ASTM A473-2017a Standard Specification for Stainless Steel Forgings《不锈钢锻件的标准规格》.pdf

《ASTM A473-2017a Standard Specification for Stainless Steel Forgings《不锈钢锻件的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A473-2017a Standard Specification for Stainless Steel Forgings《不锈钢锻件的标准规格》.pdf（7页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A473 17A473 17aStandard Specification forStainless Steel Forgings1This standard is issued under the fixed designation A473; the number immediately following the designation indicates the year oforiginal adoption or, in the case of revision, the year of last revision. A number in parenth

2、eses indicates the year of last reapproval. Asuperscript epsilon () indicates an editorial change since the last revision or reapproval.This standard has been approved for use by agencies of the U.S. Department of Defense.1. Scope*1.1 This specification covers austenitic, austenitic-ferritic, ferrit

3、ic, and martensitic stainless steel forgings for general use, andfor low- or high-temperature service.1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematicalconversions to SI units that are provided for information only and are not c

4、onsidered standard.1.3 Supplementary requirements from Specification A788/A788M may be specified when additional testing, inspection, orprocessing is required.1.4 This international standard was developed in accordance with internationally recognized principles on standardizationestablished in the D

5、ecision on Principles for the Development of International Standards, Guides and Recommendations issuedby the World Trade Organization Technical Barriers to Trade (TBT) Committee.2. Referenced Documents2.1 ASTM Standards:2A370 Test Methods and Definitions for Mechanical Testing of Steel ProductsA751

6、 Test Methods, Practices, and Terminology for Chemical Analysis of Steel ProductsA788/A788M Specification for Steel Forgings, General RequirementsA1058 Test Methods for Mechanical Testing of Steel ProductsMetricE8/E8M Test Methods for Tension Testing of Metallic MaterialsE527 Practice for Numbering

7、Metals and Alloys in the Unified Numbering System (UNS)3. Ordering Information3.1 It is the responsibility of the purchaser to specify all requirements that are necessary for material ordered under thisspecification. Such requirements may include, but are not limited to, the following:3.1.1 Quantity

8、 (weight or number of pieces),3.1.2 Dimensions, including prints or sketches,3.1.3 Name of material (stainless steel forgings),3.1.4 Type or UNS designation (Table 1),3.1.5 Condition (Table 2), and3.1.6 ASTM designation and date of issue.3.1.7 Test for magnetic permeability if specified by customer

9、purchase order when ordering Types 207 and 205.3.1.8 Special requirements.3.2 If possible the intended end use of the item should be given on the purchase order especially when the item is ordered fora specific end use or uses.NOTE 1A typical ordering description is as follows: 5 stainless steel for

10、gings, Type 410, Designation A, ASTM Specification A473 dated _.End use: pump blocks for oil well equipment.1 This specification is under the jurisdiction ofASTM Committee A01 on Steel, Stainless Steel and RelatedAlloys and is the direct responsibility of Subcommittee A01.06on Steel Forgings and Bil

11、lets.Current edition approved May 1, 2017Sept. 1, 2017. Published May 2017September 2017. Originally approved in 1962. Last previous edition approved in 20162017 asA473-16.-17. DOI: 10.1520/A0473-17.10.1520/A0473-17A.2 For referencedASTM standards, visit theASTM website, www.astm.org, or contactASTM

12、 Customer Service at serviceastm.org. For Annual Book of ASTM Standardsvolume information, refer to the standards Document Summary page on the ASTM website.This document is not an ASTM standard and is intended only to provide the user of an ASTM standard an indication of what changes have been made

13、to the previous version. Becauseit may not be technically possible to adequately depict all changes accurately, ASTM recommends that users consult prior editions as appropriate. In all cases only the current versionof the standard as published by ASTM is to be considered the official document.*A Sum

14、mary of Changes section appears at the end of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States1TABLE 1 Chemical RequirementsAUNSDesig-nationBTypeNumberCarbon,%Manga-nese,%Phos-phorus,%Sulfur,%Silicon,%Chromium,%Nickel,%Mol

15、yb-denum, %Nitrogen,%OtherElements,%Austenitic GradesS20100 201 0.15 5.57.5 0.060 0.030 1.00 16.018.0 3.55.5 . . . 0.25S20200 202 0.15 7.510.0 0.060 0.030 1.00 17.019.0 4.06.0 . . . 0.25S20500 205 0.120.25 14.015.5 0.060 0.030 1.00 16.518.0 1.001.75 . . . 0.320.40S21900 XM-10 0.08 8.010.0 0.060 0.03

