ASTM D876-2000(2007)e1 Standard Test Methods for Nonrigid Vinyl Chloride Polymer Tubing Used for Electrical Insulation《电绝缘用非硬质聚氯乙烯管的标准试验方法》.pdf

《ASTM D876-2000(2007)e1 Standard Test Methods for Nonrigid Vinyl Chloride Polymer Tubing Used for Electrical Insulation《电绝缘用非硬质聚氯乙烯管的标准试验方法》.pdf》由会员分享，可在线阅读，更多相关《ASTM D876-2000(2007)e1 Standard Test Methods for Nonrigid Vinyl Chloride Polymer Tubing Used for Electrical Insulation《电绝缘用非硬质聚氯乙烯管的标准试验方法》.pdf（13页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: D 876 00 (Reapproved 2007)e1An American National StandardStandard Test Methods forNonrigid Vinyl Chloride Polymer Tubing Used for ElectricalInsulation1This standard is issued under the fixed designation D 876; the number immediately following the designation indicates the year oforigina

2、l adoption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval. Asuperscript epsilon (e) indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the Department of Defe

3、nse.e1NOTEFootnote 5 was deleted and the fire caveat in 15.2 was revised to meet Form and Style requirements editorially inFebruary 2007.1. Scope1.1 These test methods cover the testing of general-purpose(Grade A), low-temperature (Grade B), and high-temperature(Grade C)2nonrigid vinyl chloride poly

4、mer tubing, or itscopolymers with other materials, for use as electrical insula-tion. For the purpose of these test methods nonrigid tubingshall be tubing having an initial elongation in excess of 100 %at break.NOTE 1These test methods are similar but not identical to those inIEC 606842.1.2 The valu

5、es stated in inch-pound units are to be regardedas the standard, except temperature, which shall be stated indegrees Celsius. Values in parentheses are for information only.1.3 The procedures appear in the following sections:Procedure SectionASTM ReferenceStandardBrittleness Temperature 43-45 D 746C

6、orrosion Tests 74-85 D 1000Dielectric Breakdown Voltage at High Humidity 65-73 E 104Dielectric Breakdown Voltage 58-64 D 149Dimensional Tests 8-14 D 374Effect of Elevated Temperatures 25-36 D 412Flammability Test 15-21Oil Resistance Test 35-42 D 471Penetration Test 46-51Sampling 6Strain Relief Test

7、68-73Tension Test 22-24 D 412Test Conditions 7Volume Resistivity 52-57 D 2571.4 This standard does not purport to address all of thesafety concerns, if any, associated with its use. It is theresponsibility of the user of this standard to establish appro-priate safety and health practices and determi

8、ne the applica-bility of regulatory limitations prior to use. For specific hazardstatements, see Section 3.2. Referenced Documents2.1 ASTM Standards:3D 149 Test Method for Dielectric Breakdown Voltage andDielectric Strength of Solid Electrical Insulating Materialsat Commercial Power FrequenciesD 257

9、 Test Methods for DC Resistance or Conductance ofInsulating MaterialsD 374 Test Methods for Thickness of Solid Electrical Insu-lationD 412 Test Methods for Vulcanized Rubber and Thermo-plastic ElastomersTensionD 471 Test Method for Rubber PropertyEffect of LiquidsD 746 Test Method for Brittleness Te

10、mperature of Plasticsand Elastomers by ImpactD 1000 Test Methods for Pressure-Sensitive Adhesive-Coated Tapes Used for Electrical and Electronic Applica-tionsD 1711 Terminology Relating to Electrical InsulationD 5032 Practice for Maintaining Constant Relative Humid-ity by Means of Aqueous Glycerin S

11、olutionsE 104 Practice for Maintaining Constant Relative Humidityby Means of Aqueous SolutionsE 176 Terminology of Fire Standards2.2 IEC Standards:606842 Flexible insulating sleeving, Part 2, Methods oftest43. Terminology3.1 Definitions:1These test methods are under the jurisdiction of ASTM Committe

12、e D09 onElectrical and Electronic Insulating Materials and are the direct responsibility ofSubcommittee D09.07 on Flexible and Rigid Insulating Materials.Current edition approved Feb. 15, 2007. Published July 2007. Originallyapproved in 1946. Last previous edition approved in 2000 as D 876 00.2Test

13、methods applicable to Grade B will be specified at a later date.3For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM websi

14、te.4Available from American National Standards Institute, 11 W. 42nd St., NewYork, NY 10036.1Copyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959, United States.3.1.1 For definitions pertaining to electrical insulation, referto Terminology D 1711.3.1.2 F

15、or definitions pertaining to fire standards, refer toTerminology E 176.3.2 Definitions of Terms Specific to This Standard:3.2.1 brittleness temperature, nthat temperature at which50 % of the specimens fail when the specified number aretested, using the apparatus and conditions specified.3.2.2 corros

16、ive effect, nunder the prescribed conditions,the percentage change in electrical resistance of a fine copperwire in contact with the tubing.3.2.3 resistance to penetration, nthat property of tubingindicated by its resistance to high local pressures, as deter-mined by the temperature at which a steel

