ASTM F682-1982a(2004) Standard Specification for Wrought Carbon Steel Sleeve-Type Pipe Couplings《锻制碳素钢套筒型管联接器标准规范》.pdf

《ASTM F682-1982a(2004) Standard Specification for Wrought Carbon Steel Sleeve-Type Pipe Couplings《锻制碳素钢套筒型管联接器标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM F682-1982a(2004) Standard Specification for Wrought Carbon Steel Sleeve-Type Pipe Couplings《锻制碳素钢套筒型管联接器标准规范》.pdf（6页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: F 682 82a (Reapproved 2004)An American National StandardStandard Specification forWrought Carbon Steel Sleeve-Type Pipe Couplings1This standard is issued under the fixed designation F 682; the number immediately following the designation indicates the year oforiginal adoption or, in the

2、 case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defense.1. Scope1.1 This

3、specification covers wrought carbon steel sleeve-type pipe couplings suitable for joining carbon steel pipes.1.2 Type I couplings are intended for use on all schedules ofpipe in which the pipe wall thickness does not exceed the wallthickness of standard weight pipe. Type II couplings areintended for

4、 use on all schedules of pipe in which the pipe wallthickness does not exceed the wall thickness of extra strongpipe.1.3 This specification does not cover cast steel couplings.NOTE 1The values stated in inch-pound units are to be regarded as thestandard.NOTE 2See Appendix X1 for rationale used to de

5、velop this specifi-cation.2. Referenced Documents2.1 ASTM Standards:2A 53/A 53M Specification for Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and SeamlessA 106/A 106M Specification for Seamless Carbon SteelPipe for High-Temperature ServiceA 234/A234M Specification for Piping Fittings of W

6、roughtCarbon Steel and Alloy Steel for Moderate and HighTemperature ServiceA 370 Test Methods and Definitions for Mechanical Testingof Steel ProductsE 59 Practice for Sampling Steel and Iron for Determinationof Chemical Composition32.2 Manufacturers Standardization Society of the Valveand Fittings I

7、ndustry Standard:MSS SP-25 Standard Marking System for Valves, Fittings,Flanges and Unions42.3 ASME Boiler and Pressure Vessel Code:Section VIII Unfired Pressure Vessels5Section IX Welding Qualifications52.4 Federal Regulations:Title 46, Code of Federal Regulations (CFR), Shipping,Parts 41 to 6962.5

8、 ANSI Standards:B16.5 Pipe Flanges and Flange Fittings73. Classification3.1 Couplings are furnished in two types as follows:3.1.1 Type ICouplings (see 1.2).3.1.2 Type IICouplings (see 1.2).NOTE 3Type II couplings may be used in place of Type I couplingsfor all schedules of pipe in which the pipe wal

9、l thickness does not exceedthe wall thickness of standard weight piping through 18 in. or Schedule 40piping through 16 in.4. Ordering Information4.1 Orders for material under this specification shall includethe following information:4.1.1 Quantity (number of couplings of each size and type),4.1.2 Na

10、me of material (sleeve-type pipe couplings),4.1.3 Size (nominal, see Table 1 and Table 2 and Fig. 1),4.1.4 Type (see 3.1),4.1.5 ASTM designation and date of issue.5. Materials and Manufacture5.1 MaterialsThe couplings shall be manufactured frommaterial having a chemical composition conforming to the

11、requirements of 7.1 and with the mechanical properties ofSection 9.5.2 ManufactureThe initial form of the raw material shallbe at the discretion of the manufacturer except couplings shallnot be machined from unformed plate. The material shall besuch that the finished couplings conform to all of the

12、specifiedrequirements (see Appendix X2).1This specification is under the jurisdiction of ASTM Committee F25 on Shipsand Marine Technology and is the direct responsibility of Subcommittee F25.11 onMachinery and Piping Systems.Current edition approved Nov. 1, 2004. Published November 2004. Originallya

13、pproved in 1980. Last previous edition approved in 1998 as F 682 82a (1998).2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onth

14、e ASTM website.3Withdrawn.4Available from Manufacturers Standardization Society of the Valve and FittingsIndustry (MSS), 127 Park St., NE, Vienna, VA 22180-4602.5Available from American Society of Mechanical Engineers (ASME), ASMEInternational Headquarters, Three Park Ave., New York, NY 10016-5990.6