16、0 1.00 19.021.5 5.57.5 . . . 0.150.40S21904 XM-11 0.04 8.010.0 0.060 0.030 1.00 19.021.5 5.57.5 . . . 0.150.40S28200 . . . 0.15 17.019.0 0.045 0.030 1.00 17.019.0 . . . 0.751.25 0.400.60 Cu 0.751.25S30200 302 0.15 2.00 0.045 0.030 1.00 17.019.0 8.010.0 . . . 0.10S30215 302B 0.15 2.00 0.045 0.030 2.0

17、03.00 17.019.0 8.010.0 . . . . . .S30300 303 0.15 2.00 0.20 0.15 min 1.00 17.019.0 8.010.0 0.60C . . .S30323 303 Se 0.15 2.00 0.20 0.06 1.00 17.019.0 8.010.0 . . . . . . Se 0.15 minS30400 304 0.08 2.00 0.045 0.030 1.00 18.020.0 8.010.5 . . . 0.10S30400 304 0.08 2.00 0.045 0.030 1.00 18.020.0 8.011.0

18、 . . . 0.10S30403 304L 0.030 2.00 0.045 0.030 1.00 18.020.0 8.012.0 . . . 0.10S30500 305 0.12 2.00 0.045 0.030 1.00 17.019.0 10.513.0 . . . . . .S30800 308 0.08 2.00 0.045 0.030 1.00 19.021.0 10.012.0 . . . . . .S30815 . . . 0.10 0.80 0.040 0.030 1.402.00 20.022.0 10.012.0 . . . 0.140.20 Ce 0.030.08

19、S30900 309 0.20 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . .S30908 309S 0.08 2.00 0.045 0.030 1.00 22.024.0 12.015.0 . . . . . .S31000 310 0.25 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . .S31008 310S 0.08 2.00 0.045 0.030 1.50 24.026.0 19.022.0 . . . . . .S31254 . . . 0.020 1.00 0.030

20、0.010 0.80 19.520.5 17.518.5 6.06.5 0.180.25 Cu 0.501.00S31400 314 0.25 2.00 0.045 0.030 1.503.00 23.026.0 19.022.0 . . . . . .S31600 316 0.08 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 0.10S31603 316L 0.030 2.00 0.045 0.030 1.00 16.018.0 10.014.0 2.003.00 0.10S31700 317 0.08 2.00 0.045 0.030

21、1.00 18.020.0 11.015.0 3.04.0 0.10S32100 321 0.08 2.00 0.045 0.030 1.00 17.019.0 9.012.0 . . . . . . Ti 5C minS34700 347 0.08 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . . . . . . Cb+Ta 10C,minDS34800 348 0.08 2.00 0.045 0.030 1.00 17.019.0 9.013.0 . . . . . . Cb+Ta 10C,minDTa 0.10Co 0.20Austenitic-Fer

22、ritic GradesS32550D . . . 0.04 1.50 0.040 0.030 1.00 24.0-27.0 4.5-6.5 2.9-3.9 0.10-0.25 Cu 1.502.50S32550E . . . 0.04 1.50 0.040 0.030 1.00 24.0-27.0 4.5-6.5 2.9-3.9 0.10-0.25 Cu 1.502.50S32760D . . . 0.030 1.00 0.030 0.010 1.00 24.026.0 6.08.0 3.04.0 0.200.30 Cu 0.501.00W 0.501.00S32760E . . . 0.0

23、30 1.00 0.030 0.010 1.00 24.026.0 6.08.0 3.04.0 0.200.30 Cu 0.501.00W 0.501.00S32950 . . . 0.03 2.00 0.035 0.010 0.60 26.029.0 3.55.2 1.002.50 0.150.35Ferritic GradesS40500 405 0.08 1.00 0.040 0.030 1.00 11.514.5 0.60 . . . . . . A1 0.100.30S42900 429 0.12 1.00 0.040 0.030 1.00 14.016.0 0.75 . . . .

