BS S 538-1975 Specification for chromium-nickel-molybdenum-vanadium heat-resisting steel sheet and strip (930-1130 MPa maximum thickness 6 mm) (Cr 12 Ni 2 5 Mo 1 7 V 0 3)《铬-镍-钼-钒耐热.pdf

《BS S 538-1975 Specification for chromium-nickel-molybdenum-vanadium heat-resisting steel sheet and strip (930-1130 MPa maximum thickness 6 mm) (Cr 12 Ni 2 5 Mo 1 7 V 0 3)《铬-镍-钼-钒耐热.pdf》由会员分享，可在线阅读，更多相关《BS S 538-1975 Specification for chromium-nickel-molybdenum-vanadium heat-resisting steel sheet and strip (930-1130 MPa maximum thickness 6 mm) (Cr 12 Ni 2 5 Mo 1 7 V 0 3)《铬-镍-钼-钒耐热.pdf（8页珍藏版）》请在麦多课文档分享上搜索。

1、BRITISH STANDARD AEROSPACE SERIES BS S 538:1975 (Superseding Ministry of Defence Specification DTD 5046) Incorporating Amendment No. 1 Specification for Chromium-nickel- molybdenum-vanadium heat-resisting steel sheet and strip (9301 130 MPa: maximum thickness 6 mm) (Cr 12, Ni 2.5, Mo 1.7, V 0.3) ICS

2、 49.025.10 BS S 538:1975 This British Standard, having been approved by the Aerospace Industry Standards Committee, was published under the authority of the Executive Board on 30 September 1975 BSI 9 December 2003 The following BSI references relate to the work on this standard: Committee reference

3、ACE/15 Draft for comment 73/32574 DC ISBN 0 580 08922 3 Foreword This publication does not purport to include all the necessary provisions of a contract. Users are responsible for its correct application. Compliance with a British Standard does not of itself confer immunity from legal obligations. S

4、ummary of pages This document comprises a front cover, an inside front cover, pages i and ii, pages 1 and 2, an inside back cover and a back cover. The copyright notice displayed in this document indicates whene the document was last issued. Sidelining in this document indicates the most recent chan

5、ges by amendment. Amendments issued since publication Amd. No. Date Comments 14602 9 December 2003 Indicated by a sidelineBS S 538:1975 BSI 9 December 2003 i Contents Page 1 Inspection and testing procedure 1 2 Manufacture 1 3 Chemical composition 1 4 Surface dressing 1 5 Condition 1 6 Heat treatmen

6、t 2 7 Mechanical properties 2ii blankBS S 538:1975 BSI 9 December 2003 1 1 Inspection and testing procedure 1.1 General. This British Standard shall be used in conjunction with the relevant sections of the latest edition of BS S 500. 1.2 Thickness. The thickness of the material shall be in accordanc

7、e with the latest edition of BS S 500. Material which has been finally hot rolled prior to softening shall satisfy the tolerances applicable to hot-rolled sheet and strip. Material which has been finally cold rolled prior to softening shall satisfy the tolerances applicable to cold-rolled sheet and

8、strip. 1.3 Sulfur printing or deep etching tests. Samples shall be selected in accordance with the latest edition of BS S 500. 2 Manufacture The material shall be manufactured by an electric process. 3 Chemical composition The steel shall contain: 4 Surface dressing The material shall be overall dre

9、ssed. 5 Condition The material shall be supplied in the appropriate condition stated below: Element % min. max. Carbon 0.08 0.13 Silicon 0.35 Manganese 0.5 0.9 Phosphorus 0.030 Sulphur 0.025 Chromium 11.0 12.5 Molybdenum 1.5 2.0 Nickel 2.0 3.0 Vanadium 0.25 0.40 Nitrogen 0.020 0.040 Nominal thicknes

10、s Condition of supply mm Up to and including 3 Cold rolled, softened and descaled NOTE Descaling may be omitted if softening is carried out in a suitable protective atmosphere. Over 3 up to and including 6 Hot rolled, softened and descaledBS S 538:1975 2 BSI 9 December 2003 6 Heat treatment 6.1 Soft