15、Available from Standardization Documents Order Desk, Bldg. 4 Section D, 700Robbins Ave., Philadelphia, PA 19111-5094, Attn: NPODS.7Available from American National Standards Institute (ANSI), 25 W. 43rd St.,4th Floor, New York, NY 10036.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C7

16、00, West Conshohocken, PA 19428-2959, United States.5.3 Couplings fabricated by welding shall be (a) made bywelders, welding operators, and welding procedures qualifiedunder the provisions of ASME Boiler and Pressure VesselCode, Section IX; (b) heat treated in accordance with Section6 of this specif

17、ication; and (c) nondestructively tested asfollows:5.3.1 Sizes 3-in. NPS and BelowRadiographically exam-ined throughout the entire length of each fabricated weld inaccordance with Paragraph UW-51 of ASME Code, SectionVIII.5.3.2 Sizes 312 -in. NPS Through 16-in. NPS No nonde-structive tests required,

18、 and5.3.3 Sizes 18-in. NPS and AboveAny method of nonde-structive testing may be used provided the tests are conductedin accordance with the applicable parts of ASME Code,Section VIII.6. Heat Treatment6.1 Couplings Made from Plate or Tubular Products:TABLE 1 Dimensions for Type I Couplings (See Fig.

19、 1)Nominal Size, in.Dimension A, InsideDiameter, in. (mm)ADimension B, OutsideDiameter, in. (mm)BDimension C, Thick-ness, min, in. (mm)Dimension D,Length, in. (mm)C14 0.589 (15.0) 0.875 (22.2) 0.143 (3.6) 1 (25)38 0.724 (18.4) 0.992 (25.2) 0.134 (3.4) 114 (32)12 0.889 (22.6) 1.201 (30.5) 0.156 (4.0)

20、 114 (32)34 1.099 (27.9) 1.401 (35.6) 0.151 (3.8) 112 (38)1 1.364 (34.6) 1.710 (43.4) 0.173 (4.4) 112 (38)114 1.709 (43.4) 2.057 (52.2) 0.174 (4.4) 112 (38)112 1.949 (49.5) 2.306 (58.6) 0.179 (4.5) 112 (38)2 2.424 (61.6) 2.807 (71.3) 0.192 (4.9) 112 (38)212 2.924 (74.3) 3.444 (87.5) 0.260 (6.6) 112

21、(38)3 3.545 (90.0) 4.105 (104.3) 0.280 (7.1) 112 (38)312 4.070 (103.4) 4.633 (117.7) 0.282 (7.2) 2 (51)4 4.570 (116.1) 5.164 (131.2) 0.297 (7.5) 2 (51)5 5.660 (143.8) 6.286 (159.7) 0.313 (8.0) 2 (51)6 6.720 (170.7) 7.409 (188.2) 0.345 (8.8) 2 (51)8 8.720 (221.5) 9.527 (242.0) 0.404 (10.3) 212 (64)10

22、 10.880 (276.4) 11.875 (301.6) 0.498 (12.6) 212 (64)12 12.880 (327.2) 13.800 (350.5) 0.460 (11.7) 212 (64)14 14.140 (359.2) 15.050 (382.3) 0.455 (11.6) 212 (64)16 16.160 (410.5) 17.050 (433.1) 0.445 (11.3) 212 (64)18 18.180 (461.8) 19.050 (483.9) 0.435 (11.0) 212 (64)ATolerances shall be (1) Sizes t

23、hrough 3 in. incl: +0.000, 0.010 in. (+0.000, 0.254 mm); (2) Sizes 312 through 10 in. incl: +0.030, 0.000 in. (+0.762, 0.000 mm);and (3) Sizes above 10 in.: +0.060, 0.000 in. (+1.524, 0.000 mm).BTolerances shall be (1) Sizes through 10 in. incl: +0.125, 0.000 in. (+3.175, 0.000 mm) and (2) Sizes abo

24、ve 10 in.: +1.000, 0.000 in. (+25.4, 0.000 mm).CTolerances for all sizes shall be +0.250, 0.000 in. (+6.4, 0.000 mm).TABLE 2 Dimensions for Type II Couplings (See Fig. 1)Nominal Size, in.Dimension A, InsideDiameter, in. (mm)ADimension B, OutsideDiameter, in. (mm)BDimension C, Thick-ness, min, in. (m

25、m)Dimension D,Length, in. (mm)C14 0.589 (15.0) 1.055 (26.8) 0.233 (5.9) 1 (25)38 0.724 (18.4) 1.156 (29.4) 0.216 (5.5) 114 (32)12 0.889 (22.6) 1.369 (34.8) 0.240 (6.1) 114 (32)34 1.099 (27.9) 1.557 (39.5) 0.229 (5.8) 112 (38)1 1.364 (34.6) 1.876 (47.7) 0.256 (6.5) 112 (38)114 1.709 (43.4) 2.221 (56.