24、 . .S43000 430 0.12 1.00 0.040 0.030 1.00 16.018.0 0.75 . . . . . .S43020 430F 0.12 1.25 0.06 0.15 min 1.00 16.018.0 0.75 0.60C . . .S43023S44600430F Se4460.120.201.251.500.060.0400.060.0301.001.0016.018.023.027.00.750.75. . . . . . .0.25Se 0.15 minMartensitic GradesS40300 403 0.15 1.00 0.040 0.030

25、0.50 11.513.0 . . . . . . . . . . . .S41000 410 0.15 1.00 0.040 0.030 1.00 11.513.5 0.75 . . . . . . . . .S41008 410S 0.08 1.00 0.040 0.030 1.00 11.513.5 0.75 . . . . . . . . .S41400 414 0.15 1.00 0.040 0.030 1.00 11.513.5 1.252.50 . . . . . . . . .S41425 . . . 0.05 0.501.00 0.020 0.005 0.50 12.015.

26、0 4.07.0 1.502.00 0.060.12 Cu 0.30S41500 E 0.05 0.51.0 0.030 0.030 0.60 11.514.0 3.55.5 0.400.80 . . .S41500 F 0.05 0.51.0 0.030 0.030 0.60 11.514.0 3.55.5 0.400.80 . . .S41600 416 0.15 1.25 0.06 0.15 min 1.00 12.014.0 . . . 0.60C . . .S41623 416 Se 0.15 1.25 0.06 0.06 1.00 12.014.0 . . . . . . . .

27、. Se 0.15 minS42000 420 Over 0.15 1.00 0.040 0.030 1.00 12.014.0 . . . . . . . . . . . .S43100 431 0.20 1.00 0.040 0.030 1.00 15.017.0 1.252.50 . . . . . . . . .S44002 440A 0.600.75 1.00 0.040 0.030 1.00 16.018.0 . . . 0.75 . . .S44003 440B 0.750.95 1.00 0.040 0.030 1.00 16.018.0 . . . 0.75 . . .S44

28、004 440C 0.951.20 1.00 0.040 0.030 1.00 16.018.0 . . . 0.75 . . .A Maximum, unless range or minimum is indicated.B New designation established in accordance with Practice E527 and SAE J 1086.C At manufacturers option; reported only when intentionally added.D Columbium (Cb) and Niobium (Nb) are alter

29、nate names for element 41 in the Periodic Table of the Elements.E % Cr + 3.3 % Mo + 16 % N $ 40.F Wrought version of CA6NM.A473 17a24. General Requirements4.1 Material supplied to this specification shall conform to the requirements of Specification A788/A788M, which outlinesadditional ordering info

30、rmation, manufacturing requirements, testing and retesting methods and procedures, marking, certification,product analysis variations, and additional supplementary requirements.4.2 If the requirements of this specification are in conflict with the requirements of Specification A788/A788M, therequire

31、ments of this specification shall prevail.5. Manufacture5.1 Material for forgings shall consist of ingots or blooms, billets, slabs, or bars, either forged or rolled from an ingot, and cutto the required length by a suitable process.TABLE 2 Mechanical Property RequirementsType Condition Yield Streng

32、th, min,ksi (MPa)A Tensile Strength, min,ksi (MPa)Elongationin 2 in.(50 mm) or4D, min %Reductionof Area,min, %BrinellHardnessNumber,maxAustenitic Grades201, 302, 302B, 303, 303SE, 305, 308, 309,309S, 310, 310S, 314, 317, 321, 347, 348A 30 (205) 75 (515) 40 50 . . .202 A 45 (310) 90 (620) 40 50 . . .

33、205 A 50 (345) 90 (620) 40 50 . . .304 and 316, Sections 5 in. (127 mm) andUnderA 30 (205) 75 (515) 40 50 . . .304 and 316, Sections Over 5 in. (127 mm) A 30 (205) 70 (485) 40 50 . . .304L and 316L A 25 (170) 65 (450) 40 50 . . .XM-10 and XM-11 A 50 (345) 90 (620) 45 60 . . .S28200 A 60 (415) 110 (7

34、60) 40 55 . . .S30815 A 45 (310) 87 (600) 40 50 . . .S31254 A 44 (300) 95 (650) 35 50 . . .Austenitic-Ferritic GradesS32550 A 80 (550) 109 (750) 25.0 . . . 290S32950 A 70 (480) 100 (690) 15 . . . 293S32760 A 80 (550) 109 (750) 25 . . . 290Ferritic Grades430F, 430FSE, 446 A 40 (275) 70 (485) 20 45 22

