《SAE AMS 4505K-2009 Copper Alloy (Brass) Sheet Strip and Plate 70Cu - 30Zn Annealed (OS035) (UNS C26000)《70Cu 30Zn退火的(OS035)铜合金(黄铜)薄板材 带材和厚板材》.pdf》由会员分享，可在线阅读，更多相关《SAE AMS 4505K-2009 Copper Alloy (Brass) Sheet Strip and Plate 70Cu - 30Zn Annealed (OS035) (UNS C26000)《70Cu 30Zn退火的(OS035)铜合金(黄铜)薄板材 带材和厚板材》.pdf（4页珍藏版）》请在麦多课文档分享上搜索。

1、AEROSPACE MATERIAL SPECIFICATION AMS4505 REV. K Issued 1940-01 Revised 2009-03 Reaffirmed 2014-10 Superseding AMS4505J Copper Alloy (Brass), Sheet, Strip, and Plate70Cu - 30Zn Annealed (OS035) (Composition similar to UNS C26000) RATIONALE AMS4505K has been reaffirmed to comply with the SAE five year

2、 review policy. _ SAE Technical Standards Board Rules provide that: “This report is published by SAE to advance the state of technical and engineering sciences. The use of this report is entirely voluntary, and its applicability and suitability for any particular use, including any patent infringeme

3、nt arising therefrom, is the sole responsibility of the user.” SAE reviews each technical report at least every five years at which time it may be revised, reaffirmed, stabilized, or cancelled. SAE invites your written comments and suggestions. Copyright 2014 SAE International All rights reserved. N

4、o part of this publication may be reproduced, stored in a retrieval system or transmitted, in any form or by any means, electronic, mechanical, photocopying, recording, or otherwise, without the prior written permission of SAE. TO PLACE A DOCUMENT ORDER: Tel: 877-606-7323 (inside USA and Canada) Tel

5、: +1 724-776-4970 (outside USA) Fax: 724-776-0790 Email: CustomerServicesae.org SAE WEB ADDRESS: http:/www.sae.org SAE values your input. To provide feedback on this Technical Report, please visit http:/www.sae.org/technical/standards/AMS4505K 1. SCOPE 1.1 Form This specification covers a copper-zin

6、c alloy (brass) in the form of sheet, strip, and plate. 1.2 Application These products have been used typically for formed and drawn parts, but usage is not limited to such applications. 2. APPLICABLE DOCUMENTS The issue of the following documents in effect on the date of the purchase order forms a

7、part of this specification to the extent specified herein. The supplier may work to a subsequent revision of a document unless a specific document issue is specified. When the referenced document has been cancelled and no superseding document has been specified, the last published issue of that docu

8、ment shall apply. 2.1 SAE Publications Available from SAE International, 400 Commonwealth Drive, Warrendale, PA 15096-0001, Tel: 877-606-7323 (inside USA and Canada) or 724-776-4970 (outside USA), www.sae.org. AMS2222 Tolerances, Copper and Copper Alloy Sheet, Strip, and Plate SAE INTERNATIONAL AMS4

9、505K Page 2 of 4 2.2 ASTM Publications Available from ASTM International, 100 Barr Harbor Drive, P.O. Box C700, West Conshohocken, PA 19428-2959, Tel: 610-832-9585, www.astm.org. ASTM B 248 General Requirements for Wrought Copper and Copper-Alloy Plate, Sheet, Strip, and Rolled Bar ASTM B 248M Gener

10、al Requirements for Wrought Copper and Copper-Alloy Plate, Sheet, Strip, and Rolled Bar (Metric) ASTM E 18 Rockwell Hardness and Rockwell Superficial Hardness of Metallic Materials ASTM E 112 Determining the Average Grain Size ASTM E 478 Chemical Analysis of Copper Alloys 3. TECHNICAL REQUIREMENTS 3

11、.1 Composition Shall conform to the percentages by weight shown in Table 1, determined by wet chemical methods in accordance with ASTM E 478, by spectrochemical methods, or by other analytical methods acceptable to purchaser. TABLE 1 - COMPOSITION Element (3.1.1) min max Copper 68.5 71.5 Lead - 0.07

12、 Iron - 0.05 Zinc (3.1.2) remainder - Sum of Named Elements (3.1.1) 99.7 - 3.1.1 These composition limits do not preclude the presence of other elements. Limits may be established and analysis required for unnamed elements by agreement between the manufacturer or supplier and purchaser. 3.1.2 Zinc m

13、ay be reported as “remainder”, or as the difference between the sum of results for all elements and 100%, or as the result of direct analysis. 3.1.3 When all the elements in the table are analyzed, the sum shall be 99.7% minimum, but such determination is not required for routine acceptance of each