26、4) 0.256 (6.5) 112 (38)112 1.949 (49.5) 2.469 (62.7) 0.260 (6.6) 112 (38)2 2.424 61.6) 2.986 (75.8) 0.281 (7.1) 112 (38)212 2.924 (74.3) 3.648 (92.7) 0.362 (9.2) 112 (38)3 3.545 (90.0) 4.340 (110.2) 0.398 (10.1) 112 (38)312 4.070 (103.4) 4.891 (124.2) 0.411 (10.4) 2 (51)4 4.570 (116.1) 5.444 (138.3)

27、 0.437 (11.1) 2 (51)5 5.660 (143.8) 6.613 (168.0) 0.477 (12.1) 2 (51)6 6.720 (170.7) 7.875 (200.0) 0.578 (14.7) 2 (51)8 8.720 (221.5) 10.125 (257.2) 0.703 (17.8) 212 (64)10 10.880 (276.4) 12.150 (308.6) 0.635 (16.1) 212 (64)12 12.880 (327.2) 14.150 (359.4) 0.635 (16.1) 212 (64)14 14.140 (359.2) 15.4

28、00 (391.2) 0.630 (16.0) 212 (64)16 16.160 (410.5) 17.400 (442.0) 0.620 (15.7) 212 (64)18 18.180 (461.8) 19.400 (492.8) 0.610 (15.5) 212 (64)ATolerances shall be (1) Sizes through 3 in. incl: +0.000, 0.010 in. (+0.000, 0.254 mm); (2) Sizes 312 through 10 in. incl: +0.030, 0.000 in. (+0.762, 0.000 mm)

29、;and (3) Sizes above 10 in.: +0.060, 0.000 in. (+1.524, 0.000 mm).BTolerances shall be (1) Sizes through 10 in. incl: +0.125, 0.000 in. (+3.175, 0.000 mm) and (2) Sizes above 10 in.: +1.000, 0.000 in. (+25.4, 0.000 mm).CTolerances for all sizes shall be +0.250, 0.000 in. (+6.4, 0.000 mm). Editoriall

30、y corrected.F 682 82a (2004)26.1.1 Couplings machined from tubular products need notbe heat treated.6.1.2 Hot-formed couplings upon which the final formingoperation is completed at a temperature above 1150F (621C)and below 1800F (982C) need not be heat treated providedthey are cooled in still air. I

31、f the manufacturer elects to heattreat such couplings it shall be by one of the proceduresdescribed in 6.3.6.1.3 Hot-formed couplings finished at a temperature inexcess of 1800F (982C) shall subsequently be annealed,normalized, or normalized and tempered.6.1.4 Cold-formed couplings upon which the fi

32、nal formingoperation is completed at a temperature below 1150F (621C)shall be normalized or shall be stress-relieved at 1100 to1250F (593 to 677C) for 1 h/in. of thickness.6.1.5 Couplings produced by fusion welding shall bepostweld heat treated at 1100 to 1250F (593 to 677C), whenthe nominal wall th

33、ickness at the welded joint is34 in. orgreater.6.2 Carbon Steel Couplings Made from ForgingsCouplings made from forgings shall subsequently be annealed,normalized, or normalized and tempered.6.3 Heat Treatment ProceduresCouplings after forming atan elevated temperature shall be cooled to a temperatu

34、re belowthe critical range under suitable conditions to prevent injuriesby too rapid cooling, but in no case more rapidly than thecooling rate in still air. Couplings that are to be heat treatedshall be treated as follows:6.3.1 Full AnnealingCouplings shall be uniformly re-heated to a temperature ab

35、ove the transformation range and,after being held for a sufficient time at this temperature, cooledslowly to a temperature below the transformation range.6.3.2 NormalizingCouplings shall be uniformly reheatedto a temperature above the transformation range and subse-quently cooled in air at room temp

