《BS 3L 80-1985 Specification for sheet and strip of aluminium-21 4% magnesium alloy (temper designation-O)《铝-镁2 25%合金板材和带材规范(强度符号-0)》.pdf》由会员分享，可在线阅读，更多相关《BS 3L 80-1985 Specification for sheet and strip of aluminium-21 4% magnesium alloy (temper designation-O)《铝-镁2 25%合金板材和带材规范(强度符号-0)》.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS3L80:1985 (Superseding BS2L80) Specification for Sheet and strip of aluminium-2! % magnesium alloy (Temper designation0) UDC 629.7:669.715721 41BS3L80:1985 This BritishStandard, having been prepared under the directionof the Aerospace Standards Committee, was publ

2、ished under the authorityofthe Board of BSI andcomesintoeffect on 31December1985 BSI02-2000 The following BSI references relate to the work on this standard: Committee reference ACE/24 Draft for comment 81/77624 DC ISBN 0 580 14844 0 Committees responsible for this BritishStandard The preparation of

3、 this BritishStandard was entrusted by the Aerospace Standards Committee (ACE/-) to Technical Committee ACE/24 upon which the following bodies were represented: Aluminium Federation Aluminium Stockholders Association Association of Light Alloy Refiners Limited BNF Metals Technology Centre British Fo

4、rging Industry Association British Industrial Fasteners Federation British Investment Casting Trade Association Institute of British Foundrymen Light Metal Founders Association Magnesium Industry Council Ministry of Defence Society of British Aerospace Companies Limited Amendments issued since publi

5、cation Amd. No. Date of issue CommentsBS3L80:1985 BSI 02-2000 i Contents Page Committees responsible Inside front cover 1 Inspection and testing procedure 1 2 Quality of material 1 3 Chemical composition 1 4 Condition 1 5 Heat treatment 1 6 Mechanical properties 1 Publication referred to Inside back

6、 coverBS3L80:1985 ii BSI 02-2000 NOTE 1Other forms of material of the same composition are covered by the following BritishStandards: BS L44, Forging stock, bars, extruded sections and forgings. BS L56, Tube (Temper designation0) (Seamless: tested hydraulically). BS L81, Sheet and strip (Temper desi

7、gnation H16 or H26). NOTE 2The chemical composition of this material complies with that registered as InternationalDesignation5251. NOTE 3The title of the publication referred to in this standard is listed on the inside back cover. A British Standard does not purport to include all the necessary pro

8、visions of a contract. Users of British Standards are responsible for their correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. Summary of pages This document comprises a front cover, an inside front cover, pagesi andii, pages1 and 2, an

9、 inside back cover and a back cover. This standard has been updated (see copyright date) and may have had amendments incorporated. This will be indicated in the amendment table on the inside front cover.BS3L80:1985 BSI 02-2000 1 1 Inspection and testing procedure This BritishStandard shall be used i

10、n conjunction with the relevant sections of the latest issue of BSL100. 2 Quality of material The material shall be made from aluminium of the chemical composition specified in clause3, with or without approved scrap at the discretion of the manufacturer. 3 Chemical composition The chemical composit

11、ion of the material shall be: 4 Condition The material shall be supplied annealed. 5 Heat treatment None. 6 Mechanical properties 6.1 Tensile test. The mechanical properties obtained from test pieces selected and prepared in accordance with the relevant requirements of BSL100 shall be as follows: El

12、ement % min. max. Silicon Iron Copper Manganese Magnesium Chromium Zinc a Titanium a Others: each Others: total Aluminium 0.10 1.70 0.40 0.50 0.15 0.50 2.40 0.15 0.15 0.15 0.05 0.15 Remainder a Subject to the discretion of the Quality Assurance Authority, determination of these elements need be made

13、 on a small proportion only of the samples analysed. Nominal thickness 0.2% proof stress Tensile strength Elongation on gauge length of50mm min. min. max. min. mm MPa MPa MPa % 0.4 up to and including2.6 Over2.6 up to and including6.0 60 60 160 160 200 200 18 202 blankBS3L80:1985 BSI 02-2000 Publica

14、tion referred to BS L100, Procedure for inspection and testing of wrought aluminium and aluminium alloys. BS3L80:1985 BSI 389 Chiswick High Road London W4 4AL BSIBritishStandardsInstitution BSI is the independent national body responsible for preparing BritishStandards. It presents the UK view on st

15、andards in Europe and at the international level. It is incorporated by Royal Charter. Revisions BritishStandards are updated by amendment or revision. Users of BritishStandards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality

16、 of our products and services. We would be grateful if anyone finding an inaccuracy or ambiguity while using this BritishStandard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel:02089969000. Fax:02089967400. BSI off

17、ers members an individual updating service called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel:02089969001. Fax:020899670

18、01. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as BritishStandards, unless otherwise requested. Information on standards BSI provides a wide range of information on national, European and international standa

19、rds through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel:02089967111. Fax:02089967048. Subscribing members of BSI are kept up to date wi

20、th standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel:02089967002. Fax:02089967001. Copyright Copyright subsists in all BSI publications. BSI also holds the copyright, in the UK,

21、of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying, recording or otherwise without prior

22、written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. If permission is granted, the terms may include royalty payments or a licensing agreement. Details and advice can be obtained from the Copyright Manager. Tel:02089967070.