35、3405 A 30 (205) 60 (415) 20 45 207429 A 35 (240) 65 450) 23 45 207430 A 35 (240) 70 (485) 20 45 217Martensitic Grades403, 410, 416, 416SE A 40 (275) 70 (485) 20 45 223403, 410 1 40 (275) 70 (485) 20 45 2232 85 (585) 110 (760) 15 45 2693 100 (690) 130 (895) 12 35 331410S A 35 (240) 65 (450) 22 45 217

36、414 A . . . . . . . . . . . . . . . . . . 298T 90 (620) 115 (795) 15 45 321H 100 (690) 125 (860) 15 45 321S41425 T 95 (655) 120 (825) 15 45 321S41500 normalized andtempered90 (620) 115 (795) 15 45 295420 A . . . . . . . . . . . . . . . . . . 223431 A . . . . . . . . . . . . . . . . . . 277BT 90 (620

37、) 115 (795) 15 . . . 321H 135 (930) 175 (1210) 13 . . . 440440A, 440B, 440C A . . . . . . . . . . . . . . . . . . 269A Yield strength shall be determined by the 0.2 % offset method in accordance with Test Methods and Definitions A370.An alternative method of determining yield strengthmay be used bas

38、ed on a total extension under load of 0.5 %.B Type 431 forgings of designation A, when specified, shall be capable of meeting the above mechanical property requirements of designation T after oil quenching from1800 to 1900 F (980 to 1038 C) and tempering at not less than 1100 F (595 C), or designati

39、on H when oil quenched from 1850 to 1950 F (1010 to 1065 C) andtempered at not more than 700 F (370 C).A473 17a35.2 The material shall be forged by hammering, pressing, rolling, extruding, or upsetting. It shall be brought as nearly aspossible to the finished shape and size by hot-working; and shall

40、 be processed, if practicable, so as to cause metal-flow during thehot-working operation in the direction most favorable for resisting the stresses encountered in service as may be indicated to themanufacturer by the purchaser.A473 17a45.3 When specified on the order, a sample forging may be section

41、ed and etched to show flow lines and the condition as regardsinternal imperfections. When so specified, the question of acceptable and unacceptable metal-flow shall be subject to agreementbetween the manufacturer and the purchaser prior to order entry.5.4 When specified on the order, the manufacture

42、r shall submit for approval of the purchaser a sketch showing the shape of therough forging before machining, or before heat treating for mechanical properties.5.5 The grain size shall be as fine as practicable and precautions shall be taken to minimize grain growth.6. Heat Treatment6.1 Except for S

43、31254, the austenitic steels shall receive a solution heat treatment, consisting of heating the material to aminimum temperature of 1900 F (1040 C), followed by cooling rapidly in air or water.6.2 S31254 shall receive a solution heat treatment, consisting of heating the material to a minimum tempera

44、ture of 2100 F(1150 C) followed by cooling rapidly in air or water.6.3 When specified,Types 347, 348, and 321 shall receive a stabilization heat treatment in addition to the solution heat treatmentspecified in 6.1, which shall consist of holding the forgings at 1550 to 1750 F (845 to 955 C) for 1 h

45、for each inch of sectionthickness with a minimum holding time of 2 h, followed by air-cooling or water quenching. The stabilization heat treatment is notusually specified, unless these steels are intended for severely corrosive environments in the temperature range from 800 to 1600 F(425 to 870 C).

46、When specified, the stabilization heat treatment shall be the final heat treatment and may be performed beforemachining.6.4 S32950 shall receive an annealing treatment, consisting of heating the material to a temperature of 1825 F (995 C) to1875 F (1025 C) for an appropriate time followed by water q

47、uenching or rapid cooling by other means.6.5 S32760 shall receive an annealing treatment consisting of heating the material to a minimum temperature of 2010 F(1100 C), followed by water quenching or rapid cooling by other means.6.6 The ferritic grades shall be properly annealed:6.7 Except for S41425

48、 and S41500, the martensitic grades shall be annealed, or hardened and tempered as specified. Liquidquenching shall be permitted only by agreement with the purchaser.6.8 For S41425, heat to 1700 F (925 C) minimum and hold for 1 h at temperature minimum. Air cool to below 90 F (32 C)and temper at 110

49、0 F (595 C) minimum for 1 h/in. of cross-sectional thickness minimum.6.9 For S41500 heat to 1750 F (955 C) minimum, air cool to 200 F (95 C) or lower prior to any optional intermediate temperand prior to the final temper. The final temper shall be between 1050 F (565 C) and 1150 F (620 C).6.10 Types 420, 440A, 440B, and 440C should be used by the purchaser in the hardened and tempered condition.