ASTM A447 A447M-2011(2016) Standard Specification for Steel Castings Chromium-Nickel-Iron Alloy (25-12 Class) for High-Temperature Service《高温设备用铬镍铁合金 (25-12级) 钢铸件的标准规格》.pdf

《ASTM A447 A447M-2011(2016) Standard Specification for Steel Castings Chromium-Nickel-Iron Alloy (25-12 Class) for High-Temperature Service《高温设备用铬镍铁合金 (25-12级) 钢铸件的标准规格》.pdf》由会员分享，可在线阅读，更多相关《ASTM A447 A447M-2011(2016) Standard Specification for Steel Castings Chromium-Nickel-Iron Alloy (25-12 Class) for High-Temperature Service《高温设备用铬镍铁合金 (25-12级) 钢铸件的标准规格》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、Designation: A447/A447M 11 (Reapproved 2016)Standard Specification forSteel Castings, Chromium-Nickel-Iron Alloy (25-12 Class),for High-Temperature Service1This standard is issued under the fixed designation A447/A447M; the number immediately following the designation indicates the yearof original a

2、doption or, in the case of revision, the year of last revision. A number in parentheses indicates the year of last reapproval.A superscript epsilon () indicates an editorial change since the last revision or reapproval.1. Scope*1.1 This specification covers iron-base, heat-resisting alloycastings of

3、 the 25 % chromium, 12 % nickel class, intended forstructural elements, containers, and supports in electricfurnaces, petroleum still tube supports, and for similar appli-cations up to 2000F 1095C.1.2 In the absence of significant proportions of elementsother than those prescribed in Section 5, the

4、two types of alloyscovered by this specification may in general be distinguished asfollows:1.2.1 Type IAlloys characterized by relatively low limit-ing creep stress at temperatures between 1500 and 2000F 815and 1095C, and relatively high ductility at ordinary tempera-tures after aging for short peri

5、ods at temperatures between1300 and 1500F 705 and 815C.1.2.2 Type IIAlloys having relatively high limiting creepstress but which may develop low ductility at ordinary tem-peratures when aged for short periods at temperatures between1350 and 1500F 730 and 815C.1.3 The values stated in either SI units

6、 or inch-pound unitsare to be regarded separately as standard. The values stated ineach system may not be exact equivalents; therefore, eachsystem shall be used independently of the other. Combiningvalues from the two systems may result in non-conformancewith the standard.1.3.1 Within the text, the

7、SI units are shown in brackets.2. Referenced Documents2.1 ASTM Standards:2A781/A781M Specification for Castings, Steel and Alloy,Common Requirements, for General Industrial UseA800/A800M Practice for Steel Casting, Austenitic Alloy,Estimating Ferrite Content ThereofA957 Specification for Investment

8、Castings, Steel andAlloy,Common Requirements, for General Industrial UseA1067 Specification for Test Coupons for Steel CastingsE8/E8M Test Methods for Tension Testing of Metallic Ma-terialsE21 Test Methods for Elevated Temperature Tension Tests ofMetallic Materials3. General Conditions for Delivery3

9、.1 Except for investment castings, material furnished tothis specification shall conform to the requirements of Speci-fication A781/A781M, including any supplementary require-ments that are indicated in the purchase order. Failure tocomply with the general requirements of Specification A781/A781M co

10、nstitutes nonconformance with this specification. Incase of conflict between the requirements of this specificationand Specification A781/A781M, this specification shall pre-vail.3.2 Investment castings furnished to this specification shallconform to the requirements of Specification A957, including

11、any supplementary requirements that are indicated in thepurchase order. Failure to comply with the general require-ments of Specification A957 constitutes nonconformance withthis specification. In the case of conflict between the require-ments of this specification and Specification A957, Specifica-

12、tion A957 shall prevail.4. Ordering Information4.1 The inquiry and order should include or indicate thefollowing:4.1.1 A description of the casting by pattern number ordrawing (dimensional tolerances shall be included on thecasting drawing),4.1.2 Which standard (A447 or A447M) applies,4.1.3 The vers

13、ion of the alloy, i.e., Type I or Type II, to besupplied (Sections 1, 11, 12, 13, and 14).4.1.4 Options in the specification (Section 9), and4.1.5 The supplementary requirements desired including thestandards of acceptance.1This specification is under the jurisdiction of ASTM Committee A01 on Steel,

14、Stainless Steel and Related Alloys and is the direct responsibility of SubcommitteeA01.18 on Castings.Current edition approved Sept. 1, 2016. Published September 2016. Originallyapproved in 1944. Redesignated as A447 in 1961. Last previous edition approved in2011 as A447/A447M 11. DOI: 10.1520/A0447