14、lot. 3.2 Condition Cold rolled and fully recrystallized, annealed (OS035) temper (See 8.2). 3.3 Properties The product shall conform to the following requirements: 3.3.1 Average Grain Size Shall be 0.025 to 0.050 mm, determined in accordance with ASTM E 112. 3.3.2 Hardness Shall be 25 to 38 HR30TW,

15、or equivalent, determined in accordance with ASTM E 18. 3.4 Quality The product, as received by purchaser, shall be uniform in quality and condition, sound, and free from foreign materials and from imperfections detrimental to usage of the product. SAE INTERNATIONAL AMS4505K Page 3 of 4 3.5 Toleranc

16、es Shall conform to AMS2222 as applicable to nonrefractory alloys. 4. QUALITY ASSURANCE PROVISIONS 4.1 Responsibility for Inspection The vendor of the product shall supply all samples for vendors tests and shall be responsible for the performance of all required tests. Purchaser reserves the right t

17、o sample and to perform any confirmatory testing deemed necessary to ensure that the product conforms to specified requirements. 4.2 Classification of Tests All technical requirements are acceptance tests and shall be performed on each lot. 4.3 Sampling and Testing Shall be in accordance with ASTM B

18、 248 or ASTM B 248M. 4.4 Reports The vendor of the product shall furnish with each shipment a report showing the results of tests on each lot to determine conformance to all technical requirements. This report shall include the purchase order number, lot number, AMS4505K, size, and quantity. 4.5 Res

19、ampling and Retesting If any specimen used in the above tests fails to meet the specified requirements, disposition of the product may be based on the results of testing two additional specimens for each original nonconforming specimen. Failure of any retest specimen to meet the specified requiremen

20、ts shall be cause for rejection of the product represented. Results of all tests shall be reported. 5. PREPARATION FOR DELIVERY 5.1 Identification The product shall be identified as in 5.1.1 unless line marking as in 5.1.2 is specified by purchaser. 5.1.1 Each sheet, strip, and plate shall be legibl

21、y marked near one end, coils being marked near the outside end, with AMS4505K, lot number, manufacturers identification, and nominal thickness, using any suitable marking fluid. As an alternative method, individual pieces or bundles shall have attached a durable tag marked with the above information

22、 or shall be boxed and the box marked with the same information. 5.1.2 When specified by purchaser, each sheet, strip, and plate shall be legibly marked on one face, in the respective location indicated below, with AMS4505K, lot number, manufacturers identification, and nominal thickness. The charac

23、ters shall be applied using a suitable marking fluid removable in hot alkaline cleaning solution without rubbing. The markings shall have no deleterious effect on the product or its performance and shall be sufficiently stable to withstand normal handling. The specification number, manufacturers ide

24、ntification, and nominal thickness shall be continuously line marked; the lot number may be included in the line marking or may be marked at one location on each piece. 5.1.2.1 Flat Strip 6 Inches (152 mm) and Under in Width Shall be marked in one or more lengthwise rows of characters recurring at i

25、ntervals not greater than 3 feet (914 mm). SAE INTERNATIONAL AMS4505K Page 4 of 4 5.1.2.2 Flat Sheet, Flat Strip Over 6 Inches (152 mm) in Width, and Plate Shall be marked in lengthwise rows of characters recurring at intervals not greater than 3 feet (914 mm), the rows being spaced not more than 6

26、inches (152 mm) apart and alternately staggered. 5.1.2.3 Coiled Sheet and Strip Shall be legibly marked near both the outside and inside ends of the coil; the markings shall be applied as in 5.1.2 or shall appear on a durable tag or label attached to the coil and marked with the information of 5.1.2

27、. When the product is wound on cores, the tag or label may be attached to the core. 5.2 Packaging The product shall be prepared for shipment in accordance with commercial practice and in compliance with applicable rules and regulations pertaining to the handling, packaging, and transportation of the

28、 product to ensure carrier acceptance and safe delivery. 6. ACKNOWLEDGMENT A vendor shall include this specification number and its revision letter in all quotations and when acknowledging purchase orders. 7. REJECTIONS Product not conforming to this specification, or to modifications authorized by

29、purchaser, will be subject to rejection. 8. NOTES 8.1 A change bar (|) located in the left margin is for the convenience of the user in locating areas where technical revisions, not editorial changes, have been made to the previous issue of a document. An (R) symbol to the left of the document title

30、 indicates a complete revision of the document, including technical revision. Change bars and (R) are not used in original publications, nor in documents that contain editorial changes only. 8.2 Copper temper designations are defined in ASTM B 601. 8.3 Terms used in AMS are clarified in ARP1917. 8.4

31、 Hardness conversion charts for copper alloys are presented in ASTM E 140. 8.5 Purchase documents should specify not less than the following: AMS4505K Form and size of product required Quantity of product required. 8.6 Similar Specifications ASTM B 19 and ASTM B 36 are listed for information only and shall not be construed as an acceptable alternate unless all requirements of the AMS are met. PREPARED BY AMS COMMITTEE “D“