36、erature.6.3.3 Tempering and Postweld Heat TreatmentCouplingsshall be reheated to the prescribed temperature below thetransformation range, held at temperature for not less than 1h/in. of thickness at the thickest section, and cooled in thefurnace or in still air.7. Chemical Requirements7.1 The coupl

37、ings shall conform to the requirements as tochemical composition prescribed in Table 3.7.2 Weld metal used in the construction of the couplingsshall be mild steel analysis No. Al of Table QW-442, SectionIX of the ASME Boiler and Pressure Vessel Code.8. Product Analysis8.1 Product analyses may be mad

38、e by the purchaser fromfinished products representing each lot. The chemical compo-sition thus determined shall conform to the requirementsspecified in Table 3.8.2 In the event the couplings do not conform to therequirements specified in Table 3, referee analyses shall bemade on additional couplings

39、 from the same lot in accordancewith Practice E 59.9. Mechanical Properties9.1 The steel shall conform to the requirements as to tensileproperties prescribed in Table 4.9.2 The yield strength corresponding to a permanent offsetof 0.2 % of the gage length of the specimen under load shall bedetermined

40、.9.3 Tension tests shall be made on material representative ofand in the same condition of heat treatment as the finishedcoupling.9.3.1 Records of the tension tests shall be certification thatthe material of the coupling meets the requirements of thisspecification provided the heat treatments are th

41、e same. If theraw material was not tested, the coupling manufacturer shallperform the required test on material representative of thefinished coupling.9.4 The tests required by this specification shall conform tothose described in the latest issue of Test Methods andDefinitions A 370.10. Dimensions

42、and Permissible Variations10.1 The dimensions and permissible variations for sleevecouplings to this specification are prescribed in Table 1 andTable 2.11. Workmanship, Finish, and Appearance11.1 Sleeve couplings shall have a workmanlike finish, freeof scale and injurious defects. Ends shall be fini

43、shed square andwithout burrs.FIG. 1 Sleeve-Type Pipe CouplingTABLE 3 Chemical RequirementsComposition, max, %Carbon 0.30Manganese 1.20Phosphorus 0.05Sulfur 0.06F 682 82a (2004)312. Hydrostatic Testing12.1 Hydrostatic testing is not required by this specification.12.2 All couplings shall be capable o

44、f withstanding, withoutfailure, leakage, or impairment of serviceability, a test pressureequal to that prescribed in the specification for the pipe withwhich the fitting is recommended to be used.13. Product Marking13.1 Identification marks consisting of the manufacturerssymbol or name, the ASTM des

45、ignation number, type, and sizeshall be legibly stamped on each fitting, and in such a positionas not to injure the usefulness of the fitting. SP-25 may befollowed except the word “steel” shall not be substituted for theASTM designation.13.2 Where couplings are manufactured by an activity forits own

46、 use, the marking requirements of 13.1 do not pertain.14. Keywords14.1 carbon steel sleeve-type pipe couplings; couplings;pipe couplings; Type I couplings; Type II couplingsAPPENDIXES(Nonmandatory Information)X1. RATIONALE USED FOR DEVELOPMENT OF SPECIFICATION F 682X1.1 This specification has been d

47、eveloped to provide twotypes of couplings. Type I is for use on all schedules of pipe inwhich the pipe wall thickness does not exceed the wallthickness of standard weight pipe. Type II is for use on allschedules of pipe in which the pipe wall thickness does notexceed the wall thickness of extra stro

48、ng pipe. Note 3 providesan option that allows the use of Type II couplings in place ofType I couplings, if desired.X1.2 The design criteria for the couplings is based on CFRTitle 46, Subpart 56.70-15(d)3 and 4 as follows:X1.2.1 For couplings through 3-in. IPS, the clearance be-tween the system pipe

49、outside diameter and the sleeve couplinginside diameter has been held to a maximum of 0.080 in. whenconsidering tolerances to allow these couplings to be used inClass I piping through 3 in. when not subjected to fullradiography as allowed by CFR Title 46. The inside diameterof the coupling is therefore equal to the minimum outsidediameter of the pipe to be joined +0.080 in. with a tolerance of+0.000, 0.010 in. This provides for a maximum diametralclearance of 0.080