15、_A0447M-11R16.2For referenced ASTM standards, visit the ASTM website, www.astm.org, orcontact ASTM Customer Service at serviceastm.org. For Annual Book of ASTMStandards volume information, refer to the standards Document Summary page onthe ASTM website.*A Summary of Changes section appears at the en

16、d of this standardCopyright ASTM International, 100 Barr Harbor Drive, PO Box C700, West Conshohocken, PA 19428-2959. United States15. Process5.1 The alloy for the castings shall be made by the electric-furnace process or by any other process approved by thepurchaser.6. Heat Treatment6.1 Except as o

17、therwise agreed upon between the manufac-turer and the purchaser, the manufacturer shall not be requiredto heat treat the castings.7. Chemical Composition7.1 The castings shall conform to the requirements of Table1 as to chemical composition.8. Sampling8.1 Material for the tests specified in Section

18、s 11, 13, and 14may be taken from separately cast test blocks of a form such asthat shown in Fig. 2 of Specification A1067, from another typeof test block, from the castings, or from coupons attached to thecastings, as may be agreed upon between the manufacturer andthe purchaser.8.2 Material for the

19、 magnetic permeability test specimen(Section 12) may be taken, prior to heat treatment, from thesame coupon as the specimen for the tension test after aging;from suitable specimens cast as parts of separately cast testblocks; or, by agreement between the manufacturer and thepurchaser, from castings

20、representing the melt.8.3 In the case of castings for unusual or severe service, thetest coupons shall be attached to the castings at convenientlocations as may be agreed upon between the manufacturer andthe purchaser.8.4 In all cases, it shall be the manufacturers duty toprovide a sufficient number

21、 of samples for the specified tests.9. Number of Tests9.1 The purchaser shall specify not more than two testsselected from the following list, with the restriction that notmore than one of the tension tests at high temperature (that is,9.1.3 or 9.1.4) may be required:9.1.1 Tension test after aging,9

22、.1.2 Magnetic permeability test,9.1.3 Stress-rupture test, and9.1.4 Short-time high-temperature tension test.10. Retests10.1 Mechanical TestsIf any of the specimens first chosenfor any of the mechanical tests agreed upon fail to conform tothe specified requirements, an additional specimen from thesa

23、me melt may be tested. This additional specimen shallconform to the requirements prescribed for the test in question.10.2 Magnetic TestIf the magnetic permeability of thespecimen first tested does not conform to the requirementprescribed in 12.1, three additional specimens from the samemelt may be t

24、ested. At least two of these shall conform to theprescribed requirement.11. Tensile Properties After Aging11.1 The tensile properties of the material after aging shallconform to the following requirements:Type I Type IITensile strength, min, ksi MPa 80 550 80 550ElongationAin 2 in. (4D), min, % 9 4E

25、longationBin 5D, min, % 8.7 3.9AThese minima shall apply when tested according to Test Methods E8.BThese minima shall apply when tested according to Test Methods E8M.11.2 Samples from which the tension specimens are to betaken shall be heated for 24 h at 1400 6 25F 760 6 14Cand allowed to cool at le

26、ast down to 400F 205C at rates notexceeding 200F 110C/h. The tension test specimens shallbe machined from the heat-treated sample, and shall conformto the dimensions shown in Fig. 8 of Test Methods E8/E8M.11.3 The tension test shall be made in accordance with TestMethods E8/E8M. The speed of the hea

27、d of the testing machineshall be so adjusted that the rate of separation of the gagemarks on the test specimen shall not exceed 0.1 in./min 0.05mm/s.12. Magnetic Permeability12.1 The magnetic permeability of the material shall con-form to the following requirements:Magnetic Permeability,maxType I 1.

28、70Type II 1.05NOTE 1The magnetic permeability test gives a qualitative indicationof the ferrite content for alloys falling within the range of chemicalcomposition specified in Section 7, excluding iron and other elements asmay be agreed upon. When special alloying elements are specified, themagnetic

29、 permeability test is not recommended because its significancehas not yet been established for such alloys.12.2 The specimen shall be heated in air to 2000 6 25F1095 6 14C, held within this range for 24 h, and thenquenched in water. After quenching, all scale and superficialoxidized metal shall be r

30、emoved in order to avoid errors thatmight arise from the presence of magnetizable oxides formedduring heating.12.3 Unless otherwise agreed upon between the purchaserand the manufacturer, the magnetic permeability shall bedetermined in accordance with Supplementary Requirement S1of Practice A800/A800

31、M.NOTE 2Where the test method used measures volume percent ferrite,TABLE 1 Chemical RequirementsElement Composition, %NiA10.0014.00Cr 23.0028.00C 0.200.45N, max 0.20Mn, max 2.50Si, max 1.75P, max 0.030S, max 0.030Fe and other elements as may be agreed upon between themanufacturer and the purchaserAC