17、 ball punctures thetubing under the conditions of loading and temperature risespecified in these test methods.3.2.4 wall thickness, nan average value determined as onehalf of the difference between the inside and outside diametersof the tubing measured by the test method prescribed herein.4. Signifi

18、cance and Use4.1 These test methods include most of the test methods thatare considered important to characterize nonrigid vinyl chlo-ride polymer tubing. While they were developed initially forthis type of extruded tubing, their use is not limited to this typeof tubing.4.2 Variations in these test

19、methods or alternate contempo-rary methods may be used to determine the values for theproperties in this standard provided such methods ensurequality levels and measurement accuracy equal to or better thanthose prescribed herein. It is the responsibility of the organi-zations using alternate test me

20、thods to be able to demonstratethis condition. In cases of dispute, the test methods specifiedherein shall be used.NOTE 2Provision for alternate methods is necessary because of (1)the desire to simplify procedures for specific applications without alteringthe result, and (2) the desire to eliminate

21、redundant testing and use datagenerated during manufacturing process control, including that generatedunder Statistical Process Control (SPC) conditions, using equipment andmethods other than those specified herein. An example would be the useof laser micrometers or optical comparators to measure di

22、mensions.5. Hazards5.1 Lethal voltages are a potential hazard during theperformance of this test. It is essential that the test apparatus,and all associated equipment electrically connected to it, beproperly designed and installed for safe operation. Solidlyground all electrically conductive parts w

23、hich it is possible fora person to contact during the test. Provide means for use atthe completion of any test to ground any parts which were athigh voltage during the test or have the potential for acquiringan induced charge during the test or retaining a charge evenafter disconnection of the volta

24、ge source. Thoroughly instructall operators as to the correct procedures for performing testssafely. When making high voltage tests, particularly in com-pressed gas or in oil, it is possible for the energy released atbreakdown to be suffcient to result in fire, explosion, or ruptureof the test chamb

25、er. Design test equipment, test chambers, andtest specimens so as to minimize the possibility of suchoccurrences, and to eliminate the possibility of personal injury.If the potential for fire exists, have fire suppression equipmentavailable.6. Sampling6.1 Select a sufficient number of pieces of tubi

26、ng in such amanner as to be representative of the shipment.6.2 Cut the number of specimens required for the purpose oftests from the pieces selected in accordance with 6.1, takingcare to select material that is free from obvious defects.7. Test Conditions7.1 Unless otherwise specified in these test

27、methods, con-duct tests at atmospheric pressure and at a temperature of 23 62C(736 4 F). Room temperature, as stated in these testmethods, shall be within this temperature range.DIMENSIONAL TESTS8. Significance and Use8.1 The inside diameter and wall thickness are of impor-tance as a measure of dime

28、nsional uniformity. They alsoprovide important data for design purposes, and are used in thecalculation of certain physical and electrical properties of thetubing.9. Apparatus9.1 Tapered-Steel GagesUse chromium-plated gages suit-able for covering the range of tubing sizes shown in Table 1.The gages

29、shall have a uniform taper of 0.010 in./1 in. (0.010mm/mm) of length, and shall be graduated with circularlathe-cut rings every 0.5 in. (13 mm) of length. The graduationsshall then represent a uniform increase in diameter of 0.005in./0.5 in. (0.010 mm/mm) of length.9.2 MicrometersUse machinists type

30、 micrometers suit-able for covering the range of tubing sizes shown in Table 1.9.3 Steel ScaleA steel scale graduated in 0.01 in. (0.25mm).10. Test Specimens10.1 Cut a 1-in. (25-mm) specimen free of kinks from thesample. Perform this operation perpendicular to the longitudi-nal axis of the tubing sp

31、ecimen, giving a specimen 1 in. inlength having cleanly cut square ends.11. Procedure for Measuring Inside Diameter11.1 Select a gage that will fit part way into the tubularspecimen. Slip the specimen, without forcing (Note 3), over thegage until there is no visible air space between the end of thes

32、pecimen and the gage anywhere on the circumference. Con-sider this point on the gage the inside diameter of the specimen.NOTE 3When the tubing specimen tends to stick, the gage may bedipped in water to facilitate slipping the specimen over the gage. However,when water is used as a lubricant on the g

33、age, great caution should beexercised to make certain that the specimen is not forced on the gage,thereby stretching the specimen.11.2 Determine the diameter at the point of contact betweenthe specimen and gage by referring to the nearest visiblegraduation. With the steel scale, measure any distance

34、 betweenD 876 00 (2007)e12the edge of the specimen and the nearest graduation. Each 0.1in. (2.5 mm) on the length of the gage represents an increase of0.001 in. (0.025 mm) in diameter. Since the diameter at thenearest graduation is known, obtain the inside diameter of thespecimen by interpolation an

