ASTM E2190-2002 Standard Specification for Insulating Glass Unit Performance and Evaluation《绝缘玻璃器件性能和评价的标准规范》.pdf

《ASTM E2190-2002 Standard Specification for Insulating Glass Unit Performance and Evaluation《绝缘玻璃器件性能和评价的标准规范》.pdf》由会员分享，可在线阅读，更多相关《ASTM E2190-2002 Standard Specification for Insulating Glass Unit Performance and Evaluation《绝缘玻璃器件性能和评价的标准规范》.pdf（2页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: E 2190 02Standard Specification forInsulating Glass Unit Performance and Evaluation1This standard is issued under the fixed designation E 2190; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision.

2、 A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.1. Scope1.1 This specification is applicable to preassembled perma-nently sealed insulating glass units with one or two airspacesand preassembl

3、ed insulating glass units with capillary tubesintentionally left open.1.2 This specification is applicable only to sealed insulatingglass units that are constructed with glass.1.3 The qualification of test specimens is based on frost/dewpoint and on the absence of fog after the specified testduratio

4、ns.1.4 Qualification under this specification is intended toprovide a basis for evaluating the durability of sealed insulatingglass units.1.5 This specification is not applicable to sealed insulatingglass units containing a spandrel glass coating due to testmethod limitations.1.6 This specification

5、does not cover other physical require-ments such as appearance, thermophysical properties, heat andlight transmission, and glass displacement.NOTE 1Sealed insulating glass units qualified according to thisspecification are not necessarily suitable for structurally glazed applica-tions. Factors such

6、as sealant longevity when exposed to long termultraviolet light and the structural properties of the sealant must bereviewed for these applications. For more information on the requirementsfor structural sealant glazing applications refer to Specification C 1369,Guide C 1249, and Test Method C 1265.

7、1.7 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determine the applica-bility of regulatory requirements prior to use.2. Referenced

8、Documents2.1 ASTM Standards:C 162 Terminology of Glass and Glass Products2C 717 Terminology of Building Seals and Sealants3C 1036 Specification for Flat Glass2C 1249 Guide for Secondary Seal for Sealed InsulatingGlass Units for Structural Sealant Glazing Applications3C 1265 Test Method for Determini

9、ng the Tensile Propertiesof an Insulating Glass Edge Seal for Structural GlazingApplications3C 1369 Specification for Edge Sealants for StructurallyGlazed Insulating Glass Units3E 546 Test Methods for Frost Point of Sealed InsulatingGlass Units4E 631 Terminology of Building Constructions4E 2188 Test

10、 Method for Insulating Glass Units Perfor-mance5E 2189 Test Method for Testing Resistance to Fogging inInsulating Glass Units53. Terminology3.1 Definition of Terms:3.1.1 For definitions of terms found in this Specification,refer to Terminology C 717 , Terminology C 162 and Termi-nology E 631.3.2 Def

11、initions of Terms Specific to This Standard:3.2.1 sealed insulating glass unit, na preassembled unit,comprising lites of glass, which are sealed at the edges andseparated by dehydrated space(s), intended for vision areas ofbuildings. The unit is normally used for windows, windowwalls, picture window

12、s, sliding doors, patio doors, or othertypes of fenestration.4. Performance Requirements4.1 The six units that complete the weather cycle and highhumidity phases of Test Method E 2188 unbroken shall havethe frost/dew point determined and reported.4.2 Initial, intermediate (after the weather cycle ph

13、ase) andfinal frost/dew points (after final high humidity test) shall bedetermined. For triple pane units, the frost/dew point isdetermined for all airspaces. The final frost/dew points shall be40C or colder when measured in accordance with TestMethod E 546 or equivalent.4.3 Final frost/dew points s

14、hall be determined after 24 h butno later than 7 days.4.4 FogNo fog shall be visible after testing in accordancewith Test Method E 2189.1This specification is under the jurisdiction of ASTM Committee E06 onPerformance of Buildings and is the direct responsibility of Subcommittee E06.22on Durability

15、Performance of Building Constructions.Current edition approved March 10, 2002. Published May 2002.2Annual Book of ASTM Standards, Vol 15.02.3Annual Book of ASTM Standards, Vol 04.07.4Annual Book of ASTM Standards, Vol 04.11.5Annual Book of ASTM Standards, Vol 04.12.1Copyright ASTM International, 100

16、 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.5. Test Specimens5.1 Specimen design and construction techniques shall beestablished by Test Method E 2188.5.2 The glass and airspace thickness(es) for qualificationunder this specification are 4 mm (532 in.) glass with

17、 12 mm (12in.) airspace or 5 mm (316 in.) glass with 6 mm (14 in.)airspace.5.3 Glass or airspace thickness(es), or both, may be in-creased. (For example, using 6 mm glass with 12 mm air-space.) This may result in a more rigorous test.5.4 For triple pane units, 4 mm (532 in.) glass with 6 mm (14in.)

18、airspaces are used.5.5 All of the values in 5.2 and 5.4 are nominal.5.6 Tolerance of glass thickness shall be in accordance withSpecification C 1036.5.7 Airspace tolerance(s) shall be 6 0.8 mm (132 in.).5.8 Twelve double-glazed units shall be submitted whentesting to this specification.5.9 Fourteen

19、triple-glazed units shall be submitted whentesting to this specification.6. Test Methods6.1 Unit Performance Test:6.1.1 Test six randomly selected specimens for 14 days inthe high humidity phase, followed by 63 days in the weathercycle phase followed by 28 days in the high humidity phase inaccordanc

20、e with Test Method E 2188.6.1.2 Breakage of only two specimens is permitted through-out the test.NOTE 2Breakage due to laboratory handling is not considered to betest breakage. Units broken due to handling shall be replaced and testedfrom the beginning.6.1.3 If there are more than two broken samples

21、 during thetest, do not qualify this set of test specimens.6.1.4 If a specimen has any visible deposits in the air space,do not qualify this set of test specimens for that test except aspermitted in 6.1.2 (that is, breakage).6.2 Fog Test:6.2.1 Test the two fog test specimens for 7 days in accor-danc

22、e with Test Method E 2189.6.3 The test durations are net testing periods. If the test isinterrupted for any reason, the remaining portions shall becompleted to qualify for the testing.7. Qualification7.1 When all test specimens have met the requirements asdescribed in Section 4, this set of test spe

23、cimens shall bedeemed to be qualified according to this specification.7.2 If a specimen fails to meet the requirements as describedin Section 4, this set of specimens shall not be qualifiedaccording to this specification.8. Report8.1 Test Methods:8.1.1 Report all information as required in the Repor

24、tSection of Test Method E 2188.8.1.2 Report all information as required in the ReportSection of Test Method E 2189.8.2 Test Durations:8.2.1 Report the duration of the accelerated weathering test.8.2.2 Report the duration of the high humidity testing.8.2.3 Report the duration of the fog testing.8.3 R

25、eport whether or not the set of test specimens meetsthe qualifications of this specification.9. Keywords9.1 insulating glass units; seal durability; sealed insulatingglass units; unit performance and evaluationASTM International takes no position respecting the validity of any patent rights asserted

26、 in connection with any item mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the

27、 responsible technical committee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive c

28、areful consideration at a meeting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM Internati

29、onal, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org).E 21902