32、ommercial nickel usually carries a small amount of cobalt, and within the usuallimits cobalt shall be counted as nickel.A447/A447M 11 (2016)2conversion to magnetic permeability may be accomplished using thefollowing requirements:Volume, Ferrite, %,maxMagnetic Permeability,max181.051.7013. Stress-Rup

33、ture Test13.1 The following tensile stress shall be sustained for atleast 16 h without rupturing the specimen:Tensile Stress,ksi MPaType IType II5 348 5513.2 The test specimen shall conform to the dimensionsshown in Fig. 8 of Test Methods E8/E8M.13.3 The specimen in the as-cast condition shall be mo

34、untedin the testing machine and held for1hat1600 6 10F 870 65.5C. The specimen shall then be subjected to a steady tensileload while the temperature over the gage length is maintainedat 1600 6 10F 870 6 5.5C in an air atmosphere.14. Short-Time, High-Temperature Tensile Properties14.1 The short-time,

35、 high-temperature tensile propertiesshall conform to the following requirements:Tensile Strength, min, ksiMPaElongation in 2 in. 50 mm,min, %Type I as agreed upon betweenmanufacturer and purchaseras agreed upon betweenmanufacturer and purchaserType II 20 140 814.2 The test specimen shall conform to

36、the dimensionsshown in Fig. 8 of Test Methods E8/E8M.14.3 The specimen in the as-cast condition, that is, withoutany heat treatment after cooling from the casting temperature,shall be subjected to a short-time tension test during which thetemperature shall be maintained at 1600 6 10F 870 65.5C. The

37、specimen shall be mounted in the testing furnaceand held within this range of temperature for 1 h, and the testload then applied.14.4 The test shall be made in accordance with Practice E21except that the speed of head of the testing machine shall be soadjusted that the rate of separation of the gage

38、 marks on the testspecimen shall not exceed 0.03 in. 0.8 mm/min.15. Defective Test Specimens15.1 If any specimen shows defective machining or devel-ops flaws, it may be discarded and another specimen from thesame melt substituted.15.2 If any part of the fracture in any of the specimenssubjected to t

39、ension tests is more than34 in. 19.0 mm fromthe center of the gage length as indicated by gage marks placedon the specimen before testing, another specimen may besubstituted.16. Repair by Welding16.1 Weld repairs shall be inspected to the same qualitystandards as are used to inspect the castings.16.

40、2 When heat treatment is specified, the castings shall beheat treated after welding.17. Keywords17.1 austenitic stainless steel; high temperature applica-tions; stainless steel; steel castingsSUPPLEMENTARY REQUIREMENTSThe following supplementary requirements shall not be applied unless specified in

41、the purchaseorder. A list of standardized supplementary requirements for use at the option of the purchaser isincluded in Specification A781/A781M. Those which are ordinarily considered suitable for use withthe specification are given below. Others enumerated in Specification A781/A781M may be used

42、withthis specification upon agreement between manufacturer and purchaser.S5. Examination of Weld PreparationS6. CertificationS8. MarkingA447/A447M 11 (2016)3SUMMARY OF CHANGESCommittee A01 has identified the location of selected changes to this standard since the last issue(A447/A447M 10) that may i

43、mpact the use of this standard. (Approved Oct. 1, 2011.)(1) Added citations to A957, A1067, and E8M whereapplicable,(2) Added Ordering Information,(3) Added minimum metric values for room temperature elon-gation after aging,(4) Deleted Appendix X1.Committee A01 has identified the location of selecte

44、d changes to this standard since the last issue(A447/A447M 93 (2007) that may impact the use of this standard. (Approved Oct. 1, 2010.)(1) Changed the limits for S and P in Table 1.ASTM International takes no position respecting the validity of any patent rights asserted in connection with any item

45、mentionedin this standard. Users of this standard are expressly advised that determination of the validity of any such patent rights, and the riskof infringement of such rights, are entirely their own responsibility.This standard is subject to revision at any time by the responsible technical commit

46、tee and must be reviewed every five years andif not revised, either reapproved or withdrawn. Your comments are invited either for revision of this standard or for additional standardsand should be addressed to ASTM International Headquarters. Your comments will receive careful consideration at a mee

47、ting of theresponsible technical committee, which you may attend. If you feel that your comments have not received a fair hearing you shouldmake your views known to the ASTM Committee on Standards, at the address shown below.This standard is copyrighted by ASTM International, 100 Barr Harbor Drive,

48、PO Box C700, West Conshohocken, PA 19428-2959,United States. Individual reprints (single or multiple copies) of this standard may be obtained by contacting ASTM at the aboveaddress or at 610-832-9585 (phone), 610-832-9555 (fax), or serviceastm.org (e-mail); or through the ASTM website(www.astm.org). Permission rights to photocopy the standard may also be secured from the Copyright Clearance Center, 222Rosewood Drive, Danvers, MA 01923, Tel: (978) 646-2600; http:/ 11 (2016)4