35、d report to the nearest 0.001 in.12. Procedure for Measuring Outside Diameter12.1 With the specimen located on the tapered gage asdescribed in 11.1, make three outside diameter measurementsapproximately 120 apart and adjacent to the edge of eachspecimen. Make the measurements in accordance with Test

36、Methods D 374 using Apparatus B, and observing the follow-ing additional details:12.1.1 Support the micrometer to allow both hands to befree for manipulation.12.1.2 Measure the outside diameter adjacent to, but not onor over the cut edge, and12.1.3 Rotate the tubular specimen, which is on the tapere

37、dmandrel, so that the rotation is an oscillating motion with theoutside surface of the tube just touching the fixed anvil of themicrometer. Slowly move the micrometer spindle onto thesurface of the tube until the first definite increase in theresistance to rotation of the specimen is encountered. Th

38、emicrometer reading at this time is the outside diameter of thespecimen.13. Report13.1 Report the following information:13.1.1 Inside diameter of the specimen to the nearest 0.001in. (0.025 mm),13.1.2 All readings on outside diameter of the specimen tothe nearest 0.001 in.,13.1.3 Average outside dia

39、meter, and13.1.4 Average wall thickness.14. Precision and Bias14.1 The precision of this test method has not been deter-mined due to inadequate voluntary participation and fundingneeded to conduct the round-robin testing. A statement of biasis unavailable in view of the lack of a standard referencem

40、aterial for this property.FLAMMABILITY TEST15. Scope15.1 This is a fire-test-response standard. The test proceduredescribed measures the resistance of the tubing to ignition orthe spread of flame after ignition when tested under thespecified conditions.15.2 This standard is used to measure and descr

41、ibe theresponse of materials, products, or assemblies to heat andflame under controlled conditions, but does not by itselfincorporate all factors required for fire hazard or fire riskassessment of the materials, products, or assemblies underactual fire conditions.16. Significance and Use16.1 This te

42、st may be employed to compare tubing madefrom different compounds provided that specimens with thesame dimensions are used, but it is not necessarily a measureof the flammability of the compound.17. Apparatus17.1 Sheet Metal EnclosureA three-walled sheet metalenclosure 12 in. (300 mm) wide by 14 in.

43、 (360 mm) deep by 29in. (740 mm) high, open at the top. It shall be equipped withtwo parallel horizontal metal rods 16 in. (410 mm) apart, sosituated that a wire stretched perpendicularly across each rodshall be at a 70 angle with the horizontal. The lower rod shallbe approximately 2 in. (50 mm) fro

44、m the rear wall.17.2 Bare Steel WireA length of bare steel wire, approxi-mately 0.029 in. (0.74 mm) in diameter, shall be used forsupporting the specimens during the test.17.3 BurnerAburner with a38-in. (9.5-mm) nominal boreand suitable for the gas supplied. The tube of the burner shallbe approximat

45、ely 312 in. (90 mm) long above the primary inlet.It shall be mounted upon a positioning mechanism similar tothat shown in Fig. 1. As shown in the figure, a pivotedpositioner which forms an extension of the center line of theburner barrel is attached to the barrel of the burner so as tolocate the exa

46、ct point of impingement of the inner cone on thetest specimen. The base of the burner shall be tilted 25 fromthe horizontal during the period that the flame is applied to thespecimen, and the flame shall impinge upon the specimen at anangle of 45. The system shall contain a gas regulating valve aswe

47、ll as a shutoff valve.TABLE 1 Tubing SizesSizeInside Diameter, in.AMax Min Nominal2 in. 2.070 2.000 134 in. 1.812 1.750 112 in. 1.550 1.500 114 in. 1.290 1.250 1 in. 1.036 1.000 78 in. 0.911 0.875 34 in. 0.786 0.750 58 in. 0.655 0.625 12 in. 0.524 0.500 716 in. 0.462 0.438 38 in. 0.399 0.375 516 in.

48、 0.334 0.3125 No. 0 0.347 0.325 0.330No. 1 0.311 0.289 0.294No. 2 0.278 0.258 0.263No. 3 0.249 0.229 0.234No. 4 0.224 0.204 0.208No. 5 0.198 0.182 0.186No. 6 0.178 0.162 0.166No. 7 0.158 0.144 0.148No. 8 0.141 0.129 0.133No. 9 0.124 0.114 0.118No. 10 0.112 0.102 0.106No. 11 0.101 0.091 0.095No. 12 0

49、.089 0.081 0.085No. 14 0.072 0.064 0.066No. 16 0.061 0.051 0.053No. 18 0.049 0.040 0.042No. 20 0.039 0.032 0.034ANOTEOne inch equals 25.4 mm.D 876 00 (2007)e1317.4 Gas SupplyPublic utility or propane gas may beused. For referee purposes, commercial grade propane gashaving a nominal heating value of 2521 Btu/ft3and a specificgravity of 0.508 at 60 F shall be used at a line pressure of 11in. (279 mm) water column.NOTE 4Small tanks of this gas may be obtained where regulardelivery lines are nonexistent.17.5 TimepieceA timepiece measuring seco