11、ening treatment. The material shall be softened by heating at a temperature of 690 10 C for not less than 6 h, followed by cooling in air or a protective atmosphere. 6.2 Final treatment. The final heat treatment shall be as follows. a) Hardening. Heat at a temperature of 1 050 10 C, followed by cool

12、ing in air. b) Tempering. Heat at a temperature of 650 5 C for 4 h, followed by cooling in air. 7 Mechanical properties 7.1 Tensile test at room temperature. The mechanical properties obtained from test pieces shall be as follows: Note deleted 7.2 Single bend test (applicable only to sheet or strip

13、of nominal thickness less than 1.6 mm). The test piece shall be bent at room temperature without cracking through an angle of 180 over a former with a radius equal to twice the nominal thickness of the sheet or strip. 7.3 Hardness test 7.3.1 The hardness of material heat treated in accordance with 6

14、.1 shall be not greater than 325 HV. 7.3.2 The hardness of parts and test samples heat treated in accordance with 6.2 shall be not less than 320 HV nor greater than 380 HV. Nominal thickness 0.2 % proof stress Tensile strength Elongation min. min. max. min. mm MPa MPa MPa % Less than 1.6 1.6 and ove

15、r 760 760 930 930 1 130 1 130 9blankBS S 538:1975 BSI 389 Chiswick High Road London W4 4AL BSI British Standards Institution BSI is the independent national body responsible for preparing British Standards. It presents the UK view on standards in Europe and at the international level. It is incorpor

16、ated by Royal Charter. Revisions British Standards are updated by amendment or revision. Users of British Standards should make sure that they possess the latest amendments or editions. It is the constant aim of BSI to improve the quality of our products and services. We would be grateful if anyone

17、finding an inaccuracy or ambiguity while using this British Standard would inform the Secretary of the technical committee responsible, the identity of which can be found on the inside front cover. Tel: +44 (0)20 8996 9000. Fax: +44 (0)20 8996 7400. BSI offers members an individual updating service

18、called PLUS which ensures that subscribers automatically receive the latest editions of standards. Buying standards Orders for all BSI, international and foreign standards publications should be addressed to Customer Services. Tel: +44 (0)20 8996 9001. Fax: +44 (0)20 8996 7001. Email: ordersbsi-. St

19、andards are also available from the BSI website at http:/www.bsi-. In response to orders for international standards, it is BSI policy to supply the BSI implementation of those that have been published as British Standards, unless otherwise requested. Information on standards BSI provides a wide ran

20、ge of information on national, European and international standards through its Library and its Technical Help to Exporters Service. Various BSI electronic information services are also available which give details on all its products and services. Contact the Information Centre. Tel: +44 (0)20 8996

21、 7111. Fax: +44 (0)20 8996 7048. Email: infobsi-. Subscribing members of BSI are kept up to date with standards developments and receive substantial discounts on the purchase price of standards. For details of these and other benefits contact Membership Administration. Tel: +44 (0)20 8996 7002. Fax:

22、 +44 (0)20 8996 7001. Email: membershipbsi-. Information regarding online access to British Standards via British Standards Online can be found at http:/www.bsi- Further information about BSI is available on the BSI website at http:/www.bsi-. Copyright Copyright subsists in all BSI publications. BSI

23、 also holds the copyright, in the UK, of the publications of the international standardization bodies. Except as permitted under the Copyright, Designs and Patents Act 1988 no extract may be reproduced, stored in a retrieval system or transmitted in any form or by any means electronic, photocopying,

24、 recording or otherwise without prior written permission from BSI. This does not preclude the free use, in the course of implementing the standard, of necessary details such as symbols, and size, type or grade designations. If these details are to be used for any other purpose than implementation then the prior written permission of BSI must be obtained. Details and advice can be obtained from the Copyright & Licensing Manager. Tel: +44 (0)20 8996 7070. Fax: +44 (0)20 8996 7553. Email: copyrightbsi-.