water is then used to prepare the sheets which will be used for physical testing, in either the conventional sheet former or the Ra

27、pid-Kthen sheet former. NOTE The physical properties of sheets made in accordance with this International Standard using a closed water system in retention equilibrium will differ, in general, from the properties of sheets made in accordance with ISO 5269-1 or ISO 5269-2 using an open water system.

28、4 Apparatus Use either a conventional sheet former or a Rapid-Kthen sheet former. 4.1 Conventional sheet former. All the items described in 4.1 to 4.10 in ISO 5269-1:2005, and the following. 4.1.1 Circulating water system for the conventional sheet former, consisting of a reservoir placed under the

29、drainage vessel to collect the circulating water and a pumping system which allows the sheet former to be filled from below the wire and also from above the wire. The water in the closed water system shall be in motion to avoid sedimentation of the fines. All parts of the system that come into conta

30、ct with the water shall be of a non-corrosive material (plastic or stainless steel). 4.2 Rapid-Kthen sheet former. All the items described in 4.1 to 4.2.6 in ISO 5269-2:2004, and the following. 4.2.1 Circulating water system for the Rapid-Kthen sheet former, consisting of a water reservoir, faciliti

31、es to recirculate the water and a pumping system which allows the sheet former to be filled from above the wire. The water in the closed water reservoir shall be in motion to avoid sedimentation of the fines. All parts of the system that come into contact with the water shall be of a non-corrosive m

32、aterial (plastic or stainless steel). 5 Preparation of sample 5.1 Disintegration Disintegrate mechanical and chemimechanical pulps in accordance with ISO 5263-2 or ISO 5263-3, whichever is relevant. ISO 5263-3 shall be used if the pulp exhibits latency. Disintegrate pulps made from recycled fibres i

33、n accordance with ISO 5263-2. Some chemical pulps, e.g. straw pulps, can have a high fines content. If, for that reason, this part of ISO 5269 is to be used, disintegrate the chemical pulp in accordance with ISO 5263-1. For slush pulp taken from mill streams, follow the instructions of the relevant

34、part of ISO 5263. 5.2 Dilution Dilute the stock with water to a mass fraction of between 0,2 % and 0,5 %. Use the stock for forming sheets with a minimum of delay. It is recommended to use a mass fraction between 0,2 % and 0,3 % for stocks that tend to produce flocs. NOTE Within the limits of normal

35、 tap water, the quality of the water used does not have any influence on the physical properties of the laboratory sheets prepared. BS ISO 5269-3:200836 Procedure for the conventional sheet former 6.1 Preparation of white water in retention equilibrium For sheets to be used for testing the general p

36、hysical properties, the grammage is 60,0 g/m2 2,0 g/m2on an oven-dry basis. If sheets are to be used for tests requiring another grammage, sheets shall be made to the required grammage to an accuracy of 3 %. Close the water system and fill the water reservoir with tap water at room temperature, 20 C

37、 5 C. Use the closed water system and the stock prepared in 5.2. When preparing the sheets, fill the lower section of the sheet former from the bottom with water up to the wire screen. Then fill from the top and, before the water level arrives at the mark located (350 1) mm above the wire screen, ad

38、d the required amount of the stock. Prepare at least 10 laboratory sheets having a nominal grammage of 60,0 g/m2to attain a closed water system in a state of retention equilibrium (the retention of fines). Check that the state of equilibrium is attained by weighing the dried sheets. During the build

39、-up of the white water to retention equilibrium, the mass of the sheets increases. When the oven-dry mass of the sheets remains constant even when additional sheets are prepared, the retention equilibrium is attained. Reject the laboratory sheets prepared to attain the retention equilibrium. If shee

40、ts of a grammage of 60 g/m2are required, from the mass of the last sheet, either determine the amount of stock which will produce a laboratory sheet of this oven-dry grammage, or adjust the stock concentration so that a sheet of this oven-dry grammage can be produced using a vessel of known fixed vo

41、lume. Prepare the sheets in accordance with 6.2. If sheets of a higher grammage are required, using the white water prepared above, prepare further sheets at the higher grammage until the new retention equilibrium is achieved. From the mass of the last sheet, determine the amount of stock required o

42、r adjust the stock concentration as above. Prepare the sheets in accordance with 6.2. NOTE On a conditioned basis, the grammage of laboratory sheets having a grammage of 60 g/m2is approximately 65 g/m2. 6.2 Preparation of laboratory sheets for physical testing With the exception that the sheet forme

43、r shall be filled from the bottom up to the wire screen level, and from the top from the screen up to the 350 mm mark, using the white water prepared in 6.1, use the procedure described in ISO 5269-1 and prepare laboratory sheets of the required grammage for physical testing. Before testing, conditi

44、on the laboratory sheets in accordance with ISO 1871. The testing should be performed in accordance with ISO 52704. 7 Procedure for the Rapid-Kthen sheet former 7.1 Preparation of white water in retention equilibrium For sheets to be used for testing the general physical properties, the grammage is

45、75 g/m2 2 g/m2on an oven-dry basis. If sheets are to be used for tests requiring another grammage, the grammage is 140 g/m2 4 g/m2, calculated on an oven-dry basis. Close the outlet and fill the closed water reservoir with tap water at room temperature, 20 C 5 C. Start the recirculation pump. Use th

46、e closed water system and the stock prepared in 5.2 and start to prepare sheets. The sheet former is always filled from the top. Prepare at least eight laboratory sheets having a nominal grammage of 75 g/m2to attain a closed water system in a state of retention equilibrium (the retention of fines).

47、Check that the state of equilibrium is attained by weighing the dried sheets. During the build-up of the white water to retention equilibrium, the mass of the sheets increases. When the oven-dry mass of the sheets remains constant even when additional sheets are prepared, the retention equilibrium i

48、s attained. Reject the laboratory sheets prepared to attain the retention equilibrium. BS ISO 5269-3:20084 If sheets of a grammage of 75 g/m2are required, from the mass of the last sheet, either determine the amount of stock which will produce a laboratory sheet of this oven-dry grammage, or adjust

49、the stock concentration so that a sheet of this oven-dry grammage can be produced using a vessel of known fixed volume. Prepare the sheets in accordance with 7.2. If sheets of the higher grammage (140 g/m2) are required, using the white water prepared above, prepare further sheets at the higher grammage until the new retention equilibrium is achieved. From the mass of the last sheet, determine the amount of stock required or adjust the stock concentration as above. Prepare the sheets